• The Journal of the Korea Contents Association
• /
• v.19 no.4
• /
• pp.359-367
• /
• 2019

For this study, specimens were prepared using five types of composite resin and resin-reinforced glass ionomer Fuji II LC, and 29 days precipitation was done in four kinds of solution, which were soy sauce, gochujang, wine, and distilled water. Ten specimens for each coloring sample were divided into two groups, one those surfaces was polyester film and the other with 1200-grit abrasive paper, and 20 specimens per materials. Color change (${\Delta}{\ast}ab$) in the colored specimens is measured in 2days, 7days, 14days and 29days using spectrophotometer (CM-2600d, Konica, Minolta, Ramsey, NJ). All values were considered significant when P<0.05. 1. Each material is discolored over time under the influence of different storage solutions. 2. In soy source, among the specimens polished with polyester film, color change was observed in resin-modified glass ionomer Fuji II LC, prodigy and compomer F-2000 on day 2. Meanwhile, Fuji II LC showed noticeable color change in specimens prepared with 1200-grit sandpaper on day 2, which was followed by flowable resin on day 7. 3. On day 2, there was a color change with the specimens of flowable resin, resin-modified glass ionomer Fuji II LC and Prodigy among the hybrid specimen in the groups of polyester film in gochujang.

• Restorative Dentistry and Endodontics
• /
• v.27 no.2
• /
• pp.142-149
• /
• 2002

Low-viscosity composite resins may produce better sealed margins than stiffer compositions (KempScholte and Davidson, 1988: Crim, 1989). Plowable composites have been recommended for use in Class V cavities but it is also controversial because of its high rates of shrinkage. On the other hand, in the study comparing elastic moduli and leakage, the microfill had the least leakage (Rundle et at. 1997) Furthermore, in the 1996 survey of the Reality Editorial Team, microfills were the clear choice for abfraction lesions. The purpose of this study was to evaluate the microleakage of 6 compostite resins (2 hybrids, 2 microfills, and 2 flowable composites) with and without load cycling. Notch-shaped Class V cavities were prepared on buccal surface of 180 extracted human upper premolars on cementum margin. The teeth were randomly divided into non-load cycling group (group 1) and load cycling group (group 2) of 90 teeth each. The experimental teeth of each group were randomly divided into 6 subgroups of 15 samples. All preparations were etched, and Single bond was applied. Preparations were restored with the following materials (n=15) : hybrid composite resin [Z250(3M Dental Products Inc. St. Paul, USA), Denfil(Vericom, Ahnyang, Korea)], microfill [Heliomolar RO(Vivadent, Schaan, Liechtenstein), Micronew(Bisco Inc. Schaumburg, IL, USA)], and flowable composite［AeliteFlo(Bisco Inc. Schaumburg, IL, USA), Revolution(Kerr Corp. Orange, CA, USA)]. Teeth of group 2 were subjected to occlusal load (100N for 50,000 cycles) using chewing simulator(MTS 858 Mini Bionix II system, MTS Systems Corp. Minn. USA). All samples were coated with nail polish 1mm short of the restoration, placed in 2％ methylene blue for 24 hours, and sectioned with a diamond wheel. Enamel and dentin/cementum margins were analyzed for microleakage on a sclale of 0 (no leakage) to 3 (3/3 of wall). Results were statistically analyzed by Kruscal-Wallis One way analysis, Mann-Whitney U-test, and Student-Newmann-Keuls method. (p = 0.05) Results : 1. There was significantly less microleage in enamel margins than dentinal margins of all groups (p＜0.05) 2. There was no significant between six composite resin in enamel margin of group 1. 3. In dentin margin of group 1, flowable composite had more microleakage than others but not of significant differences. 4. there was no significant difference between six composite resin in enamel margin of group 2. 5. In dentin margin of group 2, the microleakage were R＞A =H=M＞D＞Z. But there was no significant differences. 6. In enamel margins, load cycling did not affect the marginal microleakage in significant degree. 7. In enamel margins, load cycling did affect the marginal microleakage only in Revolution. (p＜0.05).

