• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.5
• /
• pp.445-449
• /
• 2005

Aging phenomena of 0.2PMN-0.8PZT multilayered ceramic actuators(MCA) have been investigated at the room temperature. The piezoelectric materials were synthesized as conventional ceramic process, and MCA were fabricatedby tape casting methods. The crystalline structures and lattice parameters were investigated by X-ray diffraction analysis, showing the structure was tetragonal and c/a was about 1.01. And, the effective electromechanical coupling coefficient keff and pseudo-piezoelectric constant $d_{33}$were measured. Variable unipolar electric fields, $2{\sim}4kV/mm$, were applied to MCh to investigate the aging characteristics. After 2 kV/mm unipolar electric field, keff and $d_{33}$ were 0.454 and 4.44 respectively. The measured and simulated values using for aging phenomena analysis, had a good fit to the linear logarithmic stretched exponential law.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.33.2-33.2
• /
• 2009

Dielectric and piezoelectric properties of Lead-free $(1-x)(Bi_{0.5}K_{0.5})TiO_3-xBiFeO_3$ceramics prepared by a conventional solid state reaction method were investigated in the range of x = 0~10 mol%. Piezoelectric coefficient was increased from 31 pC/N at x = 0 mol% to 64 pC/N at x = 6 mol% then decreased with increasing x. Electromechanical coupling factor ($K_p$) was increased up to 0.18 at x = 10 mol%. On the other hand, mechanical quality factor ($Q_m$) was decreased. Grain size was not much changed with various x and a single perovskite with tetragonal symmetry was maintained at all compositions forming a solid solution between $(Bi_{0.5}K_{0.5})TiO_3$ and $BiFeO_3$. Depolarization temperature ($T_d$) was gradually decreased with increasing x from $302^{\circ}C$ at x = 0 to $245^{\circ}C$ at x = 10 mol%.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.60 no.3
• /
• pp.594-599
• /
• 2011

A SAW strain sensor based on Shear Horizontal wave with an 92 MHz central frequency was developed. It consists of SAW sensor, PCB substrate and bonding material (Loctite 401). External force applied to PCB substrate bonded to a piezoelectric substrate induces strain at the substrate surface, which causes changes in the elastic constant and density of the substrate and hence the propagation velocity of the SAW. The change in the velocity of the SAW result in a frequency shift of the sensor and by measuring a frequency shift, we can extract the strain induced by the external force. The $41^{\circ}$ YX $LiNbO_3$ was used because it has a Leaky shear horizontal(SH) wave propagation mode and a high electromechanical coupling coefficient ($K^2$=17.2%). And to compare with Rayleigh wave mode, $128^{\circ}$ YX $LiNbO_3$ was used. And to make a stable and low insert loss, Split IDT structure was used. The obtained sensitivity and linearity of the SAW strain sensor in the case of Split IDT were measured to be 17.2 kHz / % and 0.99, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.141-144
• /
• 2003

This study proposes ZnO thin film as a piezoelectric material for SAW (surface acoustic wave) filter. The ZnO thin film with thickness $2.6{\mu}m$ was deposited (0001)-oriented sapphire by RF magnetron sputtering technique. IDTs (inter-digital transducers) electrodes were patterned upon SAW filter mask with solid finger structure unapodized using lift-off method on ZnO piezoelectric thin film. SAW propagation velocity was measured with the center frequency by HP 8753C network analyzer. A fabricated ZnO SAW filter exhibited a high propagation velocity of 5433 $^m/s$ and relatively insertion loss of -53.391dB at $\lambda=80{\mu}m$. The side-lobe attenuation of the center frequency was about 17dB. When the wavelength was $80{\mu}m$ $(\lambda/4=20{\mu}m)$, the center frequency was 67.907 MHz. $k^2$ (electromechanical coupling coefficient) was 15.84 %.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.200-203
• /
• 2000

The application of the ultrasonic nozzle has been extended because it is possible atomization of liquid material. In this study, the characteristics of the ultrasonic nozzle and ceramic oscillator were investigated. The oscillator for the ultrasonic nozzle were made piezoelectric ceramic of Pb[($Sb_{1/2}$ $Nb_{1/2}$)$_{0.035}$-($Mn_{1/3}$$Nb_{2/3}$)$_{0.065}$-($Zr_{0.49}$$Ti_{0.51}$)$_{0.90}$]$O_3$. The electromechanical coupling factor($k_p$) and mechanical quality factor(Qm) showed the values of 0.555, 1, 214 respectively when the Zr/Ti ratio was 49/51. Moreover, this oscillator will have the temperature stability because it's curie temperature is 322[$^{\circ}C$]. The driving current of ultrasonic nozzle showed the value of 80[mA] when the driving time was lO[min.]. Also, The surface temperature of ceramic oscillator showed 80[$^{\circ}C$] at driving time lO[min.] We knew that the ultrasonic nozzle had stabile driving above 10[min.].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.149-152
• /
• 1997

