• Nuclear Engineering and Technology
• /
• 제16권2호
• /
• pp.58-63
• /
• 1984

특별히 제작한 영동장치를 써서 8면체 구조의 (Ruc $l_{6}$)$^{3-}$ 를 여과지 전기영동 분리하였다. 자지전해질 용액은 다음과 같다. 0.1M-HCl $O_4$, 0.05M-HCl+0.09M-KCI, 0.1M-HCl, 5$\times$$10^{-3}$M-NTA, 0.01M-HCl, 0.01M-HCl $O_4$, 0.01M-시트르산, 0.01M-K $H_2$P $O_4$+0.01M-$Na_2$HP $O_4$, 0.05M-붕사, 0.025M-$Na_2$C $O_3$+0.025M-NaHC $O_3$, 0.01M-$Na_3$P $O_4$, 0.01M-NaOH, 0.1M-NaOH. (Ruc $l_{6}$)$^{3-}$ 은 2-4피크로 나타내며 다음 화학종으로 확인된다. (RuCl($H_2O$)$_{5}$ )$^{2+}$, cis- 및 trans-(RuC $l_2$($H_2O$)$_4$)$^{1+}$ , (RuC $l_3$($H_2O$)$_3$)$^{0}$ , (RuC $l_4$($H_2O$)$_2$)$^{1-}$, (RuC $l_{5}$ ($H_2O$))$^{2-}$ , (RuC $l_{6}$)$^{3-}$ . 리텐숀 값은 0.025M-$Na_2$C $O_3$+0.025M-NaHC $O_3$ 전해질 용액에서 가장 높다.

• 한국진공학회지
• /
• 제5권2호
• /
• pp.147-155
• /
• 1996

Optical properties of $TiO_2/M/Ag/M/TiO_2$ films have been changed with the diffusion barrier metal M. Optimum opticla properties of $TiO_2/M/Ag/M/TiO_2$ as the transparent heat mirror film, could be obtained with Ti among diffusion barrier metals of Ti, Cu, Zr and Al. $TiO_2/M/Ag/M/TiO_2$ film, which was fabricated by sputtering of 18 nm-thick $TiO_2$ and Ag, and 4nm-thick Ti, showed maximum transimittance of 89% at visible wavelength and infrared reflectance of 97% at wavelength of 3000 nm. Optical properties of this film was not degraded by Xenon-sunshine weather test for 240 hours. For specimens with barrier layers of Cu, Zr, and Al, degradation of optical properties by weather test was increased in a sequence of films with Cu, Zr, and Al barrier layers.

• 시스템엔지니어링학술지
• /
• 제14권1호
• /
• pp.83-88
• /
• 2018

Engineering is a sector with more than three times the industrial effectiveness of manufacturing. In the domestic engineering life cycle, the Operations & Maintenance (O&M) phase is a relatively high level of technology. Based on accumulated knowledge of O&M phase, it is necessary to advance operating technology and expand overseas O&M market expenditure. This study is the early stage of knowledge-based power plant O&M service framework reference model. In this study, we propose a conceptual model of architecture framework for power plant O&M. We survey the architecture framework and reference model and propose conceptual model of architecture framework for power plant O&M. The conceptual model of architecture framework for power plant O&M consists of stakeholder, O&M scenario, O&M technology. In particular, the O&M technology is defined as the fourth industrial revolution intelligence information technology. We defined a meta model from the conceptual model to define the power plant O&M architecture framework. In the future, we intend to development an architecture framework from the conceptual model and meta model.

