• Applied Chemistry for Engineering
• /
• v.20 no.5
• /
• pp.500-504
• /
• 2009

NiCuZn Ferrites, known as preventing EMI/EMC, were prepared and their properties were investigated based on the chemical composition ratio, sintering temperature, and mean particle size. The NiCuZn ferrite made of $Fe_2O_3$ 49.0 mol%, NiO 9.0 mol%, CuO 8.0 mol%, ZnO 34.0 mol% could be applied at the largest range of electromagnetic wave. The optimal calcination and sintering temperature were $900^{\circ}C$ and $1080^{\circ}C$, respectively. The electromagnetic wave loss capacity of its mean particle size $1.12{\mu}m$ was superior to others examined.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.216-216
• /
• 2009

$(Ni_{1-x-y}Zn_xCu_y)Fe_2O_4(x=0.45,\;0{\leq}y{\leq}0.3)$ was synthesized by conventional ceramic processing, and the sintering behavior and the magnetic properties of which were studied as functions of CuO content and sintering temperature. Both the densification and the grain growth rates were significantly enhanced with the increase of CuO content, while abnormal grain growth occurred when the samples of $y{\geq}0.2$ were sintered above $950^{\circ}C$. Saturation magnetization and coercive field were mainly influenced by the densification and grain growth of the specimens, respectively.

• Journal of the Korean Ceramic Society
• /
• v.39 no.7
• /
• pp.669-674
• /
• 2002

Ni-Zn ferrite was sintered by microwave hybrid sintering method using microwave energy of 2.45 GHz, 700 W in the temperature range of 900$^{\circ}C$ ∼ 1070$^{\circ}C$. A high density (98%TD) Ni-Zn ferrite, added Bi$_2$O$_3$ and CuO, with a single phase was obtained by microwave sintering at 970$^{\circ}C$ for 15 min. All the sintered samples showed sintered density over 90% of TD. These results indicate that the processing time and energy consumption can be reduced significantly by microwave hybrid sintering method.

• Journal of Powder Materials
• /
• v.2 no.1
• /
• pp.29-35
• /
• 1995

In this study the calcined condition and characteristic of Cu-Ni-Zn ferrite powder were investigated. The Cu-Ni-Zn ferrite powder has been synthesized by the thermal decomposition of the organic acid salt. This process did not require a strict pH control and provided the uniform composition and fine powder with about 0.3 $\mu\textrm{m}$. The XRD diffraction pattern of this powder showed about 50% spinel phase. The optimum calcination was found to be done at $700^{\circ}C$ for one hour. After the calcination, the amount of spinel increased to 90%. The distribution of the particle size showed bimodal peaks, one was about 0.5 $\mu\textrm{m}$ and the other was about 20 $\mu\textrm{m}$. The large particles of 20 $\mu\textrm{m}$ were the agglomeration of fine Particles. The mean Particle size of the powder was about 0.4 $\mu\textrm{m}$. The powder was compacted under 100 MPa pressure and sintered at 1100~ $1250^{\circ}C$ for one hour in air. The density of ferrites specimen was a function of the sintering temperature. The higher the temperature, the denser the ferrite. The maximum relative density of the sintered ferrite was about 93% at $1250^{\circ}C$. The grain size of sintered specimen at $1200^{\circ}C$ was 5 $\mu\textrm{m}$ and homogeneous.

• Korean Journal of Materials Research
• /
• v.13 no.8
• /
• pp.531-536
• /
• 2003

The electromagnetic properties and microstructures of the ferrites based on ($Ni_{0.2}$ $Cu_{0.2}$ $Zn_{0.6}$)$_{1.085}$($Fe_2$$O_3$)$_{0.915}$ were investigated by changing the amount of additive SnO$_2$and CaO and the sintering temperatures. Addition of $SnO_2$caused pores in the specimen. There was no variation of grain size by changing the amount of additives. Total loss was reduced when ($Ni_{0.2} $Cu_{0.2}$ $Zn_{ 0.6}$)$_{1.085}$ ($Fe_2$$O_3$)$_{0.915}$ composition was sintered at $1150^{\circ}C$ rather than $1300^{\circ}C$. Addition of CaO was useful to reduce the total loss because it increased the sintering density. The lowest total loss was obtained when 0.06 wt% $SnO_2$and 0.4 wt% CaO were added at the same time.

