• Corrosion Science and Technology
• /
• 제3권5호
• /
• pp.194-197
• /
• 2004

The corrosion resistance of several kind of ME (Metal Evaporated) tape has been investigated both in mild sulfuric acid solution and NaCl solution by electrochemical impedance spectroscopy. It was found that the degradation of ME tapes was accelerated with increasing the concentration of sulfuric acid. There was no significant change in corrosion resistance when the concentration of NaCl was under 3.5 wt%. However, the impedance value decreased when the concentration of NaCl was up to 10 wt%. The degradation of backside of ME tapes was also investigated by AC impedance measurements. The results showed that the impedance behavior of backside plastic film changed with the concentration of sulfuric acid even at the beginning of immersion, implying the changing of the permeability for the backside of ME tapes. It was also found that the corrosion resistance of DVC (Digital Video Cassette) ME tape was better that that of Hi-8mm ME tapes in sulfuric acid solutions. Also, the backside of DVC ME tape showed better water resistance than that of Hi8 ME tapes.

• Corrosion Science and Technology
• /
• 제18권3호
• /
• pp.110-116
• /
• 2019

Resistances to pitting corrosion of additive manufactured (AM) Ti-6Al-4V alloys in 0.6 M NaBr and 0.6 M NaCl aqueous solutions were compared using micro-droplet cell techniques. With respect to the pitting corrosion resistance, this study focused on two different types of halide anions in aqueous solutions, i.e. $Br^-$ and $Cl^-$. The differences between $Br^-$ and $Cl^-$ halide anions for breakdown on passive films of AM Ti-6Al-4V alloy were explained using Langmuir adsorption model with their equilibrium adsorption coefficients. The results of the analysis showed that the lower resistance to pitting potential of AM Ti-6Al-4V alloy in $Br^-$ aqueous solution was attributed to the higher equilibrium adsorption coefficient of Br-. In addition, micro-electrochemical test results showed that the pitting corrosion resistance of dark grains in additive manufactured Ti-6Al-4V alloy was lower as compared to that of bright grains due to the larger volume of ${\alpha}^{\prime}$ phase that caused the susceptibility to pit initiation.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.509-512
• /
• 2004

This research is targeting that estimate the effect on cement concrete pavement with type of chloride deicers. In order to this study objective, when chloride deicers were spread on road surface, thermal characteristics test was conducted. Also, skid resistance test according to types and concentration of chloride deicier, road surface conditions were investigated. As a test results, thermal characteristics with kind of chloride deicier could know that sodium chloride(NaCl) is exothermic reactive material, calcium chloride$(CaCl_2)$ is endothermic reactive material. And, in case of mixed salt of the calcium and sodium chloride, it could know that can change to the exothermic or endothermic reaction according to dosage ratios. Skid value by British Pendulum Tester(BPT) has shown that it is seldom difference between the types($CaCl_2$, NaCl, mixed salt) and solution concentrations(0.5, 0.8, 1.0, 4.0, $10\%$) of chloride deicier comparing with tap water except mixed salt($10\%$ solution concentration).

• Membrane and Water Treatment
• /
• 제13권4호
• /
• pp.191-199
• /
• 2022

In industrial production, the development of traditional polyamide nanofiltration (NF) membrane was limited due to its poor oxidation resistance, complex preparation process and high cost. In this study, a composite NF membrane with high flux, high separation performance, high oxidation resistance and simple process preparation was prepared by the method of dilute solution dip coating. And the sulfonated polysulfone was used for dip coating. The results indicated that the concentration of glycerin, the pore size of the based membrane, the composition of the coating solution, and the post-treatment process had important effects on the structure and performance of the composite NF membrane. The composite NF membrane prepared without glycerol protecting based membrane had a low flux, when the concentration of glycerin increased from 5% to 15%, the pure water flux of the composite NF membrane increased from 46.4 LMH to 108.2 LMH, and the salt rejection rate did not change much. By optimizing the coating system, the rejection rate of Na₂SO₄ and PEG1000 was higher than 90%, the pure water flux was higher than 40 LMH (60psi), and it can withstand 20,000 ppm.h NaClO solution cleaning. When the post treatment processes was adjusted, the salt rejection rate of NaCl solution (250 ppm) reached 45.5%, and the flux reached 62.2 LMH.

• Corrosion Science and Technology
• /
• 제21권4호
• /
• pp.282-289
• /
• 2022

Aluminum 1000 series alloy, a pure aluminum with excellent workability and weldability, is mainly used in the ship field. Aluminum alloy can combine with oxygen in the atmosphere and form a natural oxide film with high corrosion resistance. However, its corrosion resistance and durability are decreased when it is exposed to a harsh environment for a long period of time. For solving this problem, a porous oxide film can be formed on the surface using an anodizing treatment method, a typical surface technique among various methods. In this study, aluminum 1050 alloy was anodized for 2 minutes, 6 minutes, and 10 minutes. The structure and shape of the oxide film were then analyzed to determine the corrosion resistance according to the thickness of the oxide film that changed depending on working condition using 15 wt% NaCl. After it was immersed in NaCl solution for 1, 5, and 10 days, corrosion damage was observed. Results confirmed that the thickness of the oxide film increased as the anodization time became longer. The depth of surface damage due to corrosion became deeper when the film was immersed in the 15 wt% NaCl solution for a longer period of time.

