• Restorative Dentistry and Endodontics
• /
• 제27권4호
• /
• pp.382-388
• /
• 2002

Compomer is composed of matrix and filler : matrix is made of the combination of resins and polycarboxylic molecules that are light-cured, and a filler is a glass component which is capable of ion-release. The resin content of compomers produces polymerization shrinkage which can adversely affect marginal adaptation. Pretreatment is a fundamental step which is treated with conditioner or primer in the use of these materials. Microleakage of restorative materials has been investigated mostly by dye penetration method. Dye penetration method was not quantitative and not measured repeatedly. Fluid filtration method, introduced and developed by Pashley's group, has been extensively used for 20 years for research purpose to understand the physiology of dentin, as well as the effects of various restorative treatments on dentin permeability. It permits quantitative, nondestructive measurment of microleakage in a longitudinal manner. The purpose of this study was to evaluate the change of dentin permeability according to the process of compomer restoration. In this study. Cl V cavities were prepared on buccal surface of thirty extracted human molars. The prepared cavities were etched by 37% phosphoric acid. The experimental teeth were randomly divided into three groups. Each group was treated with following materials Group 1 : Prime & Bond NT/Dyract AP, Group2： Single Bond/F2000 compomer, Group 3 : Syntac Single Component/Compoglass. The bonding agent and compomer were applied for each group following manufacturers information. Dentin permeability of each group was measured at each process by fluid filtration method; Step 1 : preparation(smear layer). Step 2 : etching(smear layer removal), Step 3 : applying the bonding agent, Step 4 : filling the compomer. Dentin permeability was expressed by hydraulic conductance ($\mu\textrm{l}$ min$^{-1}$cm$H_2O$$^{-1}$). The data were analysed statistically using One-way ANOVA and Sheffe's method. The results were as follows : 1. Dentin permeability differences between each process were significant except between step 1 and step 2(p<0.01). 2. Dentin permeability after removal of smear layer was highly increased(p<0.01). 3. In most case, decrease of dentin permeability was obtained by applying bonding agent(p<0.01). 4. Dentin permeability differences among the experimental groups were not significant(p>0.05). 5. None of compomers used in this study showed perfect seal at the interface.

• 비파괴검사학회지
• /
• 제24권5호
• /
• pp.508-517
• /
• 2004

근접장의 특성과 근접장 마이크로파 현미경의 배경이론을 설명하였고 유전체 공진기 제작에 앞서 HFSS (high frequency structure simulator)를 이용한 모의 시뮬레이션을 기술하였다. 이것을 바탕으로 원통형 유전체 공진기를 제작하여 금속탐침과 결합한 근접장 마이크로파 현미경(near field scanning microwave microscope : NSMM)을 구성하였다. 제작한 유전체 공진기의 특성은 HFSS를 이용하여 모의 실험한 결과와 비교하였다 Tip의 기하학적 모양에 따른 공간분해능과 감도(sensitivity)를 연구하였고 contrast가 가장 좋은 hybrid tip을 개발하였다. 전도도가 서로 다른 금속시료에 따른 NSMM의 반사계수의 변화를 측정하였고 실험결과와 이론적 시료의 임피던스를 비교하였다. 마지막으로 유전체 공진기를 이용한 NSMM으로 공간 분해능이 $1{\mu}m$의 Cr과 NiFe 패턴의 이미지를 비접촉, 비파괴방법으로 얻었다.

• Restorative Dentistry and Endodontics
• /
• 제33권2호
• /
• pp.141-147
• /
• 2008

본 연구의 목적은 나노리터 수준의 물 흐름을 계측할 수 있는 장치를 개발하고, 상아질의 물 투과성을 측정하여 치아과민증 치료제와 상아질 접착제의 상아세관 밀폐효과를 알아보고자 하였다. 본 연구에서 제작한 미세흐름 측정장치는 첫째, 물의 흐름을 감지하는 모세관과 광 센서부, 둘째 물의 흐름을 추적하는 서보모터와 구동부, 셋째, 모터의 회전을 측정하여 물의 이동량으로 변환하는 엔코더와 컴퓨터 기록장치 등 세 부분으로 구성되어 있다. 본 장비를 이용하여 교합 면이 절단되어 노출된 상아질의 물 투과도와 치아과민증 치료제인 BisBlock과 자가부식형 상아질접착제인 Clearfil SE bond의 상아질 밀폐효과를 측정하여 다음과 같은 결과를 얻었다. 1. 나노리터 수준의 물 흐름을 측정할 수 있는 장치를 제작하였고, 이를 이용하여 상아질의 물 투과도를 측정할 수 있었다. 2. 삭제 후 노출 연마된 상아질은 0.84 - 15.2 nL/s의 물 투과도를 보였고 Oxalate 제재인 BisBlock 이나 자가부식형 접착제 Cleafil SE bond 적용 시 투과도가 39.8 - 89.6% 감소하였다.

