The objective of the present study was to investigate the characteristics of the friction and wear according to the amount of ion-irradiation for the carbon fiber reinforced plastic (CFRP). Unidirectional carbon fiber reinforced composites were fabricated with epoxy resin as a matrix and carbon fiber as a reinforcement, and its surface was modified by the ion-assisted reaction. When the amount of ion-irradiation was $1{\times}10^{16}$ $ions/cm^{2}$. the friction coefficients of composites were about 0.1 and the wear mode was stable. whereas, the friction coefficient of non-treatment composites were about 0.16 and the wear mode was very unstable. But if the amount of ion-irradiation was $5{\times}10^{16}$ $ions/cm^{2}$, the friction coefficients were higher rather than that of $1{\times}10^{16}$ $ions/cm^{2}$ Consequently. the amount of ion-irradiation was not in proportion to the friction coefficients, and it was conformed that the optimal conditions would exist between both of them.