• Korean Journal of Materials Research
• /
• v.22 no.1
• /
• pp.46-53
• /
• 2012

In this study, mechanical tests and microstructural analyses including TEM analyses with EDX of precipitates in modified 9Cr-1Mo steel were carried out to determine the cause of embrittlement observed after heat-treatment, which limits the usage of the alloy for power plants. Mod. 9Cr-1Mo steel specimens at austenite temperature were quenched to the molten salt baths at $760^{\circ}C$ and $700^{\circ}C$, in which the specimens were kept for 10 min ~ 10 hr with subsequent air-cooling. Impact tests showed that the impact value dropped abruptly when the specimens were kept longer than 30 min at $\sim760^{\circ}C$ reaching to minima in about 1 hr, and then increasing at further retention. The tensile strength of the specimens reached the minimum value without much change afterward, whereas the values of elongation showed the same trend as that of the impact value. The isothermally heat-treated steel at $700^{\circ}C$ also showed a minimum impact value in about 1 hr. These results suggest that the isothermal heattreatment at 760 and $700^{\circ}C$ for about 1 hr induces temporal embrittlement in Mod. 9Cr-1Mo steel. The microstructural examination of all the specimens with extraction replica of the carbides revealed that the specimens with temporal embrittlement had $Cr_2C$, indicating that the cause of the embrittlement was the precipitation of the $Cr_2C$. In addition, TEM/EDX results showed that the Fe/Cr ratio was 0.033 to 0.055 for $Cr_2C$, whereas it was 0.48 to 0.75 for $Cr_{23}C_6$, making the distinction of the $Cr_2C$ and $Cr_{23}C_6$ possible even without direct electron diffraction analyses.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.3
• /
• pp.158-165
• /
• 1994

Cu-Cr alloy thin film requires good quality of etching be used for TAB technology. The etched cross sec-tion was clean enough when the etching was performed in 0.1M $FeCl_3$ solution at $50^{\circ}C$. The etching rate was increased with the amount of $KMnO_4$. For enhanced profile of cross section and rate, the spray etchning was found to be superior compared to the immersion etching. A series of experiments were performed to improve the uniformity of the current distribution in electrodeposition onto the substrate with lithographic patterns. Copper was electrodeposited from quiescent-solution, paddle-agitated-solution, and air-bubbled-solution to in-vestigate the effect of the fluid flow. The thickness profile of the specimen measured by profilmetry has the non uniformity at feature scale in quiescent-solution, because of the longitudinal vortex roll caused by the natural convection. However, uniform thickness profile was achieved in paddle-agitated or air bubbled solu-tion.

• Journal of Ocean Engineering and Technology
• /
• v.22 no.6
• /
• pp.46-51
• /
• 2008

The effect of the addition of Co and N and subzero treatment on tensile strength and damping capacity was investigated in Fe-Cr-Mn alloy. Austenite was transformed into martensite by cold rollins increasing the degree of cold rollins led to an increase in the volume fraction of martensite. The damping capacity linearly increased with increasing volume fraction of ${\varepsilon}$ martensite in cold rolled specimens and subzero treated specimens after cold rolling. The volume fraction of ${\varepsilon}$ martensite, tensile strength and damping capacity was also increased by the addition of Co, while this treatment decreased the elongation. However, the volume fraction of ${\varepsilon}$ martensite, elongation and damping capacity were reduced by the addition of N, although the tensile strength increased. Tensile strength and damping capacity werealso increased by subzero treatment, while elongation decreased.

• Journal of Advanced Marine Engineering and Technology
• /
• v.23 no.3
• /
• pp.360-368
• /
• 1999

The paper describes spectroscopic characteristics of plasma induced in the pulsed YAG laser welding of alloys containing a large amount of volatile elements. The authors have conducted the spectroscopic analyses of laser induced Al-Mg alloys plasma in the air and argon atmosphere. In the air environment the identified spectra were atomic lines of Al, Mg, Cr, Mn, Cu, Fe and Zn and singly ionized Mg lines as well as the intense molecular spectra of ALO and MgO formed by chemi-cal reactions of evaporated Al and Mg atoms from the pool surface with oxygen in the air. In argon atmosphere MgO and AlO spectra vanished but AlH spectrum was detected. the hydrogen source was presumable hydrogen dissolved in the base metals water absorbed on the surface oxide layer or $H_2$ and $H_2O$ in the shielding gas. The resonant lines of Al and Mg were strongly self-absorbed in particular self-absorption of the Mg line was predominant. These results show that the laser induced plasma was made of metallic vapor with relatively low temperature and high density.

