• Journal of the Korean Society of Safety
• /
• v.18 no.3
• /
• pp.64-68
• /
• 2003

ITO_{(n)}/Si_{(p)}$ solar cell is fabricated by vaccum deposition method under the resistance heating with substrate temperature kept about 200[$^{\circ}C$] and than their properties are investigated. The maximum output of fabricated solar cell is obtained when the composition of the thin film is consisted of indium oxide 91[mole %] and tin oxide 9(mole %). The solar cell electrical charateristics can be improved by annealing but are deteriorated at temperature above 600[$^{\circ}C$] for longer than 15[min].

• Clean Technology
• /
• v.19 no.4
• /
• pp.388-392
• /
• 2013

Iindium-tin-oxide (ITO) material was had to use in display application as transparent electrode. However it would be problems comes up, the depletion of indium, tin and energy consumption of production process. Therefore recently trend was demanded alternative ITO material and recycling/reused ITO. In this conditions, the environmental impact have to express correct value about recycling/reused ITO process. The life cycle assessment was valuable method in this process. Thus first step was carried out separating in/out put (material) sources and then, exactive data base (DB) was applied. The result of environment impact was calculated by affect categories and recycling rate was set to 34% (This value was measured in previous project). The rate (g) of ITO material was calculated by chemical equivalent. In result, environmental impact were revealed acidification potential and abiotic depletion and if do not recycle/reuse ITO, $ 476 per 1 ton waste in land.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.187-187
• /
• 2015

The past thirty years have seen increasingly rapid advances in the field of Indium Tin Oxide (ITO) transparent thin film.[1] However, a major problem with this ITO thin film application is high cost compared with other transparent thin film materials.[2] So far, in order to overcome this disadvantage, we show a transparent ITO/Ag/i-ZnO multilayer thin film electrode can be the solution. In comparison with using amount of ITO as a transparent conducting material, intrinsic-Zinc-Oxide (i-ZnO) based on ITO/Ag/i-ZnO multilayer thin film showed cost-effective and it has not only highly transparent but also conductive properties. The aim of this research has therefore been to try and establish how ITO/Ag/i-ZnO multilayer thin film would be more effective than ITO thin film. Herein, we report ITO/Ag/i-ZnO multilayer thin film properties by using optical spectroscopic method and measuring sheet resistance. At a certain total thickness of thin film, sheet resistance of ITO/Ag/i-ZnO multilayer was drastically decreased than ITO layer approximately $40{\Omega}/{\square}$ at same visible light transmittance.(minimal point $5.2{\Omega}/{\square}$). Tendency, which shows lowly sheet resistive in a certain transmittance, has been observed, hence, it should be suitable for transparent electrode device.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.162-162
• /
• 2016

We present multifunctional indium tin oxide (ITO) thin films formed at room temperature by a normal sputtering system equipped with a plasma limiter which effectively blocks the bombardment of energetic negative oxygen ions (NOIs). The ITO thin film possesses not only low resistivity but also high gas diffusion barrier properties even though it is deposited on a plastic substrate at room temperature without post annealing. Argon neutrals incident to substrates in the sputtering have an optimal energy window from 20 to 30 eV under the condition of blocking energetic NOIs to form ITO nano-crystalline structure. The effect of blocking energetic NOIs and argon neutrals with optimal energy make the resistivity decrease to $3.61{\times}10-4{\Omega}cm$ and the water vapor transmission rate (WVTR) of 100 nm thick ITO film drop to $3.9{\times}10-3g/(m2day)$ under environmental conditions of 90% relative humidity and 50oC, which corresponds to a value of ~ 10-5 g/(m2day) at room temperature and air conditions. The multifunctional ITO thin films with low resistivity and low gas permeability will be highly valuable for plastic electronics applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.857-860
• /
• 2002

The material that is both conductive in electricity and transparent to the visible-ray is called transparent conducting thin film. It has many field of application such as solar cell, liquid crystal display, transparent electrical heater, selective optical filter, and a optical electric device. In this study, indium tin oxide (ITO ; Sn-doped $In_2O_3$) thin films were deposited on $SiO_2$/soda-lime glass plates by a dc magnetron sputtering technique. The crystallinity and electrical properties of the films were investigated by X-ray diffraction(XRD), atomic force microscopy (AFM) scanning and 4-point probe. The optical transmittance of ITO films in the range of 300-1000nm were measured with a spectrophotometer. As a result, we obtained polycrystalline structured ITO films with (222), (400), and (440) peak. Transmittance of all the films were higher than 90% in the visible range.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.9
• /
• pp.711-717
• /
• 1998

BST(70/30) and BST(50/50) thin films were prepared by Sol-Gel method and studied about the microstructural and dielectric properties with Pt and ITO bottom electrodes. The stock solution was synthesized and spin coated on the Pt/Ti$SiO_2$/Si and Indium Tin Oxide(ITO)/ glass substrate. the coated films were dries at 350$^{\circ}C$ for 10 minutes and annealed at $750^{\circ}C$ for 1 hour for the crystallization. The thin films coated on ITO substrate were crystallized easily and the packing density and roughness of surface were better that those of films coated on Pt substrates. In the BST(50/50) composition the structural properties were similar to the BST(70/30) composition and grain size were decreased with increasing the contents of Sr. The dielectric constant was higher in the BST(50/50) composition compared with the BST(70/30) composition. Using the ITO substrate, the dielectric constant was higher than the Pt substrate while the dielectric loss was showed a reverse trend. The dielectric constant with and increase of temperature was decreased slowly.

