• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.835-841
• /
• 1995

The deposition properties of Si$_3$N$_4$ deposited by low pressure chemical vapor deposition were studied to evaluate Si$_3$N$_4$as part of multi-layer coatings for anti-oxidation and anti-wear coating of graphite in the propellant-burning environment. Si$_3$N$_4$was deposited on the pack-SiC coated graphite and the tendencies of deposition rate and surface morphology changes with temperatures and reaction gas ratios were investigated. In low deposition temperatures the deposition rate increased tilth increasing temperature but in high temperatures the deposition rate decreased with increasing temperature. The grain size of Si$_3$N$_4$decreased with increasing temperature. In condition that the range of reaction gas ratios is 20$\leq$NH$_3$/SiH$_4$$\leq$40, the deposition rate and surface morphology did not change. The Si$_3$N$_4$deposited at 800~130$0^{\circ}C$ was amorphous, and by post-annealing at 130$0^{\circ}C$ in a $N_2$ambient, the Si$_3$N$_4$crystalized.

• Korean Chemical Engineering Research
• /
• v.56 no.6
• /
• pp.901-908
• /
• 2018

Graphite is used as a sample anode active material. However, since the maximum theoretical capacity is limited to $372mA\;h\;g^{-1}$, a new anode active material is required for the development of a high capacity lithium ion battery. The maximum theoretical capacity of Si is $4200mA\;h\;g^{-1}$, which is higher than that of graphite. However, it is not suitable for direct application to the anode active material because it has a volume expansion of 400%. In order to minimize the decrease of the discharge capacity due to the volume expansion, the Si was pulverized by the dry method to reduce the mechanical stress and the volume change of the reaction phase, and the change of the volume was suppressed by coating the carbon layers to the particle size controlled Si particles. And carbon fiber is grown like a thread on the particle surface to control secondary volume expansion and improve electrical conductivity. The physical and chemical properties of the materials were measured by XRD, SEM and TEM, and their electrochemical properties were evaluated. In this study, we have investigated the synthesis method that can be used as anode active material by improving cycle characteristics of Si.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.1
• /
• pp.7-11
• /
• 2022

Recently, Hanmi Gemological Institute & Laboratory (HGI) had an opportunity to examine 5 transparent synthetic moissanite. The round brilliants ranged from 0.93 to 0.96 ct and had a colorless, pink, yellow, blue, and red color. Advanced testing results, including Fourier-transform infrared (FTIR) and Raman spectroscopy, identified all the specimens as synthetic moissanite. Under the microscope, all samples except the colorless were confirmed to be a synthetic moissanite coated with a colored film. EDXRF chemical analysis detected very weak X-ray fluorescence peak characteristics of Ca, Ti, and Co in the colored samples. These features were not detected in the colorless sample. Raman spectroscopy investigation was unable to detect the 1332 cm^-1 (produced by sp³ bonding of carbon atoms) or the ~1550 cm^-1 (produced by graphite-related sp² bonding) peak in the colorless sample. The SEM image of the colorless sample showed no indication of a coating. The TEM image of the colorless sample revealed the presence of a 3~8 nm thick layer on the moissanite. Moreover, from the corresponding STEM Z-contrast image combined with the energy-dispersive X-ray spectroscopy (EDX) line profiles and EDX elemental maps, this layer was estimated to be carbon, silicon and oxygen.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.22 no.5
• /
• pp.530-536
• /
• 2021

This paper presents the performance measurement results of a hybrid sheet with both shielding and heat dissipation functions developed by laminating copper mesh sheets and natural graphite sheets, which are used widely as electromagnetic shielding and heat-dissipating materials in electronic devices, without a pressure-sensitive adhesive (PSA). The results were compared by measuring the vertical and horizontal thermal conductivity with two other products to confirm the heat dissipation performance. A radiation emission test confirmed the electromagnetic shielding performance using a 3m electromagnetic anechoic chamber according to the CISPR 11 standard. In the case of vertical thermal conductivity, the proposed hybrid sheet was approximately 8.63 times higher than that of an aluminum sheet with heat dissipation coating and 18.7 times higher than that of a copper sheet laminated with artificial graphite with PSA. The proposed hybrid sheet was approximately 0.64 times that of the sheet, and approximately 1.76 times that of the heat-dissipated aluminum sheet in case of horizontal thermal conductivity. Measurements after applying each sheet in the same heat source revealed the proposed hybrid sheet to have the best heat dissipation performance. The radiation emission test showed that significantly radiation noise had been removed.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.441-448
• /
• 2015

Silicon carbide (SiC) coatings for tri-isotropic (TRISO) nuclear fuel particles were fabricated using a chemical vapor deposition (CVD) process onto graphite. A micro-tensile-testing system was developed for the mechanical characterization of SiC coatings at high temperatures. The fracture strength of the SiC coatings was characterized by the developed micro-tensile test in the range of $25^{\circ}C$ to $1000^{\circ}C$. Two types of CVD-SiC films were prepared for the micro-tensile test. SiC-A exhibited a large grain size (0.4 ~ 0.6 m) and the [111] preferred orientation, while SiC-B had a small grain size (0.2 ~ 0.3 mm) and the [220] preferred orientation. Free silicon (Si) was co-deposited onto SiC-B, and stacking faults also existed in the SiC-B structure. The fracture strengths of the CVD-SiC coatings, as measured by the high-temperature micro-tensile test, decreased with the testing temperature. The high-temperature fracture strengths of CVD-SiC coatings were related to the microstructure and defects of the CVD-SiC coatings.

