• The Journal of the Korea Contents Association
• /
• v.15 no.3
• /
• pp.415-426
• /
• 2015

For a long time, evaluation of soundness and strength in concrete has been performed through ultrasonic velocity(UV), which is essential work in field assessment. Porosity in concrete is a major parameter indicating durability and strength, and UV passing concrete depends on porosity variation. In this paper, a modeling on UV through concrete is carried out considering porosity and the results are verified with those from test. Additionally UV in concrete under compression/tension loading condition is measured and UV modeling with loading condition is performed. Up to 50% of loading ratio, UV slightly increases and greatly drops at peak load in compression region, however it fluctuates in tensile region due to micro cracking in matrix. The proposed model shows a reasonable agreement with test results in control and compression region, and needs modification for tensile region considering micro cracks and local aggregate interlocking.

• Korean Journal of Materials Research
• /
• v.29 no.10
• /
• pp.609-616
• /
• 2019

Oxide coatings are formed on die-cast AZ91D Mg alloy through an environmentally friendly plasma electrolytic oxidation(PEO) process using an electrolytic solution of $NaAlO_2$, KOH, and KF. The effects of PEO condition with different duty cycles (10 %, 20 %, and 40 %) and frequencies(500 Hz, 1,000 Hz, and 2,000 Hz) on the crystal phase, composition, microstructure, and micro-hardness properties of the oxide coatings are investigated. The oxide coatings on die-cast AZ91D Mg alloy mainly consist of MgO and $MgAl_2O_4$ phases. The proportion of each crystalline phase depends on various electrical parameters, such as duty cycle and frequency. The surfaces of oxide coatings exhibit as craters of pancake-shaped oxide melting and solidification particles. The pore size and surface roughness of the oxide coating increase considerably with increase in the number of duty cycles, while the densification and thickness of oxide coatings increase progressively. Differences in the growth mechanism may be attributed to differences in oxide growth during PEO treatment that occur because the applied operating voltage is insufficient to reach breakdown voltage at higher frequencies. PEO treatment also results in the oxide coating having strong adhesion properties on the Mg alloy. The micro-hardness at the cross-section of oxide coatings is much higher not only compared to that on the surface but also compared to that of the conventional anodizing oxide coatings. The oxide coatings are found to improve the micro-hardness with the increase in the number of duty cycles, which suggests that various electrical parameters, such as duty cycle and frequency, are among the key factors controlling the structural and physical properties of the oxide coating.

• Journal of the Korean GEO-environmental Society
• /
• v.18 no.1
• /
• pp.31-35
• /
• 2017

The mechanical characteristics of frozen sand greatly depend on the frozen temperature and the fine contents according to the previous study by Chae et al. (2015). There are two hypotheses to explain this experimental results; one is the unfrozen water contents greatly affected by the fine contents and frozen temperature and the other is the sand particle spacing greatly affected by the pore-ice. To evaluate the latter hypothesis, the micro X-ray CT scan was performed. The micro X-ray CT scanning, one of the actively performed interdisciplinary research area, has a high resolution with micrometer unit allows to investigate internal structure of soils. In this study, X-ray CT technique was applied to investigate the effect of the frozen temperature and fine contents on the sand particle minimum and average spacing with the developed image processing techniques. Based on the spacing analysis, the frozen temperature and fine contents have little influence on the sand particle spacing in the frozen sand specimens.

• Microbiology and Biotechnology Letters
• /
• v.29 no.4
• /
• pp.240-247
• /
• 2001

