• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.1
• /
• pp.89-98
• /
• 2003

Titanium requires special ceramic system for veneering. Low fusing dental ceramics with coefficients of thermal expansion matching that of titanium have been developed. The purpose of this study was determine the bond strengths between cast and noncast pure titanium and two commercial titanium porcelains, and to compare the results with a conventional nickel-chromium alloy-ceramic system. The bond strengths were determined using a 3-point flexure test. Three-point flexure specimens $25{\times}3{\times}0.5mm$ were prepared After removal of ${\alpha}-case$ layer, they were veneered with $8{\times}3{\times}1mm$ of ceramics at the center of the bar. Specimens were tested in a universal testing machine. Within the limits of this study, the following conclusions were drawn: 1. The bond strengths between pure titanium and two commercial porcelains exceeded th lower limit of the bonding strength value in ISO 9693(25MPa). 2. There was no significant difference between cast and noncast titanium-porcelain bonds. 3. There was no significant difference between two commercial titanium porcelains. 4. The bond strengths of the titanium-porcelain systems ranged from 73% to 79% of that of the Ni-Cr-conventional porcelain system.

• Journal of Technologic Dentistry
• /
• v.25 no.1
• /
• pp.41-62
• /
• 2003

In this research, we manufactured the paste opaque porcelains using Propylene Glycol (PG) and Buthylene Glycol (BG) as a solvent, and compared the composition of solvents, the coefficient of thermal expansion, the particle size distribution, the viscosity and bonding strength to metal, and the tone with those of the commercial products(Duceram Plus, Duceram GmbH; VMK 95, Vita Co.; Noritake EX-3, Noritake Co.)used in the clinical field. The results of the research were as follows: 1. The result of solvent analysis indicated that the solvents included in the paste opaque porcelains of the control group were mainly composed of Glycols. 2. From the Coefficient of thermal expansion measurement, we drew out the following results; testing group: $14.0\times10^{-6}/^{\circ}C$, Duceram Plus: $13.9\times10^{-6}/^{\circ}C$, VMK 95: $14.3\times10^{-6}/^{\circ}C$, and Noritake EX-3: $13.3\times10^{-6}/^{\circ}C$. 3. Seen from the result of particle size distribution measurement, the experimental group was similar to the control group in 1$\mu m$ below, but the experimental group marked the highest distribution of 61% in the case of between 1$\mu m$ and 5$\mu m$. Between 5$\mu m$ and 10$\mu m$, they showed relatively similar distribution, and Noritake EX-3 was turned out the highest distribution of 29% in 10$\mu m$ above. 4. From the result of viscosity measurement, Duceram plus showed the highest viscosity throughout all the measurements followed by Noritake Ex-3, experimental group and VMK 95 in decreasing order. 5. The result of bonding strength measurement was EX 35.53 $\beta\acute{A}$, DU 40.88 $\beta\acute{A}$, VM 39.43 $\beta\acute{A}$, and NO 35.39 $\beta\acute{A}$, and no significant difference was found between the experimental group and the control groups(P>0.05). 6. The measurement of the tone indicated that the $L^*$ value of the experimental group was 86.89 0.63 in average, which is higher than the control group in its brightness. In the case of the $a^*$ value, Duceram Plus, VMK 95 and EX-3 showed positive value, whereas the testing group was turned out negative value. In $b^*$ value, Duceram Plus proved the highest. From the results of this research, the paste opaque porcelains using Propylene Glycol (PG) and Buthylene Glycol (BG) as a solvent did not make differences from the commercial products that are actually used in the clinical fields. Therefore, it is possible to utilize Propylene Glycol (PG) and Buthylene Glycol (BG) for the paste opaque porcelains of P.F.M crown. It is also recommended that further researches concerning the compositions and forms of powder, the types of organic solvent components and the ratio of mixture proceeded in order to improve the level of productivity in the future.

• Journal of Technologic Dentistry
• /
• v.29 no.2
• /
• pp.173-180
• /
• 2007

There was a great problem about the deposition between materials of a different kind at the beginnings of the introduction of porcelains, however, thereafter the deposition efficiency was settlded to the sufficient level of all user thanks to effort to have studied by many scholars and clinical authorities. But in a clinical process, as the difference of designs has an effect on fractures of porcelains, this researcher divided them into 4 groups of A: 1 mm, B: 2 mm, C: 3 mm, and D: 4 mm, and made 40 pieces to each 10 as the test samples to consider a length axis of tooth for studies in accordance with a position of a finishing line to meet between porcelain and metal at the contact point at the adjacent side to a metal porcelain. The sample materials are those to be use at the open market and the test samples wer completed by the same manufacturing technique to that of existent metal porcelain tube. s a result of the strength test on fractures, the average value is as in the following, A: 1 mm - 8.5bar, B: 2 mm - 10.5bar, C: 3 mm - 14.3bar, and D: 4 mm - 15.0bar. In case of the metal porcelain tube, the more faraway to process parts of metal and porcelain from the contact point of adjacent side has the stronger strength of fractures, Accordingly, the research shows that it had better to keep off more than 3 to consider a ledngth axis of tooth.

• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.3
• /
• pp.75-86
• /
• 1991

Ion exchange strengthening is a chemical process whereby large alkali ions(such as potassium) are substituted for smaller ions(sodium) within the surfaces of glasses and ceramics, thereby reducing the thermal expansion coefficient of this surface region, and creating beneficial state of compressive stress within the near surface region. The purpose of this study was to determine the effects of ion exchange and etching treatments on the strength of some dental porcelains. Two feldspathic dental porcelains(Vitadur-N, G-Cera) were used in this study. A commercial ion exchange paste and etching gel containing 8% hydrofluoric acid were used for surface conditioning. Transverse strength was measured using a universal testing machine and the technique of EPMA(electron probe micro analysis) was used to access the potassium contents. The results were as follows: 1. Improvement in strength was only obtained by treating the surface placed in tension. 2. No changes in the dimensions of the treated specimens were detected when samples were measured with a micrometer. 3. There was significant increase in transverse strength of G-Cera IV group treated with etching and ion exchange, compared with G-Cera II group only treated with ion exchange. 4. From the results of EPMA test, increase in potassium contents was observed on the surface treated with ion exchange paste.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.4
• /
• pp.309-316
• /
• 2014

PURPOSE. The color of the ceramic restorations is affected by various factors such as brand, thickness of the layered the ceramic, condensation techniques, smoothness of surface, number of firings, firing temperature and thickness of dentin. The aim of this study was to evaluate the color change and surface roughness in dental porcelain with different thicknesses during repeated firings. MATERIALS AND METHODS. Disc-shaped (N=21) metal-ceramic samples (IPS Classic; Ivoclar Vivadent; Shaar, Liechtenstein) with different thickness were exposed to repeated firings. Color measurement of the samples was made using a colorimeter and profilometer was used to determine surface roughness. ANOVA and Tukey tests with repeated measurements were used for statistical analysis. RESULTS. The total thickness of the ceramics which is less than 2 mm significantly have detrimental effect on the surface properties and color of porcelains during firings (P<.05). CONCLUSION. Repeated firings have effects on the color change and surface roughness of the dental ceramics and should be avoided.

• The Journal of Advanced Prosthodontics
• /
• v.3 no.4
• /
• pp.221-228
• /
• 2011

PURPOSE. Veneering porcelain might be delaminated from underlying zirconia-based ceramics. The aim of this study was the evaluation of the effect of different surface treatments and type of zirconia (white or colored) on shear bond strength (SBS) of zirconia core and its veneering porcelain. MATERIALS AND METHODS. Eighty zirconia disks (40 white and 40 colored; 10 mm in diameter and 4 mm thick) were treated with three different mechanical surface conditioning methods (Sandblasting with $110{\mu}m$ $Al_2O_3$ particle, grinding, sandblasting and liner application). One group had received no treatment. These disks were veneered with 3 mm thick and 5 mm diameter Cercon Ceram Kiss porcelain and SBS test was conducted (cross-head speed = 1 mm/min). Two and one way ANOVA, Tukey's HSD Past hoc, and T- test were selected to analyzed the data (${\alpha}=0.05$). RESULTS. In this study, the factor of different types of zirconia ceramics (P=.462) had no significant effect on SBS, but the factors of different surface modification techniques (P=.005) and interaction effect (P=.018) had a significant effect on SBS. Within colored zirconia group, there were no significant differences in mean SBS among the four surface treatment subgroups (P=0.183). Within white zirconia group, "Ground group" exhibited a significantly lower SBS value than "as milled" or control (P=0.001) and liner (P=.05) groups. CONCLUSION. Type of zirconia did not have any effect on bond strength between zirconia core and veneer ceramic. Surface treatment had different effects on the SBS of the different zirconia types and grinding dramatically decreased the SBS of white zirconia- porcelain.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.6
• /
• pp.427-433
• /
• 2014