• JSTS:Journal of Semiconductor Technology and Science
• /
• 제5권3호
• /
• pp.149-158
• /
• 2005

This paper describes design, fabrication, and application of the silicon based temperature controllable micro reactor. In order to achieve fast temperature variation and low energy consumption, reaction chamber of the micro reactor was thermally isolated by etching the highly conductive silicon around the reaction chamber. Compared with the model not having thermally isolated structure, the thermally isolated micro reactor showed enhanced thermal performances such as fast temperature variation and low energy consumption. The performance enhancements of the micro reactor due to etched holes were verified by thermal experiment and numerical analysis. Regarding to 42 percents reduction of the thermal mass achieved by the etched holes, approximately 4 times faster thermal variation and 5 times smaller energy consumption were acquired. The total size of the fabricated micro reactor was $37{\times}30{\times}1mm^{3}$. Microchannel and reaction chamber were formed on the silicon substrate. The openings of channel and chamber were covered by the glass substrate. The Pt electrodes for heater and sensor are fabricated on the backside of silicon substrate below the reaction chamber. The dimension of channel cross section was $200{\times}100{\mu}m^{2}$. The volume of reaction chamber was $4{\mu}l$. The temperature of the micro reactor was controlled and measured simultaneously with NI DAQ PCI-MIO-16E-l board and LabVIEW program. Finally, the fabricated micro reactor and the temperature control system were applied to the thermal denaturation and the trypsin digestion of protein. BSA(bovine serum albumin) was chosen for the test sample. It was successfully shown that BSA was successfully denatured at $75^{\circ}C$ for 1 min and digested by trypsin at $37^{\circ}C$ for 10 min.

• Restorative Dentistry and Endodontics
• /
• 제34권3호
• /
• pp.184-191
• /
• 2009

본 연구의 목적은 치면 처리와 수복물 내면의 처리가 필요 없는 자가 접착 레진 시멘트의 물성 및 lithium disilicate ceramic과 상아질에 대한 전단결합강도를 측정하고 기존의 레진 시멘트와 비교하여 임상적 유용성을 알아보고자 하는 것이다. 실험군인 자가 접착 레진 시멘트로는 Rely-X Unicem, Embrace Wetbond, Maxcem, BisCem을, 대조군으로는 기존의 레진 시멘트인 Rely-X ARC, 수복용 복합레진인 Z-350을 사용하였다. 각 레진 시멘트의 물성 평가를 위하여 테플론 주형을 이용하여 시편을 제작하고 만능 시험기를 이용하여 압축강도, 간접인장강도, 굴곡강도를 측정하였다. IPS Empress 2 및 상아질 시편에 제조사의 지시대로 Rely-X ARE군과 Z-350군에만 전처리를 시행 후 각 시멘트를 접착하고 전단결합강도를 측정하였다. 실험 결과는 다음과 같았다. 1. 자가 접착 레진 시멘트인 Biscem이 가장 낮은 물리적 성질을 나타내었다 (P<0.05). 2. 자가 접착 레진 시멘트의 상아질 및 도재에 대한 전단결합강도는 기존의 레진 시멘트에 비해 유의성 있게 낮은 값을 나타내었다. (P<0.05). 이상의 결과로 볼 때 자가 접착 레진 시멘트는 기존의 레진 시멘트에 비해 물리적 성질 및 상아질과 lithium disilicate ceramic에 대한 전단결합강도가 떨어지는 것으로 사료된다.

