• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.2
• /
• pp.79-88
• /
• 1993

The static creep mechanism and behaviour of Al-Zn-Mg alloy have been investigated under condition of constant stress tension creep test in the temperature and stress range of $170-260^{\circ}C$ and 5-12.5 $kg/mm^2$ respectively. The experimental result are follows : The stress exponent value for creep was observed to about 7.3-6.43 and the activation energy for creep deformation was 44-41 kcal/mol. Larson-Miller parameter P for the crept specimens under the creep condition was obtained as P = (T + 460) (log $t_r$ + 8.6). Emperical equation for the creep rate was obtained by the computer simulation as follows. $${\varepsilon}\;=\;\exp[(-5.519{\times}10^{-4}{\sigma}+2.33{\times}10^{-2})T-6.98{\sigma}+18.295]{\times}{\sigma}^{-0.0142+10.18}\exp[\frac{(-6{\sigma}+47.8)1000}{RT}]$$ Fracture was dominated by intergranular mechanism over the experimental range.

• Journal of the Korean Society of Mechanical Technology
• /
• v.13 no.4
• /
• pp.125-130
• /
• 2011

Technological mode progress demands the use of materials at high temperature and pressure. Constant load creep tests have been carried out over the range of stresses at high temperatures. One of the most critical factors in considering such applications as the most critical one is the creep behavior. In order to investigate the creep behavior in this study, the stress exponents during creep were determined over the temperature range of $275^{\circ}C$ to $325^{\circ}C$ and the stress range of 36MPa to 72MPa. The applicability of modified Monkman-Grant relationship was also discussed.

• Journal of Ocean Engineering and Technology
• /
• v.22 no.6
• /
• pp.52-57
• /
• 2008

The short-term high temperature creep rupture behavior of Ni-based Alloy718 steel was investigated at the elevated temperatures range of 550 to $700^{\circ}C$ under constant stress conditions. The creep rupture characteristics such as creep stress, rupture time, steady state creep rate, and initial strain were evaluated. Creep stress has a quantitative correlation between creep rupture tim and steady state creep rate. The stress exponents (n, m) of the experimental data at 550, 600, 650 and $700^{\circ}C$ were derived as 33.5, -24.9, 26.1, -21.2, 16.8, -12.8 and 10, -8.2, respectively. The stress exponent decreased with increasing creep temperature. The creep lift prediction was derived by the Larson-Miller parameter (LMP) method and the resultant equation was obtained as follows: T($logt_r$+20)=-0.00252 ${\sigma}^2$-1.377${\sigma}$+-22718.

• Journal of the Korean Society of Safety
• /
• v.9 no.4
• /
• pp.29-41
• /
• 1994

High temperature tensiles tests, steady state creep tests, internal stress tests and creep rupture tests using Al 7075 alloy were performed over the temperature range of 9$0^{\circ}C$~50$0^{\circ}C$ and stress range of 0.64~17.2(kgf/$\textrm{mm}^2$) in order to investigate the creep behavior and predict creep rupture life From the apparent activation energy Qc and the applied stress exponent n measured, at the temperature range of 9$0^{\circ}C$~l2$0^{\circ}C$, the creep deformation seemed to be controlled by cross slip. On the other hand at the temperature of 20$0^{\circ}C$~23$0^{\circ}C$ the creep deformation seemed to be controlled by dislocation climb but at 47$0^{\circ}C$~50$0^{\circ}C$, by diffusion creep. And the rupture life(t$_{f}$) might be represented by anthermal process attributed to the difference of the applied stress dependence of Internal stress and the ratio of the Internal stress to the applied stress, the thermal activated process attributied to the temperature dependence of the internal stress. Also the ratio between stress dependence of primary creep rate and that of minimum creep rate was measured 0.46, the minimum creep rate is expected to be appromately obtained from master creep curve including the relationship primary creep rate and minumum creep rate. Finally the relationship new rupture parameter and logarithmic stress was represented with including the ratio between the dependence of primary creep rate and that of minimum creep rate, using the new rupture parameter the rupture life predition is exactly expected.d.

