• Journal of Powder Materials
• /
• v.15 no.2
• /
• pp.87-94
• /
• 2008

In order to investigate a nitriding process of spent oxide fuel and the subsequent change in thermal properties after nitriding, simulated spent fuel powder was converted into a nitride pellet with simulated fission product elements through a carbothermic reduction process. Nitriding rate of simulated spent fuel was decreased with increasing of the amount of fission products. Contents of Ba and Sr in simulated spent fuel were decreased after the carbothermic reduction process. The thermal conductivity of the nitride pellet was decreased by an addition of fission product element but was higher than that of the oxide fuel containing fission product elements.

• Journal of the Korean Ceramic Society
• /
• v.45 no.3
• /
• pp.161-166
• /
• 2008

The multi-films of a metallic film and a transparent conducting oxide (TCO, indium-tin oxide, ITO) film were formed on the stainless steel 316 and 304 plates by a sputtering method and an E-beam method and then the external metallic region of the stainless steel bipolar plates was converted into the metal nitride films through an annealing process. The multi-film formed on the stainless steel bipolar plates showed the XRD patterns of the typical indium-tin oxide, the metallic phase and the metal substrate and the external nitride film. The XRD pattern of the thin film on the bipolar plates modified showed two metal nitride phases of CrN and $Cr_2N$ compound. Surface microstructural morphology of the multi-film deposited bipolar plates was observed by AFM and FE-SEM. The metal nitride film formed on the stainless steel bipolar plates represented a microstructural morphology of fine columnar grains with 10 nm diameter and 60nm length in FE-SEM images. The electrical resistivity of the stainless steel bipolar plates modified was evaluated.

• Proceedings of the KIPE Conference
• /
• 2008.06a
• /
• pp.646-648
• /
• 2008

The multi-films of a metallic film and a transparent conducting oxide (TCO, indium-tin oxide, ITO) film were formed on the stainless steel 316 and 304 plates by a sputtering method and an E-beam method and then the external metallic region of the stainless steel bipolar plates was converted into the metal nitride films through an annealing process. The multi-film formed on the stainless steel bipolar plates showed the XRD patterns of the typical indium-tin oxide, the metallic phase and the metal substrate and the external nitride film. The XRD pattern of the thin film on the bipolar plates modified showed two metal nitride phases of CrN and $Cr_2N$ compound. Surface microstructural morphology of the multi-film deposited bipolar plates was observed by AFM and FE-SEM. The electrical resistivity of the stainless steel bipolar plates modified was evaluated.

• Nuclear Engineering and Technology
• /
• v.52 no.6
• /
• pp.1208-1212
• /
• 2020

Knowledge on fuel enthalpy and its temperature derivative, the heat capacity, are important quantities in determination of fuel behavior in normal reactor operation and reactor transients. The aim of this study is to compare the heat capacity of oxide and nitrite fuels by using Einstein-Debye approximation. A simple analytical expression was performed to calculate the heat capacity of fuels. To test the validity and reliability, the calculated formulas were compared to published results for various nuclear fuels including UO₂, ThO₂, PuO₂ and UN. Calculated formulas yielded results in consistent with literature.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05a
• /
• pp.489-494
• /
• 1997

A comparative transient analyses were performed for oxide and nitride cores or a large (3000 MWt), pool-type, liquid-metal-cooled reactor (LMR). The study was focused on three representative accident initiators with failure to scram : the unprotected loss-of-flow (ULOF), the unprotected transient overpower (UTOP), and the unprotected fast transient overpower (UFTOP). The margins to fuel melting and sodium boiling have been evaluated for these representative transients. The results show that there is an increase in safety margin with nitride core which maintains the physical dimensions of the oxide core.

• Proceedings of the Korean Nuclear Society Conference
• /
• 2003.05a
• /
• pp.68-68
• /
• 2003

• Proceedings of the Korean Nuclear Society Conference
• /
• 2005.05a
• /
• pp.133-134
• /
• 2005

• Nuclear Engineering and Technology
• /
• v.55 no.3
• /
• pp.1097-1104
• /
• 2023

A preliminary criticality analysis for novel pyrochemical apparatuses for the reprocessing of mixed uranium-plutonium nitride spent nuclear fuel from the BREST-OD-300 reactor was performed. High-temperature processing apparatuses, "metallization" electrolyzer, refinery remelting apparatus, refining electrolyzer, and "soft" chlorination apparatus are considered in this work. Computational models of apparatuses for two neutron radiation transport codes (MCU-FR and MCNP) were developed and calculations for criticality were completed using the Monte Carlo method. The criticality analysis was performed for different loads of fissile material into the apparatuses including overloading conditions. Various emergency situations were considered, in particular, those associated with water ingress into the chamber of the refinery remelting apparatus. It was revealed that for all the considered computational models nuclear safety rules are satisfied.

• Journal of Adhesion and Interface
• /
• v.15 no.2
• /
• pp.63-68
• /
• 2014

Hollow mesoporous carbon nitride material with sphere shape was synthesized using polystyrene sphere as template and cyanamide as nitrogen and carbon atom sources via thermal treatment process. The process of the silica removal is not necessary because silica as template is not in use for the synthesis of hollow mesoporous carbon nitride material and any solvents are also not in use. The size of polystyrene spheres was about 170 nm. Hollow diameter and wall thickness were 82 nm and 13 nm, respectively, in hollow mesoporous carbon nitride sphere. Surface area, mesopore size and pore volume of hollow mesoporous carbon nitride material was $188m^2g^{-1}$, 3.8 nm and $0.35cm^3g^{-1}$, respectively. The wall in hollow sphere has graphitic structure. Hollow mesoporous carbon nitride material has potential applications in the area of fuel cell, catalysis, photocatalysis, electroemmision device, etc.

• Korean Chemical Engineering Research
• /
• v.50 no.1
• /
• pp.118-127
• /
• 2012

TiN or Ti/TiN was coated on stainless steel as bipolar plate in polymer electrolyte membrane fuel cells (PEMFCs) to improve their corrosion resistance and electric conductivity, and their properties were examined under fuel cell operating condition. After 200 hours operation, the behaviors for the corrosion, crack and dissolution of coating layer were investigated by various techniques. The corrosion and exfoliation of coating layer were considerably generated except for SUS316L-Ti/TiN after fuel cell operation even if the electric conductivity and corrosion resistance of coated stainless steel bipolar plates were improved. The adoption of Ti layer between TiN layer and the surface of stainless steel enhanced the adhesion of TiN layer and decreased the possibility of corrosion by the increase of coating layer.