이진홍;김기현;박병옥
- Journal of the Korean Crystal Growth and Crystal Technology
- /
- v.12 no.5
- /
- pp.247-252
- /
- 2002
$(Pb_{1-x}La_x)TiO_3$ (x = 0.1) thin films were prepared on ITO-coated glass substrates by metal organic chemical vapor deposition using ultrasonic spraying. Effects of the post-annealing and the seeding layer on crystallization, microstructures and electrical properties of thin films were investigated. Dielectric constants of films increased due to the modification of crystallization and the changing of a surface morphology by applying the post-annealing. In addition, as the application of PT seed- ing layer offered nucleation sites to PLT thin films, electrical properties of films were enhanced by the increase of crys-tallinity and grain size. The dielectric constant of the films post-heated for 60 min and with a seeding layer was 213 at 1 kHz.
PDF KSCI

김기현;곽병오;이승엽;이진홍;박병옥
- Journal of the Korean Crystal Growth and Crystal Technology
- /
- v.13 no.6
- /
- pp.272-278
- /
- 2003
$Bi_4Ti_3O_{12}$ (BIT) and $(Bi_{3.25}La_{0.75})(Ti_{2.97}V_{0.03})O_{12}$ (BLTV) thin films were deposited on ITO/glass substrates by metal organic chemical vapor deposition (MOCVD) using ultrasonic spraying. After deposition of the films in oxygen atmosphere for 30 min, the films were heated by rapid thermal annealing (RTA) method, especially direct insertion, at various temperatures. The films were investigated on phase formation temperature, microstructure and electrical properties. From x-ray diffraction (XRD) patterns, the perovskite phase formation temperature of BLTV thin film was about $600^{\circ}C$ which was lower than that of BIT, $650^{\circ}C$. The leakage current of the BLTV thin film was measured to be $1.52\times 10^{-9}$A/$cm^2$ at an applied voltage of 1 V. The remanent polarization (Pr) and coercive field (Ec) values of the BLTV film deposited at $650^{\circ}C$ were $5.6\muC/cm^2$ and 96.5 kV/cm, respectively.
PDF KSCI

김기현;이진홍;박병옥
- Journal of the Korean Crystal Growth and Crystal Technology
- /
- v.12 no.4
- /
- pp.184-189
- /
- 2002
The electrical and optical properties of $(Pb_{0.91}La_{0.09})(Zr_{0.65}Ti_{0.35})O_3$(PLZT) thin films by MOCVD using ultrasonic spraying were investigated. To compensate the Pb loss by evaporation, 5 and 10 wt% of excess Pb was added to 0.2 M precursor. After deposition of films on ITO-coated glasses in oxygen atmosphere for 30 min, films were heated by in-situ RTA (rapid thermal annealing) method. When the films were heat treated at $600^{\circ}C$, perovskite single phase was obtained. The optical property of the film with 10 wt% excess Pb was excellent showing about 84 % of transmittance near 520 nm. The dielectric constant of the film was about 308 and the leakage current of the film was lower than the Pb excess 0, 5 wt% PLZT thin films.
PDF KSCI