• Elastomers and Composites
• /
• v.50 no.1
• /
• pp.30-34
• /
• 2015

Thermo-mechanical treatment process of a compressed open-cell rigid polyurethane foam (OC-RPUF), which was fabricated for the vacuum insulation panel (VIP), was studied to obtain an optimum condition for the dimensional stability by the relaxation of compressive stress. Thermo-mechanical deformation of the sample OC-RPUF was shown to occur from about $120^{\circ}C$. Yield stress of 0.36 MPa was shown at about 10% yield strain. And, densification of the foam started to occur from 75% compressive strain and could be continued up to max. 90%. Compression set of the sample restored after initial compression to 90% at room temperature was ca. 82%. Though the expansion occurred to about twice of the originally compressed thickness in case of temperature rise to $130^{\circ}C$, it could be overcome and the dimensional stability could be maintained if the constant load of 0.3 MPa was applied. As the result, a thermo-mechanical treatment process, i.e, annealing process at temperature of $130{\sim}140^{\circ}C$ for about 20 min as is the maximum compressed state at room temperature, should be required for dimensional stability as an optimum condition for the use of VIP core material.

• Journal of the Korean Wood Science and Technology
• /
• v.23 no.4
• /
• pp.74-84
• /
• 1995

Eight types of thin composite panels were manufactured by press-lam and mat-forming process applied to optimum manufacturing condition, studied in former first research by author (1995). They were tested and compared with control boards on dimensional stability, internal bond strength, tensile strength, Screw withdrawal strength, and bending properties. These thin composite panels manufactured by mat-forming process were generally superior to those by press-lam in dimensional stability and mechanical properties. In the dimensional stability and mechanical properties of thin composite panels manufactured by mat-forming process, the thin composite panels (A and E type) composed of particle or sawdust core and veneer face with polyethylene film, were as good as those of common plywood (control board). Internal bond strength showed highest value in the thin composite panel(D type) which composed of particle core and polypropylene screen face with polyethylene film. The thin composite panels(G and H type) composed of sawdust or particle core and polypropylene screen face with polyethylene film by press-lam and mat-forming process, showed most highest value in dimensional stability and water absorption.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.4
• /
• pp.458-471
• /
• 2020

Effect of pre-treatment and compression ratio on specific gravity (SG) and dimensional stability improvement of three lesser-used wood species from natural forest area of North Kalimantan Province, Indonesia had been investigated. Hot soaking at 80℃ for 3 hours within 2 and 5% of boron solution was applied as pre-treatment, while compression ratio applied was 20 and 40% from the initial thickness. Densification was conducted using hot pressing machine at 30 kg/㎠ of pressure and 160℃ of temperature for 15 minutes. Specific gravity was measured gravimetrically, while dimensional stability was evaluated through thickness swelling and water absorption as the indicator. Results show that SG of densified wood was influenced by wood species and compression ratio, but not by pre-treatment applied; while dimensional stability was influenced by wood species, compression ratio, and pre-treatment. Specific gravity and water absorption of densified wood was improved significantly. Specific gravity increased 28.86-63.03%, while water absorption decreased 12.80-15.89%. Thickness swelling of 20% densified wood was lower than that of 40% densified wood.

• Communications of the Korean Mathematical Society
• /
• v.26 no.2
• /
• pp.237-251
• /
• 2011

In this paper, we determine some stability results concerning the 2-dimensional vector variable quadratic functional equation f(x+y, z+w) + f(x-y, z-w) = 2f(x, z) + 2f(y, w) in intuitionistic fuzzy normed spaces (IFNS). We dene the intuitionistic fuzzy continuity of the 2-dimensional vector variable quadratic mappings and prove that the existence of a solution for any approximately 2-dimensional vector variable quadratic mapping implies the completeness of IFNS.

• Journal of the Korea Furniture Society
• /
• v.19 no.3
• /
• pp.172-179
• /
• 2008

The objective of this study was to investigate the influence of the water repellents' treatment on the water absorptivity and the dimensional stability of Korean red pine wood(Pinus densiflora). The alkylketene dimer(AKD), fluororesin emulsion(Wood-seal, WS), and paraffin wax emulsions(PW25, PW40, and PW1200) were used as water repellents. PW40 and WS were proved as excellent water repellents for pine wood, because the samples treated with these agents showed high contact angles and large reduction in water absorptivities. Also, the dimensional stability(antiswelling efficiency) of pine wood was considerably improved by water repellents treatments, such as PW40 and WS at the pressure of 2MPa. The water repellent treated woods with WS, PW40, and PW1200 at the pressure of 2MPa were relatively stable to the wet-dry cyclic leaching test.

