• Korean Journal of Optics and Photonics
• /
• v.23 no.2
• /
• pp.64-70
• /
• 2012

We analyzed the changes in electrical and optical characteristics of 1 $mm^2$ multiple-quantum-well (MQW) blue LEDs grown on a c-plane sapphire substrate after a stress test. Experiments were performed by injecting 50 mA current for 200 hours to TO-CAN packaged sample chips. We selected the value of injection current for stress through the junction-temperature measurement by using the forward-voltage characteristics of a diode to maintain a sufficiently low junction temperature during the test. The junction temperature at the selected injection current of 50 mA was 308 K. Experiments were performed under the assumption that the average junction temperature of 308 K did not affect the characteristics of the ohmic contact and the GaN-based materials. Before and after the stress test, we measured and analyzed current-voltage, light-current, light distribution on the LED surface, wavelength spectrum and relative external quantum efficiency (EQE). After the stress test, it was observed experimentally that the optical power and the relative EQE decreased. We theoretically investigated and experimentally proved that these phenomena are due to the increased nonradiative recombination rate caused by the increased defect density.

• Journal of the Optical Society of Korea
• /
• v.16 no.4
• /
• pp.349-353
• /
• 2012

Uniform spreading of injection current in light-emitting diodes (LEDs) is one of the crucial requirements for better device performances. It is reported that non-uniform current spreading leads to low output power, high current crowding, heating, and reliability degradation of the LED device. This paper reports on the effects of different surface and electrode geometries in the LEDs. To increase the output power of LEDs and reduce the series resistance, a rectangular-type LED (RT-LED) with a centered island cathode has been fabricated and investigated by comparison with a conventional LED (CV-LED). The performances of RT-LEDs were prominently enhanced via uniform current spreading and low current crowding. Performances in terms of increased output power and lower forward voltage of simulated RT-LEDs are much superior to those of CV-LEDs. Based on these results, we investigated the correlation between device geometries and optical characteristics through the fabricated CV and RT-LEDs. The measured output power and forward voltage of the RT-LEDs at 100 mA are 64.7% higher and 8% smaller compared with those of the CV-LEDs.

• Journal of the Korean Ceramic Society
• /
• v.44 no.3 s.298
• /
• pp.147-151
• /
• 2007

An improvement for the efficiency of the $Sr_{2}SiO_{4}:Eu$ yellow phosphor under the $450{\sim}470\;nm$ excitation range have been achieved by adding the co-doping element ($Mg^{2+}\;and\;Ba^{2+}$) in the host. White LEDs were fabricated through an integration of an blue (InGaN) chip (${\lambda}_{cm}=450\;nm$) and a blend of two phosphors ($Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor) in a single package. The InGaN-based two phosphor blends ($Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor) LEDs showed three bands at 450 nm, 550 nm and 640 nm, respectively. The 450 nm emission band was due to a radiative recombination from an InGaN active layer. This 450 nm emission was used as an optical transition of the $Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor. As a consequence of a preparation of white LEDs using the $Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor yellow phosphor and CaS:Eu red phosphor, the highest luminescence efficiency was obtained at the 0.03 mol $Ba^{2+}$ concentration. At this time, the white LEDs showed the CCT (5300 K), CRI (89.9) and luminous efficacy (17.34 lm/W).

• Korean Journal of Metals and Materials
• /
• v.48 no.11
• /
• pp.1035-1040
• /
• 2010

The research efforts on GaN-based light-emitting diodes (LEDs) keep increasing due to their significant impact on the illumination industry. Surface mount technology (SMT) is widely used to mount the LED packages for practical application. In surface mount soldering both the device body and leads are intentionally heated by a reflow process. We studied on the effects of multiple reflows on microstructural variation and joint strength of the solder joints between the LED package and the substrate. In this study, Pb-free Sn-3.0Ag-0.5Cu solder and a finished pad with organic solderability preservatives (OSP) were employed. A $Cu_6Sn_5$ intermetallic compound (IMC) layer was formed during the multiple reflows, and the thickness of the IMC layerincreased with an increasing number of reflows. The shear force decreased after three reflows. From the observation of the fracture surface after a shear test, partially brittle fractures were observed after five reflows.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.145-146
• /
• 2006

The most Important research topic in the development of ZnO LED and LD is the production of p-type ZnO thin film that has minimal stress with outstanding stoichiometric ratio. In this study, Phosphorus diffused into the undoped ZnO thin films using the ampoule-tube method for the production of p-type znO thin films. The undoped ZnO thin films were deposited by RF magnetron sputtering system on $GaAs_{0.6}P_{0.4}$/GaP and Si wafers. 4N Phosphorus (P) was diffused into the undoped ZnO thin films in ampoule-tube which was performed and $630^{\circ}C$ during 3hr. We found the diffusion condition of the conductive ZnO films which had p-type properties with the highest mobility of above 532 $cm^2$/Vs compared with other studies PL spectra measured at 10K for the purpose of analyzing optical properties of p-type ZnO thin film showed strong PL intensity in the UV emission band around 365nm ~ 415nm and 365nm ~ 385nm.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.6
• /
• pp.304-308
• /
• 2010

