• Journal of Welding and Joining
• /
• v.32 no.4
• /
• pp.26-33
• /
• 2014

The metallurgical and mechanical characteristics, toughness and corrosion resistance of dissimilar welds between super duplex stainless steel UNS S32750 and carbon steel ASTM A516Gr.70 have been evaluated. Three heat inputs of 21.12, 24.00, 26.88kJ/cm were employed to make joints of dissimilar metals with flux cored arc welding(FCAW). Based on microstructural examination, vermicular ferrite was formed in the first layer of weld at low heat input(21.12kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.61 while acicular ferrite was formed in last layer of weld at high heat input(26.88kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.72. Ferrite percentage in dissimilar welds was lowest in the first layer of weld regardless of heat inputs and it gradually increased in the second and third layers of weld. Heat affected zone showed higher hardness than the weld metal although reheated zone showed lower hardness than weld metal due to the formation of secondary austenite. Tensile strengths of dissimilar welds increased with heat input and there was 100MPa difference. The corrosion test by ferric chloride solution showed that carbon steel had poor corrosion resistance and pitting corrosion occurred in the first layer(root pass) of weld due to the presence of reheated zone where secondary austenite was formed. The salt spray test of carbon steel showed that the surface only corroded but the amount of weight loss was extremely low.

• Journal of Environmental Science International
• /
• v.18 no.7
• /
• pp.735-746
• /
• 2009

Hydrochloric acid salt of a new $N_2O_3$ pentadentate ligand, N,N'-Bis(2-Hydroxybenzyl)-1,3-diamino-2-propanol(H-BHDP 2HCl) was synthesized. Br-BHDP 2HCl, CI-BHDP 2HCl, $CH_3-BHDP$ 2HCl and $CH_3O$-BHDP 2HCl having Br, Cl, $CH_3$ and $CH_3O$ substituents at 5-position of the phenol group of H-BHDP 2HCl were also synthesized. The potentiometry study in aqueous solution revealed that the proton dissociations of the synthesized ligands occurred in four steps and their order of the calculated overall proton dissociation constants($log{\beta}_p$) was Br-BHDP < Cl-BHDP < H-BHDP < $CH_3O-BHDP$ < $CH_3-BHDP$. The order showed a similar trend to that of Hammett substituent constants(${\delta}_p$). The order of the stability constants($logK_{ML}$) was Co(II) < Ni(II) < Cu(II) < Zn(II) < Cd(II) < Pb(II). The order in their stability constants ($logK_{ML}$) of each transition metal complex agreed with that of the overall proton dissociation constants ($log{\beta}_p$).

• Membrane Journal
• /
• v.31 no.5
• /
• pp.315-326
• /
• 2021

Lithium ion battery (LIB) demands increase every year globally to reduce the burden on fossil fuels. LIBs are used in electric vehicles, stationary storage systems and various other applications. Lithium is available in seawater, salt lakes, and brines and its extraction using environmentally friendly and inexpensive methods will greatly relieve the pressure in lithium mining. Membrane separation processes, mainly nanofiltration (NF), is an effective way for the separation of lithium metal from solutions. Electrodialysis and electrolysis are other separation processes used for lithium separation. The process of reverse osmosis (RO) is already a well-established method for the desalination of seawater; therefore, modifying RO membranes to target lithium metals is an excellent alternative method in which the only bottleneck is the interfering presence of other metal elements in the solution. Selectively removing lithium by finding or developing suitable NF membranes can be challenging, but it is nonetheless an exciting area of research. This review discusses in detail about lithium recovery via nanofiltration, electrodialysis, electrolysis and other processes.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.1 no.2
• /
• pp.136-143
• /
• 2013

In the sewage structures and wastewater facilities, concrete is exposed to hydrogen sulfide ($H_2S$) which acts as an acid material in a solution, and a strongly acidic sulfate ion ($SO{_4}^{-2}$) is generated by a sulfuric bacteria. Hence, a degradation of concrete with biochemical corrosion would be accelerated. Finally, durability of concrete and concrete structures may be greatly reduced. In this study, in order to remove the hydrogen sulfide which is used by the sulfuric bacteria organic-biologically, the antibiotic metal and metallic salt powders were mixed to concrete, and a suppressing performance of the sulfate ion was assessed. For the sulfuric acid bacteria, a comparative evaluation of antimicrobial performance on neutralized concrete specimens were carried out, also by a rapid chloride penetration test, chloride penetration depths and diffusion coefficients were measured for antibiotic concrete in accordance with the amount of metal and metallic salt-based antibacterial agents. Eventually, by an observation of the biochemical state of the surface of concrete specimens exposed outdoors, the performance and applicability of antibiotic concrete were confirmed.

• Resources Recycling
• /
• v.9 no.2
• /
• pp.11-17
• /
• 2000

Consumption of nickel is continuously increasing and the wastes of secondary battery, ferrite and catalyst containing Ni are also generated periodically. Among those wastes, the aim of this research is the recovery of nickel from used Ni-Cd recharge battery. Battery consisted of Ni 24 wt%, Fe 30 wt% and Cd 18.5 wt%. Metal was recovered by solvent extraction after leaching. Cadmium was leached completely in 1N-HCl and Ni was recovered above 70%. 30 vol% MSP-8 separated Cd and Ni completely from acidic leaching solution. In addition $NH_4NO_3$ as one of ammonium salt type leachants showed an excellent leaching selectivity to Ni and Cd. Ni in leached solution was recovered completely by LIX-extractant and more than 70% of Cd in raffinate was by D2EHPA.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.2
• /
• pp.61-67
• /
• 2022

A metal salt solution was prepared from valuable metals (Ni, Co, Mn) recovered from a scrap of waste lithium secondary batteries, and an NCM811 precursor was synthesized from the solution. The effect on precursor formation according to reaction time was confirmed by SEM, PSA, and ICP analysis. Based on the analysis results, the electrochemical properties of the synthesized NCM811 precursor and the commercial NCM811 precursor were investigated. The Galvano charge-discharge cycle, rate performance, and Cycle performance were compared, and as a result, there was no significant difference from commercial precursors.

