• The Journal of Korean Academy of Prosthodontics
• /
• v.46 no.4
• /
• pp.372-380
• /
• 2008

Purpose: The purpose of this study was to evaluate the effect of various methods of dentin bonding agent application on microtensile bond strength between dentin and resin, using a 2-step etch-and-rinse dentin bonding agent. Material and methods: Twenty freshly extracted human molars were obtained and divided into 4 groups of 5 teeth. 2-step etch-and-rinse dentin bonding agent was used for all groups. The control specimens were prepared using a direct immediate bonding technique. The delayed dentin sealing (A, C) specimens were prepared using an indirect approach with delayed dentin sealing. For group A, resin was built-up on uncured dentin bonding agent, and for group C, resin was built-up on pre-cured dentin bonding agent. Preparation of the immediate dentin sealing (B) specimens also used an indirect approach with immediate dentin sealing immediately following preparation. All teeth were prepared for a microtensile bond strength test. Specimens were stored in water for 24 hours. Ten beams (1.0 ${\times}$ 1.0 ${\times}$ 11 mm) from each tooth were selected for testing. Bond strength data (MPa) were analyzed with a one-way ANOVA test, and post hoc comparison was done using the Scheffe's test. Results: The mean microtensile bond strengths of control group, B and C (DDS with pre-cure) were not statisticaaly different from each other at 32.7, 33.3, 34.2 MPa. the bond strength for group A (DDS without pre-cure), 19.5 MPa, was statistically different (P < .01) from the other 3 groups. Conclusion: When preparing teeth for indirect bonded restorations, DDS with pre-curing dentin bonding agent and IDS results in the same bond strength between dentin and resin. On the contrast, the bond strength was decreased when DDS without pre-curing dentin bonding agent was used.

• Restorative Dentistry and Endodontics
• /
• v.28 no.3
• /
• pp.203-208
• /
• 2003

The purpose of this study was to evaluate the effect of salivary contamination of teeth on bonding efficacy of self-priming and self-etching DBSs. The materials used were Single Bond(SB, self-priming system, 3M), Unifil Bond(UB, self-etching system, GC), and Scotchbond Multi-Purpose Plus(SM, 3M) as control. Forty five human molars randomly allocated to three groups as dentin bonding systems tested and embedded in epoxy resin. Then the specimens were wet-ground to expose flat buccal enamel surface or flat occlusal dentin surface and cut bucco-lingually to form two halves with slow speed diamond saw. One of them was used under non-contamination, other under contamination with saliva. The bonding procedure was according to the manufacturer's directions and resin composite(Z-100, 3M Dental Products, St. Paul, MN) was built-up on the bonded surface 5mm high. The specimens were ground carefully at the enamel-composite interface with fine finishing round diamond bur to create an hour-glass shape yielding bonded surface areas of $1.5{\pm}0.1\textrm{mm}^2$. The specimens were bonded to the modified microtensile testing apparatus with cyanoacrylate, attached to the universal testing machine and stressed in tension at a CHS of 1mm/min. The tensile force at failure was recorded and converted to a tensile stress(MPa). Mean values and standard deviations of the bond strength are listed in table. One-way ANOVA was used to determine significant difference at the 95% level. The bond strength of SBMP and SB were not affected by salivary contamination, but that of UB was significantly affected by salivary contamination. These results indicate that DBSs with total etch technique seems less likely affected by salivary contamination in bonding procedure.

• Restorative Dentistry and Endodontics
• /
• v.30 no.6
• /
• pp.435-441
• /
• 2005

The purpose of this study was to evaluate the effect of increasing application time of single bottle adhesives (SBA) to microtensile bond strength (MTBS) of dried dentin. To expose the superficial dentin surfaces, human molars were sectioned perpendicular to the long axis of tooth. $32\%$ phosphoric acid gels were applied for 15s and rinsed. The teeth were randomly assigned to 3 groups ; S group (Single Bond), O group (One-Step), P group (Prime & Bond NT). Each group was divided to 3 subgroups (W: dentin wipe with wet gauge and light cured immediately, D, dentin dried for 30s and light cured immediately, 30: dentin dried for 30s and light cured after applying SBA for 30s). Composite resin was built up on the dentin surface and sectioned to obtain 20 specimens with $1mm^2$ cross sectional area and the MTBS was measured. For Single Bond, the mean MTBS of S-W and S-30 group were higher than that of S-D group statistically (P<0.05). For One-Step, the mean MTBS of O-D group was statistically lower than that of O-W group (P<0.05). For Prime & Bond NT, the mean MTBS of P-30 group was statistically lower than that of P-D group (P<0.05).

