• Journal of the Korean institute of surface engineering
• /
• v.40 no.6
• /
• pp.245-249
• /
• 2007

Amorphous IZO films were deposited on PET substrate by DC magnetron sputtering without substrate heating. In order to investigate effect of reactive gas addition on film properties, 0.2-0.4% of $H_2$ or $O_2$ gas was introduced during the deposition. Deposited IZO films were evaluated with mechanical property, electrical property, and water permeability. In the case of $H_2$ gas addition, mechanical property showed clear degradation compared to $O_2$ gas. In the case of $O_2$ gas, water permeability of the IZO film was increased compared to $H_2$ gas which could be attributed to the low adhesion of the film caused by bombardment of high energy negative oxygen ion. As a result, it is confirmed that water permeability of the film could be strongly affected by adhesion of the film.

• Journal of the Korean institute of surface engineering
• /
• v.55 no.2
• /
• pp.70-76
• /
• 2022

In this paper, we compared the properties of the chromium nitride (CrN) films prepared by inductively coupled plasma magnetron sputtering (ICPMS). As a comparison, CrN film prepared by a direct current magnetron sputtering (dcMS) is also studied. The crystal structure, surface and cross-sectional microstructure and composite properties of the as-deposited CrN films are compared by x-ray diffraction, field emission scanning electron microscopy, nanoindentation tester and corrosion resistance tester, respectively. It is found that the as-deposited CrN films by ICPMS grew preferentially on (200) plane when compared with that by dcMS on (111) plane. As a result, the films deposited by ICPMS have a very compact microstructure with high hardness: the nanoindentation hardness reached 19.8 GPa and 13.5 GPa by dcMS, respectively. Besides, the residual stress of CrN films prepared by ICPMS is also relatively large. After measuring the corrosion resistance, the corrosion current of films prepared by ICPMS was three order of magnitude smaller than that of CrN films deposited by dcMS.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.1
• /
• pp.74-83
• /
• 2001

In this study, the optimum structure of a magnetic thin film inductor was designed for application of DC-DC converters. The Ni$\sub$81/Fe$\sub$19/ (at%) alloy was selected as a high-frequency($\geq$MHz) magnetic thin film magnetron sputtering system. As-deposited NiFe thin films show similar magnetic properties compared to bulk NiFe alloys, indicating that they have a good film quality. The optimum design of dolenoid-type magnetic thin film inductors was performed utilizing a Maxwell computer simulator (Ansoftt HFSS V7.0 for PC) and parameters obtained from the magnetic properties of magnetic core materials selected. The high-frequency characteristics of the inductance(L) and quality factor(Q) obtained for the designed inductors through simulation agreed well with those obtained by theoretical calculations, confirming that the simulated result is realistic. The optimum structure of high-performance (Q$\geq$60, L = 1${\mu}$H, efficiency $\geq$90%), high-frequency ($\geq$5MHz), and solenoid-type magnetic thin film inductors was designed successfully.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.92-92
• /
• 2009

In the present study, impurities doped GxZO thin films were prepared by dc-magnetron sputtering on glass substrate and effect of processing variables on the growth behavior was investigated.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2008.10a
• /
• pp.416-419
• /
• 2008

In this study, we report on the characteristics of Aldoped ZnO (AZO) co-sputtered indium tin oxide (ITO) films prepared by dual target direct current (DC) magnetron sputtering at room temperature for organic light emitting diodes (OLEDs). The electrical and optical properties of co-sputtered IAZTO electrode were critically dependent on the DC power of AZO. Furthermore, the characteristics of co-sputtered IAZTO electrode were influenced by rapid thermal annealing temperature.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.163-164
• /
• 2009

dc unbalanced magnetron sputtering 방법으로 superhard quarternary Ti-B-C-N films을 합성하였다. XPS, XRD 분석 결과 Ti-B-C-N films은 solid-solution (Ti,C,N)$B_2$와 Ti(C,N) 결정이 amorphous BN에 분포된 나노 복합체를 형성하였다. 여기에서는 film내 N의 양에 따라 강도가 증가하다가 그 후 감소하는 경향을 보였다.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.3
• /
• pp.149-154
• /
• 2000

Bi-layer Mo films were deposited on soda-lime glass substrates using DC magnetron supttering. Increasing gas pressure, the resistivity varied from $1\times10^{-5}\; to\; 8.3\times10^{-3}\; \Omega.cm$. Furthermore, stress direction yielded compressive-to-tensile transition stress curves. The micro-structure of the compressively-stressed film which had poor adhesion consists of tightly packed columns, but of the tensile-stressed films had less dense structure. Under all gas pressure conditions, Mo films exhibited distinctly increasing optical reflection with decreasing gas pressure. The expansion of (110) peak width with the gas pressure meant the worse crystalline growth. The impurity levels in the Mo film exhibited highly concentrated Na, Se and O elements due to less dense micro-structure. The degree of Na diffusion depends on the type of the glass substrate used and the nature of the Mo film.

• Journal of the Korean institute of surface engineering
• /
• v.46 no.2
• /
• pp.55-60
• /
• 2013

Superhard TiN coatings were fabricated by DC and ICP (inductively coupled plasma) assisted magnetron sputtering techniques. The effect of ICP power, ranging from 0 to 300 W, on coating microstructure, preferred orientation mechanical properties were systematically investigated with HR-XRD, SEM, AFM and nanoindentation. The results show that ICP power has a significant influence on coating microstructure and mechanical properties of TiN coatings. With the increasing of ICP power, coating microstructure evolves from the columnar structure of DC process to a highly dense one. Grain sizes of TiN coatings were decreased from 12.6 nm to 8.7 nm with increase of ICP power. The maximum nanohardness of 67.6 GPa was obtained for the coatings deposited at ICP power of 300 W. Preferred orientation in TiN coatings also vary with ICP power, exerting an effective influence on film nanohardness.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.2
• /
• pp.125-133
• /
• 1999

Fluorine-doped $SnO_2$ thin films were deposited on soda-lime glass substrates by reactive DC magnetron sputtering method. Crystallinity as well as electrical and optical properties of $SnO_2$ : F thin film were investigated as the variations of deposition conditions such as substrate temperature, DC Power, $O_2$ gas pressure, $SF_6$ gas pressure. $SnO_2$ : F thin film deposited with 5% $SF_6$ gas pressure showed electrical resistivities of $2.5\times10^{-3}$cm with the average optical transparency (about 80%) These electrical and optical properties were found to be related to the crystallinity of $SnO_2$ : F thin films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.83-87
• /
• 2003

Thin films of amorphous carbon (a-C) generally combine high wear resistance with low friction coefficients and a-C films have widespread applications as protective coatings and passivation of electrical circuit and insulating layer. In this work we deposited the amorphous carbon (a-C) films on silicon substrate with a high rate DC magnetron sputtering system. It is obtained parameters on the deposition rate and physical properties of a-C films using a wide range of Ar gas pressure and DC power. The physical properties of the films were analyzed by Nanoindenter and AFM (Atomic Force Microscopy), The electrical properties were investigated by electrical conductivity measurement.