초록
Magnesium thin films were prepared on cold-rolled steel substrates by RF(Radio Frequency) magnetron sputtering technique.$^{1)}$ The crystal orientation and monitoring of the deposited films were investigated by using XRD(X-ray Diffraction) and EIS(Electrochemical Impedance Spectroscopy), respectively. The corrosion rates of Mg thin films deposited with different argon gas pressure and substrate bias voltage were monitored by AC impedance method under a cyclic wet-dry condition, which was conducted by exposure to alternate conditions of 1h immersion in 3%NaCl solution and 5h drying at 60% RH and 25$^{\circ}C$. The result of corrosion rate of Mg thin films deposited at various Ar gas pressures and substrate bias voltage under wet-dry cyclic exposure in chloride-containing solutions was showed the following conclusions. At the region I during the onset of the wet cycle, corrosion rate showed relatively low value. The increase in the Corrosion rate of region II is due to the increase in the chloride concentration. Corrosion rate of region III during the onset of the cycle zero and salt crystals remain on the metal surface.$^{2)}$