• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2003년도 하계학술대회 논문집 C
• /
• pp.1574-1576
• /
• 2003

Carbon nanotubes (CNTs) were grown on the TiN-coated silicon substrate with different thickness of Ni and Co catalysts layer at $600^{\circ}C$ using inductively coupled plasma-chemical vapor deposition (ICP-CVD). The Ni and Co catalysts were formed using the RF magnetron sputtering system with various deposition times. It was found that the growth of CNTs was strongly influenced by the surface morphology of Ni and Co catalysts. With increasing deposition time, the thickness of catalysts increased and the grain boundary size of catalysts increased. The surface morphology of catalysts and CNTs were elucidated by SEM. The Raman spectrum further confirmed the graphitic structure of the CNTs. The turn-on field of CNTs grown on Ni and Co catalysts was about 2.7V/pm and 1.9V/pm respectively. Field emission current density of CNTs grown on Ni and Co catalysts was measured as $11.67mA/cm^2$ at $5.5V/{\mu}m$ and $1.5mA/cm^2$ at $5.5V/{\mu}m$ respectively.

• 한국세라믹학회지
• /
• 제39권2호
• /
• pp.171-177
• /
• 2002

본 연구에서는 DC bias가 인가된 유도결합형 플라즈마 열선 화학기상증착법을 이용하여 580$^{\circ}C$의 저온에서 탄소나노튜브를 수직 배향시켰다. 성장된 탄소나노튜브의 기판으로는 강화유리 위에 촉매층으로 Ni과 전도층으로 Cr을 300/200 ${\AA}$(Ni/Cr) 증착된 것으로 R-F magnetron sputtering을 이용하여 제작하였다. 성장 시 RF power와 DC bias power는 150W와 80W이며 텅스텐 필라멘트 power는 7∼8 A로 인가하였다. 성장된 탄소나노튜브는 속이 비어 있는 다중벽으로 이루어 졌으며 성장된 탄소나노튜브 끝단에는 금속 촉매로 보이는 Ni이 존재하는 것을 알 수 있었다. 탄소나노튜브는 흑연화도가 우수하며 그에 따라 탄소나노튜브의 전계 방출 특성도 우수하게 평가되었다. 성장된 탄소나노튜브의 구동 전압은 약 3 V/${\mu}m$이었다.

• 반도체디스플레이기술학회지
• /
• 제9권1호
• /
• pp.41-47
• /
• 2010

The effects of thermal treatment on CNTs, which were coated with a-$CN_x$ thin film, were investigated and related to variations of chemical bonding and morphologies of CNTs and also properties of field emission induced by thermal treatment. CNTs were directly grown on nano-sized conical-type tungsten tips via the inductively coupled plasma-chemical vapor deposition (ICP-CVD) system, and a-$CN_x$ films were coated on the CNTs using an RF magnetron sputtering system. Thermal treatment on a-$CN_x$ coated CNT-emitters was performed using a rapid thermal annealing (RTA) system by varying temperature ($300-700^{\circ}C$). Morphologies and microstructures of a-$CN_x$/CNTs hetero-structured emitters were analyzed by FESEM and HRTEM. Chemical composition and atomic bonding structures were analyzed by EDX, Raman spectroscopy, and XPS. The field emission properties of the a-$CN_x$/CNTs hetero-structured emitters were measured using a high vacuum (below $10^{-7}$ Torr) field-emission measurement system. For characterization of emission stability, the fluctuation and degradation of the emission current were monitored in terms of operation time. The results were compared with a-$CN_x$ coated CNT-emitters that were not thermally heated as well as with the conventional non-coated CNT-emitters.

• 전기학회논문지
• /
• 제59권4호
• /
• pp.743-748
• /
• 2010

Boron nitride (BN) and carbon nitride (CN) films, which have relatively low work functions and commonly exhibit negative electron affinity behaviors, were coated on carbon nanotubes (CNTs) by magnetron sputtering. The CNTs were directly grown on metal-tip (tungsten, approximately 500nm in diameter at the summit part) substrates by inductively coupled plasma-chemical vapor deposition (ICP-CVD). The variations in the morphology and microstructure of CNTs due to coating of the BN and CN films were analyzed by field-emission scanning electron microscopy (FE-SEM). The energy dispersive x-ray (EDX) spectroscopy and Raman spectroscopy were used to identify the existence of the coated layers (CN and BN) on CNTs. The electron-emission properties of the BN-coated and CN-coated CNT-emitters were characterized using a high-vacuum field emission measurement system, in terms of their maximum emission currents ($I_{max}$) at 1kV and turn-on voltage ($V_{on}$) for approaching $1{\mu}A$. The results showed that the $I_{max}$ current was significantly increased and the $V_{on}$ voltage were remarkably reduced by the coating of CN or BN films. The measured values of $I_{max}-V_{on}$ were as follows; $176{\mu}A$-500V for the 5nm CN-coated emitter and $289{\mu}A$-540V for the 2nm BN-coated emitter, respectively, while the $I_{max}-V_{on}$ of the as-grown (i.e., uncoated) emitter was $134{\mu}A$-620V. In addition, the CNT emitters coated with thin CN or BN films also showed much better long-term (up to 25h) stability behaviors in electron emission, as compared with the conventional CNT emitter.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 1999년도 제17회 학술발표회 논문개요집
• /
• pp.79-79
• /
• 1999