• 대한공업교육학회지
• /
• v.35 no.2
• /
• pp.204-223
• /
• 2010

The purpose of this study was to investigate the high temperature creep behavior of anisotropic Zr-2.4%Nb alloy which includes the hydride. To minimize the effect of the anisotropy and to achieve the bi-axial stress condition, SP creep test was performed using the Zr alloys which have the 50 ppm, 100 ppm and 200 ppm hydride. Each SP creep curve was obtained and compared. While the creep degradation of 50 ppm and 100 ppm hydride specimens was clearly found, the degradation of 200 ppm was not cleared. By the comparison of SP creep constant and stree exponent, this fact was confirmed. As the degradation of 50 ppm and 100 ppm hydride was processed, the SP creep constant was decreased and the stress exponet was increased. However, while the SP creep constant of 200 ppm hydride was decreased, the stree exponent was decreased. Finally, it was confirmed that the creep degradation of 200 ppm was not found. In conclusion, the hydride was the major parameter to control the hight temperature creep degradation of Zr alloy.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2008.11a
• /
• pp.555-556
• /
• 2008

• Design & Manufacturing
• /
• v.2 no.6
• /
• pp.43-48
• /
• 2008

Magnesium alloys have given high attention to the industry of light-weigh as automobile and electronics with aluminium, titanium and composite alloys due to their high strength, low specific density and good damping characteristics. But the magnesium contained structures under high temperature have the problems related to creep deformation and rupture life, which is a reason of developing the new material against creep deformation to use them safely. The purpose of this study is to predict the creep deformation mechanism and rupture time of AZ31 magnesium alloy. For this, creep tests of AZ31 magnesium alloy were done under constant creep load and temperature with the equipment including automatic temperature controller with acquisition computer. The apparent activation energy Qc, the applied stress exponent n and rupture life have been determined over the temperature range below 0.5Tm and stress range of 109~187MPa, respectively, in order to investigate the creep behavior. AZ31 Magnesium alloy identify the activation energy for creep deformation and the stress dependence to creep rate at below 0.5Tm, and then investigate the mechanism for creep deformation and creep rupture life of AZ31 Magnesium alloy.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.9
• /
• pp.851-857
• /
• 2015

In this paper, we estimate the time-dependent C(t) integrals under elastic-plastic-creep conditions. Finite-element (FE) transient creep analyses have been performed for single-edge-notched-bend (SEB) specimens. We investigate the effect of the initial plasticity on the transient creep by systematically varying the magnitude of the initial step load. We consider both the same stress exponent and different stress exponents in the power-law creep and plasticity to elastic-plastic-creep behavior. To estimate the C(t) integrals, we compare the FE analysis results with those obtained using formulas. In this paper, we propose a modified equation to predict the C(t) integrals for the case of creep exponents that are different from the plastic exponent.

• Korean Journal of Materials Research
• /
• v.26 no.7
• /
• pp.370-375
• /
• 2016

Tensile tests and creep tests were carried out at high temperatures on an Al-$Al_4C_3$ alloy prepared by mechanical alloying technique. The material contains about 2.0% carbon and 0.9% oxygen in mass percent, and the volume fractions of $Al_4C_3$ and $Al_2O_3$ particles are estimated at 7.4 and 1.4%, respectively, from the chemical composition. Minimum creep rate decreased steeply near two critical stresses, ${\sigma}_{cl}$ (the lower critical stress) and ${\sigma}_{cu}$ (the upper critical stress), with decreasing applied stress at temperatures below 723 K. Instantaneous plastic strain was observed in creep tests above a critical stress, ${\sigma}_{ci}$, at each test temperature. ${\sigma}_{cu}$ and ${\sigma}_{ci}$ were fairly close to the 0.2% proof stress obtained by tensile tests at each test temperature. It is thought that ${\sigma}_{cl}$ and ${\sigma}_{cu}$ correspond to the microscopic yield stress and the macroscopic yield stress, respectively. The lower critical stress corresponds to the local yield stress needed for dislocations to move in the soft region within subgrains. The creep strain in the low stress range below 723 K arises mainly from the local deformation of the soft region. The upper critical stress is equivalent to the macroscopic yield stress necessary for dislocations within subgrains or in subboundaries; this stress can extensively move beyond subboundaries under a stress above the critical point to yield a macroscopic deformation. At higher temperatures above 773 K, the influence of the diffusional creep increases and the stress exponent of the creep rate decreases.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.9 s.252
• /
• pp.1034-1040
• /
• 2006

Due to the need of increasing thermal efficiency, supercritical pressure and temperature have been utilized in power plants. It is well known that 9Cr1Mo steel is suitable fer use in power plants operating at supercritical conditions. Therefore, to ensure the safety and the soundness of the power plant, creep characterization of the steel is important. In this study, the creep characterization of the gCr1Mo steel using small punch creep(SP-Creep) test has been described. The applied load and the central displacement of the specimen in SP-Creep test have been converted to bearing stress and strain of uc, respectively. The converted SP-Creep curves clearly showed the typical three-stage behavior of creep. The steady-state creep rate and the rupture time of the steel logarithmically changed with the bearing stress and satisfied the Power law relationship. Furthermore, the Larson-Miller parameter of the SP-Creep test agreed with that of the tensile creep test. From the comparison with low Cr-Mo steels, the creep characteristics of 9Cr1Mo steel proved to be superior. Thus, it can be confirmed that the 9Cr1Mo steel is suitable for supercritical power plant.