• Journal of the Korean institute of surface engineering
• /
• v.24 no.1
• /
• pp.31-41
• /
• 1991

The nodular corrosion behavior of Zircaloy-4 alloy was investigated by autoclave test at 50$0^{\circ}C$ under 1500 psi for the specimens quenched into water from $700^{\circ}C$, 80$0^{\circ}C$, 90$0^{\circ}C$, and 105$0^{\circ}C$. It was observed that the corrosion resistance of Zircalloy-4 specimen increased with increase in annealing temperature, and annealing at $\alpha$-region temperatures resulted in nodular corrosion while annealing at the temperature range of $\alpha$+$\beta$ and $\beta$ did not show nodular corrosion. It was also found that the size of nodule formed on the surface of the specimens increased with increase in exposure time in autoclave, but the total number of nodule remained uncha-nged. The corrosion of furnace-cooled specimens progressed mostly in the interior of grains where Fe and Cr alloying elements were largely depleted during the cooling process. However, the grain boundary seemed to act as a barrier to the nodular corrosion. From combining the present results with other works, it is suggested that the nodules nuc-leate in the local region where some of alloying elements are depleted.

• Journal of the Korean Society for Heat Treatment
• /
• v.10 no.3
• /
• pp.198-208
• /
• 1997

The-steady-state creep mechanism and behavior of Zircaloy-4 used as cladding materials in PWR have been investigated in air environment over the temp, ranges from 600 to $645^{\circ}C$ and stress ranges from 4 to $7kg/mm^2$. The stress exponents for the creep deformation of this alloy, n were decreased 4.81, 4.71, 4.64, and 4.56 at 600, 615, 630 and $645^{\circ}C$, respectively; the stress exponents decreased with increasing the temperature and got closer to about 5. The apparent activation energies, Q, were 62.1, 60.0, 57.9 and 55.4 kcal/mole at stresses of 4, 5, 6, $7kg/mm^2$, respectively; the activation energies decreased with increasing the stress and were close to those of volume self diffusion of Zr in Zr-Sn-Fe-Cr system. In results, it can be considered that the creep deformation for Zircaloy-4 was controlled by the dislocation climb over the ranges of this experimental conditions. Larson-Miller parameter, P, for the crept specimens was obtained as P=(T+460)(logt,+23). The failure plane observed by SEM slightly showed up intergranular fracture at this experiment ranges. However, it was essentially dominated by the dimple phenomenon, which was a characteristics of the transgranular fracture.

• Journal of Korea Foundry Society
• /
• v.23 no.5
• /
• pp.244-250
• /
• 2003

The aim of this study is fabricating of composite filler metal (CFM) by a combination of selective laser sintering (SLS) of stainless steel powders (RapidSteel $2.0^{TM}$ and liquid phase infiltration of Ag-28 wt.%Cu alloy. Porous stainless steel body with inter-connected pore channels was fabricated by SLS, binder decomposing and densification processes. By the direct contact infiltration, the narrow inter-particle channels of the porous body were completely filled with the Ag-28 wt.%Cu alloy infiltrant. During infiltration, the dissolved elements of Fe, Ni and Cr from the porous body were solved into copper solid solution phases, which consist of eutectic structure of composite metal matrix. The S10C/CFM/S10C joints, which have narrow clearance gaps between them up to 10 micrometers, were joined successfully by self-feeding of filler metal from the matrix of CFM. The CFM kept its original thickness and microstructure after brazing. The tensile strength of brazed specimen was higher than 30 kgf/$mm^2$ and showed a typical ductile fracture mode in the CFM.