• 교육시설 논문지
• /
• 제24권5호
• /
• pp.11-18
• /
• 2017

An university dorm has significant implications in terms of providing residential, living, and learning spaces. With its supportive function, a dorm enables each university to provide higher level of education. The operation & maintenance(O&M) condition of the dorm has a decisive effect on the students' satisfaction. Accordingly, high levels of O&M services should be performed for students. However, Korean dorms are being operated and maintained by their own O&M guidelines without the consideration of spatial characteristics of dorm facilities and the comprehensive and systematic understanding on effective O&M processes. Given the fact that dorm facility can be a crucial factor in determining the entire quality of university and its O&M condition is closely related to the satisfaction of students, it is imperative that we need to pay more attention to the O&M condition and services. Therefore, the main objective of this research is to improve dorm students' satisfaction levels by applying different O&M method, preventive maintenance rather than reactive maintenance which has been performed so far. In ordering for doing it, 'Facility Management(FM) Standard' from KS, 'Facility Performance Indicator(FPI)' from APPA: Leadership in educational facilities and 'Building O&M Inspection Manual' from Korean Ministry of Land, Infrastructure and Transport were analyzed to come up with 15 significant O&M factors. After extracting O&M factors, the survey was conducted to determine importance rate and performance rate of each O&M factor. Using the Important-Performance Analysis(IPA), the priority of 15 O&M factors was established. The result of this research will be helpful for the efficient dorm facility O&M services and for facility managers to appropriately allocate the limited resources and human power.

• 한국환경과학회지
• /
• 제23권5호
• /
• pp.903-910
• /
• 2014

This study examined the treatment characteristics of hard-to-degrade pollutants such as TCE which are found in organic solvent and cleaning wastewater by nZVI that have excellent oxidation and reduction characteristics. In addition, this study tried to find out the degradation characteristics of TCE by Fenton-like process, in which $H_2O_2$ is dosed additionally. In this study, different ratios of nZVI and $H_2O_2$, such as 1.0 mM : 0.5 mM, 1.0 mM : 1.0 mM, and 1.0 mM : 2.0 mM were used. When 1.0 mM of nZVI was dosed with 1.0 mM of $H_2O_2$, the removal efficiency of TOC was the highest and the first order rate constant was also the highest. When 1mM of nZVI was dosed with 0.5 mM of $H_2O_2$, the first order rate constant and removal efficiency were the lowest. The size of first order rate constant and removal efficiency was in the order of nZVI 1.0 mM : $H_2O_2$ 1.0 mM > nZVI 1.0 mM : $H_2O_2$ 2.0 mM > nZVI 1.0 mM : $H_2O_2$ 0.5 mM > $H_2O_2$ 1.0 mM > nZVI 1.0 mM. It is estimated that when 1.0 mM of nZVI is dosed with 1.0 mM of $H_2O_2$, $Fe^{2+}$ ion generated by nZVI and $H_2O_2$ react in the stoichiometric molar ratio of 1:1, thus the first order rate constant and removal efficiency are the highest. And when 1.0 mM of nZVI is dosed with 2.0 mM of $H_2O_2$, excessive $H_2O_2$ work as a scavenger of OH radicals and excessive $H_2O_2$ reduce $Fe^{3+}$ into $Fe^{2+}$. As for the removal efficiency of TOC in TCE by simultaneous dose and sequential dose of nZVI and $H_2O_2$, sequential dose showed higher first order reaction rate and removal efficiency than simultaneous dose. It is estimated that when nZVI is dosed 30 minutes in advance, pre-treatment occurs and nanoscale $Fe^0$ is oxidized to $Fe^{2+}$ and TCE is pre-reduced and becomes easier to degrade. When $H_2O_2$ is dosed at this time, OH radicals are generated and degrade TCE actively.

• 대한수학회논문집
• /
• 제21권4호
• /
• pp.739-747
• /
• 2006

By using O(m+n, 1)/$O(m){\times}O(n,1)-system$, we give an analytic version of Ribaucour transformation for flat m-dimensional submanifolds in $\mathbb{H}^{m+n}$ with flat, non-degenerate normal bundle and free of weak umbilics, where $n{\geq}m-1$.

