• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.11a
• /
• pp.13-14
• /
• 2012

This study investigates the effect of adhesive type applying to surface-strengthening Ondol floor on level of attachment. Adhesive materials of four types produced in different companies were prepared and their attaching performance was examined. Test results showed that the water-based epoxy type produced in S company was the most effective on attaching the pieces of the surface-strengthening Ondol floor product.

• Journal of Adhesion and Interface
• /
• v.5 no.2
• /
• pp.1-7
• /
• 2004

A novel carboxyl terminated butadiene-acrylonitrile (CTBN) modified, low temperature cure epoxy film adhesive was developed in this paper. It can be cured at as low as $75^{\circ}C$ for 4 hours with a pressure of 0.1MPa. After post cure at $120^{\circ}C$ for 2 hours, the bonding strengths of Phosphoric Acid Anodizing(PAA) surface treated aluminum adherend were similar to those of structural film adhesives curing at $120^{\circ}C$. It is suitable to bond both metal/composite laminate-to-laminate and laminate to honeycomb structure.

• Advances in aircraft and spacecraft science
• /
• v.4 no.6
• /
• pp.729-744
• /
• 2017

This investigation highlights rationale of electrically conductive nano adhesives for its essential application for Electromagnetic Interference (EMI) Shielding in satellites and Lightning Strike Protection in aircrafts. Carbon Nano Fibres (CNF) were functionalized by electroless process using Tollen's reagent and by Plasma Enhanced Chemical Vapour Deposition (PECVD) process by depositing silver on CNF. Different weight percentage of CNF and silver coated CNF were reinforced into the epoxy resin hardener system. Scanning Electron Microscopy (SEM) micrographs clearly show the presence of CNF in the epoxy matrix, thus giving enough evidence to show that dispersion is uniform. Transmission Electron Microscopy (TEM) studies reveal that there is uniform deposition of silver on CNF resulting in significant improvement in interfacial adhesion with epoxy matrix. There is a considerable increase in thermal stability of the conductive nano adhesive demonstrated by Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA). Four probe conductivity meters clearly shows a substantial increase in the electrical conductivity of silver coated CNF-epoxy composite compared to non-coated CNF-epoxy composite. Tensile test results clearly show that there is a significant increase in the tensile strength of silver coated CNF-composites compared to non-coated CNF-epoxy composites. Consequently, this technology is highly desirable for satellites and EMI Shielding and will open a new dimension in space research.

• Journal of Radiation Industry
• /
• v.5 no.2
• /
• pp.137-143
• /
• 2011

Epoxy resins are widely used as high performance thermosets in many industrial applications, such as coatings, adhesives and composites. Recently, a lot of research has been carried out in order to improve their mechanical properties and thermal stability in various fields. Carbon nanotubes possess high physical and mechanical properties that are considered to be ideal reinforcing materials in composites. CNT-reinforced epoxy system hold the promise of delivering superior composite materials with their high strength, light weight and multi functional features. Therefore, this study used multi-walled carbon nanotubes (MWNT) and gamma rays to improve the mechanical and thermal properties of epoxy. The diglycidyl ether of bisphenol A (DGEBA) as epoxy resins were cured by gamma ray irradiation with well-dispersed MWNTs as a reinforcing agent and triarylsulfonium hexafluoroantimonate (TASHFA) as an initiator. The flexural modulus was measured by UTM (universal testing machine). At this point, the flexural modulus factor exhibits an upper limit at 0.1 wt% MWNT. The thermal properties had improved by increasing the content of MWNT in the result of TGA (thermogravimetric analysis). However, they were decreased with increasing the radiation dose. The change of glass transition temperature by the radiation dose was characterized by DMA (dynamic mechanical analysis).

• Elastomers and Composites
• /
• v.40 no.3
• /
• pp.166-173
• /
• 2005

Effect of thermal aging on the weight loss and water absorption of epoxy adhesives was investigated in the presence of three types of different hardeners, such as D-230, G-5022, and HN-2200. Thermal and mechanical properties of the cured epoxy resins were also studied througth the glass transition temperature and shear adhesion strength measurements. Weight losses of DGEBA/D-230 and DGEBA/HN- 2200 systems were not varied. However, the weight of DGEBA/G-5022 system was significantly decreased with increasing the thermal aging time. The water absorption of the specimens was increased as the thermal aging time increased except that using G-5022. DEGBA/HN-2200 system showed higher $T_g$ value than those of other systems, due to the formation of the fine three-dimensional network structure containing aliphatic ring. Shear adhesion strength of all systems was increased with increasing the thermal aging tine, which is attributed to increased degree of cure and fine three-dimensional network structure formation. And $T_g$ values and shear adhesion strength of all specimens exposed to water was decreased as the immersion time increased.

