• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2012년도 춘계 학술논문 발표대회
• /
• pp.85-86
• /
• 2012

This application plan is hasty prepared with the actual condition in which the majority is reclaimed by the waste with the marine and the polysilicon sludge, that is the main raw material of the solar pannel support, does. In this research, by using OPC and Fly ash, the applicability as the blending material of the polysilicon sludge was analyze and it tried to contribute to the waste reduction afterward. The replacement ratio of the sludge was set to 5. 10, 15, 20(%) with the experiment based on the based test result and the air flow rate, liquidity, flexural strength, and compressive strength was measured. The liquidity was reduced in spite of as the replacement ratio of the sludge increased and the air flow rate increased.

• 한국세라믹학회지
• /
• 제53권2호
• /
• pp.215-221
• /
• 2016

In this study, the utilization of the by-products of various industries was examined using raw materials of CSA high-functional cement such as coal bottom ash, red mud, phosphate gypsum, etc. Technology to improve energy efficiency and reduce $CO_2$ was developed as part of the manufacturing process; this technology included lower temperature sintering ($150{\sim}200^{\circ}C$) than is used in the OPC cement manufacturing process, replacement of CSA cement with the main raw material bauxite, and a determination of the optimum mix condition. In order to develop CSA cement, a manufacturing system was established in the Danyang plant of the HANIL Cement Co. Ltd., in Korea. About 4,200 tons of low purity expansion agent CSA cement (about 16%) and about 850 tons of the lime-based expansion agent dead burned lime (about 8%) were produced at a rate of 60 tons per hour at the HANIL Cement rotary kiln. To improve the OPC cement properties, samples of 10%, 13%, and 16% of CSA cement were mixed with the OPC cement and the compressive strength and length variation rate of the green cement were examined. When green cement was mixed with each ratio of CSA cement and OPC cement, the compressive strength was improved by about 30% and the expansibility of the green cement was also improved. When green cement was mixed with 16% of CSA cement, the compressive strength was excellent compared with that of OPC cement. Therefore, this study indicates the possibility of a practical use of low-cost CSA cement employing industrial wastes only.

• International Journal of Concrete Structures and Materials
• /
• 제8권4호
• /
• pp.289-299
• /
• 2014

Alkali-activated slag concretes are being extensively researched because of its potential sustainability-related benefits. For such concretes to be implemented in large scale concrete applications such as infrastructural and building elements, it is essential to understand its early and long-term performance characteristics vis-a'-vis conventional ordinary portland cement (OPC) based concretes. This paper presents a comprehensive study of the property and performance features including early-age isothermal calorimetric response, compressive strength development with time, microstructural features such as the pore volume and representative pore size, and accelerated chloride transport resistance of OPC and alkali-activated binder systems. Slag mixtures activated using sodium silicate solution ($SiO_2$-to-$Na_2O$ ratio or $M_s$ of 1-2) to provide a total alkalinity of 0.05 ($Na_2O$-to-binder ratio) are compared with OPC mixtures with and without partial cement replacement with Class F fly ash (20 % by mass) or silica fume (6 % by mass). Major similarities are noted between these binder systems for: (1) calorimetric response with respect to the presence of features even though the locations and peaks vary based on $M_s$, (2) compressive strength and its development, (3) total porosity and pore size, and (4) rapid chloride permeability and non-steady state migration coefficients. Moreover, electrical impedance based circuit models are used to bring out the microstructural features (resistance of the connected pores, and capacitances of the solid phase and pore-solid interface) that are similar in conventional OPC and alkali-activated slag concretes. This study thus demonstrates that performance-equivalent alkali-activated slag systems that are more sustainable from energy and environmental standpoints can be proportioned.

• 한국건설순환자원학회논문집
• /
• 제12권1호
• /
• pp.1-7
• /
• 2024

다공성인 콘크리트에서는 외부의 수분 및 염화물 유입이 발생하며, 이는 매립된 철근의 부식을 야기한다. 본 연구에서는 촉진부식실험(ICM: Impressed Current Method)를 이용하여 10 V의 전압을 인가하였으며, 이에 따라 10 % 수준까지 부식량을 조절하였다. 부식량은 부식전류량 누계와 선형적인 관계가 도출되었으며, 균열의 영향으로 부식 유도 시간에 따라 2차 함수의 형태로 증가하였다. 부착응력에 대해서는 OPC 콘크리트에 대해서는 부식량 3.0 % 이후 급격한 부착응력의 감소가 발생하였다. 또한 치환률 30 %의 슬래그 콘크리트에서는 일반 콘크리트에 비하여 51.4~71.6 %의 낮은 부식량을 나타내었으며 5일간의 촉진실험에도 일정 수준의 부착강도를 유지하였다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2003년도 학술.기술논문 발표회
• /
• pp.43-48
• /
• 2003

