• Corrosion Science and Technology
• /
• 제7권5호
• /
• pp.243-251
• /
• 2008

Magnesium alloys become popular research topic in last decade due to its light weight and relatively high strength-to-weight ratio in the energy aspiration age. Almost all structure materials are supposed to suspend stress. Magnesium is quite sensitive to corrosive environment, and also sensitive to environmental assisted cracking. However, so far we have the limited knowledge about the environmental sensitive cracking of magnesium alloys. The corrosion fatigue (CF) test was conducted. Many factors' effects, like grain size, texture, heat treatment, loading frequency, stress ratio, strain rate, chemical composition of environment, pH value, relative humidity were investigated. The results showed that all these factors had obvious influence on the crack initiation and propagation. Especially the dependence of CF life on pH value and frequency is quite different to the other traditional structural metallic materials. In order to interpret the results, the electrochemistry tests by polarization dynamic curve and electrochemical impedance spectroscopy were conducted with and without stress. The corrosion of magnesium alloys was also studied by in-situ observation in environmental scanning electron microscopy (ESEM). The corrosion rate changed with the wetting time during the initial corrosion process. The pre-charging of hydrogen caused crack initiated at $\beta$ phase, and with the increase of wetting time the crack propagated, implying that hydrogen produced by corrosion reaction participated in the process.

• 한국광물학회지
• /
• 제26권4호
• /
• pp.219-228
• /
• 2013

방사성 폐기물을 지하에 장기 보관하는 금속 용기에 관한 생지화학적 부식 특성을 알아보기 위해 주철과 구리로 된 금속재료를 환원조건 하에서 디설프리칸스 황산염환원미생물과 3개월간 반응시켰다. 금속재료의 화학적/광물학적 변화를 알아보기 위해 주기적으로 용존 금속이온들의 농도를 측정하였으며, 실험이 종료된 이후 금속 시편 및 표면 이차생성물들을 전자현미경을 이용하여 분석하였다. 디설프리칸스가 없는 조건에서는 금속재료의 부식이 매우 미약하였으나, 미생물이 있는 경우에는 부식이 상대적으로 컸다. 관찰된 생지화학적 부식 산물은 주로 맥키나와이트와 황화구리 같은 검은색의 금속황화물이었으며, 표면에서 쉽게 분리되거나 콜로이드화되어 부유하였다. 특히, 구리 시편의 경우 용액 상에 용존 철이 존재할 때 세균에 의한 구리 부식의 가속화가 관찰되었는데, 이는 구리 표면에 다른 종의 황화철이 성장하면서 구리 간의 결속력을 약화시켰기 때문인 것으로 보인다.

• Smart Structures and Systems
• /
• 제26권4호
• /
• pp.507-520
• /
• 2020

In order to achieve effective corrosion monitoring of buried metal pipelines, a Novel nondestructive Testing (NDT) methodology using ultra-long (250 mm) Polymer Optical Fiber (POF) sensors coated with the Fe-C alloy film is proposed in this study. The theoretical principle is investigated to clarify the monitoring mechanism of this method, and the detailed fabrication process of this novel POF sensor is presented. To validate the feasibility of this novel POF sensor, exploratory research of the proposed method was performed using simulated corrosion tests. For simplicity, the geometric shape of the buried pipeline was simulated as a round hot-rolled plain steel bar. A thin nickel layer was applied as the inner plated layer, and the Fe-C alloy film was coated using an electroless plating technique to precisely control the thickness of the alloy film. In the end, systematic sensitivity analysis on corrosion severity was further performed with experimental studies on three sensors fabricated with different metal layer thicknesses of 25 ㎛, 30 ㎛ and 35 ㎛. The experimental observation demonstrated that the sensor coated with 25 ㎛ Fe-C alloy film presented the highest effectiveness with the corrosion sensitivity of 0.3364 mV/g at Δm = 9.32 × 10^-4 g in Stage I and 0.0121 mV/g in Stage III. The research findings indicate that the detection accuracy of the novel POF sensor proposed in this study is satisfying. Moreover, the simple fabrication of the high-sensitivity sensor makes it cost-effective and suitable for the on-site corrosion monitoring of buried metal pipelines.

• Corrosion Science and Technology
• /
• 제21권5호
• /
• pp.381-389
• /
• 2022

Cyclic Voltammetry and weight loss measurements were used to investigate corrosion prevention of tin in a 0.5M citric acid solution containing Anthocyanins extracted from grapes at various concentrations and temperatures. Results showed that the investigated chemicals, Anthocyanins extracted from grapes, performed well as tin corrosion inhibitors in 0.5M citric acid. Increasing the concentration of Anthocyanins increased their corrosion inhibition efficiencies. When the temperature dropped, their inhibition efficiencies, increased indicating that higher temperature tin dissolution predominated the adsorption of Anthocyanins at the surface of tin metal. When inhibitor concentrations were increased, their inhibition efficiencies were also increased. These results revealed that corrosion of tin metal was inhibited by a mixed type of adsorption on the metal surface. The adsorption isotherm of Langmuir governed the adsorption of Anthocyanins. Thermodynamic parameters such as the enthalpy of adsorption, the entropy of adsorption, and Gibbs free energy and kinetic parameters such as activation energy, enthalpy of activation, and entropy of activation were computed and discussed in this study.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2005년도 춘계 학술기술논문발표대회 논문집
• /
• pp.113-117
• /
• 2005

The ceramic metal resin paints for waterproof and anti corrosion is not long history in development of materials even many actual result. So far, no standard have been given to construction and maintenance method, Quality and property, it is real state that cannot afford to proper quality control in job site or production. This study has been test for the ceramic metal resin paints for water and anti corrosion, as the result, it have proper performance of job site and mechanical performance of compare to other existing. In particular, tensile strength indicates more high about $14.1N/mm^2$ than epoxy resin paints, and in elongation per unit length is more high It is shows having better adhesive strength than epoxy resin paint for crack on the concrete structure. Moreover, The ceramic metal paint for water and corrosion proofing have to have main performance is watertightness and resistance for external impact, chloride ion permeation, drinkable water elution.