• Proceedings of the KACD Conference
• /
• 2003.11a
• /
• pp.568-568
• /
• 2003

I. Objectives This study investigated the effect of rewetting agent on dentinal microtensile bond strengths(${\mu}TBS$), using one bottle adhesives. II. Materials and Methods Non caries human molars were sectioned to exposed the superficial dentin surfaces, etched 15 seconds using 32% phosphoric acid and 10 seconds rinsed. Samples were randomly divided into two groups according to adhesives (Single Bond, One-Step) used. Each group were subdivided into five groups by different dentin surface treatment：15 second dry(D), blot dry(BD) or 15 second dry and rewetted with distrilled water(DW), Gluma Desensitizer(GD) and Aqua-Prep(AP) during 30 second, respectively.(omitted)

• Restorative Dentistry and Endodontics
• /
• v.31 no.6
• /
• pp.415-426
• /
• 2006

In this study, the changes in the degree of conversion (DC) and the microtensile bond strength (MTBS) of self-etching adhesives to dentin was investigated according to the time after curing. The MTBS of Single Bond (SB, 3M ESPE, USA), Clearfil SE Bond (SE, Kuraray, Japan), Xeno-III (XIII, Dentsply, Germany), and Adper Prompt (AP, 3M ESPE, USA) were measured at 48h, at 1 week and after thermocycling for 5,000 cycles between 5$^{\circ}$C and 55$^{\circ}$C. The DC of the adhesives were measured immediately, at 48h and at 7 days after curing using a Fourier Transform Infra-red Spectrometer. The fractured surfaces were also evaluated with scanning electron microscope. The MTBS and DC were significantly increased with time and there was an interaction between the variables of time and material (MTBS, 2-way ANOVA, p = 0.018; DC, Repeated Measures ANOVA, p < 0.001). The low DC was suggested as a cause of the low MTBS of self-etching adhesives, XIII and AP, but the increase in the MTBS of SE and AP after 48h could not be related with the changes in the DC. The microscopic maturation of the adhesive layer might be considered as the cause of increasing bond strength.

• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.2
• /
• pp.114-119
• /
• 2011

The aim of this study was to investigate effect of specimen preparation method on the microtensile bond strength of veneering ceramic to zirconia core. Materials and methods: Cylindrical Lava zirconia block (3M ESPE, Seefeld, Germany) was cut into discs using a diamond disc. After sintering, the core specimens were placed in an adjustable mold and veneered with Lava ceram (3M ESPE, Seefeld, Germany). The disc shaped specimen of group 1 was cut into microbars ($1{\times}1{\times}7\;mm^3$) using a low speed diamond disc under water cooling (n = 15). The specimen of group 2 was cut into microbars ($1.2{\times}1.2{\times}7\;mm^3$) in the same way. Whereafter the microbars were trimmed ($1{\times}1{\times}7\;mm^3$) using a thick diamond disc under water cooling (n = 15). The microtensile bond strength was tested in a microtensile tester (Instron 8848, $Instron^{(R)}$ Co., Norwood, USA). Fractured microtensile specimens were analyzed under a stereomicroscope (MZ6, Leica Microsystems GmbH, Wetzlar, Germany) at magnification ${\times}30$. Results: The microtensile bond strength of group 1 ($28.8{\pm}7.0\;MPa$) was significantly higher than group 2 ($11.0{\pm}33\;MPa$) (P=.00). Conclusion: It appears advisable to avoid the trimming action, especially high strength ceramic specimens.

• Restorative Dentistry and Endodontics
• /
• v.33 no.5
• /
• pp.472-480
• /
• 2008

This study was conducted to evaluate the influence of the C-factor on the bond strength of a 6th generation self-etching system by measuring the microtensile bond strength of four types of restorations classified by different C-factors with an identical depth of dentin. Eighty human molars were divided into four experimental groups, each of which had a C-factor of 0.25, 2, 3 or 4. Each group was then further divided into four subgroups based on the adhesive and composite resin used. The adhesives used for this study were AQ Bond Plus (Sun Medical, Japan) and XenoIII (DENTSPLY, Germany). And composite resins used were fantasists (Sun Medical, Japan) and Ceram-X mono (DENTSPLY, Germany). The results were then analyzed using one-way ANOVA, a Tukey's test, and a Pearson's correlation test and were as follows. 1. There was no significant difference among C-factor groups with the exception of groups of Xeno III and Ceram-X mono (p<0.05). 2. There was no significant difference between any of the adhesives and composite resins in groups with C-factor 0.25, 2 and 4. 3. There was no correlation between the change in C-factor and microtensile bond strength in the Fantasista groups. It was concluded that the C-factor of cavities does not have a significant effect on the microtensile bond strength of the restorations when cavities of the same depth of dentin are restored using composite resin in conjunction with the 6th generation self-etching system.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.1
• /
• pp.38-44
• /
• 2017

