• 한국세라믹학회지
• /
• 제30권1호
• /
• pp.25-33
• /
• 1993

Formation reaction of Mn-Zn ferrite depending on various synthetic conditions of wet process was investigated using FeCl2.nH2O(n≒4), MnCl2.4H2O, ZnCl2 as starting materials. A stable intermediate precipitate was formed by the addition of H2O2. And the precipitate was hard to transform to spinel phase of Mn-Zn Fe2O4. Single phase of Mn-Zn Fe2O4 spinel was obtained above 8$0^{\circ}C$ reaction temperature. The powder had spherical particle shape and 0.02~0.05${\mu}{\textrm}{m}$ particle size. Fe(OH)2 solid solution, -FeO(OH) solid solution, -FeOOH, Mn-Zn Fe2O4 spinel were formed with air flow rate 180$\ell$/hr. However, single phase of Mn-Zn Fe2O4 spinel with cubic particle shape and 0.1~0.2${\mu}{\textrm}{m}$ particle size was formed with synthetic conditions of 8$0^{\circ}C$ and 90 munutes. The particle shape of the -FeOOH was needle-like.

• 한국전자파학회지:전자파기술
• /
• 제4권2호
• /
• pp.41-47
• /
• 1993

MnZn계 페라이트 실리콘 고무 복합체를 MnZn 페라이트의 체적비플 0.1에서 0.4까지 변화시키면서 제작하여 주파수 대역 1 GHz-lO GHz 범위에서 전기적 특성및 전파흡수 특성을 조사하였다. MnZn 페라이트의 체적비가 증가할 수록 유전율과 투자율의 증가를 보였다 반사 손실 흡수체의 두께가 1/4파장에 해당하는 주파수 대역에서 극대치가 나타났으며, 극대치는 MnZn 페라이트의 체적비가 증기할 수록 저주파 수로 이동하는 현상을 나타내었다 또한 흡수체의 두께가증가함에 따라서 반사손실 극대치는 저주파수 대역으로 안동하였다 페라이트 고무 복합체의 경우에 전파 흡수체의 사용주파수 대역에 따라서 요구되는 전파 흡수 효과를 얻기 위해서는 페라이트 체적비를 조절해야 함을 보여 주였다.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.763-764
• /
• 2006

Ceramic Injection Moulding (CIM) technology has been successfully used for the fabrication of Mn-Zn Ferrite part. The binder was composed by polypropylene and paraffin wax. The optimal powder loading (58% vol.) was determined by means of rheological measurements. Threedifferent parts, toroids, bending and tensile probes were injected. Thermal and solvent-thermal debinding was designed based on DSC and TGA studies of the binder. The time of the debinding cycle was reduced using n-heptane to dissolve previously the paraffin wax. Final properties have been determined and compared with uniaxial pressure parts values. The densities obtained were slightly higher than those of uniaxial pressure parts and the magnetic properties presented similar values.

• 한국세라믹학회지
• /
• 제29권7호
• /
• pp.539-543
• /
• 1992

The continuous growth method was developed for Mn-Zn Ferrite single crystals. It is a new process that the polycrystalline MnχZn1-χFe2O4 raw materials are supplied continuously from the powder feeding system to the crucible heated by R.F. induction and melted in the crucible, and after the single crystals seed is attached to crucible's hole, the crystals are pulled downward with rotation. Growing the crystals by using the growth method different from the conventional Bridgman or Floating Zone method, we defined the factors having effect on the crystal growing through the pre-experiments. They are temperature distribution in the crucible, melt velocity according to its height, wettability between the crucible's bottom and melt. Therefore, Mn-Zn Ferrite single crystals were to be grown by attaining the appropriate melt height in the crucible, powder feeding rate, temperature gradient between the crucible and interface, crystal growing speed, and this method was confirmed to have possibility for single crystal growing.

• Journal of Magnetics
• /
• 제21권3호
• /
• pp.308-314
• /
• 2016

Cobalt-, zinc-, and nickel-zinc-substituted nano-size manganese ferrite powders, $MnFe_2O_4$, $Mn_{0.8}Co_{0.2}Fe_2O_4$, $Mn_{0.8}Zn_{0.2}Fe_2O_4$ and $Mn_{0.8}Ni_{0.1}Zn_{0.1}Fe_2O_4$, were fabricated using a sol-gel method, and their crystallographic and magnetic properties were subsequently studied. The $MnFe_2O_4$ ferrite powder annealed at temperatures above 523 K exhibited a spinel structure, and the particle size increased as the annealing temperature increased. All ferrites annealed at 773 K showed a single spinel structure, and the lattice constants and particle size decreased with the substitution of Co, Zn, and Ni-Zn. The $M{\ddot{o}}ssbauer$ spectrum of the $MnFe_2O_4$ ferrite powder annealed at 523 K only showed a doublet due to its superparamagnetic phase, and the $M{\ddot{o}}ssbauer$ spectra of the $MnFe_2O_4$, $Mn_{0.8}Co_{0.2}Fe_2O_4$, and $Mn_{0.8}Zn_{0.2}Fe_2O_4$ ferrite powders annealed at 773 K could be fitted as the superposition of two Zeeman sextets due to the tetrahedral and octahedral sites of the $Fe^{3+}$ ions. However, the $M{\ddot{o}}ssbauer$ spectrum of the $Mn_{0.8}Ni_{0.1}Zn_{0.1}Fe_2O_4$ ferrite powder annealed at 773 K consisted of two Zeeman sextets and one quadrupole doublet due to its ferrimagnetic and paramagnetic behavior. The area ratio of the $M{\ddot{o}}ssbauer$ spectra could be used to determine the cation distribution equation, and we also explained the variation in the $M{\ddot{o}}ssbauer$ parameters by using this cation distribution equation, the superexchange interaction and the particle size. Relative to pure $MnFe_2O_4$, the saturation magnetizations and coercivities were larger in $Mn_{0.8}Co_{0.2}Fe_2O_4$ and smaller in $Mn_{0.8}Zn_{0.2}Fe_2O_4$, and $Mn_{0.8}Ni_{0.1}Zn_{0.1}Fe_2O_4$. These variations could be explained using the site distribution equations, particle sizes and magnetic moments of the substituted ions.