The varous techniques for fabrication of si or metal tip as a field emission electron source have been reported due to great potential capabilities of flat panel display application. In this report, 240nm thermal oxide was initially grown at the p-type (100) (5-25 ohm-cm) 4 inch Si wafer and 310nm Si3N4 thin layer was deposited using low pressure chemical vapor deposition technique(LPCVD). The 2 micron size dot array was photolithographically patterned. The KOH anisotropic etching of the silicon substrate was utilized to provide V-groove formation. After formation of the V-groove shape, dry oxidation at 100$0^{\circ}C$ for 600 minutes was followed. In this procedure, the orientation dependent oxide growth was performed to have a etch-mask for dry etching. The thicknesses of the grown oxides on the (111) surface and on the (100) etch stop surface were found to be ~330nm and ~90nm, respectively. The reactive ion etching by 100 watt, 9 mtorr, 40 sccm Cl2 feed gas using inductively coupled plasma (ICP) system was performed in order to etch ~90nm SiO layer on the bottom of the etch stop and to etch the Si layer on the bottom. The 300 watt RF power was connected to the substrate in order to supply ~(-500)eV. The negative ion energy would enhance the directional anisotropic etching of the Cl2 RIE. After etching, remaining thickness of the oxide on the (111) was measured to be ~130nm by scanning electron microscopy.

• 한국전기전자재료학회논문지
• /
• 제29권7호
• /
• pp.394-399
• /
• 2016

The silicon dioxide ($SiO_2$) was deposited using various gas as oxygen and nitrous oxide ($N_2O$) in nowadays. In order to improve electrical characteristics and the interface state density ($D_{it}$) in low temperature, It was deposited with carbon dioxide ($CO_2$) and silane ($SiH_4$) gas by inductively coupled plasma chemical vapor deposition (ICP-CVD). Each $D_{it}$ of $SiO_2$ using $CO_2$ and $N_2O$ gas was $1.30{\times}10^{10}cm^{-2}{\cdot}eV^{-1}$ and $3.31{\times}10^{10}cm^{-2}{\cdot}eV^{-1}$. It showed $SiO_2$ using $CO_2$ gas was about 2.55 times better than $N_2O$ gas. After 10 years when the thin film was applied to metal/insulator/semiconductor(MIS)-nonvolatile memory(NVM), MIS NVM using $SiO_2$($CO_2$) on tunneling layer had window memory of 2.16 V with 60% retention at bias voltage from +16 V to -19 V. However, MIS NVM applied $SiO_2$($N_2O$) to tunneling layer had 2.48 V with 61% retention at bias voltage from +20 V to -24 V. The results show $SiO_2$ using $CO_2$ decrease the $D_{it}$ and it improves the operating voltage.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제40회 동계학술대회 초록집
• /
• pp.147-147
• /
• 2011

High crystalline nonpolar a-plane (11-20) nitride light emitting diodes (LEDs) have been fabricated on r-plane (1-102) sapphire substrates by metalorganic chemical-vapor deposition (MOCVD). The multi-quantum wells (MQWs) active region is consists of 4 periods the nonpolar a-plane InGaN/GaN(a-InGaN/GaN) on a high quality a-plane GaN (a-GaN) template grown by using the multibuffer layer technique. The full widths at half maximum (FWHMs) of x-ray rocking curve (XRC) obtained from phiscan of the specimen that was grown up to nonpolar a-plane GaN LED layers with double crystal x-ray diffraction. The FWHM values were decreased down to 477 arc sec for $0^{\circ}$ and 505 arc sec for $-90^{\circ}$, respectively. After fabricating a conventional lateral LED chip which size was $300{\times}600{\mu}m^2$, we measured the optical output power by on-wafer measurements. N-electrode was made with Cr/Au contact, and ITO on p-GaN was formed with Ohmic contact using Ni/Au followed by inductively coupled plasma etching for mesa isolation. The optical output power of 1.08 mW was obtained at drive current of 20 mA with the peak emission wavelength of 502 nm.