• Journal of the Korea Concrete Institute
• /
• v.18 no.6 s.96
• /
• pp.801-809
• /
• 2006

Epoxy resin has widely been used as adhesives and corrosion-resistant paints in the construction industry for many years, since it has desirable properties such as high adhesion and chemical resistance. Until now, in the production of conventional epoxy cement mortars, the use of any hardener has been considered indispensable for the hardening of the epoxy resin. However we have noticed the fact that even without any hardener, the hardening process of the epoxy resin can proceed by the action of hydroxides in cement mortars. As a result the disadvantages of the two-component mixing of the epoxy resin and hardener have been overcome. The purpose of this study is to evaluate the mechanical properties and durability of epoxy cement mortar without a hardener exposed at indoor and outdoor for one year. The epoxy cement mortars without and with a hardener were prepared with various polymer-cement ratios, and tested for weight change, flexural and compressive strengths, water absorption, carbonation depth and pore size distribution. Especially, the basic properties of the epoxy cement mortars without hardener are discussed in comparison with ones with the hardener. From the test results, it is concluded thai the epoxy cement mortars without a hardener exposed at indoor and outdoor for one year have higher strength and better durability than ones with the hardener within the polymer-cement ratios of 10 to 20%.

• Elastomers and Composites
• /
• v.43 no.1
• /
• pp.39-48
• /
• 2008

Peel strength of epoxy adhesives can be increased by adding some amounts of XNBR. In this case, thermal resistance of the adhesive will be decreased by decrease of glass transition temperature of the adhesive. Epoxy resin modified with siloxane-imide was synthesized to improve thermal resistance and peel strength of the adhesive, after that the properties of modified epoxy resin were compared with the commercial epoxy resin. When 5% XNBR was added to 30% modified epoxy resin, this adhesive showed 0.42 N/mm of peel strength and $155^{\circ}C$ of glass transition temperature. These properties are enough compared to the required properties by the industry, i.e., 0.3 N/mm and $150^{\circ}C$, respectively. Weight loss of the modified epoxy resin by the treatment of nitric acid and 0.1N NaOH was reduced, but weight gain by the humid condition was increased by the presence of benzene ring and imide ring. 30% modified epoxy resin blended with 5% XNBR showed 220% improvement in tensile strength and elongation compared to the case of common epoxy resin. This is due to the flexibility of the siloxane in the modified epoxy resin.

• Restorative Dentistry and Endodontics
• /
• v.18 no.2
• /
• pp.483-496
• /
• 1993

Dentin hypersensitivity medicaments such as Gluma, Scotchbond 2, All-Bond 2, which are resin adhesives, were used to compare the sealing effects of dentinal tubule under mechanical stress. Topical application of above medicaments on the dentin surfaces of extracted teeth followed by artificial tooth brushing for 6 weeks was performed for the comparison. The following conclusions on the degree of dentinal tubule exposure versus time by were reached by using polyvinyl siloxane impression material for taking the impression, epoxy resin for the duplication and SEM for observing the surface. 1. SEM was used to compare the accuracy of the duplicated surface, but no differences were found when teeth samples and the duplicated surfaces were observed. 2. After comparing the degree of dentinal tubules exposure with varnish applied contrast group, resin adhesive materials showed much less exposure as time went by. 3. The results indicated that AU-Bond 2 adhesive, under mechanical stress, showed lesser exposure of dentinal tubules comparing with Gluma and Scotchbond 2 adhesives After the results were put together, it was demonstrated that resin replica method is an useful way to evaluate the treatment effects of the dentinal tubule hypersensitivity medicaments. Also, it was noticed that under mechanical stress, All-Bond 2, classified as fourth generation, illustrated the best dentinal tubules sealing effects.

• Journal of Adhesion and Interface
• /
• v.7 no.2
• /
• pp.12-18
• /
• 2006

Recently, as industries and technologies are increased, superior adhesives having more and more developed functions and properties have been demanded. In this article, to use the merits and viscoelastic properties of poly(ethylene/butylene) rubber resin and to supplement the demerits, semi-structure pressure sensitive adhesives (PSAs) are developed. Aslo, it can be said environmentally friendly PSAs because of not use the organic solvent and not emit volatile organic compounds (VOCs).

• Journal of Adhesion and Interface
• /
• v.21 no.1
• /
• pp.20-26
• /
• 2020

Single lap-shear joints (SLJ) specimens with and without partial round fillets were fabricated to measure the average shear strength of adhesives. The effects of the length of the adherend on the SLJ specimens were also investigated. An epoxy adhesive was used to bond aluminum alloy. Tensile tests were performed on the adhesive bulk specimens to measure the mechanical properties. The finite element analysis (FEA) method was used to measure the adhesive stress distributions, i.e., the peel and shear stresses, on the bonded part. The experimental results revealed that the specimen consisting short length of adherend and without the partial round fillets exhibited the smallest average shear strength of adhesive among the investigated specimens. FEA revealed that the low average shear strength for the specimen with a short adherend length was caused by high stress concentrations on the adhesive at the edge of the bonded part.