• Restorative Dentistry and Endodontics
• /
• 제33권2호
• /
• pp.148-161
• /
• 2008

본 연구는 상아질 혼성층의 교원섬유를 가수분해하는 효소인 MMPs (Matrix metalloproteinses)의 억제제로 알려진 chlorhexidine (CHX)을 적용 후 결합강도를 측정하였으며, 이를 각각 열순환 처리 후 결합강도를 측정하였다. 또한 주사전자현미경으로 접착계면에서의 파괴 양상을 비교 분석하였다. 우식이 없는 발거한 32개의 제3대구치의 교합면 상아질을 노출시키고 GI그룹에서는 dentin conditioner를 처리 후 2% chlorhexidine을 적용시키고, 산부식 접착제 그룹에서는 인산 산부식을 시행하고 2% chlorhexidine을 적용 후 3단계 산부식형 상아질 접착제 (Scotchbond Multipurpose, SM), 2단계 산부식형 상아질 접착제 (Single Bond, SB)를 도포하고, 자가부식 접착제 그룹에서는 2% chlorhexidine 적용 후 자가부식 상아질 접착제 (Clearfil Tri-S, TS)를 도포한다. 이후 복합 레진 (Z-250)과 GI (Fuji-II LC)를 충전한 시편을 $1\;mm^2$의 단면을 갖는 beam으로 제작하여 열순환 하지 않거나, 10,000회 열순환 ($5\;{\sim}\;55^{\circ}C$)하였다. Universal testing machine (EZ-test; Shimadzu, Japan)에서 cross head speed 1 mm/min로 인장력을 가하여, 미세인장결합강도를 측정하였다. 실험 결과는 유의수준 0.05 level에서 two-way ANOVA를 이용하여 통계분석하였다. 그 후 파절된 시편의 파괴 양상을 현미경 (SEM)으로 관찰하여 다음과 같은 결론을 얻었다; 1. 2% CHX을 적용한 모든 실험군에서 상아질과의 미세인장결합강도가 증가하였고, 열순환은 상아질과의 미세인장결합강도를 감소시켰다 (P > 0.05). 2. CHX 적용 후 열순환 한 군은 CHX을 적용하지 않고 열순환한 군에 비하여 상아질과의 미세인장결합강도가 높았으며, 특히 GI와 TS군에서 유의한 차이를 나타내었다 (P < 0.05). 3. 파괴 양상 분석 결과, 혼성층에서의 접착성 파괴를 보이며, CHX을 적용하면 혼성층 기저부에서 상부로 파괴 부위가 옮겨가는 양상을 나타내었다. 이상의 연구 결과를 토대로, MMPs 억제제인 2% CHX은 글래스 아이오노머 시멘트와 상아질 접착제의 초기 미세인장결합강도에는 영향을 미치지 않으며, CHX 적용이 접착내구성을 유지하는데 도움이 되었다.

• 한국산학기술학회논문지
• /
• 제18권4호
• /
• pp.1-7
• /
• 2017

염료감응형 태양전지 촉매층으로 CoSi의 신뢰성을 확인하기 위해 전자빔증착기를 이용하여 100 nm-Co/300 nm-Si/quartz의 적층구조를 형성하고, $700^{\circ}C$-60분의 진공열처리하여 약 350 nm-CoSi를 형성하였다. 이때 잔류 Co를 제거하기 위해 $80^{\circ}C$-30%의 황산처리를 진행하였다. 또한 비교를 위해 100 nm-Pt/glass 상대전극을 준비하였다. CoSi 상대전극이 채용된 DSSC 소자의 신뢰성을 확인하기 위해 $80^{\circ}C$ 온도조건에서 0, 168, 336, 504, 672, 840시간동안 유지하였다. 이들을 채용한 DSSC 소자의 광전기적 특성을 분석하기 위해 solar simulator와 potentiostat을 이용하였다. CoSi 상대전극의 촉매활성도, 미세구조, 그리고 조성 분석을 확인하기 위해 CV, FE-SEM, FIB-SEM, EDS를 이용하여 분석하였다. 시간에 따른 에너지변환효율 결과, Pt와 CoSi 상대전극 모두 에너지변환효율이 504시간까지는 유지되다가 672시간 경과 후 처음의 50%로 감소하는 특성을 보였다. 촉매활성도 분석 결과, 시간이 지남에 따라 Pt와 CoSi 상대전극 모두 촉매활성도가 감소하여 각각 64%, 57%의 촉매활성도를 보였다. 미세구조 분석 결과, CoSi층은 전해질에 대한 안정성은 우수하였으나, 하부 쿼츠 기판과 CoSi층의 접촉면에 스트레스가 집중되어 국부적으로 크렉이 형성되며, 궁극적으로 ${\mu}m$급의 박리현상을 확인하였다. 따라서 CoSi 상대전극은 실리사이드화 되는 과정에서 잔류응력 때문에 열화가 일어나므로 신뢰성의 확보를 위해서는 이러한 잔류응력의 대책이 필요하였다.