• 한국재료학회지
• /
• 제9권6호
• /
• pp.615-621
• /
• 1999

The new process in order to fabricate of Ni catalyst with high activity by the mechanochemical(MC) method which was combined the mechanical alloying(MA) and the chemical treatment process. The microstructure and characterization of mechanically alloyed Ni-5-wt% Al powder and Ni catalyst gained by alkali leaching were investigated byt he various analysis such as XRD, SEM-EDS, HRTEM and laser particle analyzer. The steady state powder with 1~2$\mu\textrm{m}$ mean particle size was obtained after 30hr milling with the PCA of 2 wt% stearic acid under the condition of grinding stainless steel ball to powder ratio of 60:1 and rotating speed fo 300rpm. According to result of HRTEM diffraction pattern, MA powder of the steady state was nanocrystalline $Al_3$$Ni_2$ intermetallic compound. Ni catalyst was obtained after KOH leaching of the steady state powder was about 20nm nanocrystalline which contained about 8 wt % Al.

• Korean Chemical Engineering Research
• /
• 제44권2호
• /
• pp.160-165
• /
• 2006

니켈 분말을 이용하여 제조된 다공성 니켈 지지체 위에 팔라듐-구리-니켈 합금 수소 분리막을 제조하였다. 다공성 니켈 지지체는 열적안정성과 수소취성에 강한 모습을 나타내었으며, 다공성 니켈 지지체에 기존의 습식 방식인 염산에 의한 표면 전처리 방식을 건식 방식인 플라즈마 표면개질로 대체하였다. 다공성 니켈 지지체의 기공을 매립하기 위해 전해도금방식으로 $2{\mu}m$의 두께로 코팅하였으며, 그 후 니켈 도금된 지지체 위에 스퍼터 방식으로 팔라듐을 $4{\mu}m$, 구리를 $0.5{\mu}m$의 두께로 코팅하였다. 이와 같이 제조된 시편을 $700^{\circ}C$에서 1시간 구리 리플로우를 통해 미세기공이 없는 매우 치밀한 팔라듐-구리-니켈 합금 분리막을 제조하였다. 그 결과 팔라듐-구리-니켈 합금 수소분리막은 다공성 니켈지지체와 좋은 접착성을 가지고 있으며 수소-질소 혼합가스에서 무한대의 분리도 값을 나타내었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.621-624
• /
• 2002

Lanthanum nickel oxide$(LaNiO_3)$ powders have been prepared via a mechanochemical processing without any additional heat treatment. When a mixed lanthanum and nickel oxide was mechanically activated for 6 hours with 450 rpm, a stable and single phase perovskite powder was successfully synthesized and its crystallite size of about 90 nm is calculated by using the Scherrer equation.

• Bulletin of the Korean Chemical Society
• /
• 제35권11호
• /
• pp.3213-3218
• /
• 2014

A metal organic framework-supported Nickel nanoparticle (Ni-MOF-5) was successfully synthesized using a simple impregnation method. The obtained solid acid catalyst was characterized by Powder X-ray diffraction (XRD), scanning electron microscopy (SEM), nitrogen adsorption-desorption and thermogravimetric analysis (TGA). The catalyst was highly crystalline with good thermodynamic stability (up to $400^{\circ}C$) and high surface area ($699m^2g^{-1}$). The catalyst was studied for the oxidation of ethyl benzene, and the results were monitored via gas chromatography (GC) and found that the Ni-MOF-5 catalyst was highly effective for ethyl benzene oxidation. The conversion of ethyl benzene and the selectivity for acetophenone were 55.3% and 90.2%, respectively.

