• 한국염색가공학회지
• /
• 제15권4호
• /
• pp.65-72
• /
• 2003

Poly(ethylene-co-vinylacetate) (EVA) microspheres were prepared by a thermally induced phase separation. Poly(vinyl Alcohol) (EVAL) microsphere with Core-Shell Structure were synthesized by a saponification on sheath of EVA microspheres. The size of EVA core/EVAL shell microsphere was decreased from $4.09\mu{m}\;to\;2.55\mu{m}$ by partial saponification of $NaOH/Na_2SO_4$/methanol(2 : 1 : 1 by weight) at $60^\circ{C}$ for 4h to produce a saponified surface layer of about 60% of original radius. In this process, the surface layer of EVAL microsphere was dissolved partially and morphology of surface was not showed. Add-on of cotton and silk printed with EVA core/EVAL shell microsphere was increased and that of printed PET was decreased. In case of EVA core/EVAL shell microsphere, Hand of cotton and silk printed was flexible and fullness.

• 한국염색가공학회지
• /
• 제17권3호
• /
• pp.26-33
• /
• 2005

EVA microsphere was prepared by a thermally induced phase separation. EVAL microsphere was made by a saponification on sheath of EVA microsphere. And microcapsule with EVA core-PU shell structure was synthesized by interfacial polymerization using diisocyanates with PEG in gelatin aqueous solution as the stabilizing agent. The effects of chemical structure of diisocyanate on the average particle size and distribution, morphology, color strength and friction fastness of core-shell particles were investigated to design microcapsule. The friction fastness of the fabrics printed with EVA core-PU shell microcapsules had the 4-5 grade.

• Korean Chemical Engineering Research
• /
• 제46권4호
• /
• pp.722-726
• /
• 2008

실리카 microsphere는 HPLC를 위한 흡착 충진제와 같은 용도로 사용하기에 적합한 혁신적인 소재로 널리 알려져 있다. microsphere을 기능성고분자나 금속, 생리활성 물질과 같은 특정한 성질을 지닌 물질로 표면 개질시키므로 다양한 용도로 활용할 수 있다. 콜라겐은 생체조직을 구성하는 기본 단백질로 생체적합성이 뛰어난 물질로 주목받고 있는 기능성 소재이다. 본 연구에서는 50% 이상의 세공부피를 지닌 다공성 silica microsphere를 고분자 응집법인 PICA 법을 이용하여 colloidal silica로부터 제조하고 콜라겐 hydrogel을 사용하여 표면 개질시키므로 생체적합성을 증진시키는 방법을 연구하였다. 실리카/콜라겐 microsphere 에 은 나노입자를 담지시킨 microsphere 복합체를 만들고 특성을 조사하므로 생체소재로의 활용 가능성을 조사하였다.

• 한국세라믹학회지
• /
• 제41권7호
• /
• pp.513-517
• /
• 2004

기공크기와 형태를 제어하여 열전도도 이방성을 나타내기 위해 판상의 기공이 배향된 다공질 알루미나 소결체의 제조방법을 연구하였다. 속이 가스로 차있는 열가소성 고분자 microsphere를 알루미나 분말과 혼합한 후 일축 가압 열변형 방법을 이용하여 15 MPa의 압력으로 가압한 상태에서 20$0^{\circ}C$까지 승온하여 microsphere를 판상으로 변형시킨 후, 1,00$0^{\circ}C$에서 1시간동안 소결하였다. Microsphere의 함량이 10wt%인 경우 45.3%의 기공율을 나타내었으며, 44 MPa의 꺾임강도 값을 나타내었다. 미세구조를 살펴본 결과 판상기공이 압축방향과 수직방향으로 배향되었으며, 열전도도를 측정한 결과 압축방향으로 3.803 W/mK, 측면방향으로는 7.818 W/mK로서 두 값의 비는 2 이상이었다.

• 한국임상수의학회지
• /
• 제19권2호
• /
• pp.228-235
• /
• 2002

유방염은 젖소에 있어서 유량의 감소, 유질 저하로 인한 우유 폐기문제, 젖소의 도태, 치료비 및 노동력의 부담등을 초래하는 가장 경제적 손실이 큰 질환이다. 현재까지 비유기 최종 착유 후에 항생제를 주입하는 건유기 치료법이 유방염 관리에 가장 효과적이며 폭넓게 쓰이고 있는 방법으로 알려져 있다. 하지만, 건유기 치료는 건유기 주입 항생제 제품들이 건유기 초기에만 지속적인 활성을 지니기 때문에 건유기 말기와 분만 전기에 있어서의 신규 감염은 방어할 수 없다. 따라서 본 연구는 건유기 유방염 관리를 위해 PLGA를 이용한 서방형 생분해 cephalexin microsphere를 제조하여 이의 임상적 효능을 평가하고자 하였다. PLGA는 무독성의 조직 반응을 일으키지 않는 특성으로 인해 약물 방출 조절 체계의 일환으로 인정을 받아왔다. 본 연구에서 cephalexin microsphere는 표면에 특징적인 구멍을 가지고 있는 구형 모양으로 확인이 되었으며 약물 방출 시험에서 초기 과다 방출 이후로 21일간 약물의 방출이 점차 감소한 뒤 3주와 4주 사이에 2차 방출을 보이는 맥동성 방출 양상이 관찰되었다. 현장적용 시험에서는 cephalexin microsphere를 주입한 실험군에서 대조군에 비해 분만 후 신규 감염율 및 치료율, 평균 체세포 수의 변화의 측면에서 볼 때 유의성 있는 차이가 있음을 확인하였다. 따라서 생분해 microsphere를 이용한 건유기 치료법은 건유기 동안 신규 감염을 예방하고 기감염을 감소시킴으로써 종전의 건유기 치료를 좀 더 효과적으로 증진시킬 수 있을 것으로 사료된다.

