• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.256-256
• /
• 2012

SoP용 재료에 응용하기 위하여 NiCuZn 페라이트계 이용한 이종접합의 관한연구를 하였다. NiCuZn 페라이트계와 유전체의 이종접합특성은 XRD, Dilatometer, LCR meter, FE-SEM, EDS 이용하여 물리 화학적 특성을 조사하였다. NiCuZn 페라이트계는 일반적인 세라믹 제조공정을 이용하여 분말을 제조하였으며, 이종접합은 모든 시편에서 잘 진행되었으며 일부 유전체의 이온들이 페라이트 쪽으로 확산이 진행되었으며 NCZF700계는 $900^{\circ}C$ 소결 시편에서 확산이 진행되지 않은 현상이 나타났다.

• Applied Chemistry for Engineering
• /
• v.20 no.5
• /
• pp.500-504
• /
• 2009

NiCuZn Ferrites, known as preventing EMI/EMC, were prepared and their properties were investigated based on the chemical composition ratio, sintering temperature, and mean particle size. The NiCuZn ferrite made of $Fe_2O_3$ 49.0 mol%, NiO 9.0 mol%, CuO 8.0 mol%, ZnO 34.0 mol% could be applied at the largest range of electromagnetic wave. The optimal calcination and sintering temperature were $900^{\circ}C$ and $1080^{\circ}C$, respectively. The electromagnetic wave loss capacity of its mean particle size $1.12{\mu}m$ was superior to others examined.

• Journal of the Korean Magnetics Society
• /
• v.5 no.6
• /
• pp.947-951
• /
• 1995

The electromagnetic interference is prevented by the high magnetic loss of the ferrite. The absorbing property of electromagnetic wave could be improved by the ferrite that has a finer and more uniform microstructure. The thermal decomposition of organic acid salt provided the uniform composition and fine powder. The absorbing properties of electromagnetic wave were evaluated by the relative complex permeability, permittivity, and the attenuation which is calculated from the results of network analyzer. The permeability and permittivity were increased with increase of the density and with decrease of the grain size. The matching thickness could be reduced with increasing sintered temperature. The attenuation of the Cu-Ni-Zn ferrite showed over 20dB when the matching thickness and the matching frequency range were 6.75mm and from 160MHz to 640MHz, respectively.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.5 no.5
• /
• pp.994-1000
• /
• 2001

With the development of electromagnetic communication technology and increased use of electromagnetic wave, the countermeasure of EMI(Electromagnetic Interference) becomes more important socially, and interest for the electromagnetic wave absorber has also increased. In this paper, we have studied characteristics of frequency dependency on complex permittivity and complex permeability according to the changes of composition rate and sintering temperature of NiCuZn ferrite also known as electromagnetic wave absorber and further looked into effect of electromagnetic wave absorption properties. From the measurement where the composition of $Fe_2O_3$ and ZnO of NiCuZn ferrite was fixed at 49 and 34 mol% respectively while composition of NiO and CuO has been varied at each test, we found out that Initial permeability and permittivity were high and the absorbing ability of electromagnetic wave recorded best with $loss tangent(=\mur"/\mur')$ displays more than 1 within the frequency band of 2MHz~9.5MHz when the composition ratio of NiO was ranged around 8.5~9.5 mol% and the sintering temperature was $1080^{\circ}C$.TEX>.

• Resources Recycling
• /
• v.13 no.6
• /
• pp.37-42
• /
• 2004

The power loss analysis was carried out for Ni-Cu-Zn ferrite sample with different content of NiO and ZnO. The power loss, Pcv decreases monotonically with increasing temperature and attains to a certain value at around 100~120 degrees Celsius. The frequency dependence of Pcv can be explained by Pcv~f$^n$, and n is independent of the frequency, f up to 1 MHz. The Pcv decreases with an increase in ZnO/NiO. The Pcv was separated to hysteresis loss(Ph) and residual loss(Pcv-Ph). The temperature characteristics and compositional dependence of Pcv can be attributed to the Ph, while Pcv-Ph is not affected by both temperature and ZnO/NiO. By analyzing temperature and composition dependence of Ph and initial permeability, ${\mu}_i$ like following equations could be formularized. ${\mu}_i{\mu}_0=I_s^2/(K_I+b{\sigma}_0{\lambda}_s)$ Wh=13.5(I$_s^2/{\mu}_i{\mu}_0)$ Where ${\mu}_0$ is permeability of vacuum, I$_s$ is saturation magnetization, K$_I$ is anisotropy constant, $s_0$ is internal heterogeneous stress, ${\lambda}_s$ is magnetostriction constant, b is unknown constant, and Wh is hysteresis loss per one cycle of excitation (Ph=Wh${\times}$f). Steinmetz constant of Ni-Cu-Zn ferrite, m=1.64~2.2 is smaller than that of Mn-Zn ferrites, which suggests the difference of loss mechanisms between these materials.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2004.12a
• /
• pp.3-11
• /
• 2004

