For microstructural analysis of a friction stir welded (FSWed) joint of advanced high-strength steels, dual phase (DP) and complex phase (CP) steels, are studied. FSWed joints are successfully fabricated in the following four cases: (i) DP/DP; (ii) CP/CP; (iii) DP/CP, where the advancing side is DP and the retreating side is CP; (iv) CP/DP, where the advancing side is CP and the retreating side is DP. The stir zone (SZ) of (i) the DP/DP joint mainly consists of lath martensite, while the stir zone of (ii) the CP/CP joint consists not only of lath martensite but also of bainite. In the case of (iii) DP/CP and (iv) CP/DP, they exhibit a similar microstructure including acicular-shaped phases in the joints; however, cross-sections of the joints show differences in material mixing in each case. In (iv) the CP/DP joint, temperature towards the CP steel is sufficient to cause softening, thus leading to better mixing than that in (iii) DP/CP. The phases of the SZ in each of the four cases are formed by phase transformation during the FSWed process; however, the transformed phase volume fraction of CP steel is lower than that of DP steel, indicating that dynamic recrystallization occurs mainly in CP steel. The hardness values of the SZ are significantly higher than those of the base materials, especially, the SZ of (iii) the DP/CP joint has the highest value due to highest fraction of lath martensite.

• Journal of Welding and Joining
• /
• v.35 no.3
• /
• pp.44-51
• /
• 2017

In the present study, AA 5083-O plates are joined by friction stir welding technique. A universal milling machine was used to perform the welding process of the work-pieces which were fixed on the proper position by a vice. The joints were friction stir welded by two tools with different pin profiles; cylindrical threaded pin and tapered smooth one at different rotational speed values; 400 rpm and 630 rpm, and different welding speed values; 100 mm/min and 160 mm/min. During FSW of each joint, the temperature was measured by infra-red thermal image camera. The welded joints were inspected by visually as well as by the macro- and microstructure evolutions. Furthermore, the joints were tested for measuring the hardness and the tensile strength to study the effect of changing the FSW parameters on the mechanical properties. The results show that increasing the rotational speed results in increasing the peak temperature, while increasing the welding speed results in decreasing the peak temperature for the same tool pin profile. Defect free welds were obtained at lower rotational speed by the threaded tool profile. Moreover, the threaded tool pin profile gives superior mechanical properties at lower rotational speed.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.6
• /
• pp.294-300
• /
• 2009

The Friction Stir Welding (FSW) has mainly been used for making butt joints in Al alloys. The development of Friction Stir Lap Welding (FSLW) would expand the number of applications. In this study, for effective application on thin aluminum alloy lap joint, non-heat treatment A5052 alloys were joined by FSLW with the length of probe 2.3 mm and 3.0 mm. Investigating the characteristics of joint area showed the results were as below ; When the length of probe was 2.3 mm, good joint area was formed at all welding condition except for 600 rpm-700 mm/min. In the case of 3.0 mm probe length, there was formed good joint area without defects at 1500 rpm-100 mm/min. The width of joint area, position and size of defects were very important factors for FSLW, due to heat input and stirring intensity.

• Korean Journal of Metals and Materials
• /
• v.48 no.6
• /
• pp.533-542
• /
• 2010

The specific motivation for joining an Al alloy and Zn-coated steel arises from the need to save fuel consumption by weight reduction and to enhance the durability of vehicle structures in the automobile industry. In this study, the lap joining A6K31 Al alloy (top) and SGARC340 Zn-coated steel (bottom) sheets with a thickness of 1.0 mm and 0.8 mm, respectively, was carried out using the friction stir weld (FSW) technique. The probe of a tool did not contact the surface of the lower Zn-coated steel sheet. The friction stir welding was carried out at rotation speeds of 1500 rpm and travel speeds of 80~200 mm/min. The effects of tool geometry and welding speed on the mechanical properties and the structure of a joint were investigated. The tensile properties for the joints welded with a larger tool were better than those for the joints done with a smaller tool. A good correlation between the tensile load and area of the welded region were observed. The bond strength using a larger tool (M4 and M3) decreased with an increase in welding speed. Most fractures occurred along the interface between the Zn-coated steel and the Al alloy. However, in certain conditions with a lower welding speed, fractures occurred at the A6K31 Al alloy.

