• 한국초전도학회:학술대회논문집
• /
• v.10
• /
• pp.111-120
• /
• 2000

Recently, metal oxide films such as MgO or ZrO$_2$ have been studied as buffer layers to fabricate the superconductor with preferred orientation and as diffusion barriers to prevent the reaction between superconductor and metal substrate. In this research, we focused fabrication and characterization of MgO and ZrO$_2$ films on textured metal substrates. We fabricated MgO and ZrO$_2$ films on the Ni metal sheets by sol-gel dipping method. The microstrcures of the films were investigated by SEM and AES analyses. The films were coated with different cycles and dryed at 400$^{\circ}$C and 500$^{\circ}$C . The final films were heat-treated at 700$^{\circ}$C, 800$^{\circ}$C, and 1000$^{\circ}$C, in air atmosphere. We investigated the alignment of MgO and ZrO$_2$ films on Ni metal sheets by XRD and pole figure. The grain growth of metal oxide films was improved by the increase of the drying temperature and annealing temperature. The grain growth was increased with the annealing temperature. The alignment of metal oxide films depended on the thickness.

• Journal of Technologic Dentistry
• /
• v.23 no.2
• /
• pp.161-170
• /
• 2002

The Purpose of this study was to investigate the chemically improvement of metal-ceramics bond strength in the course of recasting Ni-Cr metal composite system with 10wt.%, 20wt.% and 30wt.% aluminum respectively. We have tested the bond strength, micro-structure, chemical composition of each metal composites and metal- ceramic bond interfaces by 3-point bending strength tester, SEM and EDS. We have made the conclusions through this study as follow: 1. The most suitable amount of aluminum to the Ni-Cr metal composite recasting is 20wt. % for improving metal-ceramics bond strength with debonding strength value of 49.54 kgf/mm2. 2. The aluminum must be changed to small spread alumina like phases and second aluminum-metal composites phases in the morphology of Ni-Cr metal composite system by adding during it's casting. These second phases have inclined functional oxide phases mixed with metal elements and they must take roll to improvement of metal-ceramics bond strength. 3. In the case of 30wt.% aluminum appended to Ni-Cr metal composite system, an excess of second inclined functional oxide phases produce cracks and spalling of them apart from it's base material. It must be a important factor of reduction of metal-ceramics bond strength.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.30A no.6
• /
• pp.1-7
• /
• 1993

After the 1%S-Al metal is deposited, a thin oxide is formed thereon. Then, a single charged Argon(Ar$^{+}$) is ion implanted into the oxide layer, thereby causing the metal grain in the upper surface of the metal layer to become amorphous. Consequently, the grain size will be reduced and the rough surface of the metal layer flattened. However, the remainder of the metal layer beneath the upper surface thereof will still exhibit large grain size and low resistance, because the Argon ion is only implanted to characterized by a dual-sized grain structure which served to reduce interlayer stress, thereby decreasing the rate of stress migration, and to lower the resistivity of the metal line, thereby enhancing the electromigration characteristic thereof. Experiments have shown that the metal line exhibits a metal migration rate which is approximately 700% less than the control group and a standard deviation which is approximately 200% less than these group.p.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.7
• /
• pp.569-572
• /
• 2003

In this study, we evaluated the dilute HF cleaning to reduce residual defects made by metal CMP process. The purpose of this test is to observe the existence of barrier metal damage during DHF cleaning on condition that it should not affect metal thin film reliability, so we will get rid of slurry residual particles as a main defect of the metal CMP process for the better yield. In-line defect data showed us that slurry residual particles were removed by DHF application. The HF rinse significantly reduced metal contamination levels and surface roughness. The best effect by additional oxide loss was discovered when Dilute HF condition is 10".

• Journal of Technologic Dentistry
• /
• v.9 no.1
• /
• pp.39-49
• /
• 1987

This study done to evaluate some surface treatment methods in metal coping which can increase the bond strength between porcelain and metal. Therefore this experiment was performed according to the Mc Lean's Theory of bond strength between porcelain and strength between porcelain and metal. In the experiment the author measured respective thermal expansion coefficents in three types of metal(Tallasium, Vera Bond and Rexillium) and Vita Porcelain to get the differences in the coefficents between porcelain and metals. And using insteron testing machine, the author also performed Planar interface shear bond tests on the 45 specimens(15 specimens in oxide surface, rough surface and fine surface treatment methods respectively) to measure bond strength between metal and porcelain. The results Were as follows, 1. The differences in thermal expansion coefficients between three types of metal and Vita procelain: Talladium - $1.2\;10^{-6/0}\;C$, Vera Bond - $1.6\;10^{-6/0}\;C$, Rexillium - $1.9\;10^{-6/0}\;C$. 2. The bond strength in oxide surface on the Shear bond test was the lowest among the treatment methods. 3. There was no significant differences in treatment methods of rough surface of fine surface. 4. In the oxide surface treatment method, there were significant differences(P<0.05)between Vera bond and Rexillium, and between Talladium and Rexillium. 5. In the fine surface treatment, there was a significant difference(P<0.05)between Talladium and Rexillium.