• Transactions on Electrical and Electronic Materials
• /
• v.2 no.1
• /
• pp.22-26
• /
• 2001

ITO (Indium-tin-oxide) thin films were deposited on glass substrates by a dc magnetron sputtering system using ITO powder target. The methods of heat treatment are important factor to obtain high quality ITO films with low electrical resistivity and good optical transmittance. Therefore, both methods of the substrate temperature and post-deposition annealing temperature have been compared on the film structural, electrical and optical properties. A preferred orientations shifts from (411) to (222) peak at annealing temperature of 200$\^{C}$. Minimum resistivity of ITO film is approximately 8.7$\times$10$\^$-4/ Ωcm at substrate temperature of 450$\^{C}$. Optical transmittances at post annealing temperature above 200$\^{C}$ are 90%. As a result, the minimum value of annealing temperature that is required for the recrystallization of as-deposited ITo thin films is 200$\^{C}$.

• Applied Chemistry for Engineering
• /
• v.16 no.6
• /
• pp.742-748
• /
• 2005

Transparent conductive indium-tin oxide (ITO) films are widely used as transparent electrodes for flat panel displays. Many of the ITO films for practical use have been prepared by magnetron sputtering, chemical vapor deposition, electron beam evaporation, etc. An oxide target composed of 10 wt% $SnO_2$ and 90 wt% $In_2O_3$ has been deposited onto polycyclic olefin polymer (POP) substrate by electron beam evaporation. POP has a higher glass transition temperature ($Tg=330^{\circ}C$) than other conventional polymers. In this study, the effects of substrate temperature and the $O_2$ introduction flow rate were investigated in terms of physical, electrical and optical properties of deposited ITO films. We investigated the effects of processing variables such as substrate temperature and the oxygen introduction flow rate. The best electrical and optical properties of deposited ITO films obtained from this study were electrical resistivity value of ${\rho}=1.78{\times}10^{-3}{\Omega}{\cdot}cm$ and optical transmittance of about 85% at 8 sccm (Standard Cubic Centimeter per Minute) $O_2$ introduction flow rate, $5{\AA}/sec$ deposition rate, $1000{\AA}$ deposited ITO thickness and $200^{\circ}C$ substrate temperature.

• Journal of the Korean Ceramic Society
• /
• v.46 no.6
• /
• pp.708-712
• /
• 2009

ITO films were achieved by sintering at $500{\sim}550{^{\circ}C}$. This was possible by inducing a seeding effect on an ITO sol by producing crystalline ITO nanoparticles in situ during heat treatment. Two kinds of ITO sols (named ITO-A and ITO-B) were prepared at 2.0 wt% from indium acetate and tin(IV) chloride in different mixed solvents. The ITO-A sol showed a high degree of crystallinity of ITO without any detectable Sn$O_2$ on XRD at $350{^{\circ}C}$/1 h, but the ITO-B sol showed a small amount of Sn$O_2$ even after annealing at $600{^{\circ}C}$/1 h. The 10 wt% ITO-A//ITO-B showed the sheet resistance of 3600$\Omega$/□, while the ITO-B sol alone showed 5200 $\Omega$/□ by sintering at $550{^{\circ}C}$ for 30 min. Processing parameters were studied by TG/DSC, XRD, SEM, sheet resistance, and visible transmittance.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.3
• /
• pp.128-132
• /
• 2009

Transparent conducting thin films of indium tin oxide(ITO) co-sputtered with aluminum-doped zinc oxide(AZO) were deposited on glass substrate by dual magnetron sputtering. It was found that the electrical properties and structural characteristics of the films are significantly changed according to the sputtering power of the AZO target. The IAZTO film prepared with D.C power of ITO at 100 W and R.F power of AZO at 50 W shows an electrical resistivity of $4.6{\times}10^{-4}{\Omega}{\cdot}cm$ and a sheet resistance of $30{\Omega}/{\square}$ (for 150 nm thick). Besides of the improvement of the electrical properties, compared to the ITO films deposited at the same process conditions, the IAZTO films have very smooth surface, which is due to the amorphous nature of the films. However, the electrical conductivity of the IAZTO films was found to be deteriorated along with the crystallization in case of the high temperature deposition (above $310^{\circ}C$). In this work, high quality amorphous transparent conductive oxide layers could be obtained by mixing AZO with ITO, indicating possible use of IAZTO films as the transparent electrodes in OLED and flexible display devices.