• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 센서 박막재료 반도체 세라믹
• /
• pp.295-298
• /
• 2003

The principal problems in development of dielectric paste materials for PDP(plasma display panel)are PbO free paste and low melting temperature. We prepared PbO free paste from glasses in the system BaO-ZnO-$B_2O_3-V_2O_5$. DTA, XRD and SEM were used to study and characterize BaO-ZnO-$B_2O_3-V_2O_5$ glasses. PbO free paste developed at this paper has thermal expansion of $74{\times}10^{-7}/^{\circ}C$, DTA transformation point of $460^{\circ}C$, and firing condition of $560^{\circ}C$, 10min.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.553-554
• /
• 2007

By sol-gel method, we have fabricated silica-titania hybrid film using silane treated colloidal $TiO_2$ and characterized the film through FT-IR, TGA, UV-VIS and AFM. The silica-titania hybrid film showed Ti-O-Si chemical bond at FT-IR peak of $910{\sim}940cm^{-1}$. The fabricated hybrid film showed thermal stability of around $350^{\circ}C$(5wt% loss temperature) and transparency more than 90%. In addition, the good surface smoothness was confirmed by AFM. Therefore, the silica-titania hybrid film with outstanding properties can be potential for application in electronics and displays.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.448-448
• /
• 2007

OLED has many advantages of low voltage operation, self radiation, light weight, thin thickness, wide view angle and fast response time to overcome existing liquid crystal display (LCD)'s weakness. Therefore, It draws attention as promising display and has already developed for manufactured goods. Also, OLED is regarded as a only substitute of flexible display with a thin display. However, Indium tin oxide(ITO) thin film for electrode of OLED shows a low electrical properties and is impossible to deposit at high thermal condition because electrical characteristics of ITO is getting worse. One of the ways to realize an improved flexible OLED is to use high internal efficiency electrodes, which have higher work function than those single layer of ITO films of the same thickness. The high internal efficiency electrodes film is developed with structure of nickel oxide for bottom Emission Type of OLED.

• Transactions on Electrical and Electronic Materials
• /
• 제14권5호
• /
• pp.246-249
• /
• 2013

Graphene was obtained on Cu foil by thermal decomposition method. A gas mixture of $H_2$ and $CH_4$ and an ambient annealing temperature of $1,000^{\circ}C$ were used during the deposition for 30 Min., and for the transfer onto $SiO_2/Si$ and Si substrates. The physical properties of graphene were investigated with regard to the effect ofnitrogen atom doping and the various substrates used. The G/2D ratio decreased when the graphene became monolayer graphene. The graphene grown on $SiO_2/Si$ substrate showed a low intensity of the G/2D ratio, because the polarity of the $SiO_2$ layer improved the quality of graphene. The intensity of the G/2D ratio of graphene doped with nitrogen atoms increased with the doping time. The quality of graphene depended on the concentration of the nitrogen doping and chemical properties of substrates. High-quality monolayer graphene was obtained with a low G/2D ratio. The increase in the intensity of the G/2D ratios corresponded to a blue shift in the 2D peaks.

• E2M - 전기 전자와 첨단 소재
• /
• 제8권1호
• /
• pp.95-101
• /
• 1995

Crystallizable glasses with precipitation of celsian, anorthite, wollastonite and gahnite were prepared for the purpose of insulating dielectric layers in devices such as integrated circuit substrates. The starting glasses were prepared by melting the batches for 1 hour at 1450.deg. C and then Quenching to a distilled water. And crystallization behavior of these glasses were studied by DTA, TMA, XRD analysis and by the measurement of dielectric properties. The overall composition of the glass-ceramic consists in weight percent of 30-35% A1$_{2}$O$_{3}$, 13-26% BaO, 5-21% CaO, 10-24% ZnO, 4.5-9.0% TiO$_{2}$ and 4-8% B$_{2}$O$_{3}$. As a result, in barium-rich glasses only celsian phase was developed in the range of 850-900.deg. C. Also, the thermal expansion coefficient, dielectric constant and quality factor of these glass-ceramics were 68*10$^{-7}$ /.deg. C, about 9 and more than 1000, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.167-167
• /
• 2008