• Journal of the Korea Furniture Society
• /
• v.27 no.4
• /
• pp.302-308
• /
• 2016

It has been known that acetylation improves the dimensional stability of wood. Liquid phase acetylation is more popular than gas-phase acetylation for the effectiveness of weight gain of wood. In this study the specimens of domestic red and Korean pines are acetylated in liquid phase and their physical properties, such as density, bending strength, anti-hygroscopicity etc., are analyzed. Acetylation increases the average weights and volume of larch specimens by 11.4% and 3.4%, respectively, and their average oven-dry densities are increased by $0.03g/cm^3$. Acetylation does not influence on Modulus of Rupture (MOR) and Modulus of Elasticity (MOE). The average Percentage Reduction in Hygroscopicity (PRH) and average Percentage Reduction in Water soaking (PRW) of larch specimens are respectively 20.2% and 20.8%. Thus it can be concluded that acetylation improves the dimensional stability of larch specimens.

• The Journal of Engineering Geology
• /
• v.21 no.1
• /
• pp.57-64
• /
• 2011

Three-dimensional slope stability analysis was applied to a failed dual-lithology slope containing both granite and an andesitic dyke, taking account of the differences in shear strength of the different lithologies. A direct shear test of the soil-rock boundary was performed to examine the shear strength of two different types of failure surfaces within different lithologies, and a laboratory test was performed on an upper, weathered soil layer. The test results indicate that shear strength was lower at the soil-rock boundary than within the weathered soil layer. A representative geological section was subjected to two-dimensional slope stability analysis using a limit equilibrium method to assess whether the distribution of lithologies upon the slope influences the results of stability analysis. The results were then compared with those of three-dimensional slope stability analysis, for which input parameters can be varied according to the distribution of lithologies upon the slope. The three-dimensional analysis yielded safety factors of 1.26 under dry conditions and 0.55 under wet conditions, whereas the two-dimensional analysis yielded unstable safety factors of 0.92 and 0.32, respectively. These findings show that the results of stability analysis are affected by the distribution of different lithologies upon the slope. Given that the studied slope collapsed immediately after rainfall, it is likely that the results of the three-dimensional analysis are more reliable.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.3
• /
• pp.315-325
• /
• 2020

Boron compound had many advantages as wood preservative, but it was prone to leaching. Improving boron preservation was required to extend the service life of fast growing and low durability red jabon (Antochephalus macrophyllus) hardwood. This study aimed to evaluate the dimensional stability, color change and durability of modified red jabon wood by double impregnation with boron and methyl methacrylate (MMA) and heat treatment. Impregnation I used boric acid or borax, and impregnation II used MMA, while heat treatment used temperatures of 90 ℃ or 180 ℃ for 4 hours. The dimensional stability, leachability, water absorption, color change and decay resistance of modified red jabon wood were tested. The results showed that MMA impregnation increased the dimensional stability of red jabon wood, while the leaching and water absorption in the wood significantly reduced. Heating at 180 ℃ caused less water absorption and higher dimensional stability of the wood than that of heating at 90 ℃. Impregnation with boric acid and MMA followed by heating at 90 ℃ resulted in the highest wood ASE, 89.9%. The color change (∆E^*) of wood increased significantly after MMA impregnation and heating at 180 ℃. Boric acid impregnation caused more resistant wood than borax impregnation against decay fungi and termites. Impregnation with boric acid and MMA followed with heating at 180 ℃ increased significantly the wood resistance against decay fungi and termites.

• Journal of computational fluids engineering
• /
• v.14 no.4
• /
• pp.41-47
• /
• 2009

An immersed boundary method(IBM, Kim et al.(2001)) for simulating flows over complex geometries is applied to computation of three-dimensional Floquet stability of a periodic wake. Floquet stability analysis is employed to extract different modes of three-dimensional instability. To verify the present method, a fully-resolved Floquet stability calculation for flow past a circular cylinder is considered. There are two different instability modes with long(mode A) and short (mode B) spanwise wavelengths for the periodic wake of a circular cylinder. The critical Reynolds number and the most unstable spanwise wavelengths of modes A and B are computed using the present method, and compared with other authors' results currently available.

• Journal of the Korean Wood Science and Technology
• /
• v.47 no.5
• /
• pp.567-578
• /
• 2019

A common problem with fast-growing hardwoods is dimensional instability that limits use of their wood. In this study, we investigated the effects of pre-drying methods, temperatures, and heating duration on the specific gravity, water absorption, and dimensional stability of three tropical fast-growing hardwoods, jabon (Neolamarckia cadamba Roxb.), sengon (Falcataria moluccana Miq.), and mangium (Acacia mangium Willd.). Wood samples were pre-dried by two methods (fan and oven at $40^{\circ}C$), and heat treatments were performed at three temperatures (120, 150, and $180^{\circ}C$) for two different time periods (2 and 6 hours). The specific gravity, water absorption, dimensional stability, and structural changes of the samples were evaluated. The results revealed that heat treatments slightly reduced the specific gravity of all three wood species. In addition, the heat treatments reduced water absorption and significantly improved dimensional stability of the samples. Oven pre-drying followed by heat treatment at $180^{\circ}C$ for 6 hours resulted in good physical improvement of jabon and sengon wood. Fan pre-drying followed by heat treatment at $180^{\circ}C$ for 2 hours improved the physical properties of mangium wood. The heat treatment shows a promising technique for improving the physical characteristic of fast growing hardwoods.