• Journal of the Korean Chemical Society
• /
• v.47 no.4
• /
• pp.315-324
• /
• 2003

In this study, a new method is presented to produce stable hydrophobic metal alloy nanocluster in chloroform solution including surfactant NaAOT(sodium bis(2-ethylhexyl)-sulfosuccinate) via the chemical reduction of metal salt $(HAuCl_4,\AgNO_3,\Cu(NO_3)_2)$ by sodium borohydride. For the alloy nanocluster, several samples were prepared by changing the molar ratio of Au/Cu, Au/Ag alloy nanocluster, 3:1, 1:1, 1:3. The alloy nanoclusters were characterized by UV-Visible spectrophotometer, TEM(Transmission Electron Microscope), and XPS(X-ray Photoelectron Spectrometer). With the change of the mole ratio of the alloy component, the wavelengths of the surface plasmon absorption shift linearly from 520 nm of the pure Au nanocluster to 570 nm of the pure Cu nanocluster for Au/Cu alloy nanoclusters and from 405 nm to 520 nm for Au/Ag alloy nanoclusters. The chemical shifts of the Au4f, Ag3d, Cu2p XPS peaks were observed with changing the molar ratio of the alloy element. The alloy nanoclusters in chloroform solution were made uniformly in size and colloidally stable for long periods of time. These results indicate that the method here is a very effective method for synthesizing hydrophobic alloy nanoclusters with uniform or nearly uniform particle size distribution.

• Analytical Science and Technology
• /
• v.23 no.1
• /
• pp.45-53
• /
• 2010

For the determination of chlorine in uranium compound, analytical methods by using a steam distillation and a pyrohydrolysis have been developed. The steam distillation apparatus was composed of steam generator, distilling flask and condenser etc. The samples were prepared with an aliquot of LiCl standard solution and a simulated spent nuclear fuel. A sample aliquot was mixed with a solution containing 0.2 M ferrous ammonium sulfate-0.5 M sulfamic acid 3 mL, phosphoric acid 6 mL and sulfuric acid 15 mL. The chloride was then distilled by steam at the temperature of $140^{\circ}C$ until a volume of $90{\pm}5\;mL$ is collected. The pyrohydrolysis equipment was composed of air introduction system, water supply, quartz reaction tube, combustion tube furnace, combustion boat and absorption vessel. The chloride was separated from powdered sample which is added with $U_3O_8$ accelerator, by pyrohydrolysis at the temperature of $950^{\circ}C$ for 1 hour in a quartz tube with a stream of air of 1 mL/min supplied from the water reservoir at $80^{\circ}C$. The chlorides collected in each absorption solution by two methods was diluted to 100 mL and measured with ion chromatography to determine the recovery yield. For the ion chromatographic determination of chlorine in molten salt retained in a metal ingot, the chlorine was separated by means of pyrohydrolysis after air and dry oxidation, and grinding for the sample.

• Analytical Science and Technology
• /
• v.12 no.5
• /
• pp.397-402
• /
• 1999

The open-chain hexadentate $N_6$, ligand containing two pyridyl groups, 1,15-bis(2-pyridyl)-2,6,10,14-tetraazapentadecane (bpyped) has been synthesized as its tetrahydroehloride salt and characterized by EA, IR, NMR, and Mass. Its proton dissociation constants($logK{^n}_H$) and stability constants ($log\;K_{ML}$) for Co(II), Ni(II), Cu(II) and Zn(II) ions were determined at $25^{\circ}C$ and ionic strength 0.10 M($KNO_3$) in aqueous solution by potentiometry and compared with those or analogous $N_6$ ligands contain one or two propylenic spacers, which make six-membered chelate rings, between the aliphatic nitrogen atoms.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2005.11a
• /
• pp.192-193
• /
• 2005

Magnesium thin films were prepared on cold-rolled steel substrates by RF(Radio Frequency) magnetron sputtering technique.$^{1)}$ The crystal orientation and monitoring of the deposited films were investigated by using XRD(X-ray Diffraction) and EIS(Electrochemical Impedance Spectroscopy), respectively. The corrosion rates of Mg thin films deposited with different argon gas pressure and substrate bias voltage were monitored by AC impedance method under a cyclic wet-dry condition, which was conducted by exposure to alternate conditions of 1h immersion in 3%NaCl solution and 5h drying at 60% RH and 25$^{\circ}C$. The result of corrosion rate of Mg thin films deposited at various Ar gas pressures and substrate bias voltage under wet-dry cyclic exposure in chloride-containing solutions was showed the following conclusions. At the region I during the onset of the wet cycle, corrosion rate showed relatively low value. The increase in the Corrosion rate of region II is due to the increase in the chloride concentration. Corrosion rate of region III during the onset of the cycle zero and salt crystals remain on the metal surface.$^{2)}$