• Bulletin of the Korean Chemical Society
• /
• v.33 no.12
• /
• pp.4122-4126
• /
• 2012

Cellulose-graft-poly (L-lactide) (cellulose-g-PLLA) was successfully prepared via ring-opening polymerization (ROP) by using 4-dimethylaminopyridine (DMAP) as an organic catalyst in an ionic liquid 1-allyl-3-methylimidazolium chloride (AmimCl). The structure and morphology of the polymer was characterized by nuclear magnetic resonance (NMR) and transmission electron microscope (TEM). From wide-angle X-ray powder diffraction (WAXD) and degradation test (by acid, alkaline, PBS and enzyme solution), changes in the crystalline structure as a result of degradation was also investigated. The results indicated that materials which have low degree of crystallinity showing higher degradability, however, in acid liquor, enzyme solution, alkaline liquor and PBS system, the degradation rate of the polymer decreased by the above sequence. Moreover, with the further increase of graft degree of this material, its degradation degree decreased.

• Macromolecular Research
• /
• v.17 no.8
• /
• pp.575-579
• /
• 2009

Copolymerization of L-lactide and s-caprolactone initiated by tin (II) octoate (Sn(Oct)$_2$) was carried out in supercritical chlorodifluoromethane (R22) with varying reaction conditions (time and temperature) and amounts of monomer and catalyst, under a pressure of 250 bar. The optimum conditions were a reaction time of 10 h and a temperature of 130 $^{\circ}C$, which is similar to the temperature used in bulk copolymerization system. The conversion increased from 56% to 76% by increasing the reaction time from 1 to 10 h. The molecular weight also increased to 75,900 g.mol$^{-1}$ over the same period, while the increased monomer concentration resulted in a high molecular weight of 86,400 g.mol$^{-1}$ and a monomer conversion of 84%. Raising the reaction temperature from 90 to 130 $^{\circ}C$ increased the monomer conversion as well as the poly-L-lactide-co-${\varepsilon}$-caprolactone (PLCL) molecular weight. The variation on the stannous octoate catalyst suggested that less catalyst would decrease the caprolactone content of the polymer.

• Polymer(Korea)
• /
• v.25 no.6
• /
• pp.884-892
• /
• 2001

Biodegradable wafers were prepared with poly (L-lactide-co-glycolide) (50 : 50 mole ratio of lactide to glycolide, molecular weight:5000 g/mole) by direct compression method for the sustained release of nifedipine to investigate the possibility of the treatment of hypertension. PLGA wafers were prepared by altering initial drug/polymer loading ratio, wafer thickness, and hydroxypropyl methylcellulose (HPMC) content. These wafers showed new zero-order release patterns for 11 days, and various biphasic release patterns could be obtained by altering the composition of wafers such as addition of matrix binder as HPMC to the PLGA wafer to reduce release rate of initial phase. The onset of polymer mass loss only occured after 4 days and about 40% of mass loss was observed after 11 days nifedipine release. This system had advantages in terms of simplicity in design and obviousness of drug release rate and may be useful as an implantable dosage form.

• Polymer(Korea)
• /
• v.36 no.2
• /
• pp.124-130
• /
• 2012

The uniform nanofibers of poly(L-lactide-$co$-${\varepsilon}$-caprolactone) (PLCL) with different contents of marine collagen (MC) were successfully prepared by electrospinning method. The effects of the major parameters in electrospinning process such as tip to target distance (TTD), voltage, nozzle size and flow rate on the average diameter of the electrospun nanofiber were investigated in generating composite nanofiber. The diameter and morphology of the nanofibers were confirmed by a scanning electron microscopy (SEM). Also, we measured a water contact angle to determine the surface wettability of the nanofibers. The average diameter of the nanofibers decreased as the value of TTD, MC contents, and voltages increased in comparison with that of pristine PLCL nanofiber. In contrast, the diameter of the nanofibers increased as the flow rate and inner diameter of nozzle increased in comparison with that of pristine PLCL. In addition, the hydrophilicity of the nanofiber and attachment of MG-63 cells on the sheets increased as incorporated collagen contents increased. Therefore, the marine collagen would be a potential material to enhance cellular interactivity of synthetic materials by mimicking the natural tissue.

• Proceedings of the Polymer Society of Korea Conference
• /
• 2006.10a
• /
• pp.210-211
• /
• 2006

A series of L-LA polymerizations initiated by $Sn(Oct)_{2}\;([LA]_{0}/[Sn]_{0}=200)$ were carried out in scR22 at $130^{\circ}C$ and 300 bar, where $[LA]_{0}$ is the initial L-lactide concentration and $[Sn]_{0}$ is the initial $Sn(Oct)_{2}$ concentration. The reaction time dependences of monomer conversion and PLLA MW improved. The monomer conversion and PLLA MW increased with increasing reaction time. The effect of temperature on monomer conversion and PLLA MW was investigated in a series of polymerizations conducted at temperatures ranging from 90 to $150^{\circ}C$ and at a constant pressure of 200 bar. In all of these experiments, the ratio of monomer to R22 concentration was held constant at 12.4 wt.-%. Increasing the reaction temperature from 90 to $130^{\circ}C$ resulted in increased monomer conversion from 11.5 to 72.2 %.

