• Journal of the Korean Vacuum Society
• /
• v.5 no.4
• /
• pp.371-376
• /
• 1996

Au films with a thickness around 1600 $\AA$ were deposited onto glass at room temperature by ion beam sputtering with a 5 cm cold-hollow ion gun at pressure $1\times 10^{-6}-1\times 10^{-5}$ Torr. Irradiation of the Au deposited samples was carried out at pressure of $7\times 10^{-6}$ Torr. For the sputter depositions, $Ar^+$ ion energy was 1 keV, and the current density at the substrate surface was 15 $\mu$A/$\textrm{cm}^2$. Effects of 1 keV $Ar^+$ ion dose($I_d$) between $1\times 10^{16}\; and\;2\times 10^{17}\;Ar^+\textrm{cm}^{-2}$on properties such as crystallinity, surface roughness and adhesion, etc. of the films have been investigated. The Au films sputtered by $Ar^+$ ion beam had only (111) plane and the X-ray intensity of the films decreased with increase of $I_d$. The thickness of Au films reduced with Id. $R_{ms}$ surface roughness of the films increased from 16 $\AA$ at as-deposited to 1118 $\AA$ at ion dose= $2\times 10^{17}\;Ar^+\textrm{cm}^{-2}$. Adhesion of Au film on sputtered at $I_d$= $2\times 10^{17}\;Ar^+\textrm{cm}^{-2}$ was 9 times greater than that of Au film with untreated, as determined by a scratch test.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.20 no.1
• /
• pp.58-63
• /
• 2010

The glass-ceramics made from the mixture of coal bottom ash, produced from a thermal power plant mixed with $Na_2O$ and $Li_2O$ was fabricated and their crystallization behavior was studied using a non-isothermal analyzing method. The temperature for 50% crystallization was higher than the exothermic peak temperature $T_p$ at DTA curve and the quickest crystallization temperature was much the same as $T_p$ as identified from the relationships of crystallized fraction and crystallization rate with temperature. By using Kissinger equation describing a crystallization behavior, the activation energy (262 kJ/mol), the Avrami constant (1.7) and the frequency ($5.7{\times}10^{16}/s$) for crystallization were calculated from which the nepheline crystal could be expected as showing an 1~2-dimensional surface crystallization behavior mainly with some bulk crystallization tendency at the same time. The actual observation of microstructure using SEM showed the considerable amount of surface crystals of dendrite and the bulk crystals with low fraction, so the prediction by the Kissinger equation was in accord with the crystallization behavior of glass-ceramics fabricated in this study.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.5
• /
• pp.527-533
• /
• 1999

Hertzian indentation tests with spherical indenters in water were conducted to examine the contact fatigue in three dental ceramics, such as feldspathic porcelain, micaceous glass-ceramic (MGC) and glass-infiltrated alumina, which was used as dental restorations, and evaluated the effect of contact damage on strength. Initial damage was dependent of microstructure, showing cone cracks of brittle behavior in the feldspathic porcelain and deformation of quasi-plastic behavior in the MGC, with an intermediate case in the glass-infiltrated alumina. However, as increasing the number of cyclic loading (n=1~n =$10^6$)all materials showed an abrupt strength degradation, at which fracture was originated from damage in the contact fatigue. There were two strength degradation with increasing the number of cyclic loading in specific loads (200N, 500N, 1000N):first was from the cone cracks, and second was from the radial cracks created by cyclic loading. The radial cracks, once formed, led to rapid degradation in strength properties, Finally the material was failed at the high number of cyclic loading. Strength degradation with indentation load at fixed number of cyclic loading indicated that the feldspathic porcelain should be highly damage tolerant to the contact fatigue.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.12
• /
• pp.781-785
• /
• 2016

With trend of the miniaturization and the high-functionalizing of mobile communication system, low-loss microwave dielectric materials are widely used for high frequency communication components. These dielectric materials should be co-sintered with highly electric-conducting metal such as silver or copper for high-frequency and thick film process application. Sintering temperature of $Ca(Li_{1/3}Nd_{2/3})_{0.2}Ti_{0.8}]O_{3-{\delta}}$, which has excellent dielectric properties such as ${\varepsilon}_r$ above 40, quality factor ($Q{\cdot}f_0$) above 16,000 GHz, and TCF (temperature coefficient of resonant frequency) of $-20{\sim}-10ppm/^{\circ}C$, is reported as high as $1,175^{\circ}C$, so it could not be co-sintered with silver or copper. Therefore in this study, low-temperature melting glasses of Zn-B-O and Zn-B-Si-O systems were added to $Ca[(Li_{1/3}Nb_{2/3})_{0.8}Ti_{0.2}]O_{3-{\delta}}$ to lower its sintering temperature under $900^{\circ}C$ without losing excellency of dielectric properties. With 15 weight % of Zn-B-Si-O glass and sintered at $875^{\circ}C$, specimen showed density of $4.11g/cm^3$, ${\varepsilon}_r$ of 40.1, $Q{\cdot}f_0$ of 4,869 GHz, and TCF of $-5.9ppm/^{\circ}C$. With 15 weight % of Zn-B-O glass and sintered at $875^{\circ}C$, specimen showed density of $4.14g/cm^3$, ${\varepsilon}_r$ of 40.4, $Q{\cdot}f_0$ of 7,059 GHz, and TCF of $-0.92ppm/^{\circ}C$.

