• Restorative Dentistry and Endodontics
• /
• v.25 no.4
• /
• pp.527-535
• /
• 2000

The purpose of this study was to evaluate effects of smear layer and dentin primers on the sealing ability of root canals. 126 extracted human teeth with single, straight canals and mature apices were used. The Samples were first classified into six groups as follows: presence of smear layer; absence of smear layer; Scotchbond Bond Multi-Purpose; All Bond 2; Mac Bond 2; Clearfil Liner Bond 2. A Positive control was also established. All teeth except the control group were then obturated with thermoplasticized gutta-percha and AH26. Electrochemical and dye penetration technique were later used to evaluate the degree of micro leakage through the root canal. Seventy teeth were then immersed in a 1% potassium chloride solution and An external power supply(DC 10 V) was then applied to the circuit for the electrochemical microleakage test. The degree of Microleakage was determined over period of 28 days before being evaluated. In total, 48 teeth were submitted to the dye infiltration technique. All specimen were suspended in 2% methylene blue dye for 1 week before being longitudinally split. The degree of dye infiltration was measured under a stereo microscope at ${\times}10$ magnification and evaluated. The results were as follows: 1. Apical microleakage increased throughout the test period in all group and one group having a smear layer showed a dramatic increase under electrochemical test (p<0.05). In the group having smear layer, the degree of apical microleakage was the highest, and the micro leakage was much higher than in the smear layer removed group in electrochemical test (p<0.05). Scotchbond Multi-Purpose, All Bond 2, Mac Bond 2 and Clearfil Liner Bond 2 showed lower micro leakage than one group having smear layer. The All Bond 2 and Clearfil Liner Bond 2 treated groups showed the lowest microleakage in electrochemical test (p<0.05). 2. There was no significant difference between the experimental groups in dye penetration technique. These results suggested that the removal of the smear layer from root canal and concomitantly the application of dentin primer into root canal could improve the sealing ability of root canal obturation.

• The korean journal of orthodontics
• /
• v.40 no.5
• /
• pp.342-348
• /
• 2010

Objective: The aim of this study was to compare the shear bond strengths (SBS) of orthodontic brackets bonded to enamel with a self-etching primer after bleaching, desensitizer application and combined treatment. Methods: Forty-eight premolars were randomly divided into four groups, each with n = 12 premolar samples. The four groups were; Group1: 15% hydrogen-peroxide office bleaching agent (Illumin$\acute{e}$ Office-IO), Group 2: IO + BisBlock Oxalate Dentin-Desensitizer, Group 3: Bis Block Oxalate Dentin-Desensitizer, Group 4: No treatment (control). Twenty-four hours after bonding, the specimens were tested in SBS at a crosshead speed of 5 mm/min until the brackets debonded. The failure mode of the brackets was determined by a modified adhesive remnant index. Results: Bleaching, bleaching and desensitizer treatment, and desensitizer treatment alone all significantly reduced SBS of the orthodontic brackets ($p$ = 0.001). No statistically significant difference was found between Group 1, Group 2 and Group 3 (Group 1-Group 2, $p$ = 0.564; Group 1-Group 3, $p$ = 0.371; Group 2-Group 3, $p$ = 0.133). The predominant mode of failure for the treatment groups (Group1, Group 2 and Group 3) was at the enamel-adhesive interface leaving 100% of the adhesive on the bracket base. Conclusions: Bleaching and desensitizer treatment should be delayed until the completion of orthodontic treatment.

• Restorative Dentistry and Endodontics
• /
• v.28 no.1
• /
• pp.1-10
• /
• 2003

This study investigated the influence of IRM on marginal microleakage of 5th generation adhesives. Class V cavities with gingival margins in dentin were prepared on both buccal and lingual surfaces of 60 extract-ed human molar teeth. Prepared teeth were randomly divided into six groups. Group 1 and 4 received no temporary restoration with IRM. Group 2 and 5 were covered with IRM mixed at P/L ratio(10g/1g). Group 3 and 6 were covered with IRM mixed at P/L ratio(10g/2g). The temporary restorations were removed mechanically with an ultrasonic scaler after one-week storage in distilled water. The cavities were restored using one of two adhesives and composites ; Single Bond/Filtek Z 250(Croup 1, 2 and 3), UniFil Bond/UniFil F(Group 4, 5 and 6). Following one day storage in distilled water, the restored teeth were thermocycled for 500 cycles(between $5^{\circ}C{\;}and{\;}55^{\circ}C$) and immersed in 2 % methylene blue for dye penetration testing. The results were analysed using Kruskal-Wallis Test, Mann-Whitney and Wilcoxon signed ranked test at a significance level of 0.05. The results of this study were as follows 1. Ranking of mean microleakage scores at the enamel margins was Group 10.05) 4. At the dentin margins, the microleakage of the group not pretreated with IRM was lower than that of the group pretreated with IRM. And the microleakage of UniFil Bond was lower than that of Single Bond. 5. Compared with microleakages between the enamel and dentin margins of each groups, Group 1, 2, 3, 4, 5 and 6 at dentin margin were higher microleakage than those at enamel margin. There were significant difference between enamel and dentin microleakage of Group 2 and 3(p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.443-460
• /
• 1998