• Journal of Korean Society for Quality Management
• /
• v.45 no.4
• /
• pp.995-1002
• /
• 2017

Purpose: The purpose of this study was to evaluate the color stability of composite resins used for splinting teeth by comparing a self-cure resin cement (Superbond C&B, SB), a flowable composite resin (G-aenial Universal Flo A2, GU), and a composite resin exclusively used for splinting teeth (G-Fix, GF) before and after aging in NaOCl. Methods: Resin samples were fabricated to a size of 2 mm thickness and 8.5 mm diameter and light-cured with an LED light curing unit (G-Light, n = 12). Immediately after fabrication, CIE L*a*b* values of the resin samples were measured with a spectrophotometer (CM-5) as baseline. Then, the resin samples were immersed in 5% NaOCl at $60^{\circ}C$ and the color was measured after 23 hours every day for 4 days. Data were analyzed with one-way ANOVA followed by Duncan post hoc test (p<0.05), and color differences (${\Delta}E$) of resin samples before and after NaOCl aging were also calculated. Results: For SB, there were no changes in L* and a* values but changes were observed in b* values. For GU, there were no changes in L* and b* values but in a* values. For GF, changes were observed in L*, a*, and b* values. All resin samples showed highest ${\Delta}E$ between baseline and the 1st day of NaOCl immersion. ${\Delta}E$ of SB, GU, and GF was 4.6 - 5.8, 4.9 - 7.9, and 9.9 - 16.9, respectively. GF showed highest color change during NaOCl aging. Conclusion: The results of this color quality evaluation showed that the composite resin exclusively used for splinting teeth might be more vulnerable to color change during intraoral service.

• The korean journal of orthodontics
• /
• v.49 no.2
• /
• pp.116-123
• /
• 2019

As an alternative to the conventional fixed appliance that uses orthodontic brackets, a simple round tube without a bonding base can be bonded to the tooth surface by covering the tube with flowable resin. In this technique, bent wires cannot be inserted into the simple tubes; therefore, repositioning of the simple tubes is often required for adjustments. To reduce repositioning of simple tubes, a dome-shaped resin covering of the simple tube can be designed with a customized in-and-out compensation, using three-dimensional computer-aided design software based on digital simulation of orthodontic tooth movement. In the present case, the use of simple tubes bonded with customized resin coverings in a Class I nonextraction case is described in a 17-year-old male, in whom moderate crowding of the anterior teeth was treated over an 8-month period. This case shows that simple tubes can be used as an alternative to brackets in some Class I nonextraction cases, with the potential benefit of reducing decalcification.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.49 no.1
• /
• pp.104-112
• /
• 2022

The purpose of this study is to analyze the fracture resistance of reattached tooth according to the resin materials and tooth preparation type under physiological conditions. Uncomplicated crown fracture in the oblique direction was reproduced on the extracted 64 anterior teeth. Depending on the composite resin material, reattachment was performed using a flowable resin and a packable resin. Depending on retentive forms, reattachment was performed using simple reattachment, 1.0 mm × 1.0 mm labial chamfer bevel, 1.0 mm × 1.0 mm lingual chamfer bevel and 1.0 mm × 1.0 mm circumferential bevel. A load was applied to the palatal surface of the tooth using a universal testing machine at an angle of 125 degree, which is the interincisal angle of normal children. Under the masticatory pressure condition, fracture resistance of lingual chamfer groups was 28.28 ± 7.41 MPa and 27.54 ± 4.45 MPa, which was significantly higher than those of simple reattachment groups, 17.21 ± 5.87 MPa and 20.10 ± 6.00 MPa, in both flowable and packable resin groups. When considering the lingual force similar to masticatory pressure, the fragment retention was significantly improved when the lingual chamfer was formed compared to the simple reattachment. Clinicians may consider the design of the lingual chamfer in order to improve fracture resistance to masticatory pressure during fragment reattachment.