PURPOSE. Surface color is one of the main criteria to obtain an ideal esthetic. Many factors such as the type of the material, surface specifications, number of firings, firing temperature and thickness of the porcelain are all important to provide an unchanged surface color in dental ceramics. The aim of this study was to evaluate the color changes in dental ceramics according to the material type and glazing methods, during the multiple firings. MATERIALS AND METHODS. Three different types of dental ceramics (IPS Classical metal ceramic, Empress Esthetic and Empress 2 ceramics) were used in the study. Porcelains were evaluated under five main groups according to glaze and natural glaze methods. Color changes (${\Delta}E$) and changes in color parameters (${\Delta}L$, ${\Delta}a$, ${\Delta}b$) were determined using colorimeter during the control, the first, third, fifth, and seventh firings. The statistical analysis of the results was performed using ANOVA and Tukey test. RESULTS. The color changes which occurred upon material-method-firing interaction were statistically significant (P<.05). ${\Delta}E$, ${\Delta}L$, ${\Delta}a$ and ${\Delta}b$ values also demonstrated a negative trend. The MC-G group was less affected in terms of color changes compared to other groups. In all-ceramic specimens, the surface color was significantly affected by multiple firings. CONCLUSION. Firing detrimentally affected the structure of the porcelain surface and hence caused fading of the color and prominence of yellow and red characters. Compressible all-ceramics were remarkably affected by repeated firings due to their crystalline structure.

• The Journal of Korean Academy of Prosthodontics
• /
• v.32 no.1
• /
• pp.47-76
• /
• 1994

This study was carried out to evaluate the effect of the crack propagation characteristics and bond stress of ceramo-metal system. In order to characterize the crack propagation, the static crack propagation stored in $37^{\circ}C$ distilled water of two commerical porcelains and the dynamic crack propagation under cyclic flexure load of ceramo-metal system were examined. In order to characterize the bond stress, the shear bond test, the 3-point flexure bond test, and the finite element stress analysis of ceramo-metal system were conducted. The results obtained were as follows : 1. Bulk densities and Young's moduli of opaque porcelains increased with repeated firing. 2. Maximum fracture toughness during 4 firing cycles showed at the group of 4 firing cycles in Ceramco porcelain and 2 firing cycles in Vita porcelain. 3. Shear bond strength and flexure bond strength of Ceramco-Verabond specimen were larger than those of Ceramco-Degudent G specimen (p<0.05). 4. Interfacial stresses under three point flexure bond test were concentrated at the edges of ceramometal system. 5. When a cyclic flexure load was applied, the crack growth rate of porcelain surface of ceramometal specimens was decreased as load cycles increased.

• Journal of the Korean Academy of Esthetic Dentistry
• /
• v.24 no.2
• /
• pp.101-121
• /
• 2015

Zirconia polycrystalline (Y-TZP) showed better mechanical properties and superior resistance to fracture than other conventional dental ceramics. Zirconia-based ceramics have been successfully introduced into the clinic to fabricate fixed dental prostheses (FDPs), along with a dental computer-aided/computer-aided manufacturing (CAD/CAM) system. It has been clinically available as an alternative to the metal framework for fixed dental prostheses (FDPs). The most frequent clinical complication with zirconia-based FDPs was chipping of the veneering porcelain that was affected by many factors. Another option was full-contour zirconia FDPs using high translucent zirconia. Full-contour zirconia FDPs has many clinical advantages but it caused concern about the wear of antagonist enamel, because the hardness of Y-TZP was over double that of porcelain. However, many articles demonstrates that highly polished zirconia yielded lower antagonist wear compared with porcelains. In this article (1) advantages of full zirconia restorations, (2) clinical applications of zirconia restorations, (3) abutment preparation, (4) surface finish of zirconia restoration and antagonist enamel wear, (5) bond of zirconia with resin-based luting agents, (6) communication in clinical & lab.procedures for full zirconia restorations are reviewed.

• The Journal of Korean Academy of Prosthodontics
• /
• v.19 no.1
• /
• pp.47-54
• /
• 1981

Dental porcelains are widely used for restorative material because of its excellent esthetic property. But according to contact with natural teeth or metal in oral cavity, the porcelain may be worn and may effect on masticatory physiology and prosthetic function. The purpose of this experiment was to study on wear of porcelain surface which treated in different method. Using the abrasion device which was designed and constructed by myself, the different porcelain surface were abraded by gold alloy, nickel-chrome alloy and natural teeth in order to compare roughness. Results were as follows. 1. The group of porcelain abraded by gold alloy showed less surface roughness change (t=2.92, p<0.05), and the group of porcelain abraded by natural teeth had high surface roughness. change (t=6.84, p<0.05). 2. According to the method of surface treatment, the surface roughness were very significant (F=9.12, p<0.05). 3. After abrading, the porcelain surface roughness change was very significant (F=54.49, p<0.05). 4. There was no significant between surface treatment method and the kind of abrading materials. (F=1.01, p>0..05). 5. The group of natural glazing had the most smooth surface ($2.1{\pm}1.13{\mu}m$).