The purpose of this study was to estimate the changes of tensile bond strength according to the difference in lining materials and lining area. Seventy non-carious extracted human molars were used in the present study, and they were randomly assigned into 2 experimental groups according to the difference in lining materials. Each experimental group was subdivided into 3 groups according to the difference in lining area. Circular cavities were prepared on the dentin surface to a diameter of 1.5mm, 2.0mm, 2.5mm and the prepared cavities were filled with Fuji II LC( Glass Ionomer Cement : GIC) or Dycal. Dentin specimens without circular cavity were used as control group. The primer and bonding agent of All-Bond 2 and composite resin (Z-100, 3M Dental Products, U. S. A.) were applied to the exposed dentin surface with or without lining. Tensile bond strengths for the experimental specimens were then measured. To examine the interface between dentin and liner & between liner and composite resin, two specimens from each group were fabricated and observed under the SEM. The results were as follows. 1. Tensile bond strength for the specimens lined with GIC was higher than that for specimens lined with Dycal. However, there was no significant difference between two groups(p>0.05). 2. Tensile bond strength for the specimens lined with GIC in a diameter of 1.5mm(GIC-1.5mm lining group) was statistically higher than that for the GIC-2.0mm lining group and GIC-2.5mm lining group(p<0.05). 3. Tensile bond strength for the specimens lined with Dycal in a diameter of 2.5mm (Dycal-2.5mm lining group)was statistically lower than that for Dycal-1.5mm lining group and Dycal-2.0mm lining group(p<0.05). 4. It was possible to observe the good adhesion of the resin composite to the GIC and the presence of a fissure between GIC and dentin all along the interface. Interfacial gaps of 7.2-$72.2{\mu}m$ between GIC and dentin were observed. The interfacial gap between GIC and dentin at the cavity base was greater. However, the gap was gradually decreased toward the occlusal portion. 5. It was possible to observe the poor adhesion of the resin composite to the Dycal. The detachment of Dycal was occurred all along the composite resin-Dycal interface, and the gaps of 2.0-$30.1{\mu}m$ were formed. In all the specimens, polymerization shrinkage of resin composite caused the detachment of Dycal from the body of Dycal. At a Dycal-dentin interface. it was possible to observe the good adhesion. but poor adhesion with interfacial gap of 2.9-$26.8{\mu}m$ was observed partially.

• Restorative Dentistry and Endodontics
• /
• v.27 no.4
• /
• pp.363-369
• /
• 2002

최근에 많이 사용되어지고 있는 치과용 접착제는 산 부식 후 수분이 있는 상태에서 적용하는 wet-bonding 술식을 많이 추천하고 있다. 하지만 self-etching primer의 경우 산부식과 priming 과정이 동시에 시행되고, 제조자들은 건조된 치아표면에 적용할 것을 추천하고 있다. 그러나 건조된 정도에 대하여서는 별다른 추천사항이 없으며. 수분이 self-etching primer에 어떤 영향을 미치는지에 대하여서는 별다른 연구가 이루어져 있지 않은 상태이다. 이에 본 연구에서는 치질 삭제 후 남아있는 수분이 self-etching primer의 레진 접착 강도에 어떤 영향을 미치는 지를 알아보고자 하였다. 발거한 대구치 96개를 이용하여 물기가 있는 상태에서 #600 사포로 표면을 연마하고, 법랑질 면을 노출시킨 군과 상아질을 노출시킨 군으로 분류 후, 30분 공기 중 방치 군 (1군), 5초 공기 건조 군 (2군), 1초 공기 건조 군 (3군), 솜으로 약간의 물기를 제거한 군(blot dry) (4군) 등 총 8개의 군으로 나누었다. Self-etching adhesive system인 Clearfil SE Bond primer를 20초간 적용하고, bonding제 도포 후 10초간 광중합 시행하였다. 접착제 처리한 치아면에 몰드를 고정한 후 Clearfil AP-X 복합레진을 2mm 충전하고, 40초간 광중합을 시행하였다. 24시간 후 전단 응력 결합강도를 측정하였으며, 그 결과는 다음과 같이 나타났다. 법랑질과 상아질 모두에서, 30분 건조군과 5초 공기건조군이 1초와 blot drying 군보다 높은 결합강도를 보였으며 통계학적으로 유의한 차이를 보였다(p＜0.05). 본 실험 결과에 의하면 self-etching adhesive system을 사용함에 있어서 법랑질과 상아질군 공히 건조된 상태에서 사용하여야 하며 수분의 존재시 치아와의 결합력이 감소하는 것으로 나타났다. 따라서 임상에서 접착제의 적용시 수분의 조절에 주의하여야 할 것으로 사료된다.

