• The Korean Journal of Ceramics
• /
• v.4 no.4
• /
• pp.340-344
• /
• 1998

Failure mechanisms were investigated for the two layer thermal barrier coatings consisting of NiCrAlY bond coat and $ZrO_2$-8wt.% $Y_2O_3$ ceramic coating during cyclic oxidation. $Al_2O_3$ developed at the ceramic coating/bond coat interface first, followed by the Cr/Ni rich oxides such as $NiCr_2O_4$ and $Ni(Al, Cr)_2O_4$ during cyclic oxidation. It was observed that the spalling of ceramic coatings took place primarily within the NiCrAlY bond coat oxidation products or at the interface between the bond coat oxidation products and zirconia based ceramic coating or the bond coat. It was also observed that the fracture within these oxidation products occurred with the formation of $Ni(Cr, Al)_2O_4$ spinel or Cr/Ni rich oxides. It was therefore concluded that the formation of these oxides was a life-limiting event for the thermal barrier coatings.

• Journal of the Korean Magnetics Society
• /
• v.3 no.4
• /
• pp.277-283
• /
• 1993

The temperature dependence of DC magnetic susceptibilities of three austenitic Fe-Cr-Ni stainless alloys were measured in the temperature range of 4.2 and 300 K. Two alloys support a general magnetic description of austen-itic stsinless steels in terms of a two-magnetic-phase (spin glass + superparamagnetic cluster) model and one alloy shows magnetic double transition phenomena. Also this study shows that incressing the Ni/Cr ratio in Fe-Cr-Ni alloys causes a increase of the DC susceptibility peak value and a decrease of the magnetic transition temperature.

• Journal of Welding and Joining
• /
• v.14 no.4
• /
• pp.71-78
• /
• 1996

The effect of chemical composition on mechanical properry and corrosion resistance of austenitic stainless steel was investigated. The main results obtained were as follows : 1. There was a linear relationship between the tensile strength of stainless steel and the $Cr_{eq}/Ni_{eq}$. The larger the $Cr_{eq}/Ni_{eq}$ was the higher the tensile strength of stainless steel. 2. There was a good correlationship between $Cr_{eq}/Ni_{eq}$ and intergranular, gerneral corrsion rate. 3. Intergranular corrosion rate decreased linearly with increasing Cr content. 4. General corrosion rate decreased linearly with increasing Ni content. 5. Logarithm corrosion rate of intergranular and general corrosion has a linear relationship with all of the factor of $Cr_{eq}/Ni_{eq}$, Cr and Ni content.

• Korean Journal of Metals and Materials
• /
• v.47 no.9
• /
• pp.533-541
• /
• 2009

Materials used for a reactor pressure vessel(RPV) are required high strength and toughness, which determine the safety margin and life of a reactor. Ni-Mo-Cr low alloy steel shows better mechanical properties than existing RPV steels due to higher Ni and Cr contents compared to the existing RPV steels. The present study focuses on effects of Ni, Cr contents on the cleavage fracture toughness of Ni-Mo-Cr low alloy steels in the transition temperature region. The fracture toughness was characterized by a 3-point bend test of precracked Charpy V-notch(PCVN) specimens based on ASTM E1921-08. The test results indicated that the fracture toughness was considerably improved with an increase of Ni and Cr contents. Especially, control of Cr content was more effective in improving fracture toughness than manipulating Ni content, though Charpy impact toughness was changed more extensively by adjusting Ni content. These differences between changes in the fracture toughness and that in the impact toughness were derived from microstructural features, such as martensite lath size and carbide precipitation behavior.

• Proceedings of the KIEE Conference
• /
• 2001.11a
• /
• pp.168-170
• /
• 2001

The NiCr is an important material for present thin-film resistor application owing to its low TCR and thermal stability. In this work, the NiCr thin films were deposited on corning glass substrate by reactive magnetron sputtering and the annealing at temperatures range from 300 to $500^{\circ}C$ for 20 min in vacuum. X-ray, AFM, $R_s$(surface leakage current) have been used to study the structural and electrical properties of the NiCr thin films. The high precision NiCr thin films resistor with TCR(temperature coefficient of resistance) of less then 10 ppm/$^{\circ}C$ was obtained under in in-situ annealing at $300^{\circ}C$ on Cr buffer layer substrate. It is clear that the NiCr thin-films resistor electrical properties are low TCR related with it's annealing and buffer layer condition. NiCr thin film resistor having a good thermal stability and low TCR properties are expected for the application to the dielectric material of passive component.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.81-84
• /
• 2004

The NiCr is an important material for present thin-film resistor application owing to its low TCR and thermal stability. In this work, the NiCr thin films were deposited on coming glass substrate by reactive magnetron sputtering and the annealing at temperatures range from 300 to $500^{\circ}C$ for 20 min in vacuum. X-ray, AFM, $R_s$(surface leakage current) have been used to study the structural and electrical properties of the NiCr thin films. The high precision NiCr thin films resistor with TCR(temperature coefficient of resistance) of less then $10\;ppm/^{\circ}C$ was obtained under in in-situ annealing at $300^{\circ}C$ on Cr buffer layer substrate. It is clear that the NiCr thin-films resistor electrical properties are low TCR related with it's annealing and buffer layer condition. NiCr thin film resistor having a good thermal stability and low TCR properties are expected for the application to the dielectric material of passive component.