• 한국세라믹학회지
• /
• 제32권5호
• /
• pp.582-586
• /
• 1995

The crystal structures of (Na0.3Sr0.7)(Ti0.7M0.3)O3 (M=Ta, Nb) compounds were determined using the Rietveld method. Due to the tilting of a oxygen octahedron, (Na0.3Sr0.7)(Ti0.7Nb0.3)O3 had a superlattice of doubled a, b and c of simple perovskite. The crystal structure of (Na0.3Sr0.7)(Ti0.7M0.3)O3 was tetragonal with a space group 14/mmm. The crystal structure of (Na0.3Sr0.7)(Ti0.7M0.3)O3 was a cubic with space group Pm3m, in which no tilting of oxygen octahedron was observed. The difference in the oxygen tilting of these two materials was due to the larger covalency of Nb-O bond than that of Ta-O bond, which induced a strong $\pi$Nb0 bonding in (Na0.3Sr0.7)(Ti0.7M0.3)O3. Therefore, the higher transition temperature of (Na0.3Sr0.7)(Ti0.7M0.3)O3 could be related to the larger tilting of oxygen octahedron.

• Korean Chemical Engineering Research
• /
• 제45권6호
• /
• pp.648-655
• /
• 2007

UV/H_2O_2$, $O_3$, $O_3/H_2O_2$, $UV/H_2O_2/O_3$ 공정을 이용한 테레프탈산 제조공정 폐수의 COD 및 색도제거 연구를 수행하였다. UV/H_2O_2$, $O_3$, $O_3/H_2O_2$, $UV/H_2O_2/O_3$ 공정에서의 COD 제거율은 각각 10, 48, 56, 63%, 색도 제거율은 $UV/H_2O_2$ 공정이 80%, $O_3$, $O_3/H_2O_2$, $UV/H_2O_2/O_3$ 공정은 모두 99% 이상 효과적으로 제거되는 것으로 나타났다. COD 및 색도 제거율이 가장 우수한 $UV/H_2O_2/O_3$ 공정에서 테레프탈산 제조공정 폐수의 주요 유기물 성분인 테레프탈산, 이소프탈산 그리고 벤조산 성분은 120분 이내에 모두 99% 이상 제거되었다. 또한 $UV/H_2O_2$, $O_3/H_2O_2$, $UV/H_2O_2/O_3$ 공정에서의 최적 $H_2O_2$ 주입농도는 각각 0.5M, 25 mM 그리고 5 mM로 나타나, UV와 $H_2O_2$를 오존산화 공정에 조합함으로써 유기물 제거율 향상과 함께 사용된 $H_2O_2$의 저감효과를 동시에 얻을 수 있었다.

• 대한화학회지
• /
• 제22권5호
• /
• pp.295-303
• /
• 1978

정팔면체[Co(III)-$O_3N_3$], 정사면체[M(II)-$O_2N_2$] 및 정사각형형[M(II)-$O_2N_2$]형태 착물의 쌍극자모멘트를 중심이온의 valence basis sets와 리간드의 single basis 궤도함수($2p_z$)를 사용하여 spherical harmonics의 전개방법에 의하여 계산하였다. 이들 착물에 대하여 계산한 쌍극자모멘트의 값이 실험치와 일치하였다.

• 한국세라믹학회지
• /
• 제23권5호
• /
• pp.25-34
• /
• 1986

This study was to refined the crystal structure of solid solution to determine the position and amount of Al in diopside and to relate crystal structure changes and properties of solid solution. Single crystals of the solid solution in the system CaO.MgO.$2 SiO_2-Al_2O_3$ were made from the melt with slow cooling and used to refine the structure. The following were obtained. 1. Tetrahedra rotated around axis parallel to the direction which the angle 03-03-03 became small. 2. Tetrahedron became large and regular. Average T-O bond distance increased 0.53 percent. 3. M1 octahedron became small and average M1-O bond distance decreased 1.1 percent. 4, M2 polyhedron became small and average M2-O bond distance decreased 0.37 percent Polythedron was affected not so much compared with any cation site. 5. Distance between metal ions distances between T and oxygens which were coordinated with M2 and meighboring tetrahedron distances between M2 and oxygens which coordinated with M1 and M2 were not changed almost. 6. $Al^{3+}$ substituted 4Mg^{2+}$ and $Si^{4+}$