The effect of microsparged aeration in mammalian cell bioreactor on the oxygen transfer rate and cell viability was studied. The microspargers with differ- ent micron-sized pores were used to supply oxygen to the medium. The oxygen transfer coefficients (k$_{L}$a) measured in the bioreactor were markedly increased, which is due to the increase of the contacting area between air bubbles and liquid medium when the pore size of microsparger decreases. When the impellers of two different types (square-pitch marine impeller and $45^{\circ}$ pitched flat blade impeller) were used for agitation, the k$_{L}$a values were slightly higher with the marine impeller than with the blade impeller. The detrimental effect of direct gas sparging with microsparger on mammalian cells was investigated in bubble columns with various air flow rates and different pore sized microspargers. The first-order cell death rate constant ($k_{d}$ /7) was shown to be directly proportional to the air flow rate and inversely proportional to the pore size. During the cultivation of hybridoma cells using microsparger with the pore size of $0.57\mu$m in the mammalian cell culture bioreactor, the continuous sparging caused the cell death and suppressed the cell growth. However, cells grew normally and cell viability was maintained above 90% in the logarithmic phase when the air was intermittently sparked in order to maintain the dissolved oxygen level above 20%.

• Applied Chemistry for Engineering
• /
• v.25 no.2
• /
• pp.181-187
• /
• 2014

In order to use the spherical atomizing reduction steel slag (ladle furnace slag, LFS) instead of the fine aggregate of polymer concrete composites, various specimens were prepared with various replacement ratios of atomizing reduction steel slag and the addition ratios of polymer binder. Physical properties of these specimens were investigated through the absorption test, the compressive strength test, the flexural strength test, the hot water resistance test, the pore analysis and the micro-structure using scanning electron microscope. Results showed that the compressive strength and flexural strength of specimens with 7.5% of polymer binders increased with the increase of replacement ratios of atomizing reduction steel slag, but those of the specimens with 8.0% or more of polymer binders showed a maximum strength at a certain replacement ratio due to the material segregation causing the increase of fluidity. By hot water resistance tests, the compressive strength, flexural strength, average pore diameter, and bulk density decreased but the total pore volume and pore diameter increased. It was concluded that the amount of polymer binders could be reduced by maximum 23.8%, because the workability of the polymer concrete was remarkably improved by using the atomizing reduction steel slag instead of fine aggregate. However, since the use of atomizing reduction steel slag decreased the resistance of the polymer concrete to hot water, further studies are required.

• Journal of the Korean Chemical Society
• /
• v.20 no.6
• /
• pp.469-478
• /
• 1976

Clinoptilolite zeolite samples were treated with hydrochloric acid, sulfuric acid and phosphoric acid of different strength and the adsorption characteristics and crystal structures of the original and acid-treated clinoptilolites were studied. By treating with hydrochloric acid, the adsorbed amount increased to 5-fold for nitrogen, to 3-fold for benzene, but for methanol no significant change was observed. As acid strength increased further, there were declines both in adsorption capacity and crystallinity. The results showed that the increase of adsorbed amount was caused by the rearrangement of the pore entrance and cation exchange. A method for determination of clinoptilolite content in natural mineral based on benzene adsorption on acid-treated sample is proposed. By this method, the original sample used in this study was found to contain approximately 40% of clinoptilolite. Using pulse technique in micro-catalytic reactor system, the catalytic activities of hydrochloric acid-treated clinoptilolites in cumene cracking and toluene disproportionation reactions were measured. For cumene cracking reaction, the maximum conversion was observed for the 0.5 N hydrochloric acid-treated sample. It is instructive to note that the maximum benzene adsorption was also observed for the sample treated with 0.5 N HCl. This suggest that the conversion rate was determined mainly by the rate of transport of reactants and the products through the pore structure. In the toluene disproportionation reaction, the same trend was observed. But the rate of deactivation was high for samples with strong acid sites. Since catalyst having higher activity was deactivated more easily, the conversion maximum was shifted to the sample treated with higher concentration of acid, -1N. The catalytic activity of $Ca^{2+} and La^{3+} ion exchanged samples for the toluene disproportion was much lower than that of acid-treated samples. Introduction of Ca^{2+} and La^{3+}$ into the pore structure apparently decreases the effective pore diameter of acid-treated clinoptilolite thus limiting the diffusion of reactants and products.

