• Journal of Powder Materials
• /
• v.6 no.4
• /
• pp.270-276
• /
• 1999

Ti-Ni-Cu alloy powders were fabricated by ball milling, and the properties of these powders were characterized. Mixed 50Ti-(50-x)Ni-xCu powders of 5 to 10at.%Cu composition were milled for 100 hours using SUS 1/4" balls in argon atmosphere. Ball to powder ratio was 20:1 and rotating speed was 100 rpm. Tensile strength, microstructure and phase transformation of ball milled Ti-(50-x)Ni-xCu powders were studied. After 100 hours milling, Ti, Ni and Cu elements were alloyed completely and an amorphous phase was formed. Amorphous phase was crystallized to martensite(B 19') and austenite(B2) after heat treatment for 1 hour at $850^{\circ}C$. As the Cu contents were increased, tensile strength of extruded 6061Al/TiNiCu was decreased, and B19'martensite phases In the TiNi particles were the causes of high tensile stress of extruded 6061Al/TiNiCu.NiCu.

• Journal of Powder Materials
• /
• v.10 no.1
• /
• pp.26-33
• /
• 2003

Al-l4wt.%Ni-l4wt.% Mm(Mm=misch metal) alloy powders rapidly solidified by the gas atomization method were subjected to mechanical milling(MM). The morphology, microstructure and hardness of the powders were investigated as a function of milling time using scanning electron microscopy(SEM), transmission electron microscopy(TEM) and Vickers microhardness tester. Microstructural evolution in gas-atomized Al-l4wt.%Ni-l4wt.% Mm(Mm=misch metal) alloy powders was studied during mechanical milling. It was noted that the as-solidified particle size of $200\mutextrm{m}$ decreases during the first 48 hours and then increases up to 72 hours of milling due to cold bonding and subsequently there was continuous refinement to $20\mutextrm{m}$ on milling to 200 hours. Two microstructurally different zones, Zone A, which is fine microstructure area and Zone B, which has the structure of the as-solidified powder, were observed. The average thickness of the Zone A layer increased from about 10 to $15\mutextrm{m}$ in the powder milled for 24 hours. Increasing the milling time to 72 hours resulted in the formation of a thicker and more uniform Zone A layer, whose thickness increased to about $30~50\mutextrm{m}$. The TEM micrograph of ball milled powder for 200 hours shows formation of nano-particles, less than 20 nm in size, embedded in an Al matrix.

• Journal of Korean Vacuum Science & Technology
• /
• v.6 no.2
• /
• pp.92-96
• /
• 2002

In this paper, we treated the Ni$_3$Al based alloy samples with intense pulsed ion beams (IPIB) at the beam parameters of 250KV acceleration voltage, 100 - 200 A/cm$^2$ current density and 60 u pulse duration. We simulated the thermal-mechanical process near the surface of Ni$_3$Al based alloy with our STEIPIB codes. The surface morphology and the cross-section microstructures of samples were observed with SEM, the composition of the sample surface layer was determined by X-ray Energy Dispersive Spectrometry (XEDS) and the microstructure on the surface was observed by Transmission Electron Microscope (TEM). The results show that heating rate increases with the current density of IPIB and cooling rate reached highest value less than 150 A/cm$^2$. The irradiation of IPIB induced the segregation of Mo and adequate beam parameter can improve anti-oxidation properly of IC6 alloy. Some craters come from extraneous debris and liquid droplets, and some maybe due to the melting of the intersection region of interphase. Increasing the pulse number enlarges average size of craters and decreases number density of craters.

• Journal of the Korean Society for Heat Treatment
• /
• v.16 no.2
• /
• pp.90-96
• /
• 2003

The effect of betatizing temperature on microstructure and transformation characteristics in a Cu-AI-Ni based pseudoelastic alloy fabricated by heated mold continuous casting by using metallography, XRD and calorimetry. The microstructure of cast rod betatized at $600^{\circ}C$ revealed a ${\beta}_1$ parent phase and a ${\gamma}_2$ phase precipitated along the casting direction. When the cast rod was betatized at the elevated temperature above $600^{\circ}C$, the ${\gamma}_2$ phase is completely dissolved into the matrix so that the volume fraction of the ${\gamma}_2$ phase was decreased. The parent phase was stabilized by betatizing at $600^{\circ}C$. However, the ${\beta}_1$ parent phase was transformed to both ${{\beta}_1}^{\prime}$ and ${{\gamma}_1}^{\prime}$ martensites with increasing betatizing temperatures above $600^{\circ}C$, while $M_s$ and $A_s$ temperatures were decreased. The stress-strain curves for compression test were not same with betatizing temperature; the stress-strain curves of the specimen betatized at $600^{\circ}C$ and $700^{\circ}C$ were linear but those of the specimen betatized at $800^{\circ}C$ and $900^{\circ}C$ were not linear.