• 반도체디스플레이기술학회지
• /
• 제10권2호
• /
• pp.115-119
• /
• 2011

A tip-type carbon nanotube(CNT)-based field emitter was studied to consider it as electron source for micro-focused x-ray tube. The CNT was grown directly on a metal (tungsten) substrate by using an inductively coupled plasma-chemical vapor deposition (ICP-CVD) method. Prior to CNT growth, the metal substrate was etched to have various tip angles from $10^{\circ}$ to $180^{\circ}C$ (flat-type). The morphologies and microstructures of all the grown CNTs were analyzed via field-emission SEM. Furthermore, the effects of substrate tip-angles on the emission properties of CNT-based field emitters were characterized to estimate the maximum current density, the turn-on voltage, and the spatial distribution of electron beams. Prolonged long-term stability testing of the CNT emitters was also performed. All the experiment results obtained from this study indicated why a tip-type CNT emitter, compared with a flat-type CNT emitter, would be more desirable for a micro-focused x-ray system, in terms of the emission current level, the focused beam area, and the emission stability.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.391-392
• /
• 2012

In these days, the desire for the precise and tiny displays in mobile application has been increased strongly. Currently, laser displays ranging from large-size laser TV to mobile projectors, are commercially available or due to appear on the market [1]. In order to achieve a mobile projectors, the semiconductor laser diodes should be used as a laser source due to their size and weight. In this presentation, the continuous etch characteristics of Pd and AlGaN/GaN superlattice for the fabrication of blue laser diodes were investigated by using inductively coupled $CHF_3$ and $Cl_2$ -based plasma. The GaN laser diode samples were grown on the sapphire (0001) substrate using a metal organic chemical vapor deposition system. A Si-doped GaN layer was grown on the substrate, followed by growth of LD structures, including the active layers of InGaN/GaN quantum well and barriers layer, as shown in other literature [2], and the palladium was used as a p-type ohmic contact metal. The etch rate of AlGaN/GaN superlattice (2.5/2.5 nm for 100 periods) and n-GaN by using $Cl_2$ (90%)/Ar (10%) and $Cl_2$ (50%)/$CHF_3$ (50%) plasma chemistry, respectively. While when the $Cl_2$/Ar plasma were used, the etch rate of AlGaN/GaN superlattice shows a similar etch rate as that of n-GaN, the $Cl_2/CHF_3$ plasma shows decreased etch rate, compared with that of $Cl_2$/Ar plasma, especially for AlGaN/GaN superlattice. Furthermore, it was also found that the Pd which is deposited on top of the superlattice couldn't be etched with $Cl_2$/Ar plasma. It was indicating that the etching step should be separated into 2 steps for the Pd etching and the superlattice etching, respectively. The etched surface of stacked Pd/superlattice as a result of 2-step etching process including Pd etching ($Cl_2/CHF_3$) and SLs ($Cl_2$/Ar) etching, respectively. EDX results shows that the etched surface is a GaN waveguide free from the Al, indicating the SLs were fully removed by etching. Furthermore, the optical and electrical properties will be also investigated in this presentation. In summary, Pd/AlGaN/GaN SLs were successfully etched exploiting noble 2-step etching processes.

• 대한금속재료학회지
• /
• 제47권5호
• /
• pp.322-329
• /
• 2009

60 nm- and 20 nm-thick hydrogenated amorphous silicon (a-Si:H) layers were deposited on 200 nm $SiO_2/Si$ substrates using ICP-CVD (inductively coupled plasma chemical vapor deposition). A 10 nm-Ni layer was then deposited by e-beam evaporation. Finally, 10 nm-Ni/60 nm a-Si:H/200 nm-$SiO_2/Si$ and 10 nm-Ni/20 nm a-Si:H/200 nm-$SiO_2/Si$ structures were prepared. The samples were annealed by rapid thermal annealing for 40 seconds at $200{\sim}500^{\circ}C$ to produce $NiSi_x$. The resulting changes in sheet resistance, microstructure, phase, chemical composition and surface roughness were examined. The nickel silicide on a 60 nm a-Si:H substrate showed a low sheet resistance at T (temperatures) >$450^{\circ}C$. The nickel silicide on the 20 nm a-Si:H substrate showed a low sheet resistance at T > $300^{\circ}C$. HRXRD analysis revealed a phase transformation of the nickel silicide on a 60 nm a-Si:H substrate (${\delta}-Ni_2Si{\rightarrow}{\zeta}-Ni_2Si{\rightarrow}(NiSi+{\zeta}-Ni_2Si)$) at annealing temperatures of $300^{\circ}C{\rightarrow}400^{\circ}C{\rightarrow}500^{\circ}C$. The nickel silicide on the 20 nm a-Si:H substrate had a composition of ${\delta}-Ni_2Si$ with no secondary phases. Through FE-SEM and TEM analysis, the nickel silicide layer on the 60 nm a-Si:H substrate showed a 60 nm-thick silicide layer with a columnar shape, which contained both residual a-Si:H and $Ni_2Si$ layers, regardless of annealing temperatures. The nickel silicide on the 20 nm a-Si:H substrate had a uniform thickness of 40 nm with a columnar shape and no residual silicon. SPM analysis shows that the surface roughness was < 1.8 nm regardless of the a-Si:H-thickness. It was confirmed that the low temperature silicide process using a 20 nm a-Si:H substrate is more suitable for thin film transistor (TFT) active layer applications.