• Journal of the Korean Solar Energy Society
• /
• v.31 no.1
• /
• pp.107-114
• /
• 2011

Two-step thermochemical cycle using ferrite-oxide($Fe_3O_4$) device was investigated. The $H_2O$(g) was converted into $H_2$ in the first experiment which was performed using a dish type solar thermal system. However the experiment was lasted only for 2 cycles because the metal oxide device was sintered and broken down. Another problem was that the reaction was taken place mainly on a side of the metal oxide device. The $m-ZrO_2$, which was widely known as a material preventing sintering, was applied on the metal oxide device. The ferrite loading rate and the thickness of the metal oxide device were increased from 10.67wt% to 20wt% and from 10mm to 15mm, respectively. The chemical reactor having two inlets was designed in order to supply the reactants uniformly to the metal oxide device. The second-experiment was lasted for 5 cycles, which was for 6 hours. The total amount of the $H_2$ production was 861.30mL.

• Journal of Hydrogen and New Energy
• /
• v.21 no.2
• /
• pp.81-88
• /
• 2010

Hydrogen energy applications have recognized clean materials and high energy carrier. Accordingly, Hydrogen energy applies for fuel cell by Mg and Mg-based materials. Mg and Mg-based materials are lightweight and low cost materials with high hydrogen storage capacity. However, commercial applications of the Mg hydride are currently hinder by its high absorption/desorption temperature, and very slow reaction kinetics. Therefore one of the most methods to improve kinetics focused on addition transition metal oxide. Addition to transition metal oxide in $MgH_x$ powder produce $MgH_x$-metal oxide composition by mechanical alloy and it analyze XRD, EDS, TG/DSC, SEM, and PCT. This report considers kinetics by transition metal oxide rate and Hydrogen pressure. In this research, we can see behavior of hydriding/dehydriding profiles by addition catalyst (transition metal oxide). Results of PCI make a excellent showing $MgH_x$-5wt.% Sc2O3 at 623K, $MgH_x$-10wt.% $Sc_2O_3$ at 573K.

• Journal of Information Display
• /
• v.13 no.2
• /
• pp.61-66
• /
• 2012

The double-layered Ti/Si barrier metal is demonstrated for the source/drain Cu interconnections in oxide semiconductor thin-film transistors (TFTs). The transmission electromicroscopy and ion mass spectroscopy analyses revealed that the double-layered barrier structure suppresses the interfacial reaction and the interdiffusion at the interface after thermal annealing at $350^{\circ}C$. The underlying Si layer was found to be very useful for the etch stopper during wet etching for the Cu/Ti layers. The oxide TFTs with a double-layered Ti/Si barrier metal possess excellent TFT characteristics. It is concluded that the present barrier structure facilitates the back-channel-etch-type TFT process in the mass production line, where the four- or five-mask process is used.

• Bulletin of the Korean Chemical Society
• /
• v.17 no.7
• /
• pp.621-625
• /
• 1996

A variety of metal oxides were coated by sol-gel process from their metal alkoxides on the ribbons of Co-based and Fe-based amorphous alloys, and the effects of surface oxide coating on the magnetic properties of the alloy are investigated. The core loss is found to be reduced significantly by the oxide coating, the loss reduction becoming more prominent at higher frequencies. The shape of the hystersis loop is also dependent upon the kind of the coated metal oxide. The coatings of MgO, SiO2, MgO·SiO2 and MgO·Al2O3 induce tensile stress into the Fe-based ribbon whereas those of BaO, Al2O3, CaO·Al2O3, SrO·Al2O3 and BaO·Al2O3 induce compressive stress. These results may be explained by the modification of domain structures via magnetoelastic interactions with the shrinkage stress induced by the sol-gel coating.

• KEPCO Journal on Electric Power and Energy
• /
• v.5 no.2
• /
• pp.121-125
• /
• 2019

A YSZ electrolyte based ceramic supported Solid Oxide Cell (SOC) and a metal interconnect supported SOC was investigated under both fuel cell and co-electrolysis (steam and $CO_2$) mode at $800^{\circ}C$. The single cell performance was analyzed by impedance spectra and product gas composition with gas chromatography(GC). The long-term performance in the co-electrolysis mode under a current density of $800mA/cm^2$ was obtained using steam and carbon dioxide ($CO_2$) mixed gas condition.