• 대한기계학회논문집A
• /
• 제26권3호
• /
• pp.570-575
• /
• 2002

It is well-known that the bond strength between CFRP(Carbon Fiber Reinforced Plastic) and aluminum is significantly affected by the surface treatment of the CFRP and the aluminum. This study investigates the surface treatment of CFRP to improve the T-peel strength of CFRP/aluminum composites. The surface of %CFRP([0^0]_{14})$ was treated by the ion assisted reaction method under oxygen environment. T-peel strength tests were performed based on the procedure of ASTM D1876-95. The T-peel strength of surface-treated CFRP/aluminum composites was compared with that of untreated CFRP/aluminum composites. The results showed that the T-peel strength of surface-treated CFRP/aluminum composites was about 5.5 times higher than that of untreated CFRP/aluminum composites. SEM examination showed that the improvement of T-peel strength was attributed to the uniform spread and fracture of epoxy adhesive.

• 한국진공학회지
• /
• 제6권3호
• /
• pp.200-205
• /
• 1997

고분자 Polyethylene(PE) film 표면을 1keV의 산소 이온 빔만을 사용하여, 또는 산 소 분위기에서 1keV의 아르곤 이온 빔으로 조사하는 이온보조반응(ion assisted reaction)법 을 이용하여 개질을 하였다. 개질된 polyethylene 표면의 친수성(wettability)과 표면 에너지 를 측정하기 위해 접촉각 측정기(contact angle micrometer)를 사용하였으며, 개질된 표면의 화학적 변화를 측정하기 위해 x-ray photoelectron spectroscopy(XPS)를 이용하였다. 표면 개질을 위한 이온 조사량은 $1\times 10^{14}-1\times\;ions/\textrm{cm}^2$, 산소 가스는 0~4sccm(ml/min.)까지 변화 시켰다. 산소 이온 빔만으로 조사 후 polyethylene 표면과 물과의 접촉각은 $95^{\circ}$에서 최대 $62^{\circ}$까지 변화하였으며, 산소를 4sccm(ml/min.) 주입하면서 아르곤 이온 빔으로 조사 하면 물과의 접촉각이 최대 $28^{\circ}$까지 감소하였으며, 이때 이온 조사량은 $1\times 10^{17}-1\times\;ions/\textrm{cm}^2$이 었다. 또한 polyethylene을 산소 이온 빔으로만 표면 개질시 표면 에너지는 작은 증가를 보 였으며, 산소 분위기에서 아르곤 이온 빔으로 표면 개질 하였을 때에는 표면 에너지가 2배 에 가까운 증가를 하였다. 이와 같은 표면의 친수성과 표면 에너지의 증가는 이온보조반응 법에 의해 polyethylene의 표면을 산소 분위기에서 아르곤 이온 빔으로 조사한 시료의 XPS 의 spectra결과로 보아 PE의 표면에 C-O 또는 C=O와 관련된 결합의 증가로 인한 친수성 작용기가 poluethlene표면에 형성되었기 때문이라고 사료된다.

• 마이크로전자및패키징학회지
• /
• 제8권1호
• /
• pp.53-59
• /
• 2001

Surfaces of PTFE and PVDF were modified by ion-assisted reaction (IAR) in which 1 keV $Ar^{+}$ ions were irradiated on the surface of the polymer with varying ion dose in an oxygen gas environment, and Cu, Pt, Al and Ag thin films were deposited on the modified polymers. Wettability of the modified polymers was largely improved by the formation of hydrophilic groups due to chemical reaction between polymer surface and the oxygen gas during IAR. The change in wettability in the modified polymers was also related to the change in surface morphology and roughness. Adhesion between metal films and polymers modified by IAR was significantly improved, so that no detachment was possible in the $Scotch^{TM}$ tape test. The increase of adhesion strength between the metal film and the modified PVDF was mainly attributed to the formation of hydrophilic groups, which interacted with the metal film. In the case of the modified PTFE, the enhanced adhesion to metal film could be explained by the change in surface morphology together with the formation of hydrophilic groups. The electrical properties of the metal films on the modified polymers were also investigated.

• 한국정밀공학회지
• /
• 제18권8호
• /
• pp.122-128
• /
• 2001

The objective of the present study was to investigate the characteristics of the friction and wear according to the amount of ion-irradiation for the carbon fiber reinforced plastic(CFRP). Unidirectional carbon fiber reinforced composites were fabricated with epoxy resin as a matrix and carbon fiber as a reinforcement, and its surface was modified by the ion-assisted reaction. When the amount of ion-irradiation was $1{\times}10^{16}$ ions/$cm^2$, the friction coefficients of composites were about 0.1 and the wear mode was stable, whereas, the friction coefficient of non-treatment composites were about 0.16 and the wear mode was very unstable. But if the amount of ion-irradiation was $5{\times}10^{16}$ ions/$cm^2$, the friction coefficients were higher rather than that of $1{\times}10^{16}$ ions/$cm^2$. Consequently, the amount of ion-irradiation was not in proportion to the friction coefficients, and it was conformed that the optimal conditions would exist between broth of them.

