• Journal of the Mineralogical Society of Korea
• /
• v.26 no.1
• /
• pp.35-44
• /
• 2013

Synthetic carbon-coated olivine-like structured lithium iron phosphate ($Li^+Fe^{2+}(PO_4)^{3-}/C$) powder composites were compressed up to 35.0 GPa in the symmetrical diamond anvil cell at room temperature. Bulk modulus of $LiFePO_4/C$ was determined to be $130.1{\pm}10.3$ GPa. New peak appears at the d-spacing of 3.386 ${\AA}$ above 18 GPa, and another new one at 2.854 ${\AA}$ around 35 GPa. The crystallographic symmetry of the sample (i.e. orthorhombic) is apparently retained up to 35 GPa as no clear evidence for the phase transition into spinel structure has been observed. The pressure-induced volume change in the M1 site ($Li^+O_6$) is more significant than those in M2($Fe^{2+}O_6$) and $PO_4$ tetrahedral sites.

• Journal of the Korean Chemical Society
• /
• v.50 no.3
• /
• pp.243-246
• /
• 2006

The LiCoO2 thin films were prepared on the Pt/Ti/SiO2/Si substrate by spin coating using citrate sol. The citrate sol was spin-coated on substrate and dried at 380oC for 15 min. to evaporate the solvents and remove the organic materials. The as-deposited films were annealed at 750oC for 10 min. in air for crystallization. The X-ray diffraction patterns for the film have been indexed hexagonal system with space group R3m. The active area of LiCoO2 films for electrochemical test was about 11cm2. A Li foil and 1M LiClO4 in propylene carbonate(PC) and ethylene carbonate(EC) (1:1)were used as an anode and an electrolyte, respectively. The galvanostatic charge-discharge test was carried out at constant current density ranging from 5 A/cm2 in the voltage window between 4.2 and 3.0 V. The first discharge capacity of the film is 0.35Ah/cm2-m. The cycling behavior of the LiCoO2 film is also reported.

• Resources Recycling
• /
• v.10 no.6
• /
• pp.9-14
• /
• 2001

A sulfuric acid leaching of $LiCoO_2$as cathodic active materials of lithium ion secondary batteries was investigated in terms of reaction variables. In the absence of a reducing agent, the extraction of cobalt was less than 40% in 2 M sulfuric acid at $75^{\circ}C$ instead of that of lithium could be almost 100% in the same conditions. To improve the Co extraction, hydrogen peroxide was used as a reducing agent in the range 2~20 vol%. When over 10vo1% hydrogen peroxide was added, the extractions of both metals were improved to about 95%. It seems to be due to the reduction of Co(III) to Co(II) that can be readily dissolved. The extractions of Co and Li were increased with increasing $H_2$$SO_4$concentration and temperature, and amount of hydrogen peroxide and with decreasing of pulp density. The optimum leaching conditions were determined at $2 M H_2$$SO_4$concentration, $75^{\circ}C$ operating temperature, 100 g/L. initial pulp density, 20 vol% $H_2$$O_2$addition and 30 min.

• Journal of the Korean Electrochemical Society
• /
• v.1 no.1
• /
• pp.14-17
• /
• 1998

Mesophase pitch-based carbon fibers(MPCF) have been investigated as an anode active material for lithium ion secondary battery. Graphitized MPCF gives high discharge capacity and good Ah efficiency. MPCF/Li cell shows an initial discharge capacity of 300 mAh/g and Ah efficiency above $90\%$ at a current density of 25 mA/g at $0\~1$ V. Cylindrical lithium ion secondary battery was fabricated using mixed carbon anode and $LiCoO_2$, cathode. In order to improve the cyclability of lithiun ion secondary battery, other carbons were added to the MPCF up to $10wt\%$. The cycle performance of lithium ion secondary battery using mixed carbons was superior to those using graphitized MPCF.

• Journal of the Korean Ceramic Society
• /
• v.53 no.3
• /
• pp.306-311
• /
• 2016

Li-air batteries have received much attention due to their superior theoretical energy density. However, their sluggish kinetics on the cathode side is considered the main barrier to high performance. The rational design of electrode catalysts with high activity is therefore an important challenge. To solve this issue, we performed density functional theory (DFT) calculations to analyze the adsorption behavior of the $LiO_2$ molecule, which is considered to be a key intermediate in both the Li-oxygen reduction reaction (ORR) and the evolution reaction (OER). Specifically, to use the activity descriptor approach, the $LiO_2$ adsorption energy, which has previously been demonstrated to be a reliable descriptor of the cathode reaction in Li-air batteries, was calculated on $LaB_{1-x}B^{\prime}_xO_3$(001) (B, B' = Mn, Fe, Co, and Ni, x = 0.0, 0.5). Our fast screening results showed that $LaMnO_3$, $LaMn_{0.5}Fe_{0.5}O_3$, or $LaFeO_3$ would be good candidate catalysts. We believe that our results will provide a way to more efficiently develop new cathode materials for Li-air batteries.