This paper investigate that the effect of the concrete containing mineral admixtures(pozzolanic materials such as fly-ash, ground granulated blast-furnace slag, silica fume and meta kaolin) on the resistance properties to chloride ion invasion. The purposed testing procedure was applied to the concrete added mineral admixtures for 3~4 replacement ratios under W/B ratios ranged from 0.40 to 0.55. For the electrical migration test, Tang and Nilsson's method was used to estimate the migration coefficient of chloride ion. As a results, the W/B ratios, kinds of admixture and replacement ratios, water curing periods had a great effect on the migration coefficient of chloride ion, and the optimal replacement ratios of admixture had a limitation for each admixtures. Also, the addition of mineral admixtures by mass(replacement of OPC) enhanced the resistance of the mixture to chloride penetration compared with the plain concrete. The amount of acid soluble chloride ions and water soluble chloride ions were varied with the kinds of mineral admixtures. The compressive strength was shown related to the migration coefficient of chloride ion, the compressive strength increased with the decreasing migration coefficient of chloride ion. Below the 50MPa, the variation of migration coefficient of concrete added mineral admixtures was bigger than plain concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2003년도 학술.기술논문발표회
• /
• pp.43-48
• /
• 2003

This paper investigate that the effect of the concrete containing mineral admixtures(pozzaolanic materials such as fly-ash, ground granulated blast-furnace slag, silica fume and meta kaolin) on the resistance properties to chloride ion invasion. The purposed testing procedure was applied to the concrete added mineral admixtures for 3∼4 replacement ratios under W/B ratios ranged from 0.40 to 0.55. For the electrical migration test, Tang and Nilsson's method was used to estimate the migration coefficient of chloride ion. As a results, the W/B ratios, kinds of admixture and replacement ratios, water curing periods had a great effect on the migration coefficient of chloride ion, and the optimal replacement ratios of admixture had a limitation for each admixtures. Also, the addition of mineral admixtures by mass(replacement of OPC) enhanced the resistance of the mixture to chloride penetration compared with the plain concrete. The amount of acid soluble chloride ions and water soluble chloride ions were varied with the kinds of mineral admixtures. The compressive strength was shown related to the migration coefficient of chloride ion, the compressive strength increased with the decreasing migration coefficient of chloride ion. Below the 50MPa, the variation of migration coefficient of concrete added mineral admixtures was bigger than plain concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 춘계 학술발표회 제20권1호
• /
• pp.537-540
• /
• 2008

RC 구조물은 반영구적인 재료로 인식되어 왔으나, 최근 RC 구조물의 조기 열화에 의한 문제가 보고되고 있다. 이중 내구성능 저하 요인으로서 탄산화에 의한 공극구조의 변화로 인하여 발생하는 문제에 대한 연구가 필요한 실정이다. 따라서 본 연구에서는 물-결합재비율을 0.55로 고정하고 결합재로서 보통포틀랜드 시멘트만을 사용한 (OPC), 이성분계 콘크리트로서 결합재에 고로슬래그 미분말을 50% 치환한 (BFS50), 플라이애시를 15% 치환한 (FA15), 또한 삼성분계 콘크리트로서 플라이애시 15% 및 고로슬래그 미분말을 35% 치환한 (BFS35+FA15)로 배합을 설정하였다. 또한 탄산화에 진행에 의한 공극구조의 변화로 열화요인의 작용으로 인한 $CO_2$ 및 염화물 이온의 침투 특성을 단독열화 시험과 복합열화 시험을 통해 비교 연구하여 평가를 실시하였다. 그 결과 공극구조의 변화에 따른 영향으로 인하여 염화물 이온의 침투속도가 영향을 받는 것으로 나타났다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.577-580
• /
• 2006

This paper presents the experimental results of frost durability characteristics including freezing-thawing and de-icing salt scaling of the concrete used for gutter of the road. Mixtures were proportioned with the three level of water-binder ratio (W/B), 0.58, 0.53, and 0.48, and two binder compositions corresponding to Type I cement without any supplementary cementitious materials (OPC) and Type I cement with 30% blast-furnace slag replacement (Slag30). Also, two different solutions of calcium chloride and water that contains 0 and 8g of anhydrous calcium chloride in each 100 mL of solution, respectively, were used to evaluate their effect on the frost durability resistance. Test results showed that the Slag30 mixture exhibited higher durability factor and lower mass loss values than those made with OPC. Among the mixture tested in this work, the mixtures (OPC and Slag30) made with a relatively higher W/B of 0.58 exhibited large amount of the de-icing salt scaling regardless of calcium chloride concentration. Finally, the use of slag can be used effectively in terms of economy and frost durability of the concrete designated for gutter.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 추계 학술발표회 제17권2호
• /
• pp.639-642
• /
• 2005

Main components of metakaolin(MK) were $SiO_2\;and\;Al_2O_3$. and specific surface was 2.2 times larger than that of ordinary portland cement(OPC). MK indicated the fine particle and fiber texture. Flow value of mortar with MK was decreased linearly each $13\%$ as the replacement ratio of MK was increased each $5\%$. Compressive strength of mortar with MK was increased more than that of mortar with OPC by 3days. Compressive strength of mortar with $10\%$ MK was about 83MPa at 28 days. When MK was replaced with $10\%$ of cement volume, flexural strength and modulus of elasticity of mortar was indicated the maximum value at 28 days.

• 전기학회논문지
• /
• 제56권2호
• /
• pp.338-342
• /
• 2007

The increase of activated carbon contents in fly ashes accelerate the corrosion of steel embedded in ordinary portland cement(OPC) mortar. Cement losses its identity of colour when the % of carbon is increased. More than 60[%] area was rusted when carbon content is increased beyond 8[%] for the exposure period of one year. Comparable corrosion rate with OPC was obtained up to 6[%] carbon level only. The tolerable limit of replacement for various admixed carbon system under aggressive alternate wetting and drying condition with 3[%] NaCl was found to be 6 to 8[%].