• Korean Journal of Materials Research
• /
• v.21 no.3
• /
• pp.149-155
• /
• 2011

We investigated tribological characteristics of diamond-like carbon (DLC) in a condition with carbon nanotube (CNT) content of 1wt% in aqueous solution. Si-DLC films were deposited by radio frequency plasma enhanced chemical vapor deposition (RF-PECVD) process on Al6061 aluminum alloy. In this study, the deposition of DLC films was carried out in vacuum with a chamber pressure of 10-5 to 10-3 Torr achieved by mechanical pump followed by turbo molecular pump. The surface adsorbed oxygen on the Aluminum substrates was removed by passing Ar gas for 10 minutes. The RF power was maintained at 500W throughout the experiment. A buffer layer of HMDSO was deposited on the substrate to improve the adhesion of DLC coating. At this point CH4 gas was introduced in the chamber using gas flow controller and DLC coating was deposited on the buffer layer along with HMDSO for 50 min. The thickness of 1 ${\mu}m$ was obtained for DLC films on aluminum substrates The tribological properties of as synthesized DLC films were analyzed by wear test in the presence of dry air, water and lubricant such as CNT ink.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.9
• /
• pp.808-811
• /
• 2008

Optical and mechanical properties of diamond-like carbon (DLC) films synthesized by RF plasma enhanced chemical vapor deposition were investigated as a function the C/H ratio in gas mixture. The C/H ratio was varied from 6 to 10 %, adjusting the amount of $CH_4$ and $H_2$ as the source gas. The optical and mechanical properties of DLC films were characterized by UV spectrometer, Ellipsometer and Nano-indenter. The change of the C/H ratio during synthesis of DLC films had many effects on the growth rate, transmittance, refractive index and hardness. The growth rate of the films increased exponentially with the increase in C/H ratio. The hardness of the films showed the tendency to improve with increasing C/H ratio, whereas the transmittance decreased. The refractive index was varied from 2.03 to 2.17, and these refractive indexes close to 2.0 indicates that it can be applied to Si-based solar cell.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.39 no.10
• /
• pp.1037-1043
• /
• 1990

Diamond thin films were synthesized from the mixed gases of methane and hydrogen on silicon substrates by RF plasma chemical vapor deposition and deposited films were investigated by SEM, X-ray diffractometry and Raman spectroscopy. It is found that high quality diamond-like carbon films were successfully synthesized by PECVD under the deposition condition of 1-10 vol% of methane concentration, 0.15-0.4torr of reactor pressure, 500W of RF power, and 5-20hr of reaction time. Especially, cubo-octahedral diamond-like carbon particles were synthesized by employing 1.0 vol % of methane concentration and 0.4torr of the reactor pressure.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.11
• /
• pp.973-976
• /
• 2008

In addition to its similarity to genuine diamond film, diamond-like carbon (DLC) film has many advantages, including its wide band gap and variable refractive index. In this study, DLC films were prepared by the RF PECVD (Plasma Enhanced Chemical Vapor Deposition) method on silicon substrates using methane ($CH_4$) and hydrogen ($H_2$) gas. We examined the effects of the RF power on the electrical properties of the DLC films. The films were deposited at several RF powers ranging from 50 to 175 W in steps of 25 W. The leakage current of DLC films increased at higher deposition RF power. And the resistivities of DLC films grown at 50 W and 175 W were $5\times10^{11}$ ${\Omega}cm$ and $2.68\times10^{10}$ ${\Omega}cm$, respectively.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.1
• /
• pp.49-53
• /
• 2011

Diamond-like carbon (DLC) films is a metastable form of amorphous carbon containing a significant fraction of Sp3 bond. DLC films have been characterized by a range of attractive mechanical, chemical, tribological, as well as optical and electrical properties. In this study DLC films were prepared by the RF magnetron sputter system on $SiO_2$ substrates using graphite target. The effects of the post annealing temperature on the Property variation of the DLC films were examined. The DLC films were annealed at temperatures ranging from 300 to $500^{\circ}C$ using rapid thermal process equipment in vacuum. The variation of electrical property and surface morphology as a function of annealing treatment was investigated by using a Hall Effect measurement and atomic force microscopy. Raman and X-ray photoelectron spectroscopy analyses revealed a structural change in the DLC films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.272-272
• /
• 2008