The barium strontium calcium titanate powders were prepared by sol-gel method. Ferroelectric $(Ba_{0.54}Sr_{0.36}Ca_{0.1})TiO_3$(BSCT) thick films were fabricated by the screen-printing method on alumina substrate. And we investigated the structural and dielectric properties of BSCT thick films with the variation of sintering temperature. As a result of thermal analysis, BSCT polycrystalline perovskite phase was formed at around $660^{\circ}C$. The results of X-ray diffraction analysis were showed a cubic perovskite structure without presence of the second phase in all BSCT thick films. The average grain size and the thickness of the specimen sintered at $1450^{\circ}C$ were about 1.6 mm and 45 mm, respectively. The relative dielectric constant increased and the dielectric loss decreased with increasing the sintering temperature, the values of the BSCT thick films sintered at $1450^{\circ}C$ were 5641 and 0.4% at 1kHz, respectively.

• 한국전기전자재료학회논문지
• /
• 제14권12호
• /
• pp.1008-1015
• /
• 2001

Thin films of vanadium oxide(VO$\_$x/) have been deposited by r.f. magnetron sputtering from V$_2$O$\_$5/ target in gas mixture of argon and oxygen. The oxygen/(oxygen+argon) partial pressure ratio is changed from 0% to 8%. Crystal structure, chemical composition, bonding, optical and electrical properties of films sputter-deposited under different oxygen gas pressures are characterized through XPS, AES, RBS, FTIR, optical absorption and electrical conductivity measurements. V$_2$O$\_$5/ and lower oxides co-exist in sputter-deposited films and as the oxygen partial pressure is increased the films become more stoichiometric V$_2$O$\_$5/. The increase of O/V ratio with increasing oxygen gas pressure is attributed to the partial filling of oxygen vacancies through diffusion. It is observed that the oxygen atoms located on the V-O plane of V$_2$O$\_$5/ layer participate more readily in the oxidation process. With increasing oxygen gas pressure indirect and direct optical band gaps are increased, but thermal activation energies are decreased.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.258-259
• /
• 2005

[ $CuInSe_2$ ] thin films were fabricated at various fabrication conditions (substrate temperature, sputtering pressure, BC/RF power, vapor deposition, heat treatment). And structural and electrical properties were measured in order to certify optimum conditions for growth of the ternary compound semiconductor $CuInSe_2$ thin films with stoichiometric composition. $CuInSe_2$ thin film was well made at the heat treatment of 500[$^{\circ}C$] of SLG/Cu/In/Se stacked elemental layer which was prepared by sputter and thermal evaporator, and chemical composition of the thin film was analyzed nearly as the proportion of 1 : 1 : 2. At the same time, carrier concentration, hall mobility and resistivity of the thin films was $1.27\sim9.88\times10^{17}[cm^{-3}]$, $49.95\sim185[cm^2/V{\cdot}s]$ and $10^{-1}\sim10^{-2}[\Omega{\cdot}cm]$, respectively

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 하계학술대회 논문집 Vol.9
• /
• pp.194-194
• /
• 2008

Boron doped ZnO:Al(AZOB) thin films were prepared on glass substrates by dc magnetron sputtering. Influence of the annealing treatment on the electrical and optical properties of AZOB thin films were investigated. The lowest resistivity of $1.6\times10^{-3}\Omega$-cm was obtained at an annealing temperature of $400^{\circ}C$. The average transmittance of the films is over 80% in the visible range. It was also shown that by introducing boron impurity into AZO system improve the uniformity, the resistivity, and thermal stability of ZnO-based conducting thin films.

• 한국전기전자재료학회논문지
• /
• 제20권12호
• /
• pp.1099-1104
• /
• 2007

In order to develop non-heated STAl(super thermal resistant Aluminum alloy) for ampacity gain conductor, the systematic research was carried out. Especailly, the effect of a very small amount of Zr, Sc element in EC grade Al ingot on mechanical and electrical properties was our priority. As a result, it was found that the strength and recrystallization temperature of designed alloy was gradually increased with Zr, Sc addition up to 0.3 wt.%. However, the electric conductivity showed no drastic change. The tensile strength and recrystalliztion temperature, $17.75{\sim}20.05\;kgf/mm^2$ and $420{\sim}520\;^{\circ}C$, was obtained at 0.3 wt.% Zr, Sc addition, respectively. Particles of the $Al_3Zr$ and $Al_3Sc$ phase affected the ambient and elevated-temperature strength of the alloys.