• Corrosion Science and Technology
• /
• 제20권3호
• /
• pp.129-142
• /
• 2021

Effects of corrosion inhibitors (i.e., sodium nitrite, sodium hexametaphosphate, trimethylamine (TEA), sugar, and urea) on the corrosion resistance of carbon steel in CaCl₂ solution were investigated. The test solution was designed with response surface methodology of design of experiments (DOE) in the range of 0 ~ 50 ppm for NaNO₂, 0 ~ 200 ppm for (NaPO₃)₆, 0 ~ 2000 ppm for TEA, 0 ~ 3000 ppm for sugar, 0 ~ 200 ppm for urea with 3 wt% CaCl₂. The corrosion potential and the corrosion rate were measured with potentiodynamic polarization tests and analyzed statistically to find main effects of inhibitor concentrations and interactions between them. As a result, hexametaphosphate was the most effective compound in reducing the corrosion rate. Sugar also reduced the corrosion rate significantly possibly because it covered the surface effectively with a high molecular weight. The inhibiting action of sugar was found to be enhanced by adding trimethylamine into the solution. Nevertheless, trimethylamine did not appear to be effective in inhibiting corrosion by itself. However, urea and sodium nitrite showed almost no inhibition on corrosion resistance of steel.

• 한국염색가공학회지
• /
• 제31권3호
• /
• pp.177-186
• /
• 2019

In this study, we investigated for synthetic hydrotalcite in chloroprene rubber foam. Experiments were carried out to find the optimum content ratio by controlling the contents of MgO and Hydrotalcite. Swelling test in toluene immersion was made to measure the crosslinking density of CR foams, and the cure properties were investigated with flat die rheometer and Mooney viscosity. The difference of hardness, tensile strength and elongation at break were observed after immersing in 7% NaCl or 21% NaCl solutions for a day and four days. In addition, the volume change and water content remaining in CR foam were measured after immersing NaCl solution. As content of MgO increased, the value of the cure torque tended to increase, but it was almost constant above 2phr of MgO. However, the Mooney viscosity decreased with increasing MgO content. The crosslinking density, determined by the swelling ratio, showed that the CR compound without MgO showed a higher degree of swelling. When the content of hydrotalcite/MgO was 3:2, it was the lowest volume change of CR form. Also, As the content of hydrotalcite decreased, the difference of mechanical properties before and after immersion NaCl solution increased.

• 한국해양공학회지
• /
• 제1권2호
• /
• pp.123-129
• /
• 1987

Corrosion fatigue fracture of dual phase steel(SS41) and raw material steel(SS41) were investigated in 3.5% NaCl aqueous solution at PH 4,6,9 and 11. The fatigue limit of dual phase steel is increased approximately 1.8 times larger than that of raw material in air. The corrosion fatigue life of dual phase steel is about 5-10 times larger than that of raw material in 3.5% NaCl aqueous solution. The reduction of fatigue life is larger for the acidsalt solution than for the alkali salt solution. The reduction of stress level on the reduction ratio of corrosion fatigue life is large as pH 6-11. The reduction ratio of corrosion fatigue life of dual phase steel and raw material is nearly coincided at pH 2. While at pH4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. It has been found that the corrosion resistance effect of dual phase steel is smaller than that of raw material in corrosion fatigue crack propagation rate. As pH below 6 is changed, it can be clearly observed from raw material that the brittle intergranular fracture is characterized, and from the above result, the influence of corrosion of dual phase steel is small.

• 한국재료학회지
• /
• 제28권12호
• /
• pp.738-747
• /
• 2018

For the aerospace structural application of high-strength 2xxx series aluminum alloys, stress corrosion cracking(SCC) behavior in aggressive environments needs to be well understood. In this study, the SCC sensitivities of 2024-T62, 2124-T851 and 2050-T84 alloys in a 3.5 % NaCl solution are measured using a constant load testing method without polarization and a slow strain rate test(SSRT) method at a strain rate of 10-6 /sec under a cathodic applied potential. When the specimens are exposed to a 3.5 % NaCl solution under a constant load for 10 days, the decrease in tensile ductility is negligible for 2124-T851 and 2050-T84 specimens, proving that T8 heat treatment is beneficial in improving the SCC resistance of 2xxx series aluminum alloys. The specimens are also susceptible to SCC in a hydrogen-generating environment at a slow strain rate of $10^{-6}/sec$ in a 3.5 % NaCl solution under a cathodic applied potential. Regardless of the test method, low impurity 2124-T851 and high Cu/Mg ratio 2050-T84 alloys are found to have relatively lower SCC sensitivity than 2024-T62. The SCC behavior of 2xxx series aluminum alloys in the 3.5 % NaCl solution is discussed based on fractographic and micrographic observations.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 가을학술발표대회논문집
• /
• pp.119-120
• /
• 2023

Corrosion of the steel rebar in coastal environment caused huge economical loss of the globe. Therefore, coating on the steel rebar being used to mitigate the corrosion. In the present study, we have applied epoxy coating on arc thermal sprayed Al coating (a dual metal/polymeric coating) vis-à-vis compared with as coated one (Al coating). The corrosion studies were performed in simulated concrete pore solution with 3.5 wt. % NaCl solution. The morphology of the dual epoxy/Al coating is smooth while Al coating shows rankle and defects. Due to defects, Al coating is susceptible to corrosion while dual epoxy/Al coating has performed excellent compared to as coated one at extended period of immersion.