• 대한금속재료학회지
• /
• 제47권3호
• /
• pp.139-146
• /
• 2009

The heat-affected zone (HAZ) of SA508 Gr.4N Ni-Mo-Cr low alloy steel, which has higher Ni and Cr contents than SA508 Gr.3 Mn-Mo-Ni low alloy steel, was investigated on the microstructure and mechanical properties. The HAZ was categorized into seven characteristic zones (CGCG, FGCG, ICCG, SCCG, FGFG, ICIC and SCSC-HAZ) according to the peak temperature from the thermal cycle experienced during multi-pass welding. Post Weld Heat Treatment (PWHT) was conducted in the temperature range of $550{\sim}610^{\circ}C$ for 30 hours to evaluate the effect of PWHT conditions on the microstructure and mechanical properties. Before PWHT, CGHAZ and FGFGHAZ showed high yield strength (YS) ranging from 1000 to 1250 MPa, while YS of SCSCHAZ decreased from 607 MPa (observed for base metal) to 501 MPa. The Charpy impact energies of sub-HAZs fell below 100J at $-29^{\circ}C$, except in the SCSCHAZ. By applying PWHT to sub-HAZ specimens, YS decreased as the PWHT temperature increased. In the case of CGHAZs and FGFGHAZ heat-treated at $610^{\circ}C$, YS dropped drastically to the range of 654~686 MPa. From the Charpy impact test, the upper-shelf energy (USE) increased to approximately 250J and Index temperature ($T_{68J}$) decreased below $-50^{\circ}C$. Specifically, in FGFG, ICIC and SCSC-HAZ, $T_{68J}$ was below -110, which was lower than the case of base metal.

• 한국표면공학회지
• /
• 제50권3호
• /
• pp.164-169
• /
• 2017

Ni-Cr-X ternary interlayers were investigated to improve the adhesion of Cu/Ni-Cr/Polyimide flexible copper clad laminates. The ternary compounds are sputtered Ni-Cr-X films (where X is one of Nb, V, Mo, or Ti), and the effect of third elements on the adhesion was evaluated and investigated chemically and mechanically. The feel strength was higher in the order of Ni-Cr-Nb > Ni-Cr-V > Ni-Cr > Ni-Cr-Mo > Ni-Cr-Ti. Nb, which has a comparable standard electrode potential to Cr, increased the adhesion, while Ti, with a low standard electrode potential, degraded the adhesion. The Ni-Cr-Nb interlayer was amorphous, while Ni-Cr-Ti was partially crystalline. The similar morphology structure of the Ni-Cr-Nb interlayer with polyimide resulted in a better adhesion.

• 한국수소및신에너지학회논문집
• /
• 제9권1호
• /
• pp.16-24
• /
• 1998

최근 Ni-MH 전지의 고성능화를 위해 방전용량이 높은 Zr기 $AB_2$ 형의 수소 흡장 합금이 주목받고 있다. 본 연구에서는 이 중에서 $ZrV_{0.1}Mn_{0.7}Ni_{1.2}$ 합금을 선택하여 합금의 열처리 그리고, Mn 대신 Mo의 부분치환이 전극의 특성에 미치는 영향을 조사하였다. 합금은 먼저 아크 용해로를 사용하여 제작하였으며, 이 합금 중 일부를 $1,100^{\circ}C$에서 가열 후 각각 서냉과 급냉 처리를 행하였다. 이 세 가지 종류의 합금들을 이용하여 활성화 거동, 고율 방전 특성, 자기 방전 특성 등의 전극특성을 평가하였다. 그 결과 합금은 열처리에 의해서 방전용량이 감소하고 고율 방전율 또한 감소하였다. 그러나, 전기 화학적으로 구한 압력-조성 등온곡선의 평탄구역의 기울기를 감소시켰다. 또한 $ZrV_{0.1}Mn_{0.7}Ni_{1.2}$ 합금의 Mn을 Mo으로 부분 치환함에 의해서 방전용량의 감소 없이 자기방전특성을 크게 개선할 수 있었다.