High-power piezoelectric materials are being developed for applications such as actuators and ultrasonic motors. In this paper, ferroelectric property of iron-doped 0.57 (Sc$_{1}$2//Nb$_{1}$2/)O$_3$-0.43 PbTiO$_3$. which is the morphotropic phase boundary composition for the PSN-PT system, was investigated. The maximum dielectric constant ( $\varepsilon$$_{33}$/$\varepsilon$$_{0}$ = 2551) and the minimum dielectric loss(tan $\delta$ = 0.51 %) at room temperature were obtained at 01. wt% and 0.3 wt% of iron additions. With additions of the Fe$_2$O$_3$ the electromechanical coupling factor of radial mode k$_{p}$ and the piezoelectric coefficient d$_{33}$ were slightly decreased, on the other hand the mechanical quality factor was increased significantly. The highest mechanical quality factor (Qm= 297) was obtained at 0.3 wt% Fe$_2$O$_3$, which is 4.4 times larger than that of pure 0.57 PSN-0.43PT ceramics. The temperature dependence of the dielectric constant and dielectic loss was observed between 2$0^{\circ}C$ and 35$0^{\circ}C$ .X> .X> .

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.694-695
• /
• 2006

As a candidate for lead-free piezoelectric materials, dense $95(Na_{0.5}K_{0.5})NbO_3-5LiTaO_3$ (NKN-5LT) ceramics were developed by conventional sintering process. Sintering temperature was lowered by adding $Li_2O$ as a sintering aid. The electrical properties of NKN-5LT ceramics were investigated as a function of $Li_2O$ concentration. At the addition of 1 mol% $Li_2O$, electromechanical coupling factor $(k_P)$ and piezoelectric coefficient $(d_{33})$ of NKN-5LT ceramics were found to reach the highest values of 0.37 and 250 pC/N, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.256-256
• /
• 2007

As a candidate for lead-free piezoelectric materials, dense ($(Na_{0.47}K_{0.47}Li_{0.06})NbO_3$ (LNKN6) ceramics were developed by conventional sintering process. Sintering temperature was lowered by adding $Li_2O$ as a sintering aid. Abnormal grain growth in the LNKN6 ceramics was observed with varying $Li_2O$ content. The electrical properties of LNKN6 ceramics were investigated as a function of $Li_2O$ concentration. When the sample sintered at $1000^{\circ}C$ for 4h with the addition of 1 mol% $Li_2O$, electromechanical coupling factor ($k_p$) and piezoelectric coefficient ($d_{33}$) of LNKN6 ceramics were found to reach the highest values of 0.40 and 184 pC/N, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.315-316
• /
• 2006

Dense $0.95(Na_{0.5}K_{0.5})NbO_3-0.05LiTaO_3$ (NKN-LT) ceramics were developed by conventional sintering process. Sintering temperature was lowered by adding $Na_2O$ as a sintering aid. The electrical properties of NKN-LT ceramics were investigated as a function of $Na_2O$ concentration. When the sample sintered at $1000^{\circ}C$ for 4h with the addition of 1 mol% $Na_2O$, electromechanical coupling factor ($k_p$) and piezoelectric coefficient ($d_{33}$) of NKN-LT ceramics were found to reach the highest values of 0.43 and 190 pC/N, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.321-322
• /
• 2007

In this thesis, the sintering properties and piezoelectric properties of $Pb[(Co_{0.5}W_{0.5})_{0.03}(Ni_{1/3}Nb_{2/3})_{0.07}(Zr_{0.52}Ti_{0.48})_{0.9}]O_3+0.5[wt%]MnO_2$ ceramics has been systematically investigated as a function of the sintering temperature after manufacturing the specimens with a general method. The lattice constant from the analysis of crystal structure showed that the pychlore structure was decreased with the increase of the sintering temperature. Density was decreased by increasing $B_2O_3$. TCFr was showed its minimum variation rate of 0.35~-0.52[%] in the sintered temperature 950[$^{\circ}C$], $B_2O_3$ 3[wt%]. The electromechanical coupling coefficient (Kp) showed its maximum of 31.116[%] in the sintered temperature 1050[$^{\circ}C$], and its minimum of 20.220[%] in the sintered temperature 1150[$^{\circ}C$].