Diamond-like carbon (DLC) 박막은 높은 경도, 내 마모성, 화학적 안정성, 전기적 절연성, 높은 광 투과성을 가지고 있어, 공구강, 광학렌즈 및 플라스틱의 보호 코팅을 위해 응용되어진다. 하지만, DLC 박막은 높은 잔류응력으로 adhesion이 떨어진다는 단점이 있다. 따라서 본 연구에서는 전처리가 13.56MHz 150W RF플라즈마 화학기상 증착(RF-PECVD) 법을 통한 DLC 박막의 합성에 어떤 영향을 미치는지 알아보기 위해, $H_2$ (80 sccm), $O_2$ (10 sccm), $N_2$ (20 sccm)의 다른 가스를 사용하여 전처리를 하였다. DLC 박막 합성 후, 특성은 Raman, scratch test, contact angle 등의 측정을 통하여 분석되었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.526-529
• /
• 2002

We studied the nematic liquid crystal (NLC) aligning capabilities by the UV alignment method on a diamond like carbon (DLC) thin film surface. A good LC alignment by UV exposure on the DLC thin film surface at $200\AA$ of layer thickness was achieved. Also, a good LC alignment by the UV alignment method on the DLC thin film surface was observed at annealing temperature of $180^{\circ}C$. However, the alignment defect of the NLC was observed above annealing temperature of $200^{\circ}C$. Consequently, the good thermal stability of LC alignment by the UV alignment method on the DLC thin film surface can be achieved.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.1
• /
• pp.27-32
• /
• 2004

The diamond-like carbon (DLC) films were deposited on the Si (100) wafer by a rf-PECVD method as a function of the mixture rate of methane-hydrogen gas and bias voltage. The bonding structure and mechanical properties of these deposited DLC films were investigated using FT-IR, Raman, and nano-indenter. The deposition rates of DLC films increased with increased flow rate of methane in the gas mixtures and increased bias voltage. The $sp^3/sp^2$ bonding ratio of carbon in thin film and the hardness increased with increasing flow rate of hydrogen in the gas mixtures and increasing bias voltage.

• Journal of the Korean Vacuum Society
• /
• v.14 no.3
• /
• pp.165-170
• /
• 2005

There is an increasing interest in developing novel coating to improve the blood compatibility of medical implants. Diamond-like carbon(DLC) and titanium nitride(TiN) films have been proposed as potential biomedical coatings due to their chemical k physical properties and moderate biocompatibility. To study the correlation between blood compatibility and physical properties of the films, the fibrinogen adsorption on the surface as well as morphology & wettability were investigated. The quantity of fibrinogen adsorption are Tower for TiN than DLC, which correlates with a higher hydrophilicity of TiN film. To reduce the quantity of fibrinogen adsorption on the film, plasma treatment and furnace annealing were performed, respectively. With the use of oxygen plasma and furnace annealing, the amount of fibrinogen adsorption on TiN film was remarkably reduced, while there was no decrease of the quantity with DLC.

• Journal of the Korean Vacuum Society
• /
• v.13 no.4
• /
• pp.157-163
• /
• 2004

Dependence of residual compressive stress of diamond-like carbon (DLC) films on relative humidity was investigated. Polymeric, graphitic and diamond-like carbon films were prepared by r.f.-PACVD using methane or benzene with the negative self bias voltage of the substrate ranging from -100 to -800 V. In-situ measurements of the residual stress were carried out in an environment chamber where the relative humidity was varied from 10％ to 90％. In dense DLC film of high residual compressive stress and hardness, we could not observe any change in the residual compressive stress with relative humidity. However, in the cases of graphitic and polymeric DLC films, abrupt change in the residual stress occurred by changing the relative humidity. The quantity of the stress change was inversely proportional to the film thickness, which means that the stress change with humidity is not due to the penetration of the water molecule into the film structure, but due to surface interaction between water molecules and film surface.