• Macromolecular Research
• /
• v.10 no.5
• /
• pp.246-252
• /
• 2002

In order to the development of the delivery device of long-acting local anesthetics for postoperative analgesia and control of chronic pain of cancer patient, fentnyl-loaded poly (L-lactide-co-glycolido) (PLGA, molecular weight, 5,000 g/mole; 50 : 50 mole ratio by lactide to glycolide) microspheres (FMS) were studied. FMS were prepared by an emulsion solvent-evaporation method. The influence of several preparation parameters such as initial drug loading, PLGA concentration, emulsifier concentration, oil phase volume, and fabrication temperature has been investigated on the fentanyl release profiles. Generally, the drug showed the biphasic release patterns, with an initial diffusion followed by a lag period before the onset of the degradation phase, but there was no lag time in our system. Fentanyl was slowly released from FMS over 10 days in vitro with a quasi-zero order property. The release rate increased with increasing drug loading as well as decreasing polymer concentration with relatively small initial burst effect. From the results, FMS may be a good formulation to deliver the anesthetic for the treatment of chronic pain.

• Polymer(Korea)
• /
• v.28 no.4
• /
• pp.328-334
• /
• 2004

A series of methoxy poly(ethylene glycol) (MPEG)-poly(L-lactide-co-glycolide) (PLGA) diblock copolymers were synthesized by ring-opening polymerization of L-lactide and glycolide with carbitol (134 g/mole) or different molecular weights of MPEG (550, 2000, and 5000 g/mole) as an initiator in presence of Sn(Oct)$_2$. The properties of diblock copolymers were characterized by using $^1$H-NMR, GPC, and XRD. After uniform mixing of block copolymers and 1% albumin bovine-fluorescein isothiocyanate(FITC-BSA) with a freeze miller, the wafers loaded FITC-BSA were fabricated by using a mold with a dimensions of 3 mm${\times}$1mm diameter. The release profiles of FITC-BSA and the pH changes of wafer were examined using pH 7.4 PBS for 30 days at 37$^{\circ}C$. The release profiles of albumin showed fast initial burst as the molecular weights of MPEG increased. As a result of this study, the release behavior of BSA was controlled with introducing MPEG in the block copolymers.

• Polymer(Korea)
• /
• v.24 no.6
• /
• pp.869-876
• /
• 2000

In order to improve the cell-compatability of poly(L-lactide-co-glycolide) (75 : 25 by mole ratio of lactide to glycolide, PLGA) surfaces, the physicochemical treatments have been demonstrated. Chemical treatments were 70% perchloric acid. 50% sulfuric acid and 0.5 N sodium hydroxide solution and physical methods were corona and plasma treatment. The water contact angle of surface treated PLGA decreased from 73$^{\circ}$ to 50~60$^{\circ}$, i.e., increased hydrophilicity, due to the introduction of oxygen-containing functional group onto PLGA backbone by the measurement of an electron spectroscopy for chemical analysis. It could be observed that the adhesion and growth of fibroblast cell on physicochemically treated PLGA surfaces, especially perchloric acid treated PLGA surface, were more active than on the controt. In conclusion, it seems that surface wettability as hydrophilicity of PLGA plays an important role in cell adhesion, spreading and growth.

• Macromolecular Research
• /
• v.10 no.2
• /
• pp.54-59
• /
• 2002

ABA triblock copolymers of L-lactide and trimethylene carbonate with several different compositions were prepared by sequential ring-opening polymerization in the presence of diethylene glycol. Also chain-extension reactions of the resulting copolymers were carried out using hexamethylene diisocyanate to produce relatively high molecular weight polymers, which could be cast into elastomeric tough films. The polymers with certain L-lactide contents were partially crystalline, exhibiting two-phase morphology. The polymer films showed reversible elastic behavior under tensile tension, providing a novel thermoplastic elastomer possessing desirable properties such as biodegradability and good mechanical properties.

• Macromolecular Research
• /
• v.14 no.1
• /
• pp.59-65
• /
• 2006

We report a new approach to fabricate electrospun polymer nonwoven mats with porous surface morphology by varying the collector temperature during electrospinning. Polymers such as poly(L-lactide) (PLLA), polystyrene (PS), and poly(vinyl acetate) (PVAc) were dissolved in volatile solvents, namely methylene chloride (Me) and tetrahydrofuran (THF), and subjected to electrospinning. The temperature of the collector in the electrospinning device was varied by a heating system. The resulting nonwoven mats were characterized by using scanning electron microscopy (SEM), field emission SEM (FESEM), and atomic force microscopy (AFM). We observed that the surface morphology, porous structure, and the properties such as pore size, depth, shape, and distribution of the nonwoven mats were greatly influenced by the collector temperature.