Abstract
Dielectric and piezoelectric properties of Lead-free $(1-x)(Bi_{0.5}K_{0.5})TiO_3-xBiFeO_3$ceramics prepared by a conventional solid state reaction method were investigated in the range of x = 0~10 mol%. Piezoelectric coefficient was increased from 31 pC/N at x = 0 mol% to 64 pC/N at x = 6 mol% then decreased with increasing x. Electromechanical coupling factor ($K_p$) was increased up to 0.18 at x = 10 mol%. On the other hand, mechanical quality factor ($Q_m$) was decreased. Grain size was not much changed with various x and a single perovskite with tetragonal symmetry was maintained at all compositions forming a solid solution between $(Bi_{0.5}K_{0.5})TiO_3$ and $BiFeO_3$. Depolarization temperature ($T_d$) was gradually decreased with increasing x from $302^{\circ}C$ at x = 0 to $245^{\circ}C$ at x = 10 mol%.