The power loss analysis was carried out for Ni-Cu-Zn ferrite samples with different content of NiO and ZnO. The power loss, Pcv decreases monotonically wi increasing temperature and attains to a certain value at around $100\~120$ degrees Celsius. The frequency dependence of Pcv can be explained by $Pcv\~f^n$', and n is independent of the frequency, f up to 1MHz. The Pcv decreases with an increase in ZnO/NiO. The Pcv was separated to hysteresis loss, Ph and residual loss, (Pcv-Ph). The temperature characteristics and compositional dependence of Pcv can be attributed to the Ph, while (Pcv-Ph) is not affected by both temperature and ZnO/NiO. By analyzing temperature and composition dependence of Ph and initial permeability, ${\mu}^i$ following equations could be formularized. $${\mu}_i{\mu}o=I_x\;^2/(K_1+bs_ol_s)\;\;\;\;(1)$$ $Wh=13.5(I_s\;^2/{\mu}_i{\mu}_o)\;\;\;\;(2)$$ Were ${\mu}_o$ is permeability of vacuum, $I_s$ saturation magnetization, $K_1$ anisotropy constant, $S_o$ internal heterogeneous stress, $I_s$, magnetostriction constant, b unknown constant. Wh hysteresis loss per one cycle of excitation (Ph: Wh*f). Steinmetz constant of Ni-Cu-Zn ferrites, $m=1.64\~2.2$ is smaller than the one of Mn-Zn ferrites, which suggests the difference of loss mechanism between these materials.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1994.10b
• /
• pp.23-23
• /
• 1994

• Journal of the Korean Magnetics Society
• /
• v.17 no.6
• /
• pp.232-237
• /
• 2007

We have synthesized the low temperature sintered of Ni-Zn-Cu ferrite with nonstoichiometric composition a little deficient in $Fe_2O_3$ from $(Ni_{0.2}Cu_{0.2}Zn_{0.6})_{1+x}(Fe_2O_3)_{1-x}$. For low loss and acceleration of grain growth $TiO_2$ and $Li_2CO_3$ was added from 0.25 mol% to 1.0 mol%. The mixture of the law materials was calcinated and milled. The compacts of toroidal type were sintered at different temperature $(875^{\circ}C,\;900^{\circ}C,\;925^{\circ}C\;950^{\circ}C)$ for 2 hours in air followed by an air cooling. Then, effects of composition and sintering temperatures on the physical properties such as density, resistivity, magnetic induction, coercive force, initial permeability, and quality factor of the Ni-Zn-Cu ferrite were investigated. The density of the Ni-Zn-Cu ferrite was $4.85\sim5.32g/cm^3$, resistivity revealed $10^8\sim10^{12}\Omega-cm$. The magnetic properties obtained from the aforementioned Ni-Zn-Cu ferrite specimens were 1,300 gauss for the maximum induction, 4.5 oersted for the coercive force, 275 for the initial permeability, and 83 for the quality factor. The physical properties indicated that the specimens could be utilized as the core of high frequency range (involved microwave range) communication and deflection yoke of T.V.

• Journal of the Korean Magnetics Society
• /
• v.6 no.6
• /
• pp.382-387
• /
• 1996

The characteristics of the complex permeability of ${(Ni_{x}Cu_{0.2}Zn_{0.8-x}O)}_{1-w}{(Fe_{2}O_{3})}_{1+w}$ with various Ni and $Co_{3}O_{4}$ contents were investigated in this work. It is found that the NiCuZn ferrites with $x{\geq}0.6$ have a relatively small peak width of the imaginary part of permeability $\mu$". The resonance frequency is increased as Ni content becomes higher, where the loss is low. The $\mu$" value decreases with increasing FezO, deficiency, but the resonance frequency($f_{\mu"max}$) is only slightly affected by $Fe_{2}O_{3}$ deficiency. In case of $Co_{3}O_{4}$ addition to the NiCuZn ferrites, the $f_{\mu"max}$ increases since the initial permeability decreases with the amount of $Co_{3}O_{4}$. It is concluded that the Ni content in the NiCuZn ferrite is a dominant factor for the total loss of these spinel ferrites.

• Journal of the Korean Ceramic Society
• /
• v.39 no.7
• /
• pp.669-674
• /
• 2002

Ni-Zn ferrite was sintered by microwave hybrid sintering method using microwave energy of 2.45 GHz, 700 W in the temperature range of 900$^{\circ}C$ ∼ 1070$^{\circ}C$. A high density (98%TD) Ni-Zn ferrite, added Bi$_2$O$_3$ and CuO, with a single phase was obtained by microwave sintering at 970$^{\circ}C$ for 15 min. All the sintered samples showed sintered density over 90% of TD. These results indicate that the processing time and energy consumption can be reduced significantly by microwave hybrid sintering method.