• Journal of Advanced Marine Engineering and Technology
• /
• 제20권2호
• /
• pp.92-92
• /
• 1996

Recently, with the rapid development in the oceanic systems such as the oceanic structures and vessel, there occurs much interest in the impingement erosion-corrosion. In this paper, Cu-metal was tested by using of erosion apparatus with water-jet type and was investigated under the behaviour of impingement erosion-corrosion according to various environmental conditions, and the properties of Cu-metal were evaluated through the measurement by weight loss, weight loss rate, protective efficiency. The results were compared with those obtained using Cu-metal applied to cathodic protection and Cu-alloys added to Zn or Al-metal. As a basis of those results, the best protective efficiencies could be taken as using cathodic protection method and Cu-alloy with Al & Zn material addings, and will be suggested as the fundamental data of the anti-impingement erosion-corrosion on Cu-metal of impeller material for oceanic centrifugal pump.

• Journal of Advanced Marine Engineering and Technology
• /
• 제20권2호
• /
• pp.24-31
• /
• 1996

Recently, with the rapid development in the oceanic systems such as the oceanic structures and vessel, there occurs much interest in the impingement erosion-corrosion. In this paper, Cu-metal was tested by using of erosion apparatus with water-jet type and was investigated under the behaviour of impingement erosion-corrosion according to various environmental conditions, and the properties of Cu-metal were evaluated through the measurement by weight loss, weight loss rate, protective efficiency. The results were compared with those obtained using Cu-metal applied to cathodic protection and Cu-alloys added to Zn or Al-metal. As a basis of those results, the best protective efficiencies could be taken as using cathodic protection method and Cu-alloy with Al & Zn material addings, and will be suggested as the fundamental data of the anti-impingement erosion-corrosion on Cu-metal of impeller material for oceanic centrifugal pump.

• 열처리공학회지
• /
• 제26권6호
• /
• pp.293-299
• /
• 2013

A specimen of weld metal was prepared by GTA welding with weld wire of super duplex stainless steel. Aging treatment was conducted for the sample at the temperature range of 700 to $900^{\circ}C$ for 5 to 300 minutes. The effect of volume fraction of ${\sigma}$-phase to intergranular corrosion of weld metal has been investigated and the results were derived as follows. The volume fraction of ${\sigma}$ phase tends to increase with an increase of aging temperature and time and intergranular corrosion of weld metal was increased by an increase of ${\sigma}$ phase. Degree of sensitization representing intergranular corrosion was found to tend to increase with an increase of aging time at 700 to $800^{\circ}C$, while it decreased by an increase of aging time at $900^{\circ}C$.

• 동력기계공학회지
• /
• 제19권6호
• /
• pp.75-81
• /
• 2015

A deposited metal specimen of ER2594 which is a super duplex steel welding wire used to investigate the effect of sigma(${\sigma}$) phase on electrochemical corrosion characteristics was prepared by gas tungsten arc welding. Aging treatment was conducted for the specimen at the temperature range of $700^{\circ}C$ to $900^{\circ}C$ for 5 to 300 minutes after annealing at $1050^{\circ}C$. Corrosion current density has decreased a little with an increase of aging time over 60 minutes at $700^{\circ}C$ to $900^{\circ}C$ and the uniform corrosion of deposited metal had more influence on the precipitation of ferrite than the precipitation of sigma phase. Therefore, the precipitation of sigma phase did not have much effect on the uniform corrosion. Pitting potential representing pitting corrosion has shown decreasing tendency as the precipitation of sigma phase increased. The degree of sensitization representing intergranular corrosion has shown increasing tendency as the precipitation of sigma phase increased at $700^{\circ}C$ to $800^{\circ}C$, while it has decreased at $900^{\circ}C$ for 60 to 300 minutes.

• Corrosion Science and Technology
• /
• 제14권6호
• /
• pp.273-279
• /
• 2015

Effects of passive film quality by chemical passivation and solution flow on the corrosion behavior of 304 stainless steel in HCl solution were investigated using a coloration indicator, and by corrosion weight loss, electrochemical polarization and element dissolution measurements. A high redness degree suggests a low passive-film integrity for 304 stainless steel following air exposure, while the minimum redness degree for the samples after chemical passivation suggests a high passive-film integrity. In the static condition, samples subjected to air exposure exhibited a high corrosion rate and preferential dissolution of Fe. Chemical passivation inhibited the corrosion rate due to the intrinsically high structural integrity of the passive film and high concentrations of Cr-rich oxides and hydroxide. Solution flow accelerated corrosion by promoting both the anodic dissolution reaction and the cathodic reaction. Solution flow also altered the preferential dissolution to fast uniform dissolution of metal elements.