• Journal of Korean Society on Water Environment
• /
• v.24 no.4
• /
• pp.423-429
• /
• 2008

Microfiltration (MF) and ultrafiltration (UF) processes for removal of particulate materials (i.e., turbidity, microorganisms and viruses) have been used to produce drinking water with higher quality. As membrane filtration technique has become widely applied for drinking water treatment, the importance of membrane integrity test (MIT) has also been increasingly emphasized. The results of pressure decay test (PDT) were presented in the paper to monitor membrane integrity. In this paper the PDT was carried out with deliberately-defected membrane fibers to evaluate the sensitivity of PDT on membrane fiber damage. Variation of pressure decay rate and removal rate were investigated to evaluate the impact of defection (defection ratio) and pore size of membrane. The membrane integrity could be successfully monitored by the PDT. The pressure decay rate varied from $0.002{\sim}0.189kg_f/cm^2hr$ with the initial pressure ranged from 0.2 to $1.0kg_f/cm^2hr$. Higher initial pressure which provided with higher pressure decay rate was preferred to evaluate the defection of membrane fiber. As for the particle removal rate, the Log Removal Rate (LRV) of kaolin solution decreased significantly from 3.78 to 2.31 when one fiber out of 3,200 fibers was cut. The membranes with different pore size were tested to evaluate virus removal efficiency. The virus removal rate of the MF membrane ($0.1{\mu}m$) was about 30% although the poliovirus was smaller than the pore size of the MF membrane, indicating that the removal rate was much lower than Korea Water Works Association (KWWA) certificate LRV of 1.5.

• Applied Chemistry for Engineering
• /
• v.22 no.5
• /
• pp.501-507
• /
• 2011

To develop environmental-friendly insulating composite materials, natural cellulose and porous ceramic balls were used as core materials and activated Hwangtoh was used as a binder. Various specimens were prepared with different water/binder ratios and core material/binder ratios. The physical properties of these specimens were then investigated through compressive strengths, flexural strengths, absorption test, hot water resistance test, pore analysis, thermal conductivity, and observation of micro-structures using scanning electron microscope. Results showed that the maximum compressive strength varied appreciably with the water/binder ratios and core material/binder ratios, but the flexural strength increased with the core material/binder ratios regardless of water/binder ratios. The compressive strength and the flexural strength measured after the hot water resistance test decreased remarkably compared to those measured before test. The pore analysis measured after the hot water resistance test showed that total pore volume, porosity and average pore diameter decreased, while bulk density increased by the acceleration of hydration reaction of binder in the hot water. The thermal conductivity decreased gradually with an increase of core material/binder ratios. It can be evaluated that the composite insulation materials having good insulating properties and mechanical strengths can be used in the field.

• Carbon letters
• /
• v.24
• /
• pp.36-40
• /
• 2017

Polyacrylonitrile/pitch nanofibers were prepared by electrospinning as a precursor for a gas sensor material. Pitch nanofibers were properly fabricated by incorporating polyacrylonitrile as an electrospinning supplement component. Polyacrylonitrile/pitch nanofibers were activated with steam at various temperatures followed by subsequent carbonization to make carbon nanofibers with a highly conductive graphitic structure. Steam activation was effective in facilitating gas adsorption onto the carbon nanofibers due to the increased surface area. The carbon nanofibers activated at $800^{\circ}C$ had a larger surface area and a lower micro pore fraction resulting in a higher variation in electrical resistance for improved CO gas sensing properties.

• Journal of the Korean Society for Precision Engineering
• /
• v.31 no.4
• /
• pp.353-358
• /
• 2014

This paper reports a simple, yet effective 1-step surface modification method for stainless steel. Electrochemical etching in dilute Aqua Regia forms hierarchical micro and nanoscale structure on the surface. The surface becomes highly hydrophobic (${\sim}150^{\circ}$) as a result of the etching in terms of static contact angle (CA). However the liquid drops easily pinned on the surface because of high contact angle hysteresis (CAH), which is called a "petal effect": The petal effect occur because of gap between surface microstructures, despite of intrinsic hydrophobicity of the base material. The pore size and period of surface structure can be controlled by applied voltage during the etching. This method can be applied to wide variety of industrial demand for surface modification, while maintaining the advantageous anti-corrosion property of stainless steel.