• Nuclear Engineering and Technology
• /
• v.54 no.9
• /
• pp.3250-3259
• /
• 2022

A new approach to the use of rice straw as a difficult-to-recycle agricultural waste was proposed. Potassium aluminosilicate was obtained by spark plasma sintering as an effective material for subsequent immobilization of ¹³⁷Cs into a solid-state matrix. The sorption properties of potassium aluminosilicate to ¹³⁷Cs from aqueous solutions were studied. The effect of the synthesis temperature on the phase composition, microstructure, and rate of cesium leaching from samples obtained at 800-1000 ℃ and a pressure of 25 MPa was investigated. It was shown that the positive dynamics of compaction was characteristic of glass ceramics throughout the sintering. Glass ceramics RS-(K,Cs)AlSi₃O₈ obtained by the SPS method at 1000 ℃ for 5 min was characterized by a high density of ~2.62 g/cm³, Vickers hardness ~ 2.1 GPa, compressive strength ~231.3 MPa and the rate of cesium ions leaching of ~1.37 × 10^-7 g cm^-2·day^-1. The proposed approach makes it possible to safe dispose of rice straw and reduce emissions into the atmosphere of microdisperse amorphous silica, which is formed during its combustion and causes respiratory diseases, including cancer. In addition, the obtained is perspective to solve the problem of recycling long-lived ¹³⁷Cs radionuclides formed during the operation of nuclear power plants into solid-state matrices.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.2
• /
• pp.79-83
• /
• 2009

The glass-ceramic of the $Li_{2}O-Al_{2}O_{3}-SiO_{2}$ system was investigated to develop the low thermal expansion materials. The glass of this system was heat treated at $775^{\circ}C$ for 2 h for nucleation and subsequently at $825{\sim}900^{\circ}C$ for 2 h for crystallization. The crystal structure of the glass-ceramic of this system was a single phase of $\beta$-quartz solid solution($Li_{x}Al_{x}Si_{1-x}O_{2}$). The thermal expansion of the glass-ceramic showed $4.40{\times}10^{-7}{\sim}1.33{\times}10^{-6}K^{-1}$ between $25{\sim}300^{\circ}C$ and $1.56{\times}10^{-6}{\sim}2.53{\times}10^{-6}K^{-1}$ between $25{\sim}800^{\circ}C$, higher than lower temperature range. The mechanical strength remained almost same at around high 110 MPa with heating temperature changes.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.28 no.6
• /
• pp.229-234
• /
• 2018

The glass-ceramic of $Li_2O-Al_2O_3-SiO_2$ system was synthesized by using $ZrO_2$, $ZrSiO_4$, $ZrOCl_2$ and $Zr(SO_4)_2$, which is a raw material of Zr serving as a nucleation agent. It was confirmed that Avrami parameter of these four glasses is over 3 for bulk crystallization. The glass synthesized by $ZrOCl_2$, and $Zr(SO_4)_2$ showed high melting quality during the melting process. It is also observed that the Zr component is uniformly distributed in the glass. Various characterizations was evaluated, including composition analysis and bending strength.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.4
• /
• pp.154-159
• /
• 2019

The glass-ceramic of $Li_2O-Al_2O_3-SiO_2$ system was fabricated by using yttrium oxide and iron oxide that it can reduce the melting temperature and affect the homogenization. Zirconium sulfate was used as a nucleation agent. Calcium phosphate was used to improve the flow the glass so as reduce the viscosity of the glass. The glass-ceramics met a thermal shock test of more than $750^{\circ}C$ and the temperature at which the coefficient of thermal expansion rapidly increased at over $800^{\circ}C$ was shifted by about the above $30^{\circ}C$. Therefore, it is concluded that the glass-ceramic of $Li_2O-Al_2O_3-SiO_2$ system with yttrium oxide and iron oxide was founded to have good melting conditions and excellent thermal expansion resistance at high temperature such as special field for kitchen utensils.

• The Korean Journal of Ceramics
• /
• v.7 no.2
• /
• pp.58-62
• /
• 2001

The relationship between the addition of Sb$_2$O$_3$ and the color difference by solarization in photosensitive glasses was investigated. Glasses containing CeO$_2$ and Sb$_2$O$_3$ simultaneously and glasses with only CeO$_2$ were changed reddish and yellowish respectively after exposing to ultra violet ray. Color difference between compositions was represented by dominant wavelength and purity. Since, in glasses containing CeO$_2$ and Sb$_2$O$_3$ simultaneously, Sb$_2$O$_3$ as reduction agent affected Ce$^3+$ ions to increase in glass and more Ce$^4+$ ions were induced than in glasses with only CeO$_2$ during UV irradiation, more electrons released by photo-ionization, which were color centers, were trapped by Ce$^4+$. In conclusion, the introduction of Sb$_2$O$_3$ to photosensitive glasses with CeO$_2$ resulted in the change of color center concentration in glasses and prevented the solarization of photosensitive glasses with CeO$_2$.

• The Korean Journal of Ceramics
• /
• v.2 no.1
• /
• pp.1-10
• /
• 1996

Transparent conducting $SnO_2$-based thin films have been coated on float substrates such as fused quartz, and ceramic fiber cloths such as the Nexel and E-glass cloth from tin alkoxides by the sol-gel technique. Also, thin films of alternating layers of $SnO_2$ and $SiO_2$ have been fabricated by dip coating. The sheet resistance and average visible transmittance of the films were investigated in the aspect of the applications as transparent electrodes such as liquid crystal displays, photo-detectors and solar cells. The Nextel and E-glass cloths coated with antimony-doped tin oxide (ATO) had sheet resistance of as low as $20 \;ohm/{\Box}$ and $120ohm/\;{\Box}$, respectively. The promotion effects of additives as $La_2O_3$ and Pt on the ethanol gas sensing properties of the films were investigated in the aspects of the applications as an alcohol sensor and a breath alcohol checker. Possible evidence of quantum well effects in the oxide multilayers of $SnO_2$ and $SiO_2$ was investigated.