• 한국산학기술학회논문지
• /
• 제18권5호
• /
• pp.16-21
• /
• 2017

본 연구의 목적은 스테인레스 강 제조시 발생하는 페로니켈 슬래그를 파쇄한 미분말을 이용하여 지하매설물용 유동성 뒤채움재로 활용하기 위한 것이다. 페로니켈 슬래그 미분말을 이용한 유동성 뒤채움재의 최적배합설계를 수행하였다. 실험용 조합은 Case A (모래), Case B (흙) 등 2개 조합을 이용하였다. Case A의 최적배합비는 모래(58.4%), 페로니켈 슬래그 미분말 (21.6%), 시멘트(1.8%), 물(18.2%)이고, Case B의 최적배합비는 흙(53.0%), 페로니켈 슬래그 미분말 (20.0%), 시멘트(1.7%), 물(25.3%)로 결정되었다. 전체적으로 일반모래에 페로니켈슬래그 미분말을 혼합한 Case A의 일축압축강도가 흙을 이용한 Case B에 비해 상대적으로 크게 나타났다. 또한, 시편의 강도는 양생시간에 따라 증가하는 경향을 나타냈다. 전체적으로 양생시간에 따라 일축압축강도가 증가하는 경향을 보이고 있다. 또한, 일반모래를 주재료로 이용한 유동성뒤채움재의 일축압축강도가 흙을 주재료로 이용한 혼합재료에 비해 상대적으로 크게 나타났다. Case A의 경우 양생시간 7일, 14일 및 28일에 따른 일축압축강도의 범위는 각각 0.17-0.33 MPa, 0.21-0.39 MPa, 0.19-0.40 MPa 수준으로 평가되었다. 실험결과로부터 Case A3 정도면 FNS미분말과 시멘트 혼합비율 가장 적정한 것으로 판단되었다. 흙을 주재료로 이용한 Case B의 경우도 Case A와 전체적으로 유사한 경향을 나타냈다. FNS미분말의 환경유해성 평가를 위한 용출시험결과, 환경에 유해한 물질의 용출은 없는 것으로 나타났다.

• 한국분말재료학회지
• /
• 제3권1호
• /
• pp.49-56
• /
• 1996

The effect of$H_{2}/N_{2}$gas sintering atmosphere on the carbon content and mechanical properties during the metal injection molding process of carbonyl iron-nickel powder was studied. The carbon content of the specimen after debinding in the pure$N_{2}$atmosphere appeared 0.78 wt%. After showing the maximum value of 1.48 wt.% in the debinding atmosphere of 10%$H_{2}/N_{2}$gas mixture, the carbon content of the debinded specimen decreased gradually with increasing the$H_2$content in the$H_{2}/N_{2}$gas mixture. The carbon contents of the sintered specimen were 0.46~0.63wt% in Na gas atmosphere, while they appeared extremely low above 40%$H_{2}/N_{2}$gas atmosphere. The relative sintered density increased abruptly from 88~90% to 93~96% with the addition of Ni, while the density nearly unchanged above 2% Ni addition. The sintered density increased with increasing the fraction of$H_{2} in H_{2}/N_{2}$gas mixture. Tensile strength and hardness increased, and elongation decreased with increasing carbon and Ni content. In spite of high carbon content of 0.63 wt%, the superior elongation value of 10% was shown.

• 한국재료학회지
• /
• 제16권6호
• /
• pp.341-345
• /
• 2006

[ $Ni_2Si$ ] mixed powders were mechanically alloyed by a ball mill and then processed by hot isostatic pressing (HIP) and spark plasma sintering (SPS). In the powder that was mechanically alloyed for 15minutes(MA 15 min), only Ni and Si were observed but in the powder that was mechanically alloyed for 30minutes(MA 30 min), $Ni_2Si$, Ni and Si were mixed together. Some of the MA 15 min powder and MA 30 min powder were processed by HIP under pressure of 150MPa at the temperature of $1000^{\circ}C$ for two hours and some of them were processed by SPS under pressure of 60 MPa at the temperature of $1000^{\circ}C$ for 60 seconds. Both methods completely compounded the powders to $Ni_2Si$. The maximum density of sintered lumps by HIP method was 99.5% and the maximum density of the sintered lump by SPS method was 99.3%. with the hardness of HRc 66 with the hardness of HRc 63. Therefore, the SPS method that can sinter in short time at low cost is considered to be more economical that the HIP method that requires complicated sintering conditions and high cost and the sintering can produce target materials in desired sizes and shapes to be used for thin film.