• Transactions of the Korean hydrogen and new energy society
• /
• v.13 no.1
• /
• pp.24-33
• /
• 2002

기존 Ni-10w/o Cr 연료극과 성능은 대등하면서 creep 저항성이 뛰어난 연료극을 제조하기 위하여 Ni-5w/o Al 합금 연료극의 제조 공정을 연구하였다. 소성 분위기에 따라 완전산화 방법과 부분산화 방법으로 나누어 제조된 전극들의 미세구조 변화를 관찰하였으며, 실험 결과 부분산화 방법으로 제조한 Ni-5w/o Al 합금 연료극이 가장 우수한 소결 및 creep 저항성을 나타내었다. 이는 연료극이 산화물 분산강화 구조를 갖기 때문으로 부분산화 방법으로 제조한 Ni-5w/o Al 합금 연료극을 장착한 단전지의 경우 기계적 안정성 및 전극 안정성이 향상되었다.

• Journal of Powder Materials
• /
• v.1 no.2
• /
• pp.145-152
• /
• 1994

Atomizing mode and powder characteristics of CuA1Ni base shape memory alloy in rotating disk atomization were investigated in accordance with disk materials and additional elements. Produced powders were classified into two types of spherical and flake shape. In the case of CuAlNiBTi and CuAlNiZr alloy, high yield rate and fine powder were obtained. This tendency was same when we used oxide coated disks. We concluded that this results were steno from the wetting characteristics change between molten metal and disk surface. Especially, due to the reactive properties of Ti and Zr with ceramic disk, the change of atomizing appearance and powder characteristics were noticeable.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1316-1317
• /
• 2006

The paper investigates the possibility to avoid extrinsic embrittlement of $Ni_3Al$, also increasing the high temperature strength, by alloying with both Fe - of a high strengthening effect and Cr - able to remove a part of diffused oxygen along the grain boundaries. As Cr homogenization in $Ni_3Al$ is difficult because of its low diffusion coefficient, for its improving a mechanical alloying (MA) step before the compound synthesis by Self-propagating High-temperature Synthesis (SHS) was adopted. The obtained better homogenization resulted in higher mechanical resistance and deformability than of the unalloyed $Ni_3A/Ni_3Al$ alloys of the same composition obtained without MA step.

• Journal of the Korean institute of surface engineering
• /
• v.30 no.4
• /
• pp.248-254
• /
• 1997

The sulfidation behavior of a sputter-deposited amorphous coating of 69.0%Nb-16.9Ni-11.9%Al-2.2%Si (at.%) has been investigated as a funtion of temperature.(973-1173K) in pure sulfur pressure of 0.01atm. The sulfidation kinetics of the casting obyed the parabolic rate low over the whole temperature ranges studied. The stlfidation rate increased with the temperature, as expected. The sulfide scale, the composition of which was $Al_2S_3,\;NbS_2,\;Ni_{3-x}S_2\;and\;FeCrS_4$, formed on the amorphous coating was primarily bilayered. Both the outer fastgrowing non-protective 4Al_2S_3$scale and the inner slowly-growing protective $NbS_2$,/TEX> scale and the inner slowly-growing protective $NbS_2$ scale had some Fe and Cr dissolution, which evidently came from the base substrate alloy of stainless steel type 304. Belows the coating, Kirkendall void formation was noticed. Nevertheless, a dramatic improvement of sulfidation resistance was achieved by sputter-depositing Nb-2 Ni-Al-Si layer on the stainless steel 304.

• Applied Microscopy
• /
• v.43 no.3
• /
• pp.127-131
• /
• 2013

The crystallization behavior in the $Al_{87}Ni_3Y_{10}$ and $Al_{88}Ni_3Y_9$amorphous alloys has been investigated. As-quenched $Al_{87}Ni_3Y_{10}$ amorphous phase decomposes by simultaneous formation of Al and intermetallic phase at the first crystallization step, while as-quenched $Al_{88}Ni_3Y_9$ amorphous phase decomposes by forming Al nanocrystals in the amorphous matrix. The density of Al nanocrystals is extremely high and the size distribution is homogeneous. Such a microstructure can result from rapid explosion of the nucleation event in the amorphous matrix or growth of the preexisting nuclei embedded in the as-quenched amorphous matrix. The final equilibrium crystalline phases and their distribution at 873 K are exactly same in both $Al_{87}Ni_3Y_{10}$ and $Al_{88}Ni_3Y_9$ alloys.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.4
• /
• pp.278-285
• /
• 1996

The structure of coating layer formed by hot dip Al-Cu alloy coating on Monel 1400 metal was studied. The coating layer consists of alloyed layer adjacent to the Monel 400 substrate and Al-Cu alloy. It was found that the hardness of coating increased with dipping time and heat treatment associated with the diffusion and the formation of intermetallic compound at the interface. However the thickness of coating layer was decreased at high dipping temperature due to tile higher viscosity of liquid coating alloy. Diffusion heat treatment at $600^{\circ}C$ after coating resulted in the disappearence of adhered Al(Cu) and $CuAl_2$ phases, and then they transformed into the new phases of CuAl and Al7Cu4Ni at coating layer.