• 한국분말재료학회지
• /
• 제13권1호
• /
• pp.10-17
• /
• 2006

Model experiment was introduced to obtain the formation of a core/rim structure by only liquid phase reaction in Ti(C, N)-based cermet alloys. Infiltrated Ti(C, N)-Ni, $MO_2C-Ni$, and TaC-Ni cermets were bonded to sandwiched specimen by heat treatment $1450^{\circ}C$ for 5hr. With nitrogen addition, both (Ti, Mo) (C, N) and (Ti, Ta) (C, N) rim structure was nucleated around comer of cuboidal Ti(C, N) core. However, equilibrium shapes of(Ti, Mo) (C, N) and (Ti, Ta) (C, N) rim were different possibly due to the effect of interface energy. The core/rim and rim! binder interfaces were parallel to each other with TaC addition, while rotated to each other with $MO_2C$ addition.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2002년도 춘계학술대회 논문집
• /
• pp.952-955
• /
• 2002

$WC-3%(Cr_3C_2)-2%(Mo_2C)-12%Ni$ carbides were ground with three different types of electroplated diamond wheels with respect to grain friability. The grinding ratio in the case of the highest toughness grains, A becomes the highest at the workpiece speeds of 40 and 70mm/min exhibiting larger effect with smaller workpiece speed. The grinding ratio with the medium toughness grain is higher than that of grain A at higher workpiece speeds than 100mm/min. The surface roughness becomes smaller with increasing the grain friability The increasing rate on surface roughness with the increase of workpiece speed becomes higher with using the grain of lower friability.

• 대한치과기공학회지
• /
• 제37권1호
• /
• pp.23-29
• /
• 2015

Purpose: The selective laser melting (SLM) process for dentistry, which is one of the additive manufacturing technologies (AM) allows for rapid production of a three-dimensional model with complex shape by directly melting metal powder. This process generates detailed items of a three-dimensional model shape through consolidation of a thin powder layer by utilizing both selective melting and laser beam simultaneously. In regard to SLM process, Fe-base powder, Ti-6AI-4V powder, AI-base powder, etc. have been researched. It is believed that the aforementioned technologies will be widely utilized in manufacturing metal parts using metal powder of raw material. This study chose Ni-Cr-Mo metal powder in order to manufacture metal powder materials that would be used in the selective laser melting for dentistry. Methods: This study manufactured metal powder using mechanical alloying technique (MA) among those metal powder manufacturing techniques. Moreover, this study aimed to utilize the metal powder manufactured after observing the characteristics of powder as preliminary data of Ni-Cr-Mo metal powder. This study could obtain the following conclusions within the experimental limitations. Results: As a result of mechanically alloying Ni-Cr-Mo powder over time, its mean particle size was $66.93{\mu}m$ $54.4{\mu}m$ and $45.39{\mu}m$ at 10h, 20h and 30h, respectively. The gtain form of metal powder by mechanical alloying technique was a sponge-like shape of irregular plate; however, the gtain form manufactured by high-pressure water aromization process had the following three types: globular type, chain type and oval type. Conclusion: This study found $37.65{\mu}m$ as the mean particle size of Ni-Cr-Mo metal powder, which was manufactured using water atomization technique under the following conditions: water atomization flux of 300 liter/min, hydraulic pressure of $400kgf/cm^2$ and injection angle of $45^{\circ}$. This study confirmed that the grain form of powder (solid particle form) would vary depending on the manufacturing process.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2008년도 추계학술발표대회 및 제15회 신소재 심포지엄
• /
• pp.6.2-6.2
• /
• 2008

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2004년도 추계학술발표회 발표논문집
• /
• pp.1023-1023
• /
• 2004

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2000년도 특별강연 및 추계학술발표대회 개요집
• /
• pp.211-213
• /
• 2000

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2005년도 춘계학술발표대회 및 제8회 신소재 심포지엄 논문개요집
• /
• pp.155-155
• /