• Journal of the Korean institute of surface engineering
• /
• v.21 no.4
• /
• pp.176-182
• /
• 1988

Effects of Cr, Ni and W on the anodic polarization behavior were investigated for Fe-Cr-Ni-W alloys in deaerated 1N HCI solution. Surface films formed on the polarization were analysed using AES, SEM and EDAX. A higerconcentration of tungten was found in the surface oxide film compared to the matrix. It played an importanet role on incresing the stability of the passive film. The presence of an adequate amount of Cr was essential to increase the pitting resistance of the alloys in acid chloride media. Under 12 wt%cr,alloys containing 6wt%W did not exhidit any passivity at all. The main role of Ni was to control the microstructure rather than to modify the corrosion resistance. In 23 cr-14Ni-^W alloy, the duplex microstructure of ferrite($\delta$-phase) in an austenic matrix was developed. The reson why proferred pitting appeared in austenite and ferrite/austenite interface was that ferrite had more amount of Cr and W than austenite.

• Journal of the Microelectronics and Packaging Society
• /
• v.26 no.4
• /
• pp.133-140
• /
• 2019

The effects of thermal cycle conditions on the bonding strength and crack propagation behaviors in electroplated Cr/electroplated Ni-P coatings were systematically evaluated. 1^st heat treatment was performed at 500℃ for 3 hours after electroplating Ni-P, and then, 2^nd heat treatment was performed at 750℃ for 6 hours after electroplating Cr. The measured bonding strength by ASTM C633 were around 25.6 MPa before thermal cycling, while it increased to 47.6 MPa, after 1,000 cycles. Increasing thermal cycles led to dominant fail mode with cohesive failure inside adhesive, which seemed to be closely related to the increasing bonding strength possibly not only due to higher Cr surface roughness, but also to penetrated channeling crack density. Also, increasing density of penetrated channeling cracks in electroplating Cr layer led to slightly stronger bonding strength due to mechanical interlocking effects of adhesive inside channeling cracks.

• The korean journal of orthodontics
• /
• v.14 no.2
• /
• pp.241-248
• /
• 1984

The mechanical properties of Cr-Ni alloy of austenitic stainless steel and Co-Cr alloy orthodontic wires were studied in tension. The wires (0.018 inch) were tested in the as-manufactured and heat-treated conditions. Instron type tension testing machine was used for this study. Mean values and standard deviations were computed. The results were as follows; 1. The Cr-Ni orthodontic wires of austenitic stainless steel are generally superior than the Co-Cr orthodontic wires in ultimate tensile strength, In the elongation, however, Co-Cr orthodontic wire are superior than Cr-Ni orthodontic wires. 2. Increase in the degree of strength by heat treatment are more clearly shown in Co-Cr orthodontic wires than Cr-Ni orthodontic wires. And the elongation is decreased by heat treatment in both case. 3. The changes of the degree of strength by cooling method we not clearly shown, but in Cr-Ni orthodontic wires, air cooling are more effective, in Co-Cr orthodontic wires, cooling effect are scarcely shown.

• Corrosion Science and Technology
• /
• v.15 no.3
• /
• pp.141-146
• /
• 2016

By using Ni-Cr and Co-Cr alloys, porcelain fused to metal (PFM) samples were prepared to examine the interface and the surface corrosion behavior. The potentiodynamic polarization analysis showed that the corrosion current density of Co-Cr alloy ($1.61{\times}10^{-6}A/cm^2$) was three times lower than that of Ni-Cr alloy ($4.83{\times}10^{-6}A/cm^2$) at room temperature. A dental prosthesis consisting of the porcelain fused to Ni-Cr alloy extracted from a patient after approximately four years of usage was examined to assess its resistance to corrosion. OM and SEM images of the metal part revealed a typical pitting corrosion. As compared to porcelain fused to Ni-Cr alloy having a thick layer (${\sim}10{\mu}m$) of oxide at the interface, a relatively thin oxide layer (less than $5{\mu}m$) was formed on Co-Cr alloy, indicating that the interface between Co-Cr alloy and porcelain may have a better adhesion strength than the interface between Ni-Cr alloy and porcelain.