• Nuclear Engineering and Technology
• /
• v.51 no.4
• /
• pp.1069-1074
• /
• 2019

A novel fabrication method of oxide dispersion strengthened (ODS) steel cladding tubes for advanced fast reactors has been investigated using the cold spray powder-based materials deposition process. Cold spraying has the potential advantage for rapidly fabricating ODS cladding tubes in comparison with the conventional multi-step extrusion process. A gas atomized spherical 14YWT (Fe-14%Cr, 3%W, 0.4%Ti, 0.2% Y, 0.01%O) powder was sprayed on a rotating cylindrical 6061-T6 aluminum mandrel using nitrogen as the propellant gas. The powder lacked the oxygen content needed to precipitate the nanoclusters in ODS steel, therefore this work was intended to serve as a proof-of-concept study to demonstrate that free-standing steel cladding tubes with prototypical ODS composition could be manufactured using the cold spray process. The spray process produced an approximately 1-mm thick, dense 14YWT deposit on the aluminum-alloy tube. After surface polishing of the 14YWT deposit to obtain desired cladding thickness and surface roughness, the aluminum-alloy mandrel was dissolved in an alkaline medium to leave behind a free-standing ODS tube. The as-fabricated cladding tube was annealed at $1000^{\circ}C$ for 1 h in an argon atmosphere to improve the overall mechanical properties of the cladding.

• Journal of Powder Materials
• /
• v.18 no.5
• /
• pp.430-436
• /
• 2011

Joining of NiO-YSZ to 316 stainless steel was carried out with B-Ni2 brazing alloy (3 wt% Fe, 4.5 wt% Si, 3.2 wt% B, 7 wt% Cr, Ni-balance, m.p. 971-$999^{\circ}C$) to seal the NiO-YSZ anode/316 stainless steel interconnect structure in a SOFC. In the present research, interfacial (chemical) reactions during brazing at the NiO-YSZ/316 stainless steel interconnect were enhanced by the two processing methods, a) addition of an electroless nickel plate to NiO-YSZ as a coating or b) deposition of titanium layer onto NiO-YSZ by magnetron plasma sputtering method, with process variables and procedures optimized during the pre-processing. Brazing was performed in a cold-wall vacuum furnace at $1080^{\circ}C$. Post-brazing interfacial morphologies between NiO-YSZ and 316 stainless steel were examined by SEM and EDS methods. The results indicate that B-Ni2 brazing filler alloy was fused fully during brazing and continuous interfacial layer formation depended on the method of pre-coating NiO-YSZ. The inter-diffusion of elements was promoted by titanium-deposition: the diffusion reaction thickness of the interfacial area was reduced to less than 5 ${\mu}m$ compared to 100 ${\mu}m$ for electroless nickel-deposited NiO-YSZ cermet.

• Korean Journal of Metals and Materials
• /
• v.47 no.8
• /
• pp.482-487
• /
• 2009

In order to investigate the effects of intermediate heat treatment between cold rolling passes on the hardness and corrosion properties of a Zr alloy incorporating Nb (Zr-1.49Nb-0.38Sn-0.20Fe-0.11Cr) strip, three different intermediate heat treatment processes ($580^{\circ}C{\times}4hrs$, $600^{\circ}C{\times}2hrs$ and $620^{\circ}{\times}1hrs$) were designed based on a recrystallization map and an accumulated annealing parameter. Test samples from the different processes were investigated by a hardness test, corrosion test, and microstructure analysis and appropriate heat-treatment conditions were thereupon proposed. The sample subjected to an intermediate heat treatment of $580^{\circ}C{\times}4hrs$ was harder than that undergoing $600^{\circ}C{\times}2hrs$ and $620^{\circ}C{\times}1hr$ while the corrosion resistance of the sample that received an intermediate heat treatment of $580^{\circ}C{\times}4hrs$ was superior to that of the other specimens. Considering the trade-off of hardness and corrosion resistance, an intermediate heat treatment process of $600^{\circ}C{\times}2hrs$ is proposed to improve the manufacturing process of the alloy strip.