• Journal of the Korean Ceramic Society
• /
• v.50 no.3
• /
• pp.231-237
• /
• 2013

Thermodynamic modeling of the $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ complex ferrite system has been adopted as a rational approach to establish routes to better synthesis conditions for pure phase $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ complex ferrite. Quantitative analysis of the different reaction equilibria involved in the precipitation of $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ from aqueous solutions has been used to determine the optimum synthesis conditions. The spinel ferrites, such as magnetite and substitutes for magnetite, with the general formula $MFe_2O_4$, where M= $Fe^{2+}$, $Co^{2+}$, and $Ni^{2+}$ are prepared by coprecipitation of $Fe^{3+}$ and $M^{2+}$ ions with a stoichiometry of $M^{2+}/Fe^{3+}$= 0.5. The average particle size of the as synthesized $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$, measured by transmission electron microscopy (TEM), is 14.2 nm, with a standard deviation of 3.5 nm the size when calculated using X-ray diffraction (XRD) is 16 nm. When $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ ferrite is annealed at elevated temperature, larger grains are formed by the necking and mass transport between the $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ ferrite nanoparticles. Thus, the grain sizes of the $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ gradually increase as heat treatment temperature increases. Based on the results of Thermogravimetric Analysis (TGA) and Differential Scanning Calorimeter (DSC) analysis, it is found that the hydroxyl groups on the surface of the as synthesized ferrite nanoparticles finally decompose to $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ crystal with heat treatment. The results of XRD and TEM confirmed the nanoscale dimensions and spinel structure of the samples.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.6 no.3
• /
• pp.17-25
• /
• 1997

This paper aims to clarify the effects of grinding conditions on the grinding force, ground surface and chipping size of workpiece in surface grinding of various ferrites with the resin bond diamond wheel. The main conclusions obtained were as follows: In a constant peripheral wheel speed, the specific grinding energy is fitted by straight lines with grinding depth coefficient($\delta$) in a logarithmic graph. The effect of both depth of cut and workpiece speed on grinding energy becomes larger in the order of Mn-Zn, Cu-Ni-Zn and Sr. When using the diamond grain of the lower toughness, the roughness of the ground surface becomes lower. The ground surfaces show that the fracture process during grinding becomes more brittle in the order of Sr, Mn-Zn and Cu-Ni-Zn. The chipping size at the corner of workpiece in grinding increases with the the increases of the depth of cut and workpiece speed, and the decrease of peripheral wheel speed. The effect of both depth of cut and workpiece speed on chipping size becomes more larger in the order of Sr, Mn-Zn and Cu-Ni-Zn.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.259-262
• /
• 1999

In this study, we investigated magnetic Properties of N $i_{0.2-x}$C $u_{x}$Z $n_{0.305}$F $e_{0.495}$ (x=0 ~0.2) ferrites. As the increased, the density and shrinkage increased until 5.3g/㎤, 20% respects, but the absorption decreased rate until 0.01%. As a results of the density, absorption rate, and shrinkage rate, the grain growth progressed rapidly in x=0.125 at 105$0^{\circ}C$, x=0.075 at 115$0^{\circ}C$, and x=0.025 at 115$0^{\circ}C$ for 3hours. As the CuO concentration increased, initial permeability increased at sintered 105$0^{\circ}C$ and 115$0^{\circ}C$ for 3 hours, but decreased at 125$0^{\circ}C$ for 3 hoers. The complex permeability as a function of frequency were high values at sintered 105$0^{\circ}C$ for 3 hours in x=0.005, 0.075.5.5.5.

• Journal of the Korean Magnetics Society
• /
• v.18 no.2
• /
• pp.58-62
• /
• 2008

$Ni_{0.4}Zn_{0.4}Cu_{0.2}Fe_2O_4$ ferrite was fabricated by solid stat reaction method and sol-gel method. Because of the drawbacks of each method, we combined these two methods together. We proposed and experimentally verified that nanocrystalline ferrite additive was effective on improving the densification behavior and magnetic properties of NiZnCu ferrites for multilayer chip inductors. The initial permeability of the toroidal core Sample with 20 wt% nanocrystalline ferrite increased from 78.1 to 178.2 as annealing temperature is increased from $880^{\circ}C$ to $920^{\circ}C$. The density, shrinkage and saturation magnetization were increased with increasing annealing temperature, which was attributed to the decrease of additive grain size and increase of sintering density.

• Applied Chemistry for Engineering
• /
• v.22 no.2
• /
• pp.185-189
• /
• 2011

In this work, nano-sized M-ferrites (M=Co, Ni, Cu, Zn) for the decomposition of carbon dioxide were synthesized by the chemical co-precipitation. From the thermogravimetric analysis, it was clear that the maximum weight loss of each sample took place below $350^{\circ}C$. High temperature calcination resulted in more systematic crystallines, smaller specific surface area and larger particle size. An analysis by FTIR in the range of $375{\sim}406cm^{-1}$ revealed the presence of chelates at the octahedral site, which implies the formation of spinel structure in the ferrites. The current work showed that a $500^{\circ}C$ is the optimum heat treatment temperature of metal ferrites for $CO_2$ decomposition reaction.