• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.411-414
• /
• 2008

In order to study the effect of lubrication during hot rolling, ferritic stainless steel (FSS) sheet were hot-rolled with and without application of lubrication. The effect of two hot rolling processes on the evolution of texture and microstructure after hot rolling, cold rolling and subsequent recrystallization annealing was studied by means of macro-texture analysis and microstructure observations. After hot rolling, the specimen rolled with lubrication showed rolling textures at the sheet surface, while the specimen rolled without lubrication displayed shear textures in the outer layers of the sheet. Hot rolling with lubrication was beneficial to the formation of strong recrystallization textures at sheet surface. However, hot rolling with lubrication led to the formation of orientation colonies in outer thickness layers of the recrystallized sheet.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1997.10a
• /
• pp.161-166
• /
• 1997

Application of hot roiling oil lubrication technology was broadened to the field of RM stands of Hot Rolling Mill at Pohang works. The primary object was to improve the quality of the strip sttrface and the rolls by oil lubrication in hot rolling process. Prior to the actual field application preliminary test was conducted to evaluate the effect of hot rolling oil lubrication at RM stands. From the test, it has been found that the use of oil lubrication tends to prevent the progression of the heat cracks and thereby increases the quality of the strip surface and the wear life of the rolls. New hot rolling oil lubrication system was applied to the RM stands VSB, R1, R2, R3, R4 and edger rolls. With the introduction of a rolling lubricant, the quality of the strip surface and rolls was improved and overall roll dressing has decreased. Also there has been a improvement of productivity from the long roll life.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1996.04b
• /
• pp.126-132
• /
• 1996

A laboratory scale hot strip rolling wear simulator(HRWS) was developed for the purpose of investigating the tribological phenomena occurred in production hot strip rolling mills. The HRWS' main parts are the electric heater, the mechanical descaler, tandem type 2-4Hi rolling mill stands, the cooling chamber, the tension controller and coiler. By simulating the tribelogical phenomena in rolling process at laboratory, wear patterns, cracks, cat-ear wear, black film, effect of hot rolling oil lubrication, etc. were reproduced, and discussed on the performace of simulator.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.222-225
• /
• 2006

The effect of lubrication on the development of textures and Microstructure was studied by different lubricating condition during hot rolling of AA1050 aluminum alloy. Hot rolling without lubrication led to the evolution of the pronounced through-thickness texture gradients, whereas hot rolling with lubrication gave rise to the formation of uniform rolling texture in the whole thickness layer. The variation of texture and microstructure according to hot rolling condition are investigated by X-ray diffractometer (XRD) and Electron Back-Scattered Diffraction (EBSD). The experimental results were discussed base on the finite element method (FEM) simulation. FEM calculation reveals that a larger friction between roll and sheet causes the deviated strain state from a plane strain leading to the formation of shear textures in the thickness layers close to the surface.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1997.10a
• /
• pp.115-118
• /
• 1997

Recently, hot rolling oil lubrication technology is required to face with the new environments such as the rapid introduction of high wear resistent high speed steel roll the development of continuous hot rolling technology. In the hot strip mill, according to rolling and quality required conditions are constrict, Roll material of hot rolling finishing stand is changing Hi-Cr Roll to High Speed Steel [HSS] Roll. The problem of HSS Roll of roll force and strip scale defects are increasing in hot strip mill, So we have tested HSS Roll in hot rolling simulator as rolling condition, rolling speed, draft, hot oil concentration. To reduce roll force and prevent scale defects. We get some merit rolling force, rolling torque, roll wear reduction, roll and strip surface roughness and hot rolling critical oil concentration 0.4%. Finally we are going to investigate the effect of hot rolling oil of on rolling with HSS Roll.

• Korean Journal of Materials Research
• /
• v.19 no.5
• /
• pp.265-269
• /
• 2009

The through-thickness variations of strain and microstructure during high-speed hot rolled 5052 aluminum alloy sheet were investigated. The specimens were rolled at temperature ranges from 410 to $560^{\circ}C$ at a rolling speed of 15 m/s without lubrication and quenched into water at an interval of 30 ms after rolling. The redundant shear strain induced by high friction between rolls and the aluminum sheet was increased largely beneath the surface at a rolling reduction above 50%. Dynamic recrystallization occurred in the surface regions of the specimen rolled under conditions of high temperatures or high rolling reductions.

• Korean Journal of Materials Research
• /
• v.18 no.9
• /
• pp.492-496
• /
• 2008

The through-thickness variations of strain and microstructure of high-speed hot rolled 1050 pure aluminum sheet were investigated. The specimens of 1050 aluminum were rolled at temperatures ranging from 410 to $560^{\circ}C$ at a rolling speed of 15 m/s without lubrication and quenched in water at an interval of 30ms after rolling. The redundant shear strain induced by high friction between rolls and the aluminum sheet was increased largely beneath the surface at a rolling reduction above 50%. Recrystallization occurred in the surface regions of the specimen rolled to reduction of 65% at $510^{\circ}C$, while only recovery occurred in the other regions.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.453-455
• /
• 2005

Ferritic STS 439 Steel sheet were deformed by hot rolling with and without lubricant. The effect of friction between roll and specimen on inhomogeneous texture was studied by means of EBSD, XRD texture analysis. The textures were compared with those of obtained by Taylor FEM simulation. High friction between roll and sheet gave rise to the formation of the inhomogeneous shear texture through thickness.

• Korean Journal of Metals and Materials
• /
• v.46 no.11
• /
• pp.737-746
• /
• 2008

Mechanisms of sticking phenomena occurring during hot rolling of a modified STS 430J1L ferritic stainless steel have been investigated in this study by using a pilot-plant-scale rolling machine. As the rolling pass proceeds, the Fe-Cr oxide layer formed in a reheating furnace is destroyed, and the destroyed oxides penetrate into the rolled steel to form a thin oxide layer on the surface region. The sticking does not occur on the surface region containing oxides, whereas it occurs on the surface region without oxides by the separation of the rolled steel at high temperatures. This indicates that the resistance to sticking increases by the increase in the surface hardness when a considerable amount of oxides are formed on the surface region, and that the sticking can be evaluated by the volume fraction and distribution of oxides formed on the surface region. The lubrication and the increase of the rolling speed and rolling temperature beneficially affect to the resistance to sticking because they accelerate the formation of oxides on the steel surface region. In order to prevent or minimize the sticking, thus, it is suggested to increase the thickness of the oxide layer formed in the reheating furnace and to homogeneously distribute oxides along the surface region by controlling the hot-rolling process.

• Journal of the Korean Society of Safety
• /
• v.21 no.1 s.73
• /
• pp.6-14
• /
• 2006

The development of automatic production systems have required intelligent diagnostic and monitoring functions to overcome system failure and reduce production loss by the failure. In order to perform accurate operations of the intelligent system, implication about total system failure and fault analysis due to each mechanical component failures are required. Also solutions for repair and maintenance can be suggested from these analysis results. As an essential component of a mechanical system, a bearing system is investigated to define the failure behavior. The bearing failure is caused by lubricant system failure, metallurgical deficiency, mechanical condition(vibration, overloading, misalignment) and environmental effects. This study described slab transfer equipment fault train due to stress variation and metallurgical deficiency from lubricant failure by using FTA.