• Restorative Dentistry and Endodontics
• /
• v.41 no.3
• /
• pp.159-166
• /
• 2016

The purpose of this review was to suggest practical criteria for the clinical translucency evaluation of direct esthetic restorative materials, and to review the translucency with these criteria. For the evaluation of reported translucency values, measuring instrument and method, specimen thickness, background color, and illumination should be scrutinized. Translucency parameter (TP) of 15 to 19 could be regarded as the translucency of 1 mm thick human enamel. Visual perceptibility threshold for translucency difference in contrast ratio (${\Delta}CR$) of 0.07 could be transformed into ${\Delta}TP$ value of 2. Translucency differences between direct and indirect resin composites were perceivable (${\Delta}TP>2$). Universal and corresponding flowable resin composites did not show perceivable translucency differences in most products. Translucency differed significantly by the product within each shade group, and by the shade group within each product. Translucency of human enamel and perceptibility threshold for translucency difference may be used as criteria for the clinical evaluation of translucency of esthetic restorative materials.

• Journal of dental hygiene science
• /
• v.13 no.3
• /
• pp.330-338
• /
• 2013

In order to explore microleakage in class V cavity based on different kinds of several dentin adhesive and composite resin, 2 kinds of composite resin was restored and exposed after applying 4 kinds of dentin adhesives. Deposited in methylene blue solution for 4 hours and cut in parallel with tooth longitudinal axis. By observing dye penetration level of enamel and dentin margins of each restored resin following conclusion was obtained. 1. In composite resin Filtek Z350XT Universal (3M/ESPE Dental Products, USA) in enamel margin, Easy Bond (3M/ESPE Dental Products) showed the lowest microleakage and this leakage was represented to be high in the order of Single Bond 2 (3M/ESPE Dental Products), Scotchbond Multi-Purpose (3M/ESPE Dental Products) and Cearfil SE Bond (Kuraray Medical Inc., Japan). In case of Filtek Z350XT Flowable (3M/ESPE Dental Products), Scotchbond Multi-Purpose showed the lowest microleakage and this leakage was represented to be high in the order of Single Bond 2, Clearfil SE Bond and Easy Bond. 2. In case of Filtek Z350XT Universal in dentin margin, Easy Bond showed the lowest microleakage and this leakage was represented to be high in the order of Scotchbond Multi-Purpose, Single Bond 2 and Clearfil SE Bond. In case of Filtek Z350XT Flowable, Scotchbond Multi-Purpose and Single Bond showed the lowest microleakage and this leakage was represented to be high in the order of Clearfil SE Bond and Easy Bond. 3. In all the groups excepting S-U group (Single Bond 2+Filtek Z350XT Universal), enamel margin showed more higher microleakage than that of dentin margin. 4. There was a difference between enamel and dentin margin among each group but it was not significant statistically (p>0.05). When summarizing this result, it is considered that composite resin and dentin adhesive could be applied selectively and particularly in case of applying 1-step self-etching dentin adhesive, this method would be advantageous for manipulation convenience and shortening of operation time.

• Restorative Dentistry and Endodontics
• /
• v.27 no.4
• /
• pp.394-402
• /
• 2002