• 한국항해학회지
• /
• 제23권1호
• /
• pp.15-22
• /
• 1999

In this paper, ferrite-rubber composite has been studied in order to apply to RF-A-PF in a super wideband electromagnetic absorber in RF-A-PF type, which can be used for a general purpose anechoic chamber. $Ni_x - Mn_0.1 - Zn_{(1-x-0.1)}ㆍFe_2O_4$ ferrite powder has been fabricated, then, using this, 〔$Ni_x - Mn_0.1 - Zn_{(1-x-0.1)}ㆍFe_2O_4$〕-Rubber composite for RF-layer in the RF-A-PF type absorber has been fabricated and it's characteristics have been analyzed. As a result, it has been clearly shown that the 〔$Ni_x - Mn_0.1 - Zn_{(1-x-0.1)}ㆍFe_2O_4$〕-Rubber composite has excellent electromagnetic wave absorbing properties.

• 한국세라믹학회지
• /
• 제40권2호
• /
• pp.146-152
• /
• 2003

지구온난화의 주요 원인인 $CO_2$를 분해시키기 위하여 Ni-Zn 페라이트와 Mn-Zn 페라이트 코어 제조시 대량으로 배출되는 페라이트 폐기물을 이용하였다. 폐기물 페라이트와 페라이트 코어 완제품인 Ni-Zn 페라이트와 Mn-Zn 페라이트는 5% $H_2$/Ar과의 환원반응에서 14~16wt%가 환원되었다. 환원된 페라이트를 이용한 $CO_2$분해 반응에서는 세 종류의 페라이트 모두 약 11wt%에 해당하는 $CO_2$를 분해하였다. 이 반응에서 $CO_2$는 환원된 페라이트 중 Fe와 FeO치 산화에 의해 분해되었으며. 폐기물 페라이트의 경우 $CO_2$분해 반응 후 스피넬 결정상을 형성하였다. 대량으로 버려지는 폐기물 페라이트를 이용하여 저비용으로 $CO_2$분해가 가능한 폐기물 활용기술을 개발하였다.

• 한국세라믹학회지
• /
• 제28권10호
• /
• pp.757-766
• /
• 1991

These powder properties were investigated and prepared of ultrafine Mn-Zn ferrite powder by Direct-wet process from variation of oxidation condition. H2O2 oxidation the products were ultrafine spherical particles of about 400${\AA}$ in diameter and superparamagnetics. H2O2 and Air oxidation, Coexistance ultrafine spherical particles of about 400${\AA}$ and cubic particles of about 1000${\AA}$. The products were constructed of superparamagnetic and ferromagnetic particles, and Magnetization were about 30 emu/g. Air Oxidation, Above 6 hr Air 120 ι/hr and 4 hr of Air 180 ι/hr were uniform cubic particles of above 1000${\AA}$. The products were ferromagnetic particles and Magnetization of above 45 emu/g.

• 한국세라믹학회지
• /
• 제34권3호
• /
• pp.289-295
• /
• 1997

저손실 Mn-Zn 페라이트의 제조공정과 첨가제가 코아의 미세구조와 전기적 특성에 미치는 영향을 조사하였다. C\ulcorner와 SiO2를 원료분체혼합시에 첨가하는 경우보다 하소분체의 재분쇄시에 첨가할 때가 작고 균일한 소결체를 얻을 수 있었다. 산소분압(Po2)이 높아짐에 따라 미세구조가 불균일해졌고 DF(disaccomodation fac-색)가 증가하였다. 또한 하소온도가 높고 분쇄시간이 짧은 소결체의 경우 치밀한 속도가 감소하여, 130$0^{\circ}C$까지 정상입성장거동을 보였고, 따라서 높은 소결온도에서도 비교적 저손실 Mn-Zn 페라이트를 얻을 수 있었다. 장시간 분쇄하거나 하소온도가 낮은 시편의 경우는 치밀화속도의 증가에 기인하여 120$0^{\circ}C$이하의 저온 소결시 미립자의 저손실 Mn-Zn 페라이트를 얻을 수 있었으나 소결온도 125$0^{\circ}C$이상에서는 비정상 입성장을 유발시켰다.

• 한국세라믹학회지
• /
• 제35권10호
• /
• pp.1055-1060
• /
• 1998

고주파 저손실 재질로 사용되는 Mn-Zn ferrites의 제조공정 중 입도분포제어가 전자기적 물성에 미치는 효과에 관하여 연구하였다. 입도분포는 분쇄시간을 변화시켜 제어하였으며 철의 유입을 막기위하여 지르코니아볼을 사용하였다. 분쇄시간이 증가함에 따라 입자크기는 2.1 $\mu\textrm{m}$에서 1.0$\mu\textrm{m}$로 감소하였으며, 비표면적은 0.55에서 3.21m2/g으로 증가하였다. 비표면적 값이 증가할수록 소결체의 밀도는 증가하였으며, 높은 비표면적을 가진 분말의 경우 1300$^{\circ}C$ 이 상의 고온에서 소결할 때 불균일한 미세구조와 과대입성장이 발생하였으며, 전자기적 물성감소가 나타났다.