• Journal of the Korean institute of surface engineering
• /
• v.25 no.2
• /
• pp.66-72
• /
• 1992

Magnetite film on iron surface could be coated in strongly alkaline solution (12M NaH\OH) which contained additives such as NaHCO3, KCl and NaNO2, Iron plate was immersed in boiling solution ($130^{\circ}C$) contained above mentioned additives for 1 hour. There are some microcracks and these cracks proved to be the sites for the initiation of corrosion when immersed in 3% NaCl solution. To improve corrosion resistance of the coated steel plate, chromating was done as a post treatment. Chromate film was formed on magnetite oxide film potentiostatically at-918mV/SCE for five minutes at temperature of $70^{\circ}C$ in the alkaline solution containing 5g/l Na2Cr2O7.2H2O.Cr3O4 was electrodeposited on magnetite oxide film and Cr2O3 was electrodeposited on iron surface which was assumed as surface revealed due to microcracks. Increased corrosion resistance of chromated magnetite oxide film was proved in salt spray test & immersion test.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.3
• /
• pp.469-477
• /
• 2002

One of the major deficiencies of composite restorative resins is their insufficient resistance to wear. Of the multitude of factors that have been associated with wear, subsurface degradation within the restoration is considered to be one. The aim of this study was to evaluate the resistance to degradation of four commercial composite resins in an alkaline solution. The brands studied were Z100(3M), Clearfil AP-X(Kuraray), Tetric Ceram(Vivadent), Aelit flo(Bisco). Resistance to degradation was evaluated on the basis of the following parameters: (a) mass loss(%) - determined from pre-and post-exposure specimen weights: (b) Si loss(ppm) - obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation depth(${\mu}m$) - measured microscopically (SEM) from polished circular sections of exposed specimens. The results were as follows: 1. The sequence of the mass loss was in ascending order by AE, EL, TC, Z100. There was statistically significant difference of mass loss between AE, CL group and TC, Z100 group(p<0.05). 2. The sequence of the degree of degradation layer depth was in ascending order by AE, CL, TC, Z100. But there was no statistically significant difference of degree of degradation layer depth between AE and CL(p<0.05). 3. For the Si concentration, Z100 was the highest of all. 4. The correlation coefficient between mass loss and degradation depth was relatively high(r=0.71 p<0.05).

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.04a
• /
• pp.93-94
• /
• 2022

The presence of chloride (Cl-) ions in environments causes localized corrosion resulting decrease the durability of the structures. In this study, 5% Mg containing Al alloys (Al-5Mg) wire used vis-à-vis compared its corrosion resistance with pure Al in 3.5wt.% NaCl solution with exposure periods. Initially both wires exhibited identical open circuit potential (OCP) attributed to the presence of native oxide film on the surface but with the exposure periods it shifted towards active direction owing to the dissolution of oxide film. The pure Al continuously shifted the OCP towards active direction while Al-5Mg shows stabilization of OCP after 8 days of exposure. The OCP of Al-5Mg is slightly higher compared to pure Al wire owing to the activeness of Mg. The total impedance of the Al-5Mg alloy is almost three times greater than pure Al with exposure periods in 3.5 wt.% NaCl solution. It might be formation of Al-Mg LDH (layered double hydroxide) thin film onto the surface.

• Corrosion Science and Technology
• /
• v.12 no.1
• /
• pp.34-39
• /
• 2013

In this study, the effect of niobium addition on the passivation behavior of Ti alloys in NaCl solution was investigated using various electrochemical methods. An ${\alpha}$-phase in Ti alloy was transformed into a ${\beta}$-phase and martensite structure decreased as Nb content increased. The corrosion and passivation current density($+300mV_{SCE}$) decreased as Nb content increased, and thereby a stable passive film was formed on the Ti alloy. Potential of Ti-xNb alloy in the passive region increased, whereas, current density decreased with time from results of potentiostatic and galvanostatic tests. Also, the corrosion morphology showed the smaller pits as Nb content increased. Consequently, Ti alloy contained high Nb content showed a good resistance to pitting corrosion in 0.9% NaCl solution.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.4
• /
• pp.137-143
• /
• 2005

CrSiN coatings of stepwise changing Si concentration were deposited on stainless steel by closed field unbalanced magnetron sputtering (CFUBM) system. Microstructure of the films due to the Si concentration is measured by XRD. The corrosion behavior of CrSiN coatings in deaerated $3.5\%$ NaCl solution was investigated by potentiodynamic test, electrochemical impedance spectroscopy (EIS) and surface analyses. The microstructure of CrSiN film depends on the Si concentration. When Si/(Cr+si) was under $11.7\%$, preferred orientation is defined at CrN(220), CrN(311) and $Cr_2N(111).$ The results of potentiodynamic polarization tests showed that the corrosion current density and porosity decreased with increasing Si/(Cr+si) ratio. EIS measurements showed that the corrosion resistance of Si-bearing CrN was improved by phase transformation of the film, which leads to increase of pore resistance and charge transfer resistance. At the Si(Cr+si) ratio of 20, the Si-bearing CrN possesses the best corrosion resistance due to the highest pore resistance and charge transfer resistance.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.27 no.2
• /
• pp.370-378
• /
• 2000