• Restorative Dentistry and Endodontics
• /
• v.27 no.2
• /
• pp.150-157
• /
• 2002

One of the latest concepts in bonding are "total etch", in which both enamel and dentin are etched with an acid to remove the smear layers, and "wet dentin" in which the dentin is not dry but left moist before application of the bonding primer Ideally the application of a bonding agent to tooth structure should be insensitive to minor contamination from oral fluids. Clinically, contaminations such as saliva, gingival fluid, blood and handpiece lubricant are often encountered by dentists during cavity preparation. The aim of this study was to evaluate the effect of contamination by hemostatic agents on shear bond strength of compomer restorations. One hundred and ten extracted human maxillary and mandibular molar teeth were collected. The teeth were removed soft tissue remnant and debris and stored in physiologic solution until they were used. Small flat area on dentin of the buccal surface were wet ground serially with 400, 800 and 1200 abrasive papers on automatic polishing machine. The teeth were randomly divided into 11 groups. Each group was conditioned as follows : Group 1: Dentin surface was not etched and not contaminated by hemostatic agents. Group 2: Dentin surface was not etched but was contaminated by Astringedent$^{\circledR}$(Ultradent product Inc., Utah, U.S.A.) Group 3: Dentin surface was not etched but was contaminated by Bosmin$^{\circledR}$(Jeil Pharm, Korea.). Group 4: Dentin surface was not etched but was contaminated by Epri-dent$^{\circledR}$(Epr Industries, NJ, U.S.A.). Group 5: Dentin surface was etched and not contaminated by hemostatic agents. Group 6: Dentin sorface was etched and contaminated by Astringedent$^{\circledR}$. Group 7 : Dentin surface was etched and contaminated by Bosmin$^{\circledR}$. Group 8: Dentin surface was etched and contaminated by Epri-dent$^{\circledR}$. Group 9: Dentin surface was contaminated by Astringedent$^{\circledR}$. The contaminated surface was rinsed by water and dried by compressed air. Group 10: Dentin surface was contaminated by Bosmin$^{\circledR}$. The contaminated surface was rinsed by water and dried by compressed air. Group 11 : Dentin surface was contaminated by Epri-dent$^{\circledR}$. The contaminated surface was rinsed by water and dried by compressed air. After surface conditioning, F2000$^{\circledR}$ was applicated on the conditoned dentin surface The teeth were thermocycled in distilled water at 5$^{\circ}C$ and 55$^{\circ}C$ for 1,000 cycles. The samples were placed on the binder with the bonded compomer-dentin interface parallel to the knife-edge shearing rod of the Universal Testing Machine(Zwick Z020, Zwick Co., Germany) running at a cross head speed or 1.0 mm/min. Group 2 showed significant decrease in shear bond strength compared with group 1 and group 6 showed significant decrease in shear bond strength compared with group 5. There were no significant differences in shear bond strength between group 5 and group 9, 10 and 11.

• Restorative Dentistry and Endodontics
• /
• v.36 no.2
• /
• pp.139-148
• /
• 2011

Objectives: This study investigated the effect of the strength and wetting characteristics of adhesives on the bond strength to dentin. The experimental adhesives containing various ratios of hydrophobic, low-viscosity Bis-M-GMA, with Bis-GMA and TEGDMA, were made and evaluated on the mechanical properties and bond strength to dentin. Materials and Methods: Five experimental adhesives formulated with various Bis-GMA/Bis-MGMA/TEGDMA ratios were evaluated on their viscosity, degree of conversion (DC), flexural strength (FS), and microtensile bond strength (MTBS). The bonded interfaces were evaluated with SEM and the solubility parameter was calculated to understand the wetting characteristics of the adhesives. Results: Although there were no significant differences in the DC between the experimental adhesives at 48 hr after curing (p > 0.05), the experimental adhesives that did not contain Bis-GMA exhibited a lower FS than did those containing Bis-GMA (p < 0.05). The experimental adhesives that had very little to no TEGDMA showed significantly lower MTBS than did those containing a higher content of TEGDMA (p < 0.05). The formers exhibited gaps at the interface between the adhesive layer and the hybrid layer. The solubility parameter of TEGDMA approximated those of the components of the primed dentin, rather than Bis-GMA and Bis-M-GMA. Conclusions: To achieve a good dentin bond, a strong base monomer, such as Bis-GMA, cannot be completely replaced by Bis-M-GMA for maintaining mechanical strength. For compatible copolymerization between the adhesive and the primed dentin as well as dense cross-linking of the adhesive layer, at least 30% fraction of TEGDMA is also needed.