Deposition temperature uniformity of GaN based MQW (multiple quantum well) layers is an important key which affects the wavelength uniformity of white LEDs. Temperature uniformity was assessed by infrared images for both cases of a static and a rotating susceptor. Rotating the susceptor at 2.5 rpm over the induction heater gave 4.3% of temperature non-uniformity. Temperature distribution of the graphite susceptor over the induction heater was numerically modelled and agreed with experimental results.

• Smart Structures and Systems
• /
• v.25 no.2
• /
• pp.183-195
• /
• 2020

Mineral admixtures have been widely used to produce concrete. Pozzolans have been utilized as partially replacement for Portland cement or blended cement in concrete based on the materials' properties and the concrete's desired effects. Several environmental problems associated with producing cement have led to partial replacement of cement with other pozzolans. Furnace slag and fly ash are two of the pozzolans which can be appropriately used as partial replacements for cement in concrete. However, replacing cement with these materials results in significant changes in the mechanical properties of concrete, more specifically, compressive strength. This paper aims to intelligently predict the compressive strength of concretes incorporating furnace slag and fly ash as partial replacements for cement. For this purpose, a database containing 1030 data sets with nine inputs (concrete mix design and age of concrete) and one output (the compressive strength) was collected. Instead of absolute values of inputs, their proportions were used. A hybrid artificial neural network-genetic algorithm (ANN-GA) was employed as a novel approach to conducting the study. The performance of the ANN-GA model is evaluated by another artificial neural network (ANN), which was developed and tuned via a conventional backpropagation (BP) algorithm. Results showed that not only an ANN-GA model can be developed and appropriately used for the compressive strength prediction of concrete but also it can lead to superior results in comparison with an ANN-BP model.

• Korean Journal of Metals and Materials
• /
• v.46 no.10
• /
• pp.683-690
• /
• 2008

In order to develop transparent electrodes for high efficiency GaN-based light emitting diodes (LEDs), the electrical and optical properties of the electron beam evaporated ITO contacts have been investigated as a function of the deposition temperature and flow rate of oxygen during the deposition. As the deposition temperature increases from $140^{\circ}C$ to $220^{\circ}C$, the resistivity of the ITO films decreases slightly from $4.0{\times}10^{-4}{\Omega}cm$ to $3.3{\times}10^{-4}{\Omega}cm$, meanwhile the transmittance of the ITO films significantly increases from 67% to 88% at the wavelength of 470 nm. When the flow rate of oxygen during the deposition increases from 2 sccm to 4 sccm, the resistivity of the ITO films increases from $3.6{\times}10^{-4}{\Omega}cm$ to $7.4{\times}10^{-4}{\Omega}cm$, meanwhile the transmittance of the ITO films increases from 86% to 99% at 470 nm. Blue LEDs fabricated with the electron beam evaporated ITO electrode show that the ITO films deposited at $200^{\circ}C$ and 3 sccm of the oxygen flow rate give a low forward-bias voltage of 3.55 V at injection current of 20 mA with a highest output power.

• Proceedings of the Polymer Society of Korea Conference
• /
• 2006.10a
• /
• pp.25-26
• /
• 2006

Azobenzene functionalized polymers have been extensively investigated due to the potential applications in the areas of optical switching, optical elements, optical information storage, and nonlinear optics. These applications are mainly achievable due to photoinduced properties of azobenzene groups with photoisomerization and photoinduced anisotropy. We report applications to the optoelectronic devices using inscribed one-(1D) and two-dimensional (2D) SRGs on azo polymer films. The inscribed holographic SRGs patterns were useful to control or enhance optoelectronic properties such as transparent electrode patterning, hybrid solar cell and ultraviolet GaN-based LED.

• Journal of Advanced Marine Engineering and Technology
• /
• v.34 no.7
• /
• pp.991-996
• /
• 2010

Blue-green and green LEDs have been successfully fabricated grown by MBE, which has introduced the $ZnS_ySe_{1-x-y}:Te_x$ (x=0.04, y~0.11-0.14) ternary epilayer as an active layer. From the I-V characteristics, the built-in voltage (~2.1 V) is very small compared to other wide bandgap LEDs, such as commercial InGaN-based LEDs (>3.2 V). From the C-V profiling, the effective carrier concentration in the p-type ZnMgSSe cladding layer was evaluated as ${\sim}2.8{\times}10^{16}\;cm^{-3}$ for the present LEDs.