Charge-discharge behaviour of lithium ion secondary battery using graphitized mesophase pitch-based carbon fiber anodes

흑연화 MPCF 부극을 이용한 Li ion 2차전지의 충방전 특성

Mesophase pitch-based carbon fibers(MPCF) have been investigated as an anode active material for lithium ion secondary battery. Graphitized MPCF gives high discharge capacity and good Ah efficiency. MPCF/Li cell shows an initial discharge capacity of 300 mAh/g and Ah efficiency above $90\%$ at a current density of 25 mA/g at $0\~1$ V. Cylindrical lithium ion secondary battery was fabricated using mixed carbon anode and $LiCoO_2$, cathode. In order to improve the cyclability of lithiun ion secondary battery, other carbons were added to the MPCF up to $10wt\%$. The cycle performance of lithium ion secondary battery using mixed carbons was superior to those using graphitized MPCF.

MPCF는 Li ion 2차전지용 부극 활물질로 연구되고 있다. 흑연화 MPCF는 높은 방전 용량과 우수한 충방전 효율을 가진다. $0\~1$ V전위영역에서 25 mA/g의 정전류로 충방전할 때의 MPCF/Li전지의 초기 방전 용량은 300 mAh/g이며, 충방전 효율은 $90\%$ 이상을 나타낸다. $LiCoO_2$을 정극 활물질로, 혼합 탄소재료를 부극 활물질로 사용하여 원통형 Li ion 2차전지를 제작하였다. Li ion 2차전지의 수명 특성을 향상하기 위하여, 흑연화 MPCF에 이종 탄소 재료를 $10 wt\%$ 혼합하였다. 혼합 탄소재료를 사용한 Li ion 2차전지의 수명 성능은 흑연화 MPCF만을 사용한 전지보다 우수하였다.