• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2008.06a
• /
• pp.405-406
• /
• 2008

• Journal of the Korean Electrochemical Society
• /
• v.12 no.3
• /
• pp.251-257
• /
• 2009

In this study, we fabricated nickel oxide thin film for lithium based electrolyte using sol-gel method. This film was deposited by dip-coating method with mixed solvent of DameH (N,N-dimethylaminoethanol) and DI water. As changing the ratio between DmaeH and DI water, nickel oxide thin film was presented in different charge density and optical transmittance because they were shown various thickness. It was accounted for changing viscosity and density by the ratio of DmaeH and DI water. The thin film synthesized with 1 : 1 ratio of DmaeH and DI water was expressed best electrochromic performance in lithium based electrolyte, because of thick thickness but porous structures.

• Membrane Journal
• /
• v.17 no.4
• /
• pp.381-386
• /
• 2007

Hollow fibers were made using the nickel slurry containing nickel particles and polymers by phase inversion method. And then, metallic filters were fabricated by sintering method at $1,150^{\circ}C$ under reduction condition. Metallic microfiltration membranes were prepared by coating nickel particles on the metallic filter. The properties of the metallic hollow fiber filters and microfiltration membranes such as pore size and strength were investigated. The metallic membrane showed good resistance against acid, base and chlorine. It was observed that the membrane exhibited good recovery rate by back washing.

• Journal of the Korean Vacuum Society
• /
• v.17 no.6
• /
• pp.549-554
• /
• 2008

Nickel Chloride coated protein chip plates were developed by using a spin coating method after $H_2$ plasma treatment. The adsorption ability of histidine tagged protein was investigated at various times of plasma treatment. The properties of the nickel chloride and protein on the surface of the slides were assayed using particle size analysis and the extent of the protein adsorption was determined by using a bio imaging analyzer system. The results show that the ability of protein adsorption decreased as increasing the time of $H_2$ plasma treatment. The mechanism on the ability of protein adsorption at the plate surface is discussed on results and discussions. The results also suggest that the surface stabilization of protein chip plates treated by plasma technology may be applicable in biosensor markets.

• Applied Chemistry for Engineering
• /
• v.27 no.5
• /
• pp.502-507
• /
• 2016

This study was conducted to develop novel antimicrobial nano-composites, with the aim of fully utilizing antimicrobial properties of multi-walled carbon nanotubes (MWCNTs), nickel (Ni) and zinc oxide (ZnO). Ni coated-MWCNTs (Ni-CNT) were prepared and evaluated for their potential application as an antimicrobial material for inactivating bacteria. Field emission scanning electron microscopy (FE-SEM), and X-ray energy dispersive spectroscopy (EDS) were used to characterize the Ni coating and morphology of Ni-CNT. Staphylococcus aureus (S. aureus) and Escherichia coil (E. coil) were employed as the target bacterium on antimicrobial activities. Comparing with the nitric acid treated MWCNTs and Ni-CNT which have been previously reported to possess antimicrobial activity towards S. aureus and E. coil, Ni-CNT/ZnO exhibited a stronger antimicrobial ability. The nickel coating was confirmed to play an important role in the bactericidal action of Ni-CNTs/ZnO composites. Also, the addition of ZnO to the developed nanocomposite is suggested to improve the antimicrobial property.

• Carbon letters
• /
• v.26
• /
• pp.51-60
• /
• 2018

An electroless deposition method was used to modify the surface properties of rice husk ceramic particles (RHC) by depositing nano-nickel on the surface of the RHC (Ni-RHC). The dry tribological performances of aluminum matrix composite adobes containing different contents of RHC and Ni-RHC particles have been investigated using a micro-tribometer. Results showed that the Ni-RHC particles substantially improved both the friction and wear properties of the Ni-RHC/aluminum matrix adobes. The optimal concentration was determined to be 15 wt% for both the RHC and Ni-RHC particles. The improvements in the tribological properties of aluminum adobes including the Ni-RHC were ascribed to friction-induced peeling off of Ni coating and formation of protection layer on the wear zone, both of which led to low friction and wear volume.

• Journal of the Korean Chemical Society
• /
• v.65 no.2
• /
• pp.125-132
• /
• 2021

An electrochromic nickel oxide thin film was fabricated on a flexible PET/ITO substrate using a nanocrystallite- dispersed coating sol and bar coater. Nanocrystalline NiOx of 3-4 nm crystallite size was first synthesized by base precipitation and thermal conversion. This NiOx nanocrystallite powder was mechanically dispersed in an alcoholic solvent mixed with a silane binder to prepare a coating sol for thin film. This sol method is different from the normal sol-gel method in that it does not require the conversion of precursor by heat treatment. Therefore, this method provides a very facile method to prepare NiOx thin films on any kind of substrate and it can be easily applied to mass production. The electrochromic performance of this NiOx thin film on PET/ITO electrode with a thickness of about 400 nm was investigated in a nonaqueous LiClO4 electrolyte solution by cyclic voltammetric and repeated chronoamperometric measurements in conjunction with spectrophotometry. The visible light modulation of 44% and the colorization efficiency of 41 ㎠/C at 550 nm were obtained at the step potentials of -0.8/+1.2 V vs Ag and a duration of 30 s.

• Applied Chemistry for Engineering
• /
• v.8 no.4
• /
• pp.685-693
• /
• 1997

We have studied the reforming of carbon dioxide with methane over various supported nickel catalysts. The nickel supported on natural zeolite showed the highest activity and the nickel on acidic support showed higher activity and slow deactivation compared to nickel on basic support. The activity of nickel on natural zeolite increased with increasing loading ratio and showed almost constant activity above 10wt.% loading of nickel. The conversion and yield of products were affected by the mole ratio of reactants and the highest yields of CO and $H_2$ were obtained at $CH_4/CO_2=1$. The deactivation of catalyst was caused by deposition of coke which was formed by the decomposition of methane. The shape of coke was shown to be whisker tripe carbon, and it brought out the slow deactivation of catalyst.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.3
• /
• pp.115-120
• /
• 2006

The codeposition behavior of WC particles from an additive-free nickel sulfate and sulfamate solution has been investigated. Electroplating of Ni/WC composites was carried out at different current density with variation of WC particle size. The Guglielmi adsorption mechanism is applied to the electroplating of the fine WC in Ni matrix. The contents of WC in Ni composite coating were increased both by increasing current density and WC concentration in the bath. The hardness of Ni/WC composite coating at low current density is higher than that at high current density since finer WC particles dispersed through the coating. The codeposition behaviors of Co coated WC particles were also investigated. Conducting layer of particles promoted the codeposition behavior of Ni/WC-Co composite coatings.

• Journal of the Korean institute of surface engineering
• /
• v.25 no.2
• /
• pp.57-65
• /
• 1992

Increasing demands of high corrosion resistant sheet steels for the automotive body panels have been leading to a tendency toward heavier coatings of electroplated sheet steels. The specimens were prepared from lab-scale electroplating simulator with various coating weights of zinc, zinc-iron and zinc-nickel coated sheet steels and evaluated in the light of the application for the automotive body panels. Corrosion resistances by sacrificial action were improved with increasing coating weights for all electroplated sheet under survey, but blistering resistances of pure zinc coated sheet steels were not as much. On the other hand, the adhesions of heavy alloy coatings showed poor powdering performances by the external compressive or tensile forces.