• 한국분말재료학회지
• /
• 제12권1호
• /
• pp.64-69
• /
• 2005

The copper oxide nano powders were synthesized by levitational gas condensation(LGC) method, and their high heterogeneous catalytic effects of oxidation of 2,3,5-trimethyl-1,4- hydroquinone (TMHQ) and catalase activity were studied. The observation of transmission electron microscopy (TEM) shows that most of these nano powders are uniform in size, with the average particle size of 35 nm. The nano powder consists of mainly $Cu_2O$, but it is aged to CuO phase. The catalytic effect which was clarified by oxidation of TMHQ and catalase depends on the amount of cuprite phase and the particle size.

• 한국분말재료학회지
• /
• 제9권2호
• /
• pp.124-132
• /
• 2002

Nano Cu powders, synthesized by Pulsed Wire Evaporation (PWE) method, have been compacted by Magnetic Pulsed Cojpaction(MPC) method. The microstructure and mechanical properties were analyzed. The optimal condition for proper mechanical properties with nanostructure was found. Both pure nano Cu powders and passivated nano Cu powders were compacted, and the effect of passivated layer on the mechanical properties was investigated. The compacts by MPC, which had ultra-fine and uniform nanostructure, showed higher density of 95% of theoretical density than that of static compaction. The pur and passivated Cu compacted at $300^{\circ}C$ exhibited maximum hardnesses of 248 and 260 Hv, respectively. The wear resistance of those compacts corresponded to the hardness.

• 소성∙가공
• /
• 제16권3호
• /
• pp.210-214
• /
• 2007

Manufacturing bulk nanostructured materials with least grain growth from initial powders is challenging because of the bottle neck of bottom-up methods using the conventional powder metallurgy via compaction and sintering. In the study, densification behavior of nano Cu powders during pressureless sintering was investigated using an in-situ optical dilatometer technique. The initial heating and steady temperature stages during the sintering of nano Cu powder compacts were observed. At the initial heating stage, the powder compact has many porosities and full densification needs high temperature and/or high pressure sintering. In the experimental analysis, changes in geometry and density were measured and discussed for optimal consolidation and densification by the in-situ optical dilatometer.

• 한국분말재료학회지
• /
• 제25권5호
• /
• pp.435-440
• /
• 2018

In the present study, we develop a conductive copper/carbon nanomaterial additive and investigate the effects of the morphologies of the carbon nanomaterials on the conductivities of composites containing the additive. The conductive additive is prepared by mechanically milling copper powder with carbon nanomaterials, namely, multi-walled carbon nanotubes (MWCNTs) and/or few-layer graphene (FLG). During the milling process, the carbon nanomaterials are partially embedded in the surfaces of the copper powder, such that electrically conductive pathways are formed when the powder is used in an epoxy-based composite. The conductivities of the composites increase with the volume of the carbon nanomaterial. For a constant volume of carbon nanomaterial, the FLG is observed to provide more conducting pathways than the MWCNTs, although the optimum conductivity is obtained when a mixture of FLG and MWCNTs is used.

• 한국입자에어로졸학회지
• /
• 제6권1호
• /
• pp.37-46
• /
• 2010

Cu nano-colloid was prepared by wire electric explosion process under de-mineralized water and anhydrous ethanol. To control the properties of Cu nano-colloid, experimental conditions such as diameter of Cu wire and applied voltage were changed. The optimal Cu nano-colloid was prepared when the 0.1mm diameter of Cu wire with the applied voltage of 2000 V was used. The shape of Cu particles in colloid was spherical and the XRD result revealed that the phase of Cu particles was cubic phase. About 20nm Cu nanoparticles with high crystallinity were successfully prepared using wire explosion process under anhydrous ethanol and they showed more than 100 hours dispersion stability.

