• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.126-129
• /
• 2002

This article presents that the affecting factors to solderability and initial reliability. It was discussed that effect of the solder ball hardness and composition on the reliability of solder joints. In this study, lead free solder alloys with compositions of Sn-Cu, Sn-Ag, Sn-Ag-Cu, Sn-Ag-Cu-Bi were applied to the $\muBGA$ packages. As a result of experiments, the high degree of hardness with the displacement of 0.22mm was obtained Sn-2.0Ag-0.7Cu-3.0Bi. The shear strength of lead free solder was higher than of Sn-37Pb solder, and it was increased about 150% in Sn-2.0Ag-0.7Cu-3.0Bi.

• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.3
• /
• pp.55-61
• /
• 2022

In this study, properties of Pb-free solder joints which were combined using Sn-3.0Ag-0.5Cu (SAC305) Pb-free solder with a mid-temperature type of melting temperature and Sn-57Bi-1Ag Pb-free solder with a low-temperature type of melting temperature were reported. Combined Pb-free solder joints were formed by reflow soldering processes with ball grid array (BGA) packages which have SAC305 solder balls and flame retardant-4 (FR-4) printed circuit boards (PCBs) which printed Sn-57Bi-1Ag solder paste. The reflow soldering processes were performed with two types of temperature profiles and interfacial properties of combined Pb-free solder joints such as interfacial reactions, formations of intermetallic compounds (IMCs), diffusion mechanisms of Bi, and so on were analyzed with the reflow process conditions. In order to compare reliability characteristics of combined Pb-free solder joints, we also conducted thermal shock test and analyzed changes of mechanical properties for joints from a shear test during the thermal shock test.

• Journal of Welding and Joining
• /
• v.31 no.3
• /
• pp.4-10
• /
• 2013

In electronic industry, the trend of future electronics will be flexible, bendable, wearable electronics. Until now, there is few study on bonding technology and reliability of bonding joint between chip with micro solder bump and flexible substrate. In this study, we investigated joint properties of Si chip with eutectic Sn-58Bi solder bump on Cu pillar bump bonded on flexible substrate finished with ENIG by flip chip process. After flip chip bonding, we observed microstructure of bump joint by SEM and then evaluated properties of bump joint by die shear test, thermal shock test, and bending test. After thermal shock test, we observed that crack initiated between $Cu_6Sn_5IMC$ and Sn-Bi solder and then propagated within Sn-Bi solder and/or interface between IMC and solder. On the other hands, We observed that fracture propated at interface between Ni3Sn4 IMC and solder and/or in solder matrix after bending test.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.2 s.43
• /
• pp.35-40
• /
• 2007

The pull strength and fracture mechanism were investigated to evaluate the reliability and compatibility of Sn-8Zn-3Bi joints, the solder paste on lead and lead-free plating under thermal shock conditions. At the Sn-8Zn-3Bi solder joint, no crack initiation was observed during thermal shock test. After 1000 cycles, the strength of the solder joint decreased not sharply but reduced gradually compared with initial conditions. The decrement of strength was affected by ${\gamma}-Cu_5Zn_8$ IMC growth which caused the IMC fracture on the fracture surface and a change in fracture mode and initial crack point. Clearly, the Sn-8Zn-3Bi solder shows good reliability properties and compatibility with lead-free plated Cu LF under thermal shock temperatures between 248K and 423K.

• 한국초전도학회:학술대회논문집
• /
• v.15
• /
• pp.58-58
• /
• 2005

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.2
• /
• pp.95-103
• /
• 2021

Sn-58Bi-xRu composite solders were prepared by adding Ru nanoparticles to Sn-58Bi, a typical low-temperature solder, and the interfacial reaction and solder joint reliability were analyzed by reacting with Cu/OSP and ENIG surface treated PCB boards. The Cu₆Sn₅ IMC formed by the reaction with Cu/OSP had little change in thickness depending on the Ru content, and ductile fracture occurred inside the solder during the high-speed shear test without any significant change even after 100 hr aging. In reaction with ENIG, the Ni₃Sn₄ IMC thickness tended to decrease as the Ru content increased, and ENIG-specific brittle fracture was found in some specimens. Since Ru element is not found near the interface, it is judged not to be significantly involved in the interfacial reaction, and it is analyzed that it mainly exists together with the Bi phase.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.05a
• /
• pp.25-26
• /
• 1996

• Proceedings of the KWS Conference
• /
• 1996.10a
• /
• pp.64-65
• /
• 1996

• Proceedings of the KWS Conference
• /
• 2001.10a
• /
• pp.168-170
• /
• 2001

• Journal of Korea Foundry Society
• /
• v.21 no.4
• /
• pp.239-245
• /
• 2001

Microstructure and mechanical properties of Sn-3.1 wt.%Ag-6.9 wt.%Bi system solders on Cu-substrate were studied. The Sn3.1 wt.%Ag-6.9 wt.%Bi alloy was designed by phase diagram and chemical properties and was prepared by melting in argon atmosphere. The mechanical properties of solder/Cu joints were examined by shear strength test, and also creep test. The microstructure of Sn-3.1 wt.%Ag-6.9 wt.%Bi alloy consists of Bi-rich phase and $Ag_3Sn$ precipitate in {\beta}-Sn$ matrix phase. The shear strength of the joint was decreased with aging treatment. Crack path under shear test was through the solder. Similar crack path change mode was observed at the creep test of solder/Cu joint. The creep behavior of Sn-3.1 wt.%Ag-6.9 wt.%Bi alloy represented the inverse primary creep behavior at all test condition. It is suggested that the inverse primary creep behavior is induced from Bi solute atoms in Sn-matrix. The creep resistance of Sn-3.1Ag-6.9Bi alloy is better than that of Sn-3.5 wt.%Ag alloy at all test conditions.