• Restorative Dentistry and Endodontics
• /
• 제40권1호
• /
• pp.68-74
• /
• 2015

Objectives: This study examined the effects of additional acid etching on the dentin bond strength of one-step self-etch adhesives with different compositions and pH. The effect of ethanol wetting on etched dentin bond strength of self-etch adhesives was also evaluated. Materials and Methods: Forty-two human permanent molars were classified into 21 groups according to the adhesive types (Clearfil SE Bond [SE, control]; G-aenial Bond [GB]; Xeno V [XV]; Beauti Bond [BB]; Adper Easy Bond [AE]; Single Bond Universal [SU]; All Bond Universal [AU]), and the dentin conditioning methods. Composite resins were placed on the dentin surfaces, and the teeth were sectioned. The microtensile bond strength was measured, and the failure mode of the fractured specimens was examined. The data were analyzed statistically using two-way ANOVA and Duncan's post hoc test. Results: In GB, XV and SE ($pH{\leq}2$), the bond strength was decreased significantly when the dentin was etched (p < 0.05). In BB, AE and SU (pH 2.4 - 2.7), additional etching did not affect the bond strength (p > 0.05). In AU (pH = 3.2), additional etching increased the bond strength significantly (p < 0.05). When adhesives were applied to the acid etched dentin with ethanol-wet bonding, the bond strength was significantly higher than that of the no ethanol-wet bonding groups, and the incidence of cohesive failure was increased. Conclusions: The effect of additional acid etching on the dentin bond strength was influenced by the pH of one-step self-etch adhesives. Ethanol wetting on etched dentin could create a stronger bonding performance of one-step self-etch adhesives for acid etched dentin.

• 구강회복응용과학지
• /
• 제29권1호
• /
• pp.37-44
• /
• 2013

근관치료 후 적절한 치관부 밀폐를 위해 레진을 이용한 코어수복방법이 현재 많이 사용되고 있다. 하지만, 근관치료 과정에서 사용되는 NaOCl이나 EDTA같은 근관세척제는 레진 접착에 영향을 주는 것으로 알려져 있으며, 이에 관한 많은 연구들이 이루어져 왔다. 본 연구에서는 ethanol wet bonding을 치수강 상아질에 적용 시에 NaOCl과 EDTA가 결합강도에 미치는 영향에 대해 조사하였다. 30개의 인간 대구치로부터 총 60개의 시편을 얻었고, 이를 무작위로 4개의 군으로 분류했다. G1: 증류수로 세척후 증류수로 마무리 세척, G2: NaOCl로 세척 후 NaOCl로 마무리세척, G3: NaOCl로 세척 후 EDTA로 마무리세척, G4: NaOCl로 세척 후 EDTA로 마무리세척하고 접착과정에서 산부식과정 생략. 접착과정은 인산부식 후 에탄올의 농도를 50%, 70%, 80%, 95% 그리고 100%로 순차적으로 증가시켜가면서 상아질을 탈수시키고 에탄올에 적셔지도록 하였다. 프라이머는 HEMA가 포함되지 않은 상용화된 접착제인 ALL-BOND 3 RESIN과 에탄올을 반반씩 섞어 만들었다. 프라이머 적용 후 ALL-BOND 3 RESIN을 접착제로 사용하였다. 저점도 복합레진을 이용하여 6mm 두께로 적층충전한 후 빔 형태로 잘라 미세인장결합강도 실험을 하였다. NaOCl 처리한 그룹은 미세인장결합강도에 통계적으로 유의한 차이를 보여주지는 않았지만 낮은 평균값을 보여주었다(p=0.052). NaOCl 처리 후 1분간 EDTA로 처리한 그룹은 다른 그룹보다 유의하게 높은 결합강도를 보여주었다(p<0.05). EDTA 처리가 결합강도를 향상 시켰지만, 산부식 과정을 생략할 경우 유의하게 낮은 결합 강도를 보여주었으며, 이는 EDTA처리가 산부식 과정을 대신할 수는 없다는 것을 보여준다.

• Restorative Dentistry and Endodontics
• /
• 제37권1호
• /
• pp.2-8
• /
• 2012

The limited durability of resin-dentin bonds severely compromises the longevity of composite resin restorations. Resin-dentin bond degradation might occur via degradation of water-rich and resin sparse collagen matrices by host-derived matrix metalloproteinases (MMPs). This review article provides overview of current knowledge of the role of MMPs in dentin matrix degradation and four experimental strategies for extending the longevity of resin-dentin bonds. They include: (1) the use of broadspectrum inhibitors of MMPs, (2) the use of cross-linking agents for silencing the activities of MMPs, (3) ethanol wet-bonding with hydrophobic resin, (4) biomimetic remineralization of water-filled collagen matrix. A combination of these strategies will be able to overcome the limitations in resin-dentin adhesion.

• Restorative Dentistry and Endodontics
• /
• 제34권1호
• /
• pp.42-50
• /
• 2009

장기적인 상아질 접착의 내구성 악화는 접착층과 혼성충의 친수성 부위에서의 가수분해에 의해 일어나는 것으로 보고 되고 있다. 본 연구의 가설은 콜라겐 망상체를 유기용매로 프라이밍하면 콜라겐 조직을 붕괴시키지 않고 수분을 밀어내고 소수성 단량체와 유기용매로 이루어진 접착제가 침투하여 접착강도를 얻을 수 있다는 것이다. 두 소수성 단량체인 Bisphenol-A-glycidylmethacrylate (Bis-GMA)와 triethyleneglycol dimethacrylate (TEGDMA)를 아세톤, 에탄올 또는 메탄올에 용해시켜 세 가지의 실험용 접착제를 준비하였다. 산 부식과 수세과정 후에, 접착제를 습윤 상아질 표면(습윤 접착)이나 동일한 용매로 프라이밍 된 상아질 표면(용매 프라이밍 접착)에 적용하였다. 48시간 후와 1개월 후, 및 10,000회의 열순환 후에 미세인장결합강도를 측정하였다. 접착계면은 주사전자현미경을 이용하여 관찰하였다. 접착 방법에 무관하게 대부분의 시편의 접착계면에서 잘 발달된 혼성층을 관찰할 수 있었고, 가장 높은 평균 미세인장결합강도는 에탄올을 포함하는 접착제의 48시간 후 시편에서 관찰되었다. 용매를 이용하여 프라이밍하는 접착 방법에서는 에탄올이나 메탄올을 포함하는 접착제에서 열순환 후에 미세인장접착강도가 증가하는 경향을 보였다. 그러나, 습윤 접착의 경우에는 시효처리 후 미세인장결합강도의 증가가 관찰되지 않았다. 본 연구에서 에탄올을 이용한 상아질 프라이밍으로 우수한 접착력을 얻을 수 있었고, 열순환 후 접착력 이 더욱 증가하였다.