• 한국수소및신에너지학회논문집
• /
• 제3권2호
• /
• pp.45-54
• /
• 1992

An applicability microencapsulation, using electroless copper plating, of hydrogen storage alloy powder as an anode material for nickel-hydrogen secondary batteries was investigated. Alloys employed were $LaNi_{4.7}Al_{0.3}$ and $MmNi_{4.5}Al_{0.5}$(Mm=mischmetal) which have an appropriate equilibrium pressure and capacity. The microencapsulation of the alloy powder was found to accelerate initial activation of electrodes and to increase capacity which is about 285mAh/g for $LaNi_{4.7}Al_{0.3}$. In addition, other charge and discharge characteristics, such as polarization and flatness of charge and discharge potential, were improved due to the role of copper layer as a microcurrent collector and an oxidation barrier of the alloy powder. $MmNi_{4.5}Al_{0.5}$ alloy showed lower capacity than $LaNi_{4.7}Al_{0.3}$ because of higher equilibrium pressure. Cyclic characteristics of both alloys were somewhat poor because of mainly shedding and partial oxidation of alloy powder during the cycling. However, it was considered that the microencapsulation method is effective to improve the performances of the hydrogen storage alloy electrodes.

• 공업화학
• /
• 제17권5호
• /
• pp.458-464
• /
• 2006

팔라듐 합금 복합막의 제조는 니켈 분말과 무기화합물의 혼합물로 개질된 튜브형 다공성 스테인레스 스틸 지지체 표면 위에 무전해 도금법(elctroless plating technique)에 의해 팔라듐 - 니켈 - 은을 박막으로 도금하는 형태로 이루어졌다. 일반적인 다공성 금속 지지체는 기공이 크기 때문에 그 자체로서 도금에 적합한 지지층이 되기가 어렵고, 결함이 없는 팔라듐 복합막의 제조가 쉽지 않아 본 연구에서는 금속 지지체와 팔라듐 사이에 중간층(intermediate layer)을 형성하여 이와 같은 문제점을 극복하고자 하였다. 중간층의 소재인 실리카 졸, 알루미나 졸, 이산화티타늄 졸 등의 무기화합물과 니켈 분말의 혼합물로 다공성 금속 지지체 위에 코팅하여 박막을 형성하고 제조 조건에 따른 질소 투과도를 측정하고 비교하였다. SEM 분석법에 의해 니켈과 무기화합물 혼합물의 표면층의 형성 모습도 측정하였다. 제조된 중간층 가운데 이산화티타늄 졸과 니켈의 혼합물이 가장 낮은 질소 투과도와 치밀한 표면층을 나타내었다. 최종적으로 니켈과 실리카의 혼합 중간층으로 이루어진 팔라듐-니켈-은 합금 복합막을 제조하고 수소와 질소의 투과도를 측정하였다. 1기압 이하에서 질소에 대한 수소 선택도는 무한대였으며 수소투과 속도는 1 기압, $500^{\circ}C$에서 $1.39{\times}10^{-2}mol/m^2{\cdot}s$의 값을 나타냈다.

• 한국표면공학회지
• /
• 제45권6호
• /
• pp.248-256
• /
• 2012

A Pd-based hydrogen membranes for hydrogen purification and separation need high hydrogen perm-selectivity. The surface roughness of the support is important to coat the pinholes free and thin-film membrane over it. Also, The pinholes drastically decreased the hydrogen perm-selectivity of the Pd-based composite membrane. In order to remove the pinholes, we introduced various surface pre-treatment such as alumina powder packing, nickel electro-plating and micro-polishing pre-treatment. Especially, the micro-polishing pretreatment was very effective in roughness leveling off the surface of the porous nickel support, and it almost completely plugged the pores. Fine Ni particles filled surface pinholes with could form open structure at the interface of Pd alloy coating and Ni support by their diffusion to the membrane and resintering. In this study, a $4{\mu}m$ surface pore-free Pd-Cu-Ni ternary alloy membrane on a porous nickel substrate was successfully prepared by micro-polishing, high temperature sputtering and Cu-reflow process. And $H_2$ permeation and $N_2$ leak tests showed that the Pd-Cu-Ni ternary alloy hydrogen membrane achieved both high permeability of $13.2ml{\cdot}cm^{-2}{\cdot}min^{-1}{\cdot}atm^{-1}$ permation flux and infinite selectivity.