2급 복합레진 수복 와동의 치은 변연이 상아질 상에 있을 때 유동성 레진 이장의 유무와 두께가 미세누출에 미치는 영향을 알아보기 위해 본 실험을 시행하였다. 60개의 발거된 대구치의 근, 원심면에 각각 협설측 3mm, 치은벽 깊이 1mm의 2급 와동을 형성하고 치은 변연은 법랑-백아 경계에서 약 1mm 하방에 위치 시켰다. 모든 와동을 32% 인산으로 15초 처리 및 30초 수세 후 Prime & Bond$^{\circledR}$ NT 상아질 접착제를 적용하였고, Tetric Ceram(TC), Tetric Flow(TF)를 이용하여 다음의 6가지 군으로 나누어 수복하였다. (1) TC로 수평 적층 충전, (2) TC로 수직 적층 충전, (3) 0.5-1mm두께로 TF 이장 후 TC로 수평적층 충전, (4) 0.5-1mm 두께로 TF 이장 후 TC로 수직 적층 충전, (5) 2-3mm 두께로 TF 이장 후 TC로 수평적층 충전, (6) 2-3mm두께로 TF이장 후 TC로 수직 적층 충전. 충전된 시편을 37$^{\circ}C$ 100% humidity에서 24시간 보관하고 5$^{\circ}C$와 55$^{\circ}C$에서 500회의 열순환을 실시하여 치은 변연의 0.5mm 외부에 nail varnish를 도포 하여 2% methylene blue 용액에 12시간 침잠시켰다. 시편을 아크릴릭 레진에 매몰하여 수복물의 중앙에서 종절단 한 후 입체현미경하에서 색소의 침투도를 관찰하여 다음과 같은 결과를 얻었다. 유동성 레진의 이장을 시행한 군과 하지 않은 군간에 미세누출은 유의차를 보이지 않았다(p>0.05) 유동성 레진의 두께에 따른 미세누출의 차이는 나타나지 않았다(p>0.05) 경사면 충전법을 시행한 군에서는 유동성 레진을 이장한 군들이 이장하지 않은 군보다 유의하게 많은 누출을 보였다(p<0.05). 수평적층 충전법을 시행한 군에서는 유동성 레진 이장이 미세누출에 유의한 차이를 보이지 않았다(p>0.05).

• Restorative Dentistry and Endodontics
• /
• v.34 no.6
• /
• pp.477-483
• /
• 2009

The purpose of this study was to compare the microleakage of low and high viscosity flowable resins in class V cavities applied with 1-step adhesives. Forty Class V cavities were prepared on the cervices of buccal and lingual surfaces of extracted molar teeth and divided into four groups (n=8). Cavities were restored with AQ Bond Plus /Metafil Flo $\alpha$, G-Bond/ UniFil LoFlo Plus (Low flow groups), AQ Bond Plus/Metafil Flo and G-Bond/UniFil Flow (High flow group), respectively. Specimens were immersed in a 2% methylene blue solution for 24 hours, and bisected longitudinally. They were observed microleakages at the enamel and dentinal margins. In conclusion, the low viscosity flowable resins showed lower marginal microleakage than do the high vis cosity flowable resins in class V cavities.

• Restorative Dentistry and Endodontics
• /
• v.32 no.1
• /
• pp.69-79
• /
• 2007

The purpose of this study was to investigate the effects of composite resin restorations on the stress distribution of notch shaped noncarious cervical lesion using three-dimensional (3D) finite element analysis (FEA). Extracted maxillary second premolar was scanned serially with Micro-CT (SkyScan1072 ; SkyScan, Aartselaar, Belgium). The 3D images were processed by 3D-DOCTOR (Able Software Co., Lexington, MA, USA). ANSYS (Swanson Analysis Systems, Inc., Houston, USA) was used to mesh and analyze 3D FE model. Notch shaped cavity was filled with hybrid or flowable resin and each restoration was simulated with adhesive layer thickness ($40{\mu}m$) A static load of 500 N was applied on a point load condition at buccal cusp (loading A) and palatal cusp (loading B). The principal stresses in the lesion apex (internal line angle of cavity) and middle vertical wall were analyzed using ANSYS. The results were as follows 1. Under loading A, compressive stress is created in the unrestored and restored cavity. Under loading B, tensile stress is created. And the peak stress concentration is seen at near mesial corner of the cavity under each load condition. 2. Compared to the unrestored cavity, the principal stresses at the cemeto-enamel junction (CEJ) and internal line angle of the cavity were more reduced in the restored cavity on both load con ditions. 3. In teeth restored with hybrid composite, the principal stresses at the CEJ and internal line angle of the cavity were more reduced than flowable resin.