• Composites Research
• /
• v.25 no.3
• /
• pp.70-75
• /
• 2012

Interfacial durability and electrical properties of CNT, ITO or xGnP coated PVDF nanocomposites were investigated for acoustic actuator applications. The xGnP coated PVDF nanocomposite exhibited better electrical conductivity than CNT and ITO case due to the unique electrical property of xGnP, and this nanocomposite also showed good sound characteristics. Interfacial adhesion durability between either neat CNT or plasma treated CNT and plasma treated PVDF were measured by static contact angle, surface energy, work of adhesion, and spreading coefficient tests. The optimum acoustic actuation performance of xGnP coated PVDF nanocomposite was measured using sound level meter with changing radius of curvature and coating conditions. As compared to CNT and ITO, the xGnP was known as more appropriate acoustic actuator due to the characteristic electrical property. It is the most appropriate condition when the radius of curvature is 15 degree. Although sound characteristics were different with various coating thicknesses, it is possible to manufacture transparent actuator with good sound quality.

• Transactions of the Korean hydrogen and new energy society
• /
• v.26 no.6
• /
• pp.554-559
• /
• 2015

Single cell of PEMFC (polymer electrolyte membrane fuel cell) is composed of bipolar plates, gasket, GDL and the MEA. Bipolar plate's function is the collecting electricity, helping oxygen/hydrogen gas diffuse evenly and draining the water and heat. In this work, we have conducted experiments to low contact resistance and improve the performance of a $25cm^2$ single cell by using metal forms. We have following experimental cases: 1) Conventional graphite serpentine channel bipolar plate; 2) Channel-less bipolar plate with nickel(Ni) based metal foam which coated by various materials. We focused the difference in contact resistance and performance of the single cell with metal foam depending on various coating materials. The experimental results show the similar performance of single cells between with serpentine channel bipolar plates and with channel-less bipolar plate using metal foams. In addition, single cell with metal foam shows potential to higher performance than conventional channel.

• Applied Microscopy
• /
• v.47 no.1
• /
• pp.36-42
• /
• 2017

Field electron emission measurements were performed on dielectric-coated tungsten emitters, with apex radii in the nanometer and micrometer range, which were prepared by electrochemical etching in NaOH solution. Measurements were performed in a field electron microscopy (FEM) with a base pressure <$10^{-6}$ Pascal ($10^{-8}$ mbar). Four different types of dielectric were used, namely: (1) Clark Electromedical Instruments epoxylite resin, (2) Epidian 6 produced by Ciech Sarzyna S. A., (3) a Radionox solution of colloidal graphite; and (4) Molyslip 2001 E compound ($MoS_2$ and MoS). Current-voltage measurements and FEM images were used to investigate the characteristics of these composite emitters, and to assess how the different types of dielectric coating affect the suitability of the composite emitter as a potential electron source.

• Corrosion Science and Technology
• /
• v.16 no.5
• /
• pp.235-240
• /
• 2017

Regional cathodic protection has significant impact on pipeline integrity management. After risk analyses of a newly built gas distribution station constructed in an area with large dwelling density, risk score was high because of potential threat caused by galvanic corrosion. Except reinforced steel in concrete, there are four kinds of metal buried under earth: carbon steel, galvanized flat steel, zinc rod and graphite module. To protect buried pipeline from external corrosion, design and construction of regional cathodic protection was proposed. Current density was measured with potential using potential dynamic test and boundary element method (BEM) was used to calculate current requirement and optimize best anode placement during design. From our calculation on the potential, optimized conditions for this area were that an applied current was 3A and anode was placed at 40 meters deep from the soil surface. It results in potential range between $-1.128V_{CSE}$ and $-0.863V_{CSE}$, meeting the $-0.85V_{CSE}$ criterion and the $-1.2V_{CSE}$ criterion that no potential was more negative than $-1.2V_{CSE}$ to cause hydrogen evolution at defects in coating of the pipeline.

• Journal of the Korean Ceramic Society
• /
• v.49 no.2
• /
• pp.167-172
• /
• 2012

Fine diamond powders are synthesized with a 420 ${\phi}$ cubic press and stack-cell composed of Kovar ($Fe_{54}Ni_{29}Co_{17}$) (or Kovar+7 ${\mu}m$-thick Zn electroplated) alloy and graphite disks. The high pressure high temperature (HPHT) process condition was executed at $1500^{\circ}C$ for 280 seconds by varying the nominal pressure of 5.7~10.6 GPa. The density of formation, size, shape, and phase of diamonds are determined by optical microscopy, field emission scanning electron microscopy, thermal gravimetric analysis-differential thermal ammnlysis (TGA-DTA), X-ray diffraction (XRD), and micro-Raman spectroscopy. Through the microscopy analyses, we found that 1.5 ${\mu}m$ super-fine tetrahedral diamonds were synthesized for Zn coated Kovar cell with whole range of pressure while ~3 ${\mu}m$ super-fine diamond for conventional Kovar cell with < 10.6 GPa. Based on $750^{\circ}C$ exothermic reaction of diamonds in TGA-DTA, and characteristic peaks of the diamonds in XRD and micro-Raman analysis, we could confirm that the diamonds were successfully formed with the whole pressure range in this research. Finally, we propose a new process for super-fine diamonds by lowering the pressure condition and employing Zn electroplated Kovar disks.