• 한국분말재료학회지
• /
• 제21권3호
• /
• pp.207-214
• /
• 2014

In this study, nano-scale copper powders were reduction treated in a hydrogen atmosphere at the relatively high temperature of $350^{\circ}C$ in order to eliminate surface oxide layers, which are the main obstacles for fabricating a nano/ultrafine grained bulk parts from the nano-scale powders. The changes in composition and microstructure before and after the hydrogen reduction treatment were evaluated by analyzing X-ray diffraction (XRD) line profile patterns using the convolutional multiple whole profile (CMWP) procedure. In order to confirm the result from the XRD line profile analysis, transmitted electron microscope observations were performed on the specimen of the hydrogen reduction treated powders fabricated using a focused ion beam process. A quasi-statically compacted specimen from the nano-scale powders was produced and Vickers micro-hardness was measured to verify the potential of the powders as the basis for a bulk nano/ultrafine grained material. Although the bonding between particles and the growth in size of the particles occurred, crystallites retained their nano-scale size evaluated using the XRD results. The hardness results demonstrate the usefulness of the powders for a nano/ultrafine grained material, once a good consolidation of powders is achieved.

• 한국재료학회지
• /
• 제30권3호
• /
• pp.149-154
• /
• 2020

A powder-in-sheath rolling method is applied to the fabrication of a carbon nano tube (CNT) reinforced copper composite. A copper tube with outer diameter of 30 mm and wall thickness of 2 mm is used as sheath material. A mixture of pure copper powder and CNTs with a volume content of 3 % is filled in a tube by tap filling and then processed to an 93.3 % reduction using multi-pass rolling after heating for 0.5 h at 400 ℃. The specimen is then sintered for 1h at 500 ℃. The relative density of the 3 vol%CNT/Cu composite fabricated using powder in sheath rolling is 98 %, while that of the Cu powder compact is 99 %. The microstructure is somewhat heterogeneous in width direction in the composite, but is relatively homogeneous in the Cu powder compact. The hardness distribution is also ununiform in the width direction for the composite. The average hardness of the composites is higher by 8Hv than that of Cu powder compact. The tensile strength of the composite is 280 MPa, which is 20 MPa higher than that of the Cu powder compact. It is concluded that the powder in sheath rolling method is an effective process for fabrication of sound CNT reinforced Cu matrix composites.

• 한국분말재료학회지
• /
• 제19권5호
• /
• pp.343-347
• /
• 2012

In this study, an oxygen plasma treatment was used as a low temperature debinding method to form a conductive copper feature on a flexible substrate using a direct printing process. To demonstrate this concept, conductive copper patterns were formed on polyimide films using a copper nanoparticle-based paste with polymeric binders and dispersing agents and a screen printing method. Thermal and oxygen plasma treatments were utilized to remove the polymeric vehicle before a sintering of copper nanoparticles. The effect of the debinding methods on the phase, microstructure and electrical conductivity of the screen-printed patterns was systematically investigated by FE-SEM, TGA, XRD and four-point probe analysis. The patterns formed using oxygen plasma debinding showed the well-developed microstructure and the superior electrical conductivity compared with those of using thermal debinding.

• 한국기계가공학회지
• /
• 제19권12호
• /
• pp.49-55
• /
• 2020

In order to improve the electromagnetic shielding rate of Carbon Fiber (CF), it was produced using the nickel nano-powder impregnating method. Using two types of nickel powder having thicknesses of 50 ㎛ and 100 ㎛, and a thermoplastic elastomer resin, a compound containing 10-20% nickel content was mixed and then manufactured through an extruder. The CF coated with the compound was woven and manufactured using a 1-ply specimen. The final nickel content of the specimen was verified using TGA and the distribution of nickel powder on the CF surface was verified using SEM. The metal shows a high shielding rate in the low-frequency band, but the shielding rate decreases at higher-frequency bands. The CF improves at the higher frequency band, and metals reflect electromagnetic waves while carbon absorbs electromagnetic waves. The study of shielding materials, which are stronger and lighter than metal, by using CF lighter than metal and enabling the shielding rate from low-frequency band to high-frequency band, confirmed that the larger the area coated with nickel nano-powder, the better the electromagnetic shielding performance. In particular, CF coated with a thickness of 100 ㎛ has a shielding rate similar to that of copper and can also be used for EV/HEV automotive cables and other applications in the future.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.912-912
• /
• 2006