• Journal of the Korean Electrochemical Society
• /
• v.13 no.4
• /
• pp.246-250
• /
• 2010

In this study, nano-crystallized $Al_2O_3$ was coated on the surface of $LiFePO_4$ powders via a novel dry coating method. The influence of coated $LiFePO_4$ upon electrochemical behavior was discussed. Surface morphology characterization was achieved by transmission electron microscopy (TEM), clearly showing nano-crystallized $Al_2O_3$ on $LiFePO_4$ surfaces. Furthermore, it revealed that the $Al_2O_3$-coated $LiFePO_4$ cathode exhibited a distinct surface morphology. It was also found that the $Al_2O_3$ coating reduces capacity fading especially at high charge/discharge rates. Results from the cyclic voltammogram measurements (2.5-4.2 V) showed a significant decrease in both interfacial resistance and cathode polarization. This behavior implies that $Al_2O_3$ can prevent structural change of $LiFePO_4$ or reaction with the electrolyte on cycling. In addition, the $Al_2O_3$ coated $LiFePO_4$ compound showed highly improved area-specific impedance (ASI), an important measure of battery performance. From the correlation between these characteristics of bare and coated $LiFePO_4$, the role of $Al_2O_3$ coating played on the electrochemical performance of $LiFePO_4$ was probed.

• Journal of Astronomy and Space Sciences
• /
• v.27 no.1
• /
• pp.55-68
• /
• 2010

It has been generally known that Datong-li (a Chinese calendar in the Ming dynasty) was first introduced into Korea in the nineteenth reign of King Gongmin (1370) of the Goryeo dynasty and lasted to the third reign of King Hyeojong (1652) of the Joseon dynasty. This understanding is based on the records of Goryeo-sa (History of the Goryeo dynasty) and of Seoungwan-ji (Official book of Seoungwan)/Jeungbomunheon-bigo (Explanatory Notes of Library Document). To verify the period of the use of Datong-li in Korea, we develop a Fortran code to calculate the calendar day by Datong-li and also investigate historical literatures and extant almanacs. As a result, we find the possibility that Datong-li had been in use since 1389 at least. However, we cannot confirm whether Datong-li was first enforced in 1370 or not. On the other hand, we confirm that Datong-li was used until 1653 and reintroduced during the period from 1667 to 1669. Also, we find that previous studies had some errors in the sexagenary cycle of the real first day of a month. We think that this study will contribute to understanding the calendrical history of the Joseon dynasty.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.8
• /
• pp.702-707
• /
• 2005

Spinel $LiMn_2O_4$ has become appealing because manganese is inexpensive and environmentally benign. In general, cathodes for lithium ion batteries include carbon as a conductive agent that provides electron transfer between the active material and the current collector. In this work, we selected Acetylene Black and Super P Black as conductive agents, and then carried out their comparative investigation for the performances of the $Li/LiMn_2O_4$ cells using different conductive agents with different particle size. In addition, their electrochemical impedance characteristic of $Li/Mn_2O_4$ cells using different conductive agents is effectively identified through a.c. impedance technique. As a consequence, $Li/LiMn_2O_4$ cells with Super P Black show better electrochemical performances ascribed to the significant contribution of feasible ionic conduction due to larger particle size than those with Acetylene Black.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.4
• /
• pp.168-171
• /
• 2005

The electrochemical properties of $LiFePO_4$ as a cathode for Li-ion batteries were improved by incorporating conductive carbon into the $LiFePO_4$. X-ray diffraction analysis and SEM observations revealed that the carbon-coated $LiFePO_4$ consisted of fine single crystalline particles, which were smaller than the bare $LiFePO_4$. The electrochemical performance of the carbon-coated $LiFePO_4$ was tested under various conditions. The carbon-coated $LiFePO_4$ showed much better performance in terms of the discharge capacity and cycling stability than the bare $LiFePO_4$. The improved electrochemical performances were found to be attributed to the reduced particle size and enhanced electrical conductivity of the $LiFePO_4$ by the carbon.

• Journal of the Korean Ceramic Society
• /
• v.44 no.1 s.296
• /
• pp.58-64
• /
• 2007

In this study, we investigated $Li_2ZrO_3$ membrane as a candidate material for high-temperature $CO_2$ separation and evaluated mechanical property. $Li_2ZrO_3$ powder was synthesized by solid state reaction of $Li_2CO_3\;and\;ZrO_2$. Then we fabricated $Li_2ZrO_3$ tape using tape casting method. Dense $Li_2ZrO_3$ membrane prepared by sintering at $1600^{\circ}C$ for 2 h after pressing $Li_2ZrO_3$ tape using lamination machine. Mechanical properties before and after $CO_2$ absorption of fabricated $Li_2ZrO_3$ membrane such as Hertzian indentation, Victors hardness and 3-point bending testing were evaluated.