The composite restorative resins have their insufficient resistance to wear. The subsurface degradation within the restoration is considered to be associated with wear. The aim of this study was to evaluate the resistance to degradation of six commercial composite resins in an alkaline solution. The brands studied were Clearfil APX(Kuraray), Heliomolar(Vivadent), Surefil(Dentsply), TPH(Dentsply), Tetric Ceram(Vivadent), and Z100(3M). Preweighed discs of each brand were exposed 0.1N NaOH solution at $60^{\circ}C$. After 14 days they were removed, neutralized with HCL, washed with water and dried to constant mass at $60^{\circ}C$. Resistance to degradation was evaluated on the basis of the following parameters: (a) mass loss(%) - determined from pre-and post-exposure specimen weights; (b) Si loss (ppm)-obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation depth$({\mu}m)$ - measured microscopically (SEM) from polished circular sections of exposed specimens. The results were as follows: 1. The mass loss was in descending order by Z100, TC H, S, CL, TPH and in the range of $0.45\sim3.64%$ 2. The degradation layer depth was in descending order by H, Z100, S, TC, TPH, CL and in the range of $10.85\sim73.38{\mu}m$ 3. For the Si concentration, Z100 was the highest of all 4. The highly significant correlation(r=0.81, p<0.05) was observed between mass loss and degradation depth. 5. Under scanning electronmicroscopy, the degradation of connection between resin matrix and fillers was observed 2 weeks after soaking in NaOH solution.

• Journal of Korea Foundry Society
• /
• v.36 no.4
• /
• pp.117-125
• /
• 2016

The effects of the Zn content on the microstructure and corrosion behavior in 1M NaCl solution were investigated in Mg-(0~6)%Zn casting alloys. The MgZn phase was scarcely observed in the Mg-1%Zn alloy, while the Mg-(2~6)%Zn alloy consisted of ${\alpha}$-(Mg) and MgZn phases. With an increase in the Zn content, the amount of the MgZn phase was gradually increased. Immersion and electrochemical corrosion tests indicated that the Mg-1%Zn alloy had the lowest corrosion rate among the alloys, and a further increase in the Zn content resulted in the deterioration of the corrosion resistance. Microstructural examinations of the corroded surfaces and EIS analyses of surface corrosion films revealed that the best corrosion resistance at 1%Zn was associated with the absence of MgZn phase particles in the microstructure and the contribution of Zn element to the formation of a protective film on the surface. A micro-galvanic effect by the MgZn particles led to the increased rate of corrosion at a higher Zn content.

• Journal of Power System Engineering
• /
• v.18 no.6
• /
• pp.29-33
• /
• 2014

The electrochemical characteristics of Al-Si casting alloys (Al-10%Si, Al-9%Si, Al-7%Si) in 3.5% NaCl solution at room temperature was studied using potentiodynamic techniques. The electrochemical values of corrosion potential($E_c$), corrosion current density($I_c$) and corrosion rate(mpy) were examined. The Al-Si alloys had several compounds such as $Mg_2Si$, ${\pi}$-$Al_8Si_6Mg_2Fe$ and $Al_2CuMg$ which could affect corrosion resistance significantly. The potentiodynamic polarization curve exhibited typical active behavior in anodic polarization curve. The major corrosion mechansim for the Al-Si alloys were pitting and grain boundary corrosion. As increasing Si and Cu contents, their corrosion resistance was decreased.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.4
• /
• pp.167-173
• /
• 2005

Surface characteristics of HA(hydroxyapatite) coated dental implant alloy by Sol-Gel method were investigated using potentiostat, ICP, SEM, EDX, EPMA and surface roughness tester. Surface roughness of HA coated specimen by Sol-Gel showed higher than that of PVD coated specimen. Corrosion resistance increased in the order of $1\%$ lactic acid, artificial saliva, $0.5\%$ HCI and $0.9\%$ NaCl solution. Amount of Ca element release was higher than that of V and P in the $0.5\%$ HCI and $0.9\%$ NaCl solution.

• Corrosion Science and Technology
• /
• v.17 no.3
• /
• pp.116-122
• /
• 2018

The secondary coolant of a nuclear power plant has small amounts of various impurities (S, Pb, and Cl, etc.) introduced during the initial construction, maintenance, and normal operation. While the concentration of impurities in the feed water is very low, the flow of the cooling water is restricted, so impurities can accumulate on the Top of Tubesheet (TTS). This environment is chemically very complicated and has a very wide range of pH from acidic to alkaline. In this study, the characteristics of the oxide and the mechanism of stress corrosion cracking (SCC) are investigated for Alloy 690 TT in alkaline solution containing Pb, Cl, and S. Reverse U-bend (RUB) specimens were used to evaluate the SCC resistance. The test solution comprises 3m NaCl + 500ppm Pb + 0.31m $Na_2SO_4$ + 0.45m NaOH. Experimental results show that Alloy 690 TT of the crevice environment containing Pb, S, and Cl has significant cracks, indicating that Alloy 690 is vulnerable to stress corrosion cracking under this environment.