PURPOSE. The objective of this study was to investigate the effect of surface treatments on microtensile bond strengths (MTBSs) of two types of indirect resin composites bonded to a conventional direct resin composite. MATERIALS AND METHODS. Indirect resin composite blocks of Ceramage and SR Nexco were prepared in a plastic mold having a dimension of $10{\times}10{\times}4\;mm$. These composite blocks were divided into three groups according to their surface treatments: Group1: Sandblast (SB); Group2: Sandblast and ultrasonically clean (SB+UL); Group3: Sandblast plus silane (SB+SI). After bonding with direct resin composite, indirect-direct resin composite blocks were kept in distilled water for 24 hours at $37^{\circ}C$ and cut into microbars with the dimension of $1{\times}1{\times}8\;mm$. Microbar specimens (n = 40 per group) were loaded using a universal testing machine. Failure modes and compositions were evaluated by SEM. The statistical analyses of MTBS were performed by two-way ANOVA and Dunnett's test at ${\alpha}=.05$. RESULTS. Surface treatments and brands had effects on the MTBS without an interaction between these two factors. For SR Nexco, the MTBSs of SB and SB+SI group were significantly higher than that of SB+UL. For Ceramage, the MTBSs of SB and SB+SI were significantly higher than that of SB+UL. The mean MTBS of the Ceramage specimens was significantly higher than that of SR Nexco for all surface treatments. CONCLUSION. Sandblasting with or without silane application could improve the bond strengths of repaired indirect resin composites to a conventional direct resin composite.

• Restorative Dentistry and Endodontics
• /
• v.28 no.6
• /
• pp.498-503
• /
• 2003

The purpose of this study was to evaluate the rewetting effect of water-based primer on the air-dried dentin. In this in vitro study, freshly extracted non-caries human molars and three-step adhesive system(SBMP) were used. Freshly extracted non-caries human molars and three-step adhesive system(SBMP) were used. Flat occlusal dentin surface were prepared using low-speed diamond saw, Prepared teeth were randomly divided into three groups. Group 1.(W): etched(35% phosphoric acid for 15s) and blot-dried, Group 2.(5D): 5s air-dried, Group 3.(30D): 30s ail-dried, To obtain color contrast in CLSM observation, primer was mixed with rhodamine B and bonding resin was mixed with fluorescein. Microscopic sample of each group were obtained after longitudinal section. Morphological investigation of resin-dentin interface and thickness of hybrid layer measurement using CLSM were done. Microtensile bond strength for each specimen was measured. Specimen were observed under microscope to examine the failure patterns of interface between resin and dentin. The results of this study were as follows: 1. The results(mean) of Thickness of hybrid layer were W:19.67, 5D:20.9, 30D:10$\mu\textrm{m}$. Only 30D had statistically significant differences to Wand 5D(P<0.05). 2. The results(mean) of Microtensile bond strength were W:16.02, 5D:14.69, 30D:11.14MPa. Only 30D had statistically significant differences to Wand 5D(P<0.05). 3. There were positive correlation between Thickness of hybrid layer and microtensile bond strength(P<0.05).

• Restorative Dentistry and Endodontics
• /
• v.34 no.5
• /
• pp.406-414
• /
• 2009

The purpose of this study was to examine the effect of hydrogen peroxide at different application time and concentrations on the microtensile bond strength of resin restorations to the deep and the pulp chamber dentin. A conventional endodontic access cavity was prepared in each tooth, and then the teeth were randomly divided into 1 control group and 4 experimental groups as follows: Group 1, non treated; Group 2, with 20% Hydrogen peroxide ($H_2O_2$); Group 3, with 10% $H_2O_2$; Group 4, with 5% $H_2O_2$; Group 5, with 2.5% $H_2O_2$; the teeth of all groups except group 1 were treated for 20, 10, and 5min. The treated teeth were filled using a Superbond C&B (Sun medical Co., Shiga, Japan). Thereafter, the specimens were stored in distilled water at $37^{\circ}C$ for 24-hours and then sectioned into the deep and the chamber dentin. The microtensile bond strength values of each group were analyzed by 3-way ANOVA and Tukey post hoc test(p < 0.05). In this study, the microtensile bond strength of the deep dentin (D1) was significantly greater than that of the pulp chamber dentin (D2) in the all groups tested. The average of microtensile bond strength was decreased as the concentration and the application time of $H_2O_2$ were increased. Analysis showed significant correlation effect not only between the depth of the dentin and the concentration of $H_2O_2$ but also between the concentration of H202 and the application time(p < 0.05), while no significant difference existed among these three variables(p > 0.05). The higher $H_2O_2$ concentration, the more opened dentinal tubules under a scanning electron microscope(SEM) examination.