• Tribology and Lubricants
• /
• 제18권1호
• /
• pp.61-67
• /
• 2002

The objective of the present study was to investigate the characteristics of the friction and wear according to the amount of ion-irradiation for the carbon fiber reinforced plastic (CFRP). Unidirectional carbon fiber reinforced composites were fabricated with epoxy resin as a matrix and carbon fiber as a reinforcement, and its surface was modified by the ion-assisted reaction. When the amount of ion-irradiation was $1{\times}10^{16}$ $ions/cm^{2}$. the friction coefficients of composites were about 0.1 and the wear mode was stable. whereas, the friction coefficient of non-treatment composites were about 0.16 and the wear mode was very unstable. But if the amount of ion-irradiation was $5{\times}10^{16}$ $ions/cm^{2}$, the friction coefficients were higher rather than that of $1{\times}10^{16}$ $ions/cm^{2}$ Consequently. the amount of ion-irradiation was not in proportion to the friction coefficients, and it was conformed that the optimal conditions would exist between both of them.

• 폴리머
• /
• 제26권6호
• /
• pp.718-727
• /
• 2002

본 연구에서는 최종 복합재료의 기계적 계면특성을 향상시키기 위하여 산소 분위기 하에서 반응성 기체를 사용하는 이온 보조 반응법에 의해 탄소섬유 표면에 Ar+ 이온 빔을 조사하였다. 그리고, 단일 섬유 pull-out 시험을 실시하여 가해진 이온 에너지 세기에 대한 수지 내의 섬유의 뽑힘 정도를 측정한 후 Greszczuk의 .기하학적 모델에 기초하여 섬유/매트릭스 간의 계면특성을 알아보고자 하였다. 그 결과, 탄소섬유를 이온 빔으로 처리함에 따라 섬유와 매트릭스 간의 부착력 증가의 원인이 되는 섬유축 방향으로의 표면 etching 및 반응성 그룹이 형성되어 계면 전단강도가 향상되었으며 0.8 keV 이온 빔 세기에서 최대값을 나타내었다.

• 한국생물공학회:학술대회논문집
• /
• 한국생물공학회 2003년도 생물공학의 동향(XIII)
• /
• pp.782-782
• /
• 2003

• 한국마이크로전자및패키징학회:학술대회논문집
• /
• 한국마이크로전자및패키징학회 2001년도 The IMAPS-Korea Workshop 2001 Emerging Technology on packaging
• /
• pp.142-145
• /
• 2001

• 한국방사성폐기물학회:학술대회논문집
• /
• 한국방사성폐기물학회 2004년도 학술논문집
• /
• pp.32-42
• /
• 2004

Recently, plasma surface-cleaning or surface-etching techniques have been focused in respect of the decontamination of spent or used nuclear parts and equipment. In this study the removal rate of metallic cobalt surface is experimentally investigated via its surface etching rate with a $CF_4-o_2$mixed gas plasma. Experimental results reveal that a mixed etchant gas with about 80% $CF_4$-20% $O_2$ (molar) gives the highest reaction rate and the rate reaches 0.06 ${\mu}m$/min at $380^{\circ}C$ and ion-assisted etching dramatically enhances the surface reaction rate. With a negative 300 V DC bias voltage applied to the substrate, the surface reaction initiation temperature lowers and the rate increases about 20 times at $350^{\circ}C$ and up to 0.43 ${\mu}m$/min at $380^{\circ}C$, respectively. Surface morphology analysis confirms the etching rate measurements. Auger spectrum analysis clearly shows the adsorption of fluorine atoms on the reacted surface. From the current experimental findings and the results discussed in previous studies, mechanistic understanding of the surface reaction, fluorination and/or fluoro-carbonylation reaction, is provided.

• Korean Chemical Engineering Research
• /
• 제51권4호
• /
• pp.460-464
• /
• 2013

본 연구에서는 $LiMn_2O_4$ 제조에서 Mn 원료로 사용되는 CMD를 seed 첨가법을 사용하여 제조하고자 하였으며, Seed의 열처리 온도가 CMD 합성에 미치는 영향을 고찰하고, 그로부터 제조되는 $LiMn_2O_4$의 전기화학적 특성을 평가하고자 하였다. 제조한 시료의 물성평가는 X-선 회절 분석법(XRD), 주사전자현미경(SEM)을 통하여 실시하였다. 그 결과, $MnCO_3$를 $300^{\circ}C$ 이상의 온도에서 열처리하여 seed로 사용할 경우 ${\gamma}-MnO_2$ 상의 CMD가 얻어졌으며, 그 CMD를 LMO 제조에 사용할 경우 전기화학적 특성이 비교적 우수한 LMO가 얻어졌다.