Abstract
Epoxy resin has widely been used as adhesives and corrosion-resistant paints in the construction industry for many years, since it has desirable properties such as high adhesion and chemical resistance. Until now, in the production of conventional epoxy cement mortars, the use of any hardener has been considered indispensable for the hardening of the epoxy resin. However we have noticed the fact that even without any hardener, the hardening process of the epoxy resin can proceed by the action of hydroxides in cement mortars. As a result the disadvantages of the two-component mixing of the epoxy resin and hardener have been overcome. The purpose of this study is to evaluate the mechanical properties and durability of epoxy cement mortar without a hardener exposed at indoor and outdoor for one year. The epoxy cement mortars without and with a hardener were prepared with various polymer-cement ratios, and tested for weight change, flexural and compressive strengths, water absorption, carbonation depth and pore size distribution. Especially, the basic properties of the epoxy cement mortars without hardener are discussed in comparison with ones with the hardener. From the test results, it is concluded thai the epoxy cement mortars without a hardener exposed at indoor and outdoor for one year have higher strength and better durability than ones with the hardener within the polymer-cement ratios of 10 to 20%.
기존의 에폭시 수지는 많은 우수한 성질을 갖고 있음에도 불구하고, 주제와 경화제의 2성분 혼합의 복잡성, 높은 폴리머 시멘트비에 따른 경제성 등이 사용성을 제약하고 있다. 여기에서 저자들은 에폭시 수지가 경화제를 첨가하지 않아도 시멘트 모르타르의 수화에 의해 생성되는 알카리 성분에 의해 경화할 수 있다는 것을 알아냈다. 본 연구는 기존의 경화제 무첨가 에폭시 시멘트 모르타르의 연구 결과를 기초로 하여 1년간 실내외에 노출하여 내후성을 평가하였다. 다양한 폴리머 시멘트비로 만든 에폭시 시멘트 모르타르를 제작하여, 노출기간 28일, 6개월, 1년에 대한 중량변화율, 휨강도 및 압축강도, 흡수율, 중성화 깊이를 측정하였으며, 세공입경 분포와 내부 미세조직 구조 등을 관찰하였다. 시험 결과, 경화제를 첨가하지 않아도 에폭시 시멘트 모르타르의 내후성은 기존의 경화제를 첨가한 경우에 비해 역학적 성질 및 내구성 면에서 동등 이상으로 우수하였으며, 이상적인 경화제 무첨가 에폭시 시멘트 모르타르의 폴리머 시멘트비는 10% 또는 20%로 제안할 수 있었다.