• 한국전기전자재료학회논문지
• /
• 제35권4호
• /
• pp.392-397
• /
• 2022

We present the structural and optical properties of Au@TiO₂ core-shell microsphere structure prepared by a hydrothermal synthesis method. As a way to improve the efficiency of organic solar cells, the Au@TiO₂ core-shell microsphere was synthesized to use the local surface plasmon resonance (LSPR) phenomenon. The synthesized results were confirmed to have the Au@TiO₂ core-shell structure using a high-resolution transmission electron microscopy. An absorption was observed to occur at 527 nm belonging to the visible light region using a visible light spectroscopy, which supports the LSPR phenomenon. We suggest that the Au@TiO₂ core-shell microsphere is highly likely to be applied to organic solar cells including dye-sensitized solar cells. In addition, we expect it to be widely used not only in the energy but also in the bio as well as in the environmental fields.

• 한국세라믹학회지
• /
• 제46권1호
• /
• pp.108-115
• /
• 2009

In this study, a novel-processing route for producing microcellular zirconia ceramics has been developed. The proposed strategy for making the microcellular zirconia ceramics involves hollow microsphere as a pore former which has extremely low density of $0.025\;g/cm^3$. Effects of hollow microsphere content and sintering temperature on microstructure, porosity, pore distribution, and compressive strength were investigated in the processing of microcellular zirconia ceramics. By controlling the content of hollow microsphere, it was possible to make the porous zirconia ceramics with porosities ranging from 45% to 75%. Typical compressive strength value of microcellular zirconia ceramics with ${\sim}65%$ porosity was over 50 MPa. By adjusting the mixing ratio of large and small zirconia powders, it was possible to control the pore structure from close to open pores.

• 한국생산제조학회지
• /
• 제24권4호
• /
• pp.368-373
• /
• 2015

Porous alumina ceramics with two different pore sizes were fabricated using hollow microspheres as the pore-forming agent. The relative density, total porosity, and microstructure of the obtained alumina ceramics were studied. It was found that the total porosity of sintered samples with different amounts of hollow microsphere content, from 2.0 to 4.0 wt%, was 69.3-75.6%. The interconnected and spherical cell morphology was obtained with 3.0 wt% hollow microsphere content. The resulting ceramics consist of a hierarchical structure with large-sized cells, and small-sized pores in the cell walls. Moreover, the compressive strength of the sintered samples varied from 8.3-11.5 MPa, corresponding to hollow microsphere contents of 2.0-4.0 wt%.

• International Journal of Industrial Entomology and Biomaterials
• /
• 제6권2호
• /
• pp.151-155
• /
• 2003

Using gel filtration chromatography, high molecular silk fibroin with high purity was obtained and silk flbroin microsphere particles (SFMP) could be simply made by spray dryer method. Also, some of the physicochemical properties of SFMP and morphology were investigated. The average molecular weight of pure silk fibroin protein dissolved in calcium chloride is about 61,500g/㏖ as measured by gel permeation chromatography. SFMP was spherical in shape, and particles, sized average of 2 ${\pm}$ 10 ${\mu}$, were observed by SEM and particle analyzer, respectively. Obtaining microspheres particles by spray dryer method accelerated the transition from the random coil to the $\beta$-sheet structure during spray dryer treatment. It was identified by the basic fourier transform infrared spectroscopy of SFMP. The swelling ratio of SFMP is majorly dependent on the pH of the solution, not on the occurred gelation. The characteristic structure, which might be applicable to immobilization of drugs is superior to other matrix materials for the use of biomaterials with skin affinity.

• 폴리머
• /
• 제39권1호
• /
• pp.144-150
• /
• 2015

젤란검은 천연재료로써 내열성, 내산성, 내효소성 등이 우수하여 용도가 광범위하나 기계적 강도가 약하다는 단점이 있다. 따라서 본 연구에서는 기계적 성질을 개선하고자 젤란검 스폰지에 PLGA 미립구를 혼합하였다. PLGA 미립구의 다양한 함량의 젤란검 스폰지는 기계적 강도를 알아보고자 압축강도를 측정하였고, MTT 분석, SEM, 생체활성조직학적 평가 및 RT-PCR을 통해 세포의 증식 및 ECM 분비 효과를 확인하였다. 그 결과, PLGA 미립구가 50% 함유된 젤란검 지지체에서 섬유륜세포의 꾸준한 증식과 세포외기질 분비가 우수한 것을 확인할 수 있었다. 이 연구를 통하여 PLGA 미립구가 함유된 젤란검이 디스크조직 재건을 위한 지지체로서 적합함을 알 수 있었으며, 젤란검의 다양한 응용가능성을 제시하였다.