• Restorative Dentistry and Endodontics
• /
• v.36 no.5
• /
• pp.409-418
• /
• 2011

Objectives: The purpose of this study was to compare the microshear bond strength (${\mu}$SBS) and bonding interfaces of two-step total-etching and self-etching adhesive systems to three etch types of dentin either the acid etched, laser etched or laser and acid etched. Materials and Methods: The occlusal dentinal surfaces of thirty human molars were used. They were divided into six groups: group 1, 37% $H_3PO_4$ + Single Bond 2 (3M ESPE); group 2, Er:YAG laser (KEY Laser 3, KaVo) + Single Bond 2; group 3, Er:YAG laser + 37% $H_3PO_4$ + Single Bond 2; group 4, Clearfil SE Primer + Bond (Kuraray); group 5, Er:YAG laser + Clearfil SE Bond; group 6, Er:YAG laser + Clearfil SE Primer + Bond. The samples were subjected to ${\mu}$SBS testing 24 hr after bonding. Also scanning microscopic evaluations were made on the resin-dentin interfaces of six specimens. Results: The ${\mu}$SBS of group 2 was significantly lower than that of groups 1 and 3 in Single Bond 2 (p < 0.05). There were significant differences among the uSBS of groups 4, 5, and 6 in Clearfil SE Bond (p < 0.05). Very short and slender resin tags were observed in groups 2 and 5. Long and slender resin tags and lateral branches of tags were observed in groups 3 and 6. Conclusions: Treatment of dentin surface using phosphoric acid or self-etching primer improved the adhesion of Er:YAG lased dentin.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.1
• /
• pp.107-114
• /
• 2002

The purpose of this study was to determine and compare the shear bond strength of two self-etching primer systems to primary teeth contaminated with saliva and blood. Clearfil SE Bond and AQ Bond were evaluated. One hundred specimens were made by seventy-five deciduous teeth(fifty anterior and twenty-five posterior teeth) and divided randomly into ten groups. Small flat dentinal surfaces were prepared by grinding the buccal, lingual and labial areas. Specific surface treatments were applied to each group: (1) a self-etching primer application(control group), (2) saliva contamination followed by primer(Group I), (3) primer curing followed by saliva contamination (Group II), (4) blood contamination followed by primer(Group III), (5) primer curing followed by blood contamination(Group IV). After bonding of composite resin(Z100, 3M, USA) to contaminated sample surfaces and thermocycling(1,000 cycles), shear bond strengths were measured using Universal Testing Machine(Zwick Z020, Zwick Co., Germany). The results were as follows; 1. Group I showed lower shear bond strength than control group but no statistically significant difference was found(P>0.05). 2. Group II and blood contamination group(Group III & IV) showed significantly lower shear bond strength than control group(P<0.01). 3. The shear bond strength of Clearfil SE Bond was significantly higher than that of AQ Bond(P<0.05).

• Restorative Dentistry and Endodontics
• /
• v.33 no.5
• /
• pp.419-427
• /
• 2008

This study analyzed the influence of dental adhesive/primer on the bond strength between indirect resin composite and the resin cement. Seventy disc specimens of indirect resin composite (Tescera Dentin, Bisco) were fabricated. And bonding area of all specimens were sandblasted and silane treated for one minute. The resin cements were used with or without application of adhesive/primer to bonding area of indirect resin restoration, Variolink-II (Ivoclar-Vivadent) : Exite DSC, Panavia-F (Kuraray) : ED-Primer, RelyX Unicorn (3M ESPE) Single- Bond, Duolink (Risco) : One-step, Mulitlink (Ivoclar-Vivadent) : Multilinh Primer. Shear bond strength was measured by Instron universal testing machine. Adhesive application improved shear bond strength (p<0.05) But Variolink II and Panavia-F showed no statistically significant difference according to the adhesive application. With the above results, when resin inlay is luted by resin cement it seems that application of dental adhesive/primer is necessary in order to improve the bond strength.