• Advances in nano research
• /
• v.14 no.2
• /
• pp.117-126
• /
• 2023

This experimental study investigated friction stir welding (FSW) of the acrylonitrile-butadiene-styrene (ABS) T-joint in the presence of various nano-silica levels. This study aim to handle the drawbacks of the friction stir welding (FSW) of an ABS T-joint with various quantity of nanoparticles and assess the performance of nanoparticles in the welded joint. Moreover, the relationship between the nanoparticle quantity and FSW was analyzed using response surface methodology (RSM) Box-Behnken design. The input parameters were the tool rotation speed (400, 600, 800 rpm), the transverse speed (20, 30, 40 mm/min), and the nano-silica level (0.8, 1.6, 2.4 g). The tensile strength of the prepared specimens was determined by the universal testing machine. Silica nanoparticles were used to improve the mechanical properties (the tensile strength) of ABS and investigate the effect of various FSW parameters on the ABS T-joint. The results of Box-Behnken RSM revealed that sound joints with desired characteristics and efficiency are fabricated at tool rotation speed 755 rpm, transverse speed 20 mm/min, and nano-silica level 2.4 g. The scanning electron microscope (SEM) images revealed the crucial role of silica nanoparticles in reinforcing the ABS T-joint. The SEM images also indicated a decrease in the nanoparticle size by the tool rotation, leading to the filling and improvement of seams formed during FSW of the ABS T-joint.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.1
• /
• pp.85-90
• /
• 2010

Friction welding is a common practice to join axially symmetrical parts for automobile industry applications. The shaft for automobile reverse idle gear is generally produced by forging steel, SF 45. This method is not so good because of high cost of material and production. In this study, in order to investigate the possibility of application of SM 45C to SF 45 dissimilar friction welding, the dissimilar friction welded joints were performed using 20 mm diameter solid bar in forging steel(SF 45) to carbon steel(SM 45C). The optimal friction welding parameters were selected to ensure reliable quality welds on the basis of visual examination, tensile test, micro-Virkers hardness surveys of the bond of area and optical microstructure investigations for welded joint parts. Finally, post weld heat treatment(PWHT) of the high-frequency induction hardening was performed for the friction welded specimens under the optimal welding conditions. And then, the mechanical properties were compared for as-welded and PWHT in SM 45C to SF 45.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.10a
• /
• pp.234-243
• /
• 1998

In this paper, thermite and gas pressure weldings have been used to join rails in-track and analyzed as functions of hardness and wear characteristics. The wear rate of thermite welded rail is low compared with that of gas pressure welded rail, which is tested in a pin-on-disk wear tester. The hardness of thermite welded materials is relatively high and narrow distributed between three zones, welded part, thermally affected zone, and a base matrix. Wear of a welded rail may be a major factor in railroad maintenance costs and failures at the rail-rail butt joint.

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1747-1751
• /
• 2003

The paper shows properties such as vickers hardness, yielding and ultimate stresses for the weld zone of the butt and the lap jointed specimens, and compare maximum loads, stress-strain curves, deformation appearance after guided bending test and fracture appearance for butt and lap jointed specimens. The research in this experiment also shows the weldability of the butt joint specimen is better than that of the lap joint specimen using FSW with $2mm^{t}$ aluminum alloy sheet in milling machine.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2003.10a
• /
• pp.158-162
• /
• 2003

A study on friction welding of chrome molybedenum steel(SCM440) to carbon steel(S45C) is examined experimentally through tensile test, hardness test. So, this paper deals with optimizing the welding conditions and analyzing various mechanical properties about friction welds of SCM440 to S45C steel. The tensile strength of the friction welded joint was increased up to 100% of the S45C base matal under the condition of all heating time. Optimal welding conditions were n=2,000(rpm), $P_{1}=60(MPa)$, $P_{2}=100(MPa)$, $t_{1}=4(s)